CN104479207A - 一种农用环保薄膜 - Google Patents

一种农用环保薄膜 Download PDF

Info

Publication number
CN104479207A
CN104479207A CN201410777430.4A CN201410777430A CN104479207A CN 104479207 A CN104479207 A CN 104479207A CN 201410777430 A CN201410777430 A CN 201410777430A CN 104479207 A CN104479207 A CN 104479207A
Authority
CN
China
Prior art keywords
parts
agricultural
environment
film
protecting film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410777430.4A
Other languages
English (en)
Inventor
郝永强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN KAIXUAN PLASTIC PRODUCTS CO Ltd
Original Assignee
TIANJIN KAIXUAN PLASTIC PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN KAIXUAN PLASTIC PRODUCTS CO Ltd filed Critical TIANJIN KAIXUAN PLASTIC PRODUCTS CO Ltd
Priority to CN201410777430.4A priority Critical patent/CN104479207A/zh
Publication of CN104479207A publication Critical patent/CN104479207A/zh
Pending legal-status Critical Current

Abstract

一种农用环保薄膜，其是采用在塑料薄膜的双面涂敷除虫剂制得；其组分及重量份数为：聚乙烯100份，聚碳酸酯10-20份，乙烯-丁烯聚合物12-15份，聚乙烯蜡5-10份，抗氧剂2-4份，紫外线吸收剂0.5-1份，普鲁兰多糖5-8份，PBM降解材料60-80份，润滑剂10-30份，复合填料6-8份，每平方米薄膜上涂覆除虫剂浆体4-6g。本发明提供的隔氧且可降解塑料薄膜在富氧及微生物的作用下会自动分解，废弃后的薄膜能被自然界中微生物完全降解消化，最终生成二氧化碳和水，较相同厚度的LDPE薄膜隔氧性能可提高40％。本发明的制备方法工艺简单、生产效率高、工业化实施容易、可用普通塑料吹膜机进行生产。

Description

一种农用环保薄膜
技术领域
本发明属于塑料薄膜材料领域，尤其是一种农用环保薄膜。
背景技术
可降解薄膜既具有传统塑料的功能和特性、又可在达到使用寿命之后，通过土壤和水中的微生物作用或通过阳光中的紫外线的作用，在自然环境中分裂降解，最终以还原形式重新进入生态环境中，回归大自然。国内研发的品种已涵盖光降解、光生物降解、光氧化生物降解、高淀粉含量型生物降解、高碳酸钙填充型光氧降解、全生物降解等。目前可降解材料市场有很多材料，但大致分为光热降解塑料及纯生物降解塑料，但是现有降解产品只顾及降解环境的一个方面，而对产品的物理机械性能即拉伸性能、断裂伸长率等不能满足最终产品的实际物理性能需求。
发明内容
本发明的目的在于克服现有技术的不足之处，提供一种具有更加优越的拉伸性能以及断裂伸长率的一种农用环保薄膜。
本发明实现目的的技术方案是：
一种农用环保薄膜，其是采用在塑料薄膜的双面涂敷除虫剂制得；其组分及重量份数为：
每平方米薄膜上涂覆除虫剂浆体4-6g。
而且，所述聚乙烯为低密度聚乙烯、中密度聚乙烯、高密度聚乙烯按照质量比2:2:1混料。
而且，所述润滑剂包括脂肪酸酰胺、脂肪酸酯、脂肪酸盐成分在内的润滑成分中的至少一种。
而且，所述的除虫剂浆体是由下述重量份的原料混匀制得：聚乙烯醇65-75份，中药除虫提取物3-5份，交联剂TAIC 1-2份，氯化石蜡0.3-0.5份，醇醚糖苷0.3-0.5份；
而且，所述抗氧剂是抗氧剂1010或抗氧剂168。
而且，所述紫外线吸收剂是水杨酸苯酯或紫外线吸收剂UV-531。
而且，所述聚乙烯蜡采用PE520。
而且，所述的中药除虫提取物是由下述重量份的原料制得：红花1-2份、山豆根2-4份、土荆皮1-2份、百部3-5份、狼毒1-2份，木槿花1-3份，除虫菊1-2份。
而且，所述的复合填料由下述重量份的原料制得：白云石6-8份、贝壳1-2份、钾长石5-7份、丙烯酸甲酯0.1-0.2份、壬基酚聚氧乙烯醚0.1-0.2份、辣椒籽油0.3-0.5份、氢氧化镁3-6份。
本发明的优点和有益效果为：
1、本发明提供的隔氧且可降解塑料薄膜在富氧及微生物的作用下会自动分解，废弃后的薄膜能被自然界中微生物完全降解消化，最终生成二氧化碳和水，较相同厚度的LDPE薄膜隔氧性能可提高40％。本发明的制备方法工艺简单、生产效率高、工业化实施容易、可用普通塑料吹膜机进行生产。
2、当本发明铺设后，借助于雨水的作用均匀的把除虫剂溶解地面上，来达到除虫的目。除虫菊是一种既有较高的经济价值又有观赏价值的菊科植物,它根、茎、叶、花等都含有毒虫素物质,可用来提取除虫菊酯的原料,用以配制各种杀虫剂。
具体实施方式
下面通过具体实施例对本发明作进一步详述，以下实施例只是描述性的，不是限定性的，不能以此限定本发明的保护范围。
如无特殊说明，本发明中所使用的试剂为常规试剂；如无特殊说明，所使用的方法为常规方法。
实施例1
(1)一种农用环保薄膜，其是采用在塑料薄膜的双面涂敷除虫剂制得，所述的塑料薄膜由下述重量(kg)的原料制得：
每平方米薄膜上涂覆除虫剂浆体4g。
(2)所述的除虫剂浆体是由下述重量份的原料混匀制得：
聚乙烯醇65、
中药除虫提取物3、
交联剂TAIC 1、
氯化石蜡0.3、
醇醚糖苷0.3；
(3)所述的中药除虫提取物是由下述重量份的原料制得：
红花1、
山豆根2、
土荆皮1、
百部3、
狼毒1、
木槿花1、
除虫菊1；
(4)所述的中药除虫提取物的制备方法为：将各原料混匀后，加入相当于所有原料重量3倍的水，煎煮去渣后，滤液浓缩干燥，即得；
所述的复合填料由下述重量份的原料制得：
白云石6、
贝壳1、
钾长石5、
丙烯酸甲酯0.1、
壬基酚聚氧乙烯醚0.1、
辣椒籽油0.3、
氢氧化镁3。
实施例2
(1)一种农用环保薄膜，其是采用在塑料薄膜的双面涂敷除虫剂制得，所述的塑料薄膜由下述重量(kg)的原料制得：
每平方米薄膜上涂覆除虫剂浆体5g；
(2)所述的除虫剂浆体是由下述重量份的原料混匀制得：
聚乙烯醇70、
中药除虫提取物4、
交联剂TAIC 1.5、
氯化石蜡0.4、
醇醚糖苷0.4；
(3)所述的中药除虫提取物是由下述重量份的原料制得：
红花1.5、
山豆根3、
土荆皮1.5、
百部4、
狼毒1.5，
木槿花2，
除虫菊1.5；
(4)所述的中药除虫提取物的制备方法为：将各原料混匀后，加入相当于所有原料重量4倍的水，煎煮去渣后，滤液浓缩干燥，即得；
所述的复合填料由下述重量份的原料制得：
白云石7、
贝壳1.5、
钾长石6、
丙烯酸甲酯0.15、
壬基酚聚氧乙烯醚0.15、
辣椒籽油0.4、
氢氧化镁4.5。
实施例3
(1)一种农用环保薄膜，其是采用在塑料薄膜的双面涂敷除虫剂制得，所述的塑料薄膜由下述重量(kg)的原料制得：
每平方米薄膜上涂覆除虫剂浆体6g。
(2)所述的除虫剂浆体是由下述重量份的原料混匀制得：
聚乙烯醇75、
中药除虫提取物5、
交联剂TAIC 2、
氯化石蜡0.5、
醇醚糖苷0.5；
(3)所述的中药除虫提取物是由下述重量份的原料制得：
红花2、
山豆根4、
土荆皮2、
百部5、
狼毒2、
木槿花3、
除虫菊2；
(4)所述的中药除虫提取物的制备方法为：将各原料混匀后，加入相当于所有原料重量5倍的水，煎煮去渣后，滤液浓缩干燥，即得；
所述的复合填料由下述重量份的原料制得：
白云石8、
贝壳2、
钾长石7、
丙烯酸甲酯0.2、
壬基酚聚氧乙烯醚0.2、
辣椒籽油0.5、
氢氧化镁6。

Claims (9)

1.一种农用环保薄膜，其是采用在塑料薄膜的双面涂敷除虫剂制得；其特征在于：其组分及重量份数为：
每平方米薄膜上涂覆除虫剂浆体4-6g。
2.根据权利要求1所述的一种农用环保薄膜，其特征在于：所述聚乙烯为低密度聚乙烯、中密度聚乙烯、高密度聚乙烯按照质量比2:2:1混料。
3.根据权利要求1所述的一种农用环保薄膜，其特征在于：所述抗氧剂是抗氧剂1010或抗氧剂168。
4.根据权利要求1所述的一种农用环保薄膜，其特征在于：所述紫外线吸收剂是水杨酸苯酯或紫外线吸收剂UV-531。
5.根据权利要求1所述的一种农用环保薄膜，其特征在于：所述聚乙烯蜡采用PE520。
6.根据权利要求1所述的一种农用环保薄膜，其特征在于：所述润滑剂包括脂肪酸酰胺、脂肪酸酯、脂肪酸盐成分在内的润滑成分中的至少一种。
7.根据权利要求1所述的一种农用环保薄膜，其特征在于：所述的除虫剂浆体是由下述重量份的原料混匀制得：聚乙烯醇65-75份，中药除虫提取物3-5份，交联剂TAIC 1-2份，氯化石蜡0.3-0.5份，醇醚糖苷0.3-0.5份。
8.根据权利要求7所述的一种农用环保薄膜，其特征在于：所述的中药除虫提取物是由下述重量份的原料制得：红花1-2份、山豆根2-4份、土荆皮1-2份、百部3-5份、狼毒1-2份，木槿花1-3份，除虫菊1-2份。
9.根据权利要求1所述的一种农用环保薄膜，其特征在于：所述的复合填料由下述重量份的原料制得：白云石6-8份、贝壳1-2份、钾长石5-7份、丙烯酸甲酯0.1-0.2份、壬基酚聚氧乙烯醚0.1-0.2份、辣椒籽油0.3-0.5份、氢氧化镁3-6份。
CN201410777430.4A 2014-12-16 2014-12-16 一种农用环保薄膜 Pending CN104479207A (zh)