CN103485191B - 高透明聚氨酯合成革 - Google Patents
高透明聚氨酯合成革 Download PDFInfo
- Publication number
- CN103485191B CN103485191B CN201310437873.4A CN201310437873A CN103485191B CN 103485191 B CN103485191 B CN 103485191B CN 201310437873 A CN201310437873 A CN 201310437873A CN 103485191 B CN103485191 B CN 103485191B
- Authority
- CN
- China
- Prior art keywords
- synthetic leather
- transparency
- polyurethane resin
- slurry
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种具有高透明特性合成革的制造方法，其特征是包括以下步骤：将聚氨酯树脂、高固丙烯酸改性聚氨酯树脂、丁酮、HDI三聚体固化剂、异辛酸铋促进剂按比例搅拌均匀配成无色高透明浆料。通过印刷处理将无色高透明浆料涂饰在聚氨酯合成革表面，涂饰量控制在50-90g/m2。烘干温度控制在110~140℃，烘干时间控制在3~5分钟。本发明所述的高透明聚氨酯合成革具有透明度高、水晶感强、纹理清晰，且本发明聚氨酯合成革的制备成本低、生产操作简便效率高。
Description
技术领域
本发明涉及一种聚氨酯合成革，更具体地说是一种高透明聚氨酯合成革产品及其制作方法。
背景技术
目前，合成革产品逐渐成为未来流行的趋势，合成革已广泛应用于生产箱包、服装、鞋类、家具等产品中。但同时随着社会经济的发展，人们生活水平的提高，对于这些生活必须品的附加值要求也越来越高。目前具有高透明效果的工艺包括湿气固化及二次贴面等工艺。湿气固化类产品易产生发雾，光泽变暗，不耐黄变等问题；而二次贴面工艺的产品虽能解决此类问题，但是成本过高，生产操作难度大。因此，发明一种透明度高、水晶感强、纹理清晰、耐发雾性能的聚氨酯合成革产品具有一定的市场优势，同时该产品操作简便，生产成本优势强。
发明内容
本发明所要解决的技术问题就是克服现有技术及工艺的不足，提供一种具有透明度高、水晶感强、纹理清晰、操作工艺简便、成本优势强的高透明聚氨酯合成革。
本发明的一种高透明聚氨酯合成革，采用下述方法步骤制备得到：
（a）将聚氨酯树脂、高固丙烯酸改性聚氨酯树脂、丁酮、HDI三聚体固化剂、异辛酸铋促进剂按比例搅拌均匀配成无色高透明浆料；所述原料组分质量配比如下：
聚氨酯树脂TC-1088A 40～70份
高固丙烯酸改性聚氨酯树脂BF-2669A 30～60份
丁酮 30～50份
HDI三聚体固化剂 5～8份
异辛酸铋促进剂 0.2～0.6份；
（b）将无色高透明浆料涂饰在聚氨酯合成革表面；
（c）将涂饰后的聚氨酯合成革于110~140℃烘干3~5分钟。
步骤（a）中的无色高透明浆料黏度为在400-800cps/25℃。
步骤（a）中聚氨酯树脂TC-1088A为高鼎精细化工（昆山）有限公司生产的透明性佳、触感滑爽的聚氨酯树脂。
步骤（a）高固丙烯酸改性聚氨酯树脂BF-2669A为清远市美乐仕油墨有限公司生产的高固丙烯酸改性聚氨酯树脂，其固含量在75%-85%，该材料具有水晶效果强特点；
步骤（a）中异辛酸铋促进剂的加入量可根据HDI三聚体固化剂含量的增加而有所提高。
步骤（b）中的无色浆料涂饰量在50-90g/m2，涂饰厚度可控制在0.6~1.0丝。
本发明与现有技术相比，具有以下优势：所得聚氨酯合成革透明度高、水晶效果强、纹理清晰，且本发明聚氨酯合成革的制备成本低、生产操作简便效率高。
具体实施方式
下述实施例是对于本发明内容的进一步说明以作为对本发明技术内容的阐释，但本发明的实质内容并不仅限于下述实施例所述，本领域的普通技术人员可以且应当知晓任何基于本发明实质精神的简单变化或替换均应属于本发明所要求的保护范围。
实施例1
（a）将聚氨酯树脂、高固丙烯酸改性聚氨酯树脂、丁酮、HDI三聚体固化剂、异辛酸铋促进剂按比例搅拌均匀配成无色高透明浆料；各原料的质量组成为：
聚氨酯树脂TC-1088A 40份
高固丙烯酸改性聚氨酯树脂BF-2669A 60份
丁酮 50份
HDI三聚体固化剂 5份
异辛酸铋促进剂 0.2份
（b）通过印刷处理将无色高透明浆料涂饰在聚氨酯合成革表面，涂饰量控制在60g/m2。
（c）烘干温度控制在120℃，烘干时间控制在3分钟。
实施例2
（a）将聚氨酯树脂、高固丙烯酸改性聚氨酯树脂、丁酮、HDI三聚体固化剂、异辛酸铋促进剂按比例搅拌均匀配成无色高透明浆料；各原料的质量组成为：
聚氨酯树脂TC-1088A 50份
高固丙烯酸改性聚氨酯树脂BF-2669A 50份
丁酮 40份
HDI三聚体固化剂 6份
异辛酸铋促进剂 0.3份
（b）通过印刷处理将无色高透明浆料涂饰在聚氨酯合成革表面，涂饰量控制在70g/m2。
（c）烘干温度控制在125℃，烘干时间控制在4分钟。
实施例3
（a）将聚氨酯树脂、高固丙烯酸改性聚氨酯树脂、丁酮、HDI三聚体固化剂、异辛酸铋促进剂按比例搅拌均匀配成无色高透明浆料；各原料的质量组成为：
聚氨酯树脂TC-1088A 60份
高固丙烯酸改性聚氨酯树脂BF-2669A 40份
丁酮 50份
HDI三聚体固化剂 7份
异辛酸铋促进剂 0.4份
（b）通过印刷处理将无色高透明浆料涂饰在聚氨酯合成革表面，涂饰量控制在80g/m2。
（c）烘干温度控制在130℃，烘干时间控制在5分钟。
实施例4
（a）将聚氨酯树脂、高固丙烯酸改性聚氨酯树脂、丁酮、HDI三聚体固化剂、异辛酸铋促进剂按比例搅拌均匀配成无色高透明浆料；各原料的质量组成为：
聚氨酯树脂TC-1088A 55份
高固丙烯酸改性聚氨酯树脂BF-2669A 45份
丁酮 50份
HDI三聚体固化剂 8份
异辛酸铋促进剂 0.5份
（b）通过印刷处理将无色高透明浆料涂饰在聚氨酯合成革表面，涂饰量控制在100g/m2。
（c）烘干温度控制在140℃，烘干时间控制在5分钟。
实施例5
（a）将聚氨酯树脂、高固丙烯酸改性聚氨酯树脂、丁酮、HDI三聚体固化剂、异辛酸铋促进剂按比例搅拌均匀配成无色高透明浆料；各原料的质量组成为：
聚氨酯树脂TC-1088A 70份
高固丙烯酸改性聚氨酯树脂BF-2669A 30份
丁酮 30份
HDI三聚体固化剂 6份
异辛酸铋促进剂 0.6份
（b）通过印刷处理将无色高透明浆料涂饰在聚氨酯合成革表面，涂饰量控制在80g/m2。
（c）烘干温度控制在115℃，烘干时间控制在5分钟。
Claims (4)
1.一种高透明聚氨酯合成革，采用下述方法步骤制备得到：
（a）将聚氨酯树脂、高固丙烯酸改性聚氨酯树脂、丁酮、HDI三聚体固化剂、异辛酸铋促进剂按比例搅拌均匀配成无色高透明浆料；所述浆料组分质量配比如下：
聚氨酯树脂TC-1088A 40～70份
高固丙烯酸改性聚氨酯树脂BF-2669A 30～60份
丁酮 30～50份
HDI三聚体固化剂 5～8份
异辛酸铋促进剂 0.2～0.6份；
（b）将无色高透明浆料涂饰在聚氨酯合成革表面；
（c）将涂饰后的聚氨酯合成革于110~140℃烘干3~5分钟。
2.如权利要求1所述高透明聚氨酯合成革，其特征在于，步骤（a）中的无色高透明浆料在25℃下的黏度为400-800cps。
3.如权利要求1所述高透明聚氨酯合成革，其特征在于，步骤（a）中高固丙烯酸改性聚氨酯树脂BF-2669A，固含量在75%-85%。
4.如权利要求1所述高透明聚氨酯合成革，其特征在于，步骤（b）中的无色浆料涂饰量在50-100g/m2。