CN103509281B - 一种抗冻电缆料 - Google Patents

一种抗冻电缆料 Download PDF

Info

Publication number
CN103509281B
CN103509281B CN201310405046.7A CN201310405046A CN103509281B CN 103509281 B CN103509281 B CN 103509281B CN 201310405046 A CN201310405046 A CN 201310405046A CN 103509281 B CN103509281 B CN 103509281B
Authority
CN
China
Prior art keywords
diatomite
minute
nano
cable material
infusorial earth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310405046.7A
Other languages
English (en)
Other versions
CN103509281A (zh
Inventor
李小康
吴中东
陶天宝
李业胜
方刚
李强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU YIPUDUN NEW MATERIAL TECHNOLOGY Co.,Ltd.
Original Assignee
Anhui Huatong Cable Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Huatong Cable Group Co Ltd filed Critical Anhui Huatong Cable Group Co Ltd
Priority to CN201310405046.7A priority Critical patent/CN103509281B/zh
Publication of CN103509281A publication Critical patent/CN103509281A/zh
Application granted granted Critical
Publication of CN103509281B publication Critical patent/CN103509281B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗冻电缆料，其是由下述重量份的原料制得：聚氯乙烯树脂90-100，三氧化二锑4-6、改性硅藻土30-40、纳米碳酸钙5-10，硅烷偶联剂KH570？1.5-3、丁苯橡胶5-8、钛酸正丁酯2-4、过氧化二异丙苯1-2，醋酸纤维素1-2、乙撑基双硬酯酰胺1-2，硬酯酸单甘油酯1-2，二辛酯2.5-3.5、古马隆0.5-1。

Description

一种抗冻电缆料
技术领域
本发明涉及电缆料领域，确切地说是一种抗冻电缆料。
背景技术
聚氯乙烯电缆料即PVC电缆料品质的优劣，根本上是由PVC电缆料配方以及所选用的原料来决定的。随着PVC的各种助剂和填充物的不断更新和发展，也使得PVC电缆料的配方不断完善和提高。
发明内容
本发明的目的在于提供一种抗冻电缆料
上述目的通过以下方案实现：
一种抗冻电缆料，其特征在于：其是由下述重量份的原料制得：聚氯乙烯树脂90-100，三氧化二锑4-6、改性硅藻土30-40、纳米碳酸钙5-10，硅烷偶联剂KH5701.5-3、丁苯橡胶5-8、钛酸正丁酯2-4、过氧化二异丙苯1-2，醋酸纤维素1-2、乙撑基双硬酯酰胺1-2，硬酯酸单甘油酯1-2，二辛酯2.5-3.5、古马隆0.5-1；
改性硅藻土的制备方法为：
(1)首先，取硅藻土，加入为硅藻土质量9-12倍的去离子水里，于40-50℃下搅拌均匀后，浸泡8-12小时后，1700-2300r/min离心处理12-15min，干燥；
(2)将步骤（1）干燥后的硅藻土在闪烧窑中700-900℃闪烧10-12秒，再向硅藻土中倒入相当于硅藻土重量4-5倍的浓度为5-8%的乙酸溶液,于45-55℃下搅拌25-30分钟后，去离子水洗涤、烘干，粉碎，过60-100目筛；
（3）反应釜预热至70-80℃，然后在步骤（2）处理后的硅藻土中加入相当于其重量0.3-1.3%的邻苯二甲酸二异癸酯、1.1-2.8%的纳米碳、0.1-0.2%的异构十三醇聚氧乙烯醚搅拌均匀后，装入反应釜，然后升温至90-95℃时,保温4-8分钟,再加入当于硅藻土重量0.5-0.7%的硬脂酸，0.2-0.4%的环烷酸锌，0.3-0.5%的抗氧剂626，升温至110-120℃,保温8-15分钟取出，冷却，即得。
所述的一种抗冻电缆料，其特征在于：
制备方法为：
（1）取聚氯乙烯树脂、三氧化二锑、改性硅藻土、纳米碳酸钙、硅烷偶联剂KH570、丁苯橡胶、钛酸正丁酯、过氧化二异丙苯、醋酸纤维素，双螺杆挤出机混炼10-20分钟，控制温度在150-160℃；
（2）再加入剩余各原料混匀，混炼、造粒，控制温度160-170℃，得到成品。
本发明的有益效果为：本发明制备方法简单，操作方便，组成原料配方合理，制得的电缆料不仅抗冻、而且具有柔软度高、燃烧时低烟无毒等优点。
具体实施方式
一种抗冻电缆料，其是由下述重量份（kg)的原料制得：聚氯乙烯树脂100，三氧化二锑4、改性硅藻土40、纳米碳酸钙10，硅烷偶联剂KH5703、丁苯橡胶7、钛酸正丁酯3、过氧化二异丙苯1.4，醋酸纤维素2、乙撑基双硬酯酰胺1，硬酯酸单甘油酯1.3，二辛酯2.7、古马隆0.7；
改性硅藻土的制备方法为：
(1)首先，取硅藻土，加入为硅藻土质量12倍的去离子水里，于50℃下搅拌均匀后，浸泡8小时后，1700r/min离心处理15min，干燥；
(2)将步骤（1）干燥后的硅藻土在闪烧窑中900℃闪烧10秒，再向硅藻土中倒入相当于硅藻土重量4倍的浓度为8%的乙酸溶液,于48℃下搅拌28分钟后，去离子水洗涤、烘干，粉碎，过100目筛；
（3）反应釜预热至70℃，然后在步骤（2）处理后的硅藻土中加入相当于其重量0.8%的邻苯二甲酸二异癸酯、1.6%的纳米碳、0.2%的异构十三醇聚氧乙烯醚搅拌均匀后，装入反应釜，然后升温至95℃时,保温7分钟,再加入当于硅藻土重量0.7%的硬脂酸，0.3%的环烷酸锌，0.5%的抗氧剂626，升温至120℃,保温8分钟取出，冷却，即得。
所述的一种抗冻电缆料，
制备方法为：
（1）取聚氯乙烯树脂、三氧化二锑、改性硅藻土、纳米碳酸钙、硅烷偶联剂KH570、丁苯橡胶、钛酸正丁酯、过氧化二异丙苯、醋酸纤维素，双螺杆挤出机混炼20分钟，控制温度在160℃；
（2）再加入剩余各原料混匀，混炼、造粒，控制温度170℃，得到成品。

Claims (2)

1.一种抗冻电缆料，其特征在于：其是由下述重量份的原料制得：聚氯乙烯树脂90-100，三氧化二锑4-6、改性硅藻土30-40、纳米碳酸钙5-10，硅烷偶联剂KH5701.5-3、丁苯橡胶5-8、钛酸正丁酯2-4、过氧化二异丙苯1-2，醋酸纤维素1-2、乙撑基双硬酯酰胺1-2，硬酯酸单甘油酯1-2，二辛酯2.5-3.5、古马隆0.5-1；
改性硅藻土的制备方法为：
(1)首先，取硅藻土，加入为硅藻土质量9-12倍的去离子水里，于40-50℃下搅拌均匀后，浸泡8-12小时后，1700-2300r/min离心处理12-15min，干燥；
(2)将步骤（1）干燥后的硅藻土在闪烧窑中700-900℃闪烧10-12秒，再向硅藻土中倒入相当于硅藻土重量4-5倍的浓度为5-8%的乙酸溶液,于45-55℃下搅拌25-30分钟后，去离子水洗涤、烘干，粉碎，过60-100目筛；
（3）反应釜预热至70-80℃，然后在步骤（2）处理后的硅藻土中加入相当于其重量0.3-1.3%的邻苯二甲酸二异癸酯、1.1-2.8%的纳米碳、0.1-0.2%的异构十三醇聚氧乙烯醚搅拌均匀后，装入反应釜，然后升温至90-95℃时,保温4-8分钟,再加入当于硅藻土重量0.5-0.7%的硬脂酸，0.2-0.4%的环烷酸锌，0.3-0.5%的抗氧剂626，升温至110-120℃,保温8-15分钟取出，冷却，即得。
2.根据权利要求1所述的一种抗冻电缆料，其特征在于：
制备方法为：
（1）取聚氯乙烯树脂、三氧化二锑、改性硅藻土、纳米碳酸钙、硅烷偶联剂KH570、丁苯橡胶、钛酸正丁酯、过氧化二异丙苯、醋酸纤维素，双螺杆挤出机混炼10-20分钟，控制温度在150-160℃；
（2）再加入剩余各原料混匀，混炼、造粒，控制温度160-170℃，得到成品。
CN201310405046.7A 2013-09-06 2013-09-06 一种抗冻电缆料 Active CN103509281B (zh)