CN104151679A - 一种环保塑料薄膜 - Google Patents
一种环保塑料薄膜 Download PDFInfo
- Publication number
- CN104151679A CN104151679A CN201410436099.XA CN201410436099A CN104151679A CN 104151679 A CN104151679 A CN 104151679A CN 201410436099 A CN201410436099 A CN 201410436099A CN 104151679 A CN104151679 A CN 104151679A
- Authority
- CN
- China
- Prior art keywords
- plastic film
- parts
- environmentally
- friendly plastic
- film according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种环保塑料薄膜,其组分及重量份数为:聚乙烯100份,聚碳酸酯10-20份,乙烯-丁烯聚合物12-15份,聚乙烯蜡5-10份,抗氧剂2-4份,紫外线吸收剂0.5-1份,普鲁兰多糖5-8份,PBM降解材料60-80份。本发明提供的隔氧且可降解塑料薄膜在富氧及微生物的作用下会自动分解,废弃后的薄膜能被自然界中微生物完全降解消化,最终生成二氧化碳和水,较相同厚度的LDPE薄膜隔氧性能可提高40%。本发明的制备方法工艺简单、生产效率高、工业化实施容易、可用普通塑料吹膜机进行生产。
Description
技术领域
本发明属于塑料薄膜材料领域,尤其是一种环保塑料薄膜。
背景技术
可降解薄膜既具有传统塑料的功能和特性、又可在达到使用寿命之后,通过土壤和水中的微生物作用或通过阳光中的紫外线的作用,在自然环境中分裂降解,最终以还原形式重新进入生态环境中,回归大自然。国内研发的品种已涵盖光降解、光生物降解、光氧化生物降解、高淀粉含量型生物降解、高碳酸钙填充型光氧降解、全生物降解等。目前可降解材料市场有很多材料,但大致分为光热降解塑料及纯生物降解塑料,但是现有降解产品只顾及降解环境的一个方面,而对产品的物理机械性能即拉伸性能、断裂伸长率等不能满足最终产品的实际物理性能需求。
发明内容
本发明的目的在于克服现有技术的不足之处,提供一种具有更加优越的拉伸性能以及断裂伸长率的一种环保塑料薄膜。
本发明实现目的的技术方案是:
一种环保塑料薄膜,其组分及重量份数为:
而且,所述聚乙烯为低密度聚乙烯、中密度聚乙烯、高密度聚乙烯按照质量比2:2:1混料。
而且,所述抗氧剂是抗氧剂1010或抗氧剂168。
而且,所述紫外线吸收剂是水杨酸苯酯或紫外线吸收剂UV-531。
而且,所述聚乙烯蜡采用PE520。
而且,所述乙烯-丁烯聚合物采用DF-740。
而且,所述PBM降解材料是利用农业生物质资源为主要原料生产的生物降解材料,是采用淀粉、植物油脂等为主要原料合成的全降解天然高分子材料经特殊处理后,与水溶性高分子材料及少量树脂复合而成,该PBM降解材料为市售商品。
本发明的优点和有益效果为:
本发明提供的隔氧且可降解塑料薄膜在富氧及微生物的作用下会自动分解,废弃后的薄膜能被自然界中微生物完全降解消化,最终生成二氧化碳和水,较相同厚度的LDPE薄膜隔氧性能可提高40%。本发明的制备方法工艺简单、生产效率高、工业化实施容易、可用普通塑料吹膜机进行生产。
具体实施方式
下面通过具体实施例对本发明作进一步详述,以下实施例只是描述性的,不是限定性的,不能以此限定本发明的保护范围。
如无特殊说明,本发明中所使用的试剂为常规试剂;如无特殊说明,所使用的方法为常规方法。
实施例1
一种环保塑料薄膜,其组分及重量数为:
实施例2
一种环保塑料薄膜,其组分及重量数为:
实施例3
一种环保塑料薄膜,其组分及重量数为:
Claims (7)
1.一种环保塑料薄膜,其特征在于:
其组分及重量份数为:
2.根据权利要求1所述的一种环保塑料薄膜,其特征在于:所述聚乙烯为低密度聚乙烯、
中密度聚乙烯、高密度聚乙烯按照质量比2:2:1混料。
3.根据权利要求1所述的一种环保塑料薄膜,其特征在于:所述抗氧剂是抗氧剂1010
或抗氧剂168。
4.根据权利要求1所述的一种环保塑料薄膜,其特征在于:所述紫外线吸收剂是水杨酸苯酯或紫外线吸收剂UV-531。
5.根据权利要求1所述的一种环保塑料薄膜,其特征在于:所述聚乙烯蜡采用PE520。
6.根据权利要求1所述的一种环保塑料薄膜,其特征在于:所述乙烯-丁烯聚合物DF-740。
7.根据权利要求1所述的一种环保塑料薄膜,其特征在于:所述PBM降解材料是利用农业生物质资源为主要原料生产的生物降解材料,是采用淀粉、植物油脂等为主要原料合成的全降解天然高分子材料经特殊处理后,与水溶性高分子材料及少量树脂复合而成,该PBM降解材料为市售商品。