CN103467041A - 一种瓷砖及其制作方法 - Google Patents

一种瓷砖及其制作方法 Download PDF

Info

Publication number
CN103467041A
CN103467041A CN 201310408971 CN201310408971A CN103467041A CN 103467041 A CN103467041 A CN 103467041A CN 201310408971 CN201310408971 CN 201310408971 CN 201310408971 A CN201310408971 A CN 201310408971A CN 103467041 A CN103467041 A CN 103467041A
Authority
CN
China
Prior art keywords
ceramic tile
parts
mixture
shell powder
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201310408971
Other languages
English (en)
Inventor
杨益
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201310408971 priority Critical patent/CN103467041A/zh
Publication of CN103467041A publication Critical patent/CN103467041A/zh
Pending legal-status Critical Current

Abstract

一种瓷砖，包括粘土50-100份、石英砂20-60份、甲基丙烯酸甲酯10-15份、甲基丙烯酸10-15份、次氮基三乙酸钠盐2-8份、贝壳粉末6-20份、颜料1-5份和硅酸盐水泥10-20份。一种制作瓷砖的方法，包括下列步骤：第一步、取上述材料进行均匀混合。第二步、将上述混合物进行粉碎，使总体粒度达到100-200微米，加入水，水和混合物的质量比例为1：1.5。第三步、将上部得到的加水的混合物放入模具中，静止5-8小时，然后休整。瓷砖坯。第四步，将瓷砖坯放入窑中进行烧结，得到瓷砖。本瓷砖中加入贝壳粉末，可以在瓷砖中产生晶莹的贝壳光泽，装饰效果好。解决传统瓷砖只有瓷装饰的效果单一的问题。

Description

一种瓷砖及其制作方法
技术领域
本发明属于瓷砖领域，特别涉及一种瓷砖及其制作方法。
背景技术
瓷砖，是以耐火的金属氧化物及半金属氧化物，经由研磨、混合、压制、施釉、烧结之过程，而形成之一种耐酸碱的瓷质或石质等的建筑或者装饰材料。
但是目前使用的瓷砖多是陶瓷效果的，装饰效果单一。
发明内容
本发明的目的是提供一种瓷砖及其制作方法，本方法制作的瓷砖，光泽好，装饰效果好，原料易得，方便实用。
采用的技术方案是：
一种瓷砖，包括粘土50-100份、石英砂20-60份、甲基丙烯酸甲酯10-15份、甲基丙烯酸10-15份、次氮基三乙酸钠盐2-8份、贝壳粉末6-20份、颜料1-5份和硅酸盐水泥10-20份。
贝壳粉末粒度为100-200微米。
一种制作瓷砖的方法，包括下列步骤：
第一步、取质量为粘土50-100份、石英砂20-60份、甲基丙烯酸甲酯10-15份、甲基丙烯酸10-15份、次氮基三乙酸钠盐2-8份、贝壳粉末6-20份、颜料1-5份和硅酸盐水泥10-20份。贝壳粉末粒度为100-200微米。
进行均匀混合。
第二步、将上述混合物进行粉碎，使总体粒度达到100-200微米，加入水，水和混合物的质量比例为1：1.5。
第三步、将上部得到的加水的混合物放入模具中，静置5-8小时，然后休整。瓷砖坯。
第四步，将瓷砖坯放入窑中进行烧结，得到瓷砖。
其优点在于：
本瓷砖中加入贝壳粉末，可以在瓷砖中产生晶莹的贝壳光泽，装饰效果好。解决传统瓷砖只有瓷装饰的效果单一的问题。
具体实施方式
实施例1
一种瓷砖，包括粘土50份、石英砂20份、甲基丙烯酸甲酯10份、甲基丙烯酸10份、次氮基三乙酸钠盐2份、贝壳粉末6份、颜料1份和硅酸盐水泥10份。
贝壳粉末粒度为100微米。
一种制作瓷砖的方法，包括下列步骤：
第一步、取质量为粘土50份、石英砂20份、甲基丙烯酸甲酯10份、甲基丙烯酸10份、次氮基三乙酸钠盐2份、贝壳粉末6份、颜料1份和硅酸盐水泥10份。贝壳粉末粒度为100微米。
进行均匀混合。
第二步、将上述混合物进行粉碎，使总体粒度达到100微米，加入水，水和混合物的质量比例为1：1.5。
第三步、将上部得到的加水的混合物放入模具中，静置5小时，然后休整。瓷砖坯。
第四步，将瓷砖坯放入窑中进行烧结，得到瓷砖。
实施例２
一种瓷砖，包括粘土100份、石英砂60份、甲基丙烯酸甲酯15份、甲基丙烯酸15份、次氮基三乙酸钠盐8份、贝壳粉末20份、颜料5份和硅酸盐水泥20份。
贝壳粉末粒度为200微米。
实施例３
一种瓷砖，包括粘土55份、石英砂26份、甲基丙烯酸甲酯18份、甲基丙烯酸17份、次氮基三乙酸钠盐6.5份、贝壳粉末16份、颜料3份和硅酸盐水泥12份。
贝壳粉末粒度为150微米。

Claims (2)

1.一种瓷砖，其特征在于包括粘土50-100份、石英砂20-60份、甲基丙烯酸甲酯10-15份、甲基丙烯酸10-15份、次氮基三乙酸钠盐2-8份、贝壳粉末6-20份、颜料1-5份和硅酸盐水泥10-20份；
贝壳粉末粒度为100-200微米。
2.制作权利要求１所述的一种瓷砖的方法，包括下列步骤：
第一步、取质量为粘土50-100份、石英砂20-60份、甲基丙烯酸甲酯10-15份、甲基丙烯酸10-15份、次氮基三乙酸钠盐2-8份、贝壳粉末6-20份、颜料1-5份和硅酸盐水泥10-20份；贝壳粉末粒度为100-200微米；
进行均匀混合；
第二步、将上述混合物进行粉碎，使总体粒度达到100-200微米，加入水，水和混合物的质量比例为1：1.5；
第三步、将上部得到的加水的混合物放入模具中，静止5-8小时，然后休整；瓷砖坯；
第四步，将瓷砖坯放入窑中进行烧结，得到瓷砖。
CN 201310408971 2013-09-11 2013-09-11 一种瓷砖及其制作方法 Pending CN103467041A (zh)