CN103570276B - 一种人造夜明珠的制备方法 - Google Patents
一种人造夜明珠的制备方法 Download PDFInfo
- Publication number
- CN103570276B CN103570276B CN201310584495.2A CN201310584495A CN103570276B CN 103570276 B CN103570276 B CN 103570276B CN 201310584495 A CN201310584495 A CN 201310584495A CN 103570276 B CN103570276 B CN 103570276B
- Authority
- CN
- China
- Prior art keywords
- powder
- pearl
- speed stirring
- luminous
- artificial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种人造夜明珠的制备方法。采用固化透明度高的不饱和聚酯型水晶树脂作为粘结剂，通过加入玉石粉、萤石粉和荧光粉作为填料，在一些其它辅助助剂的帮助下，混合浆料浇铸入珠型玻璃钢模具内，通过抽真空去气泡，固化脱模制成毛珠，而后通过精细抛光最终制成能吸光发光的蓝绿色珠子，即为人造夜明珠。本发明方法的生产工艺和设备简单，生产周期短，易于大规模推广，所制备人造夜明珠成本相对较低，可为大众客户接受，且外观及功能仿真程度达到95%以上，且通过人工选材，所制备的夜明珠环保无辐射。
Description
技术领域
本发明属于人造玉石工艺品技术领域，特别涉及一种人造夜明珠的制备方法。
背景技术
夜光石就是莹石，夜明珠在我国古代民间又名叫夜光壁、夜光石、放光石，相传是世界上极为罕见的夜间能发出光芒的奇石。有专家指出夜明珠事实上就是能发光的萤石。我国虽然是萤石矿产大国，但夜晚能发光的萤石并不多，所以就显得珍贵和价值连城了。英国着名学者李约瑟在巨着《中国科学技术史》中记载，古代中国人喜爱夜明珠，就是因为认为夜明珠有灵性，是镇山之宝。所以人们对它看得很珍贵之宝物。它能镇宅，能除掉一切邪恶。永保全家平安、给人带来好运之说法。印度一些人把夜明珠称为蛇眼石,日本学家玲木敏于1916年编《宝石志》称夜明珠为神圣的宝石。
天然夜明珠较为稀有，多被当做一种宝物收藏，但是其实夜明珠具有很高贵的带有功能性的装饰效果，可以当做一种装饰工艺品对我们室内已经进行神秘点缀，但是天然夜明珠奇少且敖贵，因此为了室内夜间装饰的需要，我们发明制备一种仿天然夜明珠材质及功能的工艺品人造夜明珠，用来满足消费者的需要。
发明内容
本发明的目的是提供一种人造夜明珠的制备方法。
本发明的思路：采用固化透明度高的不饱和聚酯型水晶树脂作为粘结剂，通过加入玉石粉、萤石粉和荧光粉作为填料，在一些其它辅助助剂的帮助下，混合浆料浇铸入珠型玻璃钢模具内，通过抽真空去气泡，固化脱模制成毛珠，而后通过精细抛光最终制成能吸光发光的蓝绿色珠子，即为人造夜明珠。
具体步骤为：
(1)按照以下质量比称取原料，不饱和聚酯型水晶树脂:玉石粉:萤石粉:荧光粉:消泡剂:异辛酸钴:过氧化甲乙酮=15~40:20~50:10~30:3~20:0.05~0.5:0.2~1:0.2~2。
(2)将步骤(1)称取的不饱和聚酯型水晶树脂倒入浆料高速搅拌桶中，开启搅拌机，设置搅拌速率为200~1500转/分钟，然后将步骤(1)称取的玉石粉、萤石粉和荧光粉加入高速搅拌的浆料高速搅拌桶中，混合搅拌5~30分钟，而后将步骤(1)称取的消泡剂和异辛酸钴加入高速搅拌的浆料高速搅拌桶中，搅拌2~10分钟，最后将步骤(1)称取的过氧化甲乙酮加入高速搅拌的浆料高速搅拌桶中，搅拌速率改为500~2000转/分钟，搅拌2~20分钟后，制得混合浆料。
(3)将步骤(2)制得的混合浆料浇铸入珠型玻璃钢组合模具内，抽真空去泡，固化脱模制成毛珠，然后通过精细抛光最终制成能吸光发光的蓝绿色珠子，即为人造夜明珠。
所述玉石粉为天然玉石粉末、翡翠粉和玛瑙粉中一种或几种。
所述玉石粉、萤石粉和荧光粉的粉体粒径范围为200~3000目。
所述荧光粉为储能储光发光型绿光和/或黄光荧光粉。
采用本发明方法制备人造夜明珠具有以下优点：
(1)本发明方法的生产工艺和设备简单，生产周期短，易于大规模推广。
(2)本发明方法制备人造夜明珠成本相对较低，可为大众客户接受，且外观及功能仿真程度达到95%以上。
(3)本发明方法制备的人造夜明珠通过人工选材，环保无辐射。
具体实施方式
以下实施例使用的主要原料是：不饱和聚酯型水晶树脂（工业级）、玉石粉（工业级）、萤石粉（工业级）、绿光荧光粉（工业级）、消泡剂（工业级）、异辛酸钴（工业级）、过氧化甲乙酮（工业级）。
实施例1：
(1)按照以下质量称取原料，3.5千克不饱和聚酯型水晶树脂、4千克玉石粉、1.5千克萤石粉、0.9千克荧光粉、0.01千克消泡剂、0.04千克异辛酸钴、0.05千克过氧化甲乙酮。
(2)将步骤(1)称取的不饱和聚酯型水晶树脂倒入浆料高速搅拌桶中，开启搅拌机，设置搅拌速率为800转/分钟，然后将步骤(1)称取的玉石粉、萤石粉和荧光粉加入高速搅拌的浆料高速搅拌桶中，混合搅拌10分钟，而后将步骤(1)称取的消泡剂和异辛酸钴加入高速搅拌的浆料高速搅拌桶中，搅拌5分钟，最后将步骤(1)称取的过氧化甲乙酮加入高速搅拌的浆料高速搅拌桶中，搅拌速率改为1200转/分钟，搅拌10分钟后，制得混合浆料。
(3)将步骤(2)制得的混合浆料浇铸入珠型玻璃钢组合模具内，抽真空去泡，固化脱模制成毛珠，然后通过精细抛光最终制成能吸光发光的蓝绿色珠子，即为人造夜明珠。
所述玉石粉为天然玉石粉末；所述玉石粉、萤石粉和荧光粉的粉体粒径范围为200~3000目；所述荧光粉为储能储光发光型绿光荧光粉。
检测结果：本实施例制备的人造夜明珠，仿真程度评定达到95%以上，非专业人士很难判断；发光效果持久，白天室内自然光照射6小时以上，晚上可以持续发光12小时以上；发光强度高，10厘米直径人造夜明珠，1.5米范围内人民币字面清晰可见。
实施例2：
(1)按照以下质量称取原料，3千克不饱和聚酯型水晶树脂、4千克玉石粉、1.4千克萤石粉、1.5千克荧光粉、0.01千克消泡剂、0.03千克异辛酸钴、0.06千克过氧化甲乙酮。
(2)将步骤(1)称取的不饱和聚酯型水晶树脂倒入浆料高速搅拌桶中，开启搅拌机，设置搅拌速率为900转/分钟，然后将步骤(1)称取的玉石粉、萤石粉和荧光粉加入高速搅拌的浆料高速搅拌桶中，混合搅拌8分钟，而后将步骤(1)称取的消泡剂和异辛酸钴加入高速搅拌的浆料高速搅拌桶中，搅拌6分钟，最后将步骤(1)称取的过氧化甲乙酮加入高速搅拌的浆料高速搅拌桶中，搅拌速率改为1200转/分钟，搅拌6分钟后，制得混合浆料。
(3)将步骤(2)制得的混合浆料浇铸入珠型玻璃钢组合模具内，抽真空去泡，固化脱模制成毛珠，然后通过精细抛光最终制成能吸光发光的蓝绿色珠子，即为人造夜明珠。
所述玉石粉为翡翠粉；所述玉石粉、萤石粉和荧光粉的粉体粒径范围为200~3000目；所述荧光粉为储能储光发光型黄光荧光粉。
检测结果：本实施例制备的人造夜明珠，仿真程度评定达到95%以上，非专业人士很难判断；发光效果持久，白天室内自然光照射6小时以上，晚上可以持续发光14小时以上；发光强度高，10厘米直径人造夜明珠，2米范围内人民币字面清晰可见。
Claims (1)
1.一种人造夜明珠的制备方法，其特征在于具体步骤为：
(1)按照以下质量比称取原料，不饱和聚酯型水晶树脂:玉石粉:萤石粉:荧光粉:消泡剂:异辛酸钴:过氧化甲乙酮=15~40:20~50:10~30:3~20:0.05~0.5:0.2~1:0.2~2；
(2)将步骤(1)称取的不饱和聚酯型水晶树脂倒入浆料高速搅拌桶中，开启搅拌机，设置搅拌速率为200~1500转/分钟，然后将步骤(1)称取的玉石粉、萤石粉和荧光粉加入高速搅拌的浆料高速搅拌桶中，混合搅拌5~30分钟，而后将步骤(1)称取的消泡剂和异辛酸钴加入高速搅拌的浆料高速搅拌桶中，搅拌2~10分钟，最后将步骤(1)称取的过氧化甲乙酮加入高速搅拌的浆料高速搅拌桶中，搅拌速率改为500~2000转/分钟，搅拌2~20分钟后，制得混合浆料；
(3)将步骤(2)制得的混合浆料浇铸入珠型玻璃钢组合模具内，抽真空去泡，固化脱模制成毛珠，然后通过精细抛光最终制成能吸光发光的蓝绿色珠子，即为人造夜明珠；
所述玉石粉为天然玉石粉末、翡翠粉和玛瑙粉中一种或几种；
所述玉石粉、萤石粉和荧光粉的粉体粒径范围为200~3000目；
所述荧光粉为储能储光发光型绿光和/或黄光荧光粉。