CN103554997A - 碳包覆二氧化钒纳米颗粒及其制备方法 - Google Patents
碳包覆二氧化钒纳米颗粒及其制备方法 Download PDFInfo
- Publication number
- CN103554997A CN103554997A CN201310483224.8A CN201310483224A CN103554997A CN 103554997 A CN103554997 A CN 103554997A CN 201310483224 A CN201310483224 A CN 201310483224A CN 103554997 A CN103554997 A CN 103554997A
- Authority
- CN
- China
- Prior art keywords
- carbon
- coated
- vanadium dioxide
- rutile
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (10)