CN109749299A - 一种新型pvc环保手套及制备方法 - Google Patents
一种新型pvc环保手套及制备方法 Download PDFInfo
- Publication number
- CN109749299A CN109749299A CN201811471729.1A CN201811471729A CN109749299A CN 109749299 A CN109749299 A CN 109749299A CN 201811471729 A CN201811471729 A CN 201811471729A CN 109749299 A CN109749299 A CN 109749299A
- Authority
- CN
- China
- Prior art keywords
- parts
- plasticizer
- fingerprint
- environmental protection
- pvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及手套技术领域,尤其涉及一种新型PVC环保手套及制备方法。本发明采用的技术方案是:一种PVC手套,由以下重量份数的原料制成:PVC糊树脂86‑94份、替代粉A 2‑6份、替代粉B 4‑8份、增塑剂A15‑25份、增塑剂B 30‑45份、二元酸二丁酯增塑剂5‑10份、钙锌稳定剂1‑2份、降粘剂20‑45份。本发明的优点是:本发明的PVC手套,采用二元酸二丁酯增塑剂代替部分的复合植物油增塑剂,该产品不含有害重金属,不含苯类物质,符合绿色环保要求,同时可以减少体系增塑剂总量,又可提高手套物理性能与降低工艺温度,提高燃煤的利用率,有利于降低企业的生产成本,提高企业的经济效益。
Description
技术领域
本发明涉及手套技术领域,尤其涉及一种新型PVC环保手套及制备方法。
背景技术
PVC具有性能优异、价格低廉、加工简单等优点,广泛应用在建筑材料、地板革、管材、包装膜、发泡材料等各个方面,其中,PVC手套广泛应用于卫生检查、食品业、化工业、电子业、制药业、油漆涂料业、印染业等行业的劳动防护及家庭卫生。但随着人们环保意识的增强和对产品品质要求的提升,PVC手套的使用问题引起越来越多的关注。现有的制备PVC手套所使用的增塑剂都是传统的植物油增塑剂,对车间环境以及工作人员的身体健康都会造成危害,而且使用成本很高,已越来越不能满足使用需求。因此,应该提供一种新的技术方案解决上述问题。
发明内容
本发明的目的是:提供一种可以有效提高产品的物理性能、降低生产成本、提高企业经济效益的新型环保PVC手套及制备方法。
为实现上述目的,本发明采用的技术方案是:
一种新型环保PVC手套,由以下重量份数的原料制成:
进一步的技术方案:
所述替代粉A为碳酸钙。
所述替代粉B为碳酸钙加低聚合度树脂粉的混合物。
所述增塑剂A为WT1增塑剂。
所述增塑剂B为DOTP增塑剂。
所述降粘剂型号为D70降粘剂。
所述低聚合度的树脂粉为1500-1600聚合度的树脂粉。
一种新型PVC环保手套的制备方法,包括如下步骤:
a、搅拌桶中依次加入5-10份二元酸二丁酯增塑剂、15-25份WT1增塑剂、30-45份DOTP增塑剂和1-2份钙锌稳定剂,慢速搅拌,然后加入86-94份PVC糊树脂,2-6份替代粉A,4-8份替代粉B,快速搅拌2-4小时,再加入20-45份的D70降粘剂,真空脱泡后静置备用;
b、将手模预热至60-70℃,然后浸渍到步骤a制备的浆料中,手模垂滴1-3分钟,将手模上的浆料流净后,进入205-215℃的烘箱中烘烤5-6分钟,烘烤过程中手模保持手模转动以保证受热均匀;
c、烘烤结束后,手模冷却到75-85℃后,浸渍聚氨酯浆料,然后经过120-140℃的烤箱1.5-2.5分钟,烘干手模表面水分;
d、继续冷却,卷边机卷边,脱模,获得手套成品。
由于上述技术方案的应用,本发明与现有技术相比具有如下优点:
1、本发明的PVC手套在制备过程中加入了替代粉,使原配方中的PVC糊树脂的添加量可以相应减少,有利于降低企业的生产成本,提高企业的经济效益。
2、本发明的PVC手套,采用二元酸二丁酯增塑剂代替部分的复合植物油增塑剂,该产品不含有害重金属,不含苯类物质,符合绿色环保要求。采用二元酸二丁酯增塑剂可以减少体系增塑剂总量,又可提高手套物理性能与降低工艺温度,提高燃煤的利用率,有利于降低企业的生产成本,提高企业的经济效益。
具体实施方式
下面结合具体实施例对本发明作进一步描述:
实施例1:
一种环保PVC手套,由以下重量份数的原料制成:PVC糊树脂86份、碳酸钙6份、碳酸钙加低聚合度树脂粉的混合物8份、WT1增塑剂15份、DOTP增塑剂45份、二元酸二丁酯增塑剂5份、钙锌稳定剂1份、D70降粘剂20份。
以上环保PVC手套的制备方法,包括如下步骤:
a、搅拌桶中依次加入5份二元酸二丁酯增塑剂、15份WT1增塑剂、DOTP增塑剂45份和1份钙锌稳定剂,慢速搅拌,然后加入86份PVC糊树脂,6份碳酸钙,8份碳酸钙加低聚合度树脂粉的混合物,快速搅拌2小时,再加入D70降粘剂20份,真空脱泡后静置备用;
b、将手模预热至60℃,然后浸渍到步骤a制备的浆料中,手模垂滴1分钟,将手模上的浆料流净后,进入205℃的烘箱中烘烤6分钟,烘烤过程中手模保持手模转动以保证受热均匀;
c、烘烤结束后,手模冷却到75℃后,浸渍聚氨酯浆料,然后经过120℃的烤箱2.5分钟,烘干手模表面水分;
d、继续冷却,卷边机卷边,脱模,获得手套成品。
实施例2
一种环保PVC手套,由以下重量份数的原料制成:PVC糊树脂90份、碳酸钙4份、碳酸钙加低聚合度树脂粉的混合物6份、WT1增塑剂20份、DOTP增塑剂30份、二元酸二丁酯增塑剂10份、钙锌稳定剂1.5份、D70降粘剂33份。
以上环保PVC手套的制备方法,包括如下步骤:
a、搅拌桶中依次加入10份二元酸二丁酯增塑剂、20份WT1增塑剂、30份DOTP增塑剂和1.5份钙锌稳定剂,慢速搅拌,然后加入90份PVC糊树脂,4份碳酸钙,6份碳酸钙加低聚合度树脂粉的混合物,快速搅拌3小时,再加入33份的降粘剂,真空脱泡后静置备用;
b、将手模预热至65℃,然后浸渍到步骤a制备的浆料中,手模垂滴2分钟,将手模上的浆料流净后,进入210℃的烘箱中烘烤5分钟,烘烤过程中手模保持手模转动以保证受热均匀;
c、烘烤结束后,手模冷却到80℃后,浸渍聚氨酯浆料,然后经过130℃的烤箱2分钟,烘干手模表面水分;
d、继续冷却,卷边机卷边,脱模,获得手套成品。
实施例3
一种新型环保PVC手套,由以下重量份数的原料制成:PVC糊树脂94份、碳酸钙2份、碳酸钙加低聚合度树脂粉的混合物4份、WT1增塑剂25份、DOTP增塑剂38份、二元酸二丁酯增塑剂7份、钙锌稳定剂2份、D70降粘剂45份。
以上环保PVC手套的制备方法,包括如下步骤:
a、搅拌桶中依次加入7份二元酸二丁酯增塑剂、25份WT1增塑剂、38份DOTP增塑剂和2份钙锌稳定剂,慢速搅拌,然后加入94份PVC糊树脂,2份碳酸钙,4份碳酸钙加低聚合度树脂粉的混合物,快速搅拌4小时,再加入45份的D70降粘剂,真空脱泡后静置备用;
b、将手模预热至70℃,然后浸渍到步骤a制备的浆料中,手模垂滴3分钟,将手模上的浆料流净后,进入215℃的烘箱中烘烤5分钟,烘烤过程中手模保持手模转动以保证受热均匀;
c、烘烤结束后,手模冷却到85℃后,浸渍聚氨酯浆料,然后经过140℃的烤箱2分钟,烘干手模表面水分;
d、继续冷却,卷边机卷边,脱模,获得手套成品。
对本实施例制备的环保手套,进行性能测试,检测的结果见表1。
表1
结论:由表1可见,采用本发明公开的原料配方和制备方法,制作的样品手套外观正常,样品手套物理性能优良,粘度较低,可以部分替代DOTP使用,降低了制作成本,同时减少了3—5份的降粘剂使用,提高了企业的经济效益。
以上所述是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明所述原理的前提下,还可以作出若干改进或替换,这些改进或替换也应视为本发明的保护范围。
Claims (8)
1.一种新型PVC环保手套,其特征在于,由以下重量份数的原料制成:
2.根据权利要求1所述的一种PVC环保手套,其特征在于:所述替代粉A为碳酸钙。
3.根据权利要求1所述的一种PVC环保手套,其特征在于:所述替代粉B为碳酸钙加低聚合度树脂粉的混合物。
4.根据权利要求1所述的一种PVC环保手套,其特征在于:所述增塑剂A为WT1增塑剂。
5.根据权利要求1所述的一种PVC环保手套,其特征在于:所述增塑剂B为DOTP增塑剂。
6.根据权利要求1所述的一种PVC环保手套,其特征在于:所述降粘剂型号为D70降粘剂。
7.根据权利要求3所述的一种PVC环保手套,其特征在于:所述低聚合度的树脂粉为1500-1600聚合度的树脂粉。
8.如权利要求1-7中任一项的PVC环保手套的制备方法,其特征在于:包括如下步骤:
a、搅拌桶中依次加入5-10份二元酸二丁酯增塑剂、15-25份WT1增塑剂、30-45份DOTP增塑剂和1-2份钙锌稳定剂,慢速搅拌,然后加入86-94份PVC糊树脂,2-6份替代粉A,4-8份替代粉B,快速搅拌2-4小时,再加入20-45份的D70降粘剂,真空脱泡后静置备用;
b、将手模预热至60-70℃,然后浸渍到步骤a制备的浆料中,手模垂滴1-3分钟,将手模上的浆料流净后,进入205-215℃的烘箱中烘烤5-6分钟,烘烤过程中手模保持手模转动以保证受热均匀;
c、烘烤结束后,手模冷却到75-85℃后,浸渍聚氨酯浆料,然后经过120-140℃的烤箱1.5-2.5分钟,烘干手模表面水分;
d、继续冷却,卷边机卷边,脱模,获得手套成品。