CN103450970A - 铌与铌合金板带材成品冷轧润滑剂 - Google Patents

铌与铌合金板带材成品冷轧润滑剂 Download PDF

Info

Publication number
CN103450970A
CN103450970A CN2013104154220A CN201310415422A CN103450970A CN 103450970 A CN103450970 A CN 103450970A CN 2013104154220 A CN2013104154220 A CN 2013104154220A CN 201310415422 A CN201310415422 A CN 201310415422A CN 103450970 A CN103450970 A CN 103450970A
Authority
CN
China
Prior art keywords
niobium
finished product
product cold
alloy plate
plate band
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013104154220A
Other languages
English (en)
Other versions
CN103450970B (zh
Inventor
黄福川
毛汉领
莫宇飞
粟满荣
唐兴中
蓝明新
肖友程
李胜
梁慧
唐彩珍
田宗义
廖丹葵
刘琨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi University
Original Assignee
Guangxi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi University filed Critical Guangxi University
Priority to CN201310415422.0A priority Critical patent/CN103450970B/zh
Publication of CN103450970A publication Critical patent/CN103450970A/zh
Application granted granted Critical
Publication of CN103450970B publication Critical patent/CN103450970B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种铌与铌合金板带材成品冷轧润滑剂，采用15号工业白油作为基础油，配合多种复合添加剂，包括抗磨剂、油性剂、抗氧防腐剂、抗氧剂、抗泡剂、清净剂、分散剂等。采用在退火时不产生油斑的低粘度、低含硫的矿物油润滑剂，减少成品冷轧时轧辊和材料的粘着现象，满足板形和表面光洁度要求。

Description

铌与铌合金板带材成品冷轧润滑剂
技术领域
本发明属铌与铌合金板带材成品冷轧润滑剂领域。
背景技术
铌是灰白色金属，熔点2468℃，沸点4742℃，密度8.57g/cm3。室温下铌在空气中稳定，在氧气中红热时也不被完全氧化，高温下与硫、氮、碳直接化合，能与钛、锆、铪、钨形成合金。不与无机酸或碱作用，也不溶于王水，但可溶于氢氟酸。铌能吸收气体，用作除气剂，也是一种良好的超导体。用铌制造的合金，临界温度高达绝对温度十八点五到二十一度，是目前最重要的超导材料。在钢的各种微合金化元素中，铌是最有效的微合金化元素，铌的作用如此之大，以至于铁原子中含有丰富的铌原子，就能达到改善钢性能的目的。
实际上钢中加入0.001%～0.1%的铌，就足以改变钢的力学性能。铌还可以通过诱导析出和控制冷却速度，实现析出物弥散分布。在较宽的范围内调整钢的韧性水平。因此，加入铌不仅可以提高钢的强度，还可以提高钢的韧性、抗高温氧化性和耐蚀性，降低钢脆性转变温度，获得好的焊接性能和成型性能。
成品冷轧轧制时，由于弹性压扁使带材边部的单位压力很小，而带材中部的单位压力很高。若采用随压力增加而摩擦系数显著增加的润滑剂，薄带会产生很大的边缘延伸而影响其平直度。铌在冷轧时，随着道次压下量的加大和轧制速度加快，表面光洁度会降低，这就是轧辊和材料的热粘现象，这时生成的微小磨损粉末附着在轧辊或材表面上，使板材表面粗糙。在铌冷轧(精轧)时，由于侧重于产品表面质量，在满足板形要求的情况下，尽量少加润滑剂。因此，应采用在退火时不产生油斑的低粘度、低含硫的矿物油润滑剂。
发明内容
本发明要解决的技术问题是提供一种在退火时不产生油斑的低粘度、低含硫的矿物油润滑剂，可减少冷轧时轧辊和材料的粘着现象、满足板形和表面光洁度要求的铌与铌合金板带材成品冷轧润滑剂。
本发明以如下技术方案解决上述技术问题：采用15号工业白油作为基础油，配合多种复合添加剂，其各组分及其质量百分数为：
组分 含量(质量百分比)
基础油 75%～85%
抗磨剂 5.0%～9.0%
油性剂 4.0%～6.0%
抗氧防腐剂 0.3%～1.2%
抗氧剂 0.2%～0.8%
抗泡剂 0.001%～0.005%
清净剂 1.0%～3.0%
分散剂 2.0%～5.0%
基础油是15号工业白油。
抗磨剂是质量比70%～60%的硫化异丁烯与30%～40%的硫代磷酸铵盐复合。
油性剂是质量比40%～50%的油酸与60%～50%的磷酸酯复合。
抗氧防腐剂是硫磷丁辛基锌盐。
抗氧剂是对,对二异辛基二苯胺。
抗泡剂是二甲基硅油。
清净剂是环烷酸镁。
分散剂是多烯基丁二酰亚胺。
本发明的铌与铌合金板带材成品冷轧润滑剂，采用在退火时不产生油斑的低粘度、低含硫的矿物油润滑剂，以减少成品冷轧时轧辊和材料的粘着现象，满足板形和表面光洁度要求。
具体实施方式
实施例1：
将下列组分按质量百分比调和而成：
组分 含量(质量百分比)
15号工业白油 75％
质量比60%的硫化异丁烯与40%的硫代磷酸铵盐复合 9.0％
质量比50%的油酸与50%的磷酸酯复合 6.0％
硫磷丁辛基锌盐 1.2％
对，对二异辛基二苯胺 0.795％
二甲基硅油 0.005%
环烷酸镁 3.0％
多烯基丁二酚亚胺 5.0％
以上组分总和为100%。
实施例2：
将下列组分按质量百分比调和而成：
组分 含量(质量百分比)
15号工业白油 80％
质量比70%的硫化异丁烯与30%的硫代磷酸铵盐复合 7.0%
质量比40%的油酸与60%的磷酸酯复合 5.0%
硫磷丁辛基锌盐 1.0%
对，对二异辛基二苯胺 0.596%
二甲基硅油 0.004%
环烷酸镁 2.4%
多烯基丁二酚亚胺 4.0%
以上组分总和为100%。
实施例3：
将下列组分按质量百分比调和而成：
组分 含量(质量百分比)
15号工业白油 85％
质量比65%的硫化异丁烯与35%的硫代磷酸铵盐复合 5.5％
质量比45%的油酸与55%的磷酸酯复合 4.0％
硫磷丁辛基锌盐 0.9％
对，对二异辛基二苯胺 0.798％
二甲基硅油 0.002％
环烷酸镁 1.6％
多烯基丁二酚亚胺 2.2％
以上组分总和为100%。
以下是实施例1产品的主要理化指标：
项目 质量指标
水分，% 痕迹
40℃运动粘度mm2/s 15.3
闪点(开口)℃， 140
机械杂质，% 无
最大无卡咬负荷(Pb)，Kg 90
倾点，℃， -8
水溶性酸或碱 无
腐蚀试验(铜片、100℃、3h)，级 1
粘度指数 90

Claims (9)

1.一种铌与铌合金板带材成品冷轧润滑剂，其特征在于采用15号工业白油作为基础油，配合多种复合添加剂，其各组分及其质量百分数为：
组分 质量百分比含量 基础油 75%～85% 抗磨剂 5.0%～9.0% 油性剂 4.0%～6.0% 抗氧防腐剂 0.3%～1.2% 抗氧剂 0.2%～0.8% 抗泡剂 0.001%～0.005% 清净剂 1.0%～3.0% 分散剂 2.0%～5.0%
                                 。
2.如权利要求1所述的铌及铌合金板带材成品冷轧润滑剂，其特征在于基础油是15号工业白油。
3.如权利要求1所述的铌与铌合金板带材成品冷轧润滑剂，其特征在于抗磨剂是质量比70%～60%的硫化异丁烯与30%～40%的硫代磷酸铵盐复合。
4.如权利要求1所述的铌与铌合金板带材成品冷轧润滑剂，其特征在于油性剂是质量比40%～50%的油酸与60%～50%的磷酸酯复合。
5.如权利要求1所述的铌与铌合金板带材成品冷轧润滑剂，其特征在于抗氧防腐剂是硫磷丁辛基锌盐。
6.如权利要求1所述的铌与铌合金板带材成品冷轧润滑剂，其特征在于抗氧剂是对,对二异辛基二苯胺。
7.如权利要求1所述的铌与铌合金板带材成品冷轧润滑剂，其特征在于抗泡剂是二甲基硅油。
8.如权利要求1所述的铌与铌合金板带材成品冷轧润滑剂，其特征在于清净剂是环烷酸镁。
9.如权利要求1所述的铌与铌合金板带材成品冷轧润滑剂，其特征在于分散剂是多烯基丁二酰亚胺。
CN201310415422.0A 2013-09-12 2013-09-12 铌与铌合金板带材成品冷轧润滑剂 Active CN103450970B (zh)