CN103449817A - 一种硅碳棒冷端及其生产方法 - Google Patents

一种硅碳棒冷端及其生产方法 Download PDF

Info

Publication number
CN103449817A
CN103449817A CN2012101720759A CN201210172075A CN103449817A CN 103449817 A CN103449817 A CN 103449817A CN 2012101720759 A CN2012101720759 A CN 2012101720759A CN 201210172075 A CN201210172075 A CN 201210172075A CN 103449817 A CN103449817 A CN 103449817A
Authority
CN
China
Prior art keywords
kilograms
silicon carbide
powder
mesh
size
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012101720759A
Other languages
English (en)
Inventor
朱丽辉
刘冬义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIAOYANG HONGTU CARBIDE Co Ltd
Original Assignee
LIAOYANG HONGTU CARBIDE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIAOYANG HONGTU CARBIDE Co Ltd filed Critical LIAOYANG HONGTU CARBIDE Co Ltd
Priority to CN2012101720759A priority Critical patent/CN103449817A/zh
Publication of CN103449817A publication Critical patent/CN103449817A/zh
Pending legal-status Critical Current

Abstract

硅碳棒冷端及其生产方法涉及一种硅碳棒冷端及其生产方法。主要是为解决现有的硅碳棒冷端中含有沥青，生产时对人体有害，污染环境的问题而发明的。配方中包括绿碳化硅50公斤、分解石墨粉10公斤、煅后焦粉40公斤、小麦粉10公斤、糊精5公斤、木粉5公斤、机油5公斤。将上述各种原料按所述的重量比称好后，放入卧式混料锅内混合均匀，然后放入500吨卧式压力机的料缸中压制成型，在200℃温度中进行烘干，烘干后用碳管炉烧结。所述的绿碳化硅是150目的，分解石墨粉是200目的，煅后焦粉是100目的，木粉是100目的。优点是生产时对人体无害，不会污染环境。

Description

一种硅碳棒冷端及其生产方法
技术领域：
本发明涉及一种硅碳棒冷端及其生产方法。
背景技术：
现有的硅碳棒冷端一般是以绿碳化硅、分解石墨粉、煅后焦粉和沥青为原料生产的，缺点是：由于原料中含有沥青，生产时对人体有害，污染环境。
发明内容：
本发明所要解决的技术问题是提供一种原料中不含沥青，生产时对人体无害，不会污染环境的硅碳棒冷端及其生产方法。
上述目的是这样实现的：配方中包括绿碳化硅50公斤、分解石墨粉10公斤、煅后焦粉40公斤、小麦粉10公斤、糊精5公斤、木粉5公斤、机油5公斤。
所述的绿碳化硅是150目的，分解石墨粉是200目的，煅后焦粉是100目的，木粉是100目的。
生产方法是：将上述各种原料按所述的重量比称好后，放入卧式混料锅内混合均匀，然后放入500吨卧式压力机的料缸中压制成型，在200℃温度中进行烘干，烘干后用碳管炉烧结。
本发明的优点是：由于配方中不含有沥青，所以生产时对人体无害，不会污染环境。
具体实施方式：
配方中包括绿碳化硅50公斤、分解石墨粉10公斤、煅后焦粉40公斤、小麦粉10公斤、糊精5公斤、木粉5公斤、机油5公斤。
所述的绿碳化硅是150目的，分解石墨粉是200目的，煅后焦粉是100目的，木粉是100目的。
生产方法是：将上述各种原料按所述的重量比称好后，放入卧式混料锅内混合均匀，然后放入500吨卧式压力机的料缸中压制成型，在200℃温度中进行烘干，烘干后用碳管炉烧结。
。

Claims (2)

1.一种硅碳棒冷端及其生产方法，其特征是：配方中包括绿碳化硅50公斤、分解石墨粉10公斤、煅后焦粉40公斤、小麦粉10公斤、糊精5公斤、木粉5公斤、机油5公斤；将上述各种原料按所述的重量比称好后，放入卧式混料锅内混合均匀，然后放入500吨卧式压力机的料缸中压制成型，在200℃温度中进行烘干，烘干后用碳管炉烧结。
2.按照权利要求1所述的硅碳棒冷端，其特征是：所述的绿碳化硅是150目的，分解石墨粉是200目的，煅后焦粉是100目的，木粉是100目的。
CN2012101720759A 2012-05-30 2012-05-30 一种硅碳棒冷端及其生产方法 Pending CN103449817A (zh)