CN103600451B - 以再生塑料为原料制备建筑、包装模板的方法 - Google Patents

以再生塑料为原料制备建筑、包装模板的方法 Download PDF

Info

Publication number
CN103600451B
CN103600451B CN201310582054.9A CN201310582054A CN103600451B CN 103600451 B CN103600451 B CN 103600451B CN 201310582054 A CN201310582054 A CN 201310582054A CN 103600451 B CN103600451 B CN 103600451B
Authority
CN
China
Prior art keywords
raw material
material prepares
shaping
regenerated plastics
sawdust
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310582054.9A
Other languages
English (en)
Other versions
CN103600451A (zh
Inventor
赵强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310582054.9A priority Critical patent/CN103600451B/zh
Publication of CN103600451A publication Critical patent/CN103600451A/zh
Application granted granted Critical
Publication of CN103600451B publication Critical patent/CN103600451B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

以再生塑料为原料制备建筑、包装模板的方法，其步骤如下：将塑料废弃物粉碎成片径≤1cm的碎片，制得塑料碎屑；取锯末，或将树枝、树叉打碎至片径≤1cm的木碎屑；将木碎屑或锯末与塑料碎屑按照重量比2：1～1;1混合搅拌；将混合物装入模具，模具内上、下表面放置牛皮纸或铝塑膜，在200～400℃下加热，100Mpa～200Mpa下加压，10分钟～30分钟后进行冷却定型，栽边，制成厚度为1cm～10cm的模板。有益效果是：原料易得，生产成本低；制作工艺简单，利用热压成型，无需使用粘合剂，产品强度高，耐水、耐酸碱，各种技术指标优于木制胶合板，重复使用次数多，并且可回收利用。

Description

以再生塑料为原料制备建筑、包装模板的方法
技术领域
本发明涉及一种以再生塑料为原料制备建筑、包装模板的方法。
背影技术
现有的建筑、包装模板用原木加工成木皮，用尿酫树脂粘合而成。存在的问题是：浪费资源，强度差，自然环境下受潮、淋水后造成开裂，使用次数只有3～5次。
发明内容
本发明要解决的技术问题是提供一种以再生塑料为原料制备建筑、包装模板的方法，利用废塑料，原料易得，成本低，制作简单、强度高，耐水、耐酸碱，重复使用次数多，可回收利用。
本发明涉及的以再生塑料为原料制备建筑、包装模板的方法，其步骤如下：
1、将塑料废弃物粉碎成片径≤1cm的碎片，制得塑料碎屑；
2、取锯末，或将树枝、树叉打碎至片径≤1cm的木碎屑；
3、将木碎屑或锯末与塑料碎屑按照重量比2：1～1;1混合搅拌；
4、成型
将混合物装入模具，模具内上、下表面放置牛皮纸或铝塑膜，在200～400℃下加热，100Mpa～200Mpa下加压，10分钟～30分钟后进行冷却定型，栽边，制成厚度为1cm～10cm的模板。
成型时在牛皮纸内表面铺设废旧聚丙烯包装袋，以使模板表面平整。
所述碎片为圆片、正方形片或长方形片。
所述废塑料是聚乙烯、聚氯乙烯、地膜和大棚膜废弃物中一种或二种或三种或四种。
成型时冷却温度为5～15℃。
本发明的有益效果是：利用废塑料和锯末或树枝、树叉，原料易得，生产成本低；制作工艺简单，利用热压成型，无需使用粘合剂，产品强度高，耐水（用水浸泡120小时不变形不开裂）、耐酸碱（分别用5%硫酸、5%的碱水浸泡120小时不变形不开裂），各种技术指标优于木制胶合板，重复使用次数多，并且可回收利用。
具体实施方式
实施例1
1、将塑料废弃物粉碎成圆片，所述塑料废弃物为聚乙烯、聚氯乙烯、地膜、大棚膜废弃物中一种，本实施例选用聚乙烯废弃物，所述圆片的直径≤1cm，制得塑料碎屑；
2、取锯末；
3、将锯末与塑料碎屑按照重量比2：1混合，搅拌；
4、成型
将混合物装入模具，模具内上、下表面放置牛皮纸，在200℃下加热，100Mpa下加压，30分钟后进行冷却定型，所述冷却温度为5℃，并利用循环水冷却；栽边，制成厚度为1cm的模板。
实施例2
1、将塑料废弃物粉碎成正方形片，所述塑料废弃物为聚乙烯、聚氯乙烯、地膜和大棚膜废弃物中的二种或三种，本实施例选用聚乙烯废弃物和聚氯乙烯废弃物，所述正方形片的边长≤1cm，制得塑料碎屑；
2、将树枝、树叉打碎至片径≤1cm的木碎屑；
3、将木碎屑与塑料碎屑按照重量比1：1混合，搅拌；
4、成型
将混合物装入模具，模具内上、下表面放置牛皮纸，在400℃下加热，200Mpa下加压，10分钟后进行冷却定型，所述冷却温度为15℃。并利用循环水冷却；栽边，制成厚度为10cm的模板。
实施例3
1、将塑料废弃物粉碎成长方形片，所述塑料废弃物为聚乙烯、聚氯乙烯、地膜和大棚膜的废弃物，所述长方形片的长边长度≤1cm，制得塑料碎屑；
2、取锯末；
3、将锯末与塑料碎屑按照重量比1.5：1混合，搅拌;
4、成型
将混合物装入模具，模具内上、下表面放置牛皮纸，在300℃下加热，150Mpa下加压，20分钟后进行冷却定型，所述冷却温度为10℃。并利用循环水冷却；栽边，制成厚度为5cm的模板。
实施例4
将树枝、树叉打碎至直径≤1cm的木碎屑代替锯末，其它同实施例1。
实施例5
利用锯末代替将木碎屑，其它同实施例2；
实施例6
将树枝、树叉打碎至直径≤1cm的木碎屑代替锯末，其它同实施例3。
实施例7
成型时用铝塑膜代替牛皮纸，其它同实施例1-实施例6。
实施例8
成型时，在牛皮纸内表面铺设废旧聚丙烯包装袋，其它同实施例1-实施例6。
实施例9
成型时，在铝塑膜内表面铺设废旧聚丙烯包装袋，其它同实施例7。
实施例1-实施例9制得的模板，用水浸泡120小时不变形、不开裂，用5%硫酸浸泡120小时不变形、不开裂，用5%碱水浸泡120小时不变形、不开裂。

Claims (5)

1.以再生塑料为原料制备建筑、包装模板的方法，其特征是步骤如下：
（1）、将塑料废弃物粉碎成片径≤1cm的碎片，制得塑料碎屑；
（2）、取锯末，或将树枝、树叉打碎至片径≤1cm的木碎屑；
（3）、将木碎屑或锯末与塑料碎屑按照重量比2：1～1;1混合搅拌；
（4）、成型
将混合物装入模具，模具内上、下表面放置牛皮纸或铝塑膜，在300℃或400℃下加热，100Mpa～200Mpa下加压，10分钟～30分钟后进行冷却定型，栽边，制成厚度为1cm～10cm的模板。
2.根据权利要求1所述的以再生塑料为原料制备建筑、包装模板的方法，其特征是成型时在牛皮纸内表面铺设废旧聚丙烯包装袋。
3.根据权利要求1所述的以再生塑料为原料制备建筑、包装模板的方法，其特征是所述碎片为圆片、正方形片或长方形片。
4.根据权利要求1所述的以再生塑料为原料制备建筑、包装模板的方法，其特征是所述废塑料是聚乙烯、聚氯乙烯、地膜和大棚膜废弃物中一种或二种或三种或四种。
5.根据权利要求1所述的以再生塑料为原料制备建筑、包装模板的方法，其特征是成型时冷却温度为5℃～15℃。
CN201310582054.9A 2013-11-20 2013-11-20 以再生塑料为原料制备建筑、包装模板的方法 Expired - Fee Related CN103600451B (zh)