CN103554417A - 聚醚型透明聚氨酯弹性体及其制备方法 - Google Patents

聚醚型透明聚氨酯弹性体及其制备方法 Download PDF

Info

Publication number
CN103554417A
CN103554417A CN201310529629.0A CN201310529629A CN103554417A CN 103554417 A CN103554417 A CN 103554417A CN 201310529629 A CN201310529629 A CN 201310529629A CN 103554417 A CN103554417 A CN 103554417A
Authority
CN
China
Prior art keywords
polyurethane elastomer
polyether
type transparent
transparent polyurethane
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310529629.0A
Other languages
English (en)
Other versions
CN103554417B (zh
Inventor
王宝山
耿佃勇
董伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zibo Dexin Lianbang Chemical Industry Co Ltd
Original Assignee
Zibo Dexin Lianbang Chemical Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zibo Dexin Lianbang Chemical Industry Co Ltd filed Critical Zibo Dexin Lianbang Chemical Industry Co Ltd
Priority to CN201310529629.0A priority Critical patent/CN103554417B/zh
Publication of CN103554417A publication Critical patent/CN103554417A/zh
Application granted granted Critical
Publication of CN103554417B publication Critical patent/CN103554417B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种聚醚型透明聚氨酯弹性体及其制备方法，原料及其质量份数：聚醚多元醇60～100；黑料20～35；扩链剂5～15；1,3丁二醇2～8。本发明聚醚型透明聚氨酯弹性体及其制备方法，聚醚多元醇和黑料以及扩链剂为带侧链不对称的结构，提高产品的透明性，产品生产过程环保无毒。制备方法简单，操作容易。

Description

聚醚型透明聚氨酯弹性体及其制备方法
技术领域
本发明涉及一种聚氨酯弹性体，具体涉及一种聚醚型透明聚氨酯弹性体及其制备方法。
技术背景
聚氨酯弹性体具有很好的抗拉强度、抗撕裂强度、耐冲击性、耐磨性、耐候性、耐水解性、耐油性等优点。主要用作涂覆材料，如软管、垫圈、轮带、辊筒、齿轮、管道等的保护、绝缘体、鞋底以及实心轮胎等方面。透明弹性体以高透光率可以用到制鞋、广告等行业。
发明内容
本发明的目的是提供一种聚醚型透明聚氨酯弹性体及其制备方法。聚醚多元醇和黑料以及扩链剂为带侧链不对称的结构，提高产品的透明性，产品生产过程环保无毒。制备方法简单，操作容易。
本发明所述的聚醚型透明聚氨酯弹性体，原料及其质量份数如下：
Figure BDA0000405874390000011
黑料为异氰酸酯，优选TDI-100；TDI-100生产厂家为巴斯夫股份公司。
扩链剂为MN-500。
聚醚多元醇为DDL1000D。
DDL1000D、MN-500生产厂家为淄博德信联邦化学工业有限公司。
聚醚多元醇和黑料以及扩链剂上选择带侧链不对称的结构，影响材料的结晶度提高透明性。
聚醚型透明聚氨酯弹性体的制备方法如下：
将DDL1000D投入将三口瓶，升温100-120℃抽真空脱水1.5-2.0h，降温55-65℃后加入TDI-100，合成含量为4-8％的预聚体，合成预聚体后加入扩链剂MN-500、1,3-丁二醇搅拌均匀，到入模具硫化25-32min后脱模放入80-100℃烘箱硫化8-12h，得到聚醚型透明聚氨酯弹性体。
与现有技术相比，本发明具有以下有益效果：
本发明聚醚型透明聚氨酯弹性体及其制备方法，聚醚多元醇和黑料以及扩链剂为带侧链不对称的结构，提高产品的透明性，产品生产过程环保无毒。制备方法简单，操作容易。
具体实施方式
下面结合实施例对本发明做进一步的说明。
实验设备：平板硫化机、万能拉力机、搅拌装置、橡胶磨耗试验机。
实施例1
聚醚型透明聚氨酯弹性体，原料及其质量份数如下：
Figure BDA0000405874390000021
将DDL1000D投入将三口瓶，升温100℃抽真空脱水2.0h，降温55℃后加入TDI-100，合成含量为8％的预聚体，合成预聚体后加入MN-500、1,3-丁二醇搅拌均匀，到入模具硫化25min后脱模放入80℃烘箱硫化8h，得到聚醚型透明聚氨酯弹性体。
室温硫化7天后进行硬度、拉伸强度、伸长率和透光率进行测试，测试结果如表1。
实施例2
聚醚型透明聚氨酯弹性体，原料及其质量份数如下：
Figure BDA0000405874390000022
将DDL1000D投入将三口瓶，升温110℃抽真空脱水1.5h，降温60℃后加入TDI-100，合成含量为5％的预聚体，合成预聚体后加入MN-500、1,3-丁二醇搅拌均匀，到入模具硫化32min后脱模放入90℃烘箱硫化10h，得到聚醚型透明聚氨酯弹性体。
室温硫化7天后进行硬度、拉伸强度、伸长率和透光率进行测试，测试结果如表1。
实施例3
聚醚型透明聚氨酯弹性体，原料及其质量份数如下：
将DDL1000D投入将三口瓶，升温120℃抽真空脱水2.0h，降温65℃后加入TDI-100，合成含量为4％的预聚体，合成预聚体后加入MN-500、1,3-丁二醇搅拌均匀，到入模具硫化30min后脱模放入100℃烘箱硫化12h，得到聚醚型透明聚氨酯弹性体。
室温硫化7天后进行硬度、拉伸强度、伸长率和透光率进行测试，测试结果如表1。
表1实施例1-3产品硬度、拉伸强度、伸长率和透光率进行测试结果。
硬度 拉伸强度 伸长率 透光率
实施例1 85-88A 25.39 456 93.2
实施例2 75～80A 24.35 468 92.6
实施例3 60～70A 20.26 479 90.8

Claims (5)

1.一种聚醚型透明聚氨酯弹性体，其特征在于，原料及其质量份数如下：
Figure FDA0000405874380000011
2.根据权利要求1所述的聚醚型透明聚氨酯弹性体，其特征在于，黑料为异氰酸酯。
3.根据权利要求1所述的聚醚型透明聚氨酯弹性体，其特征在于，扩链剂为MN-500。
4.根据权利要求1所述的聚醚型透明聚氨酯弹性体，其特征在于，聚醚多元醇为DDL1000D。
5.一种权利要求1所述的聚醚型透明聚氨酯弹性体的制备方法，其特征在于，制备方法如下：
将DDL1000D投入将三口瓶，升温100-120℃抽真空脱水1.5-2.0h，降温55-65℃后加入TDI-100，合成nco含量为4-8％的预聚体，合成预聚体后加入扩链剂MN-500、1,3-丁二醇搅拌均匀，到入模具硫化25-32min后脱模放入80-100℃烘箱硫化8-12h，得到聚醚型透明聚氨酯弹性体。
CN201310529629.0A 2013-10-31 2013-10-31 聚醚型透明聚氨酯弹性体及其制备方法 Active CN103554417B (zh)