CN103436084A - 一种导电性油墨 - Google Patents
一种导电性油墨 Download PDFInfo
- Publication number
- CN103436084A CN103436084A CN2013103403194A CN201310340319A CN103436084A CN 103436084 A CN103436084 A CN 103436084A CN 2013103403194 A CN2013103403194 A CN 2013103403194A CN 201310340319 A CN201310340319 A CN 201310340319A CN 103436084 A CN103436084 A CN 103436084A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- parts
- conductive ink
- printing ink
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种导电性油墨,以质量份计含有以下成分:丙烯酸树脂M109为25~40质量份,二醇型柔性凸版导电油墨连结料60~70质量份,乙二醇10~20质量份,氯化橡胶液15~18质量份,尿素10~15质量份,三乙醇胺5~10质量份,一缩二乙二醇10~20质量份,硬脂酸铝0.1~0.4质量份,一乙醇胺0.5~1质量份,气相二氧化硅1~4质量份,导电炭黑25~30质量份。本发明提供的导电性油墨,导电性优良、附着力、印刷适性和耐溶剂性好,适用于QB/T2023-1994规定的标准,黏度30000mPa·s/25℃,酸值120mgKOH/g,细度≤20微米,流动度35mm/25℃。
Description
技术领域
本发明涉及一种油墨,尤其涉及一种导电性油墨。
背景技术
导电油墨,用导电材料(金、银、铜和碳)分散在连结料中制成的糊状油墨,俗称糊剂油墨。具有一定程度导电性质,可作为印刷导电点或导电线路之用。金系导电墨、银系导电墨、铜系导电墨、碳系导电墨等已达到实用化,用于印刷电路、电极、电镀底层、键盘接点、印制电阻等材料。
导电性油墨是指印刷于导电承印物上,使之具有传导电流和排除积累静电荷能力的油墨,一般是印在塑料、玻璃、陶瓷或纸板等非导电承印物上。印刷方法很广,如丝网印刷、凸版印刷、柔性版印刷、凹版印刷和平板印刷等均可采用。可根据膜厚的要求而选用不同的印刷方法、膜厚不同则电阻、阻焊性及耐摩擦性等亦各异。这种油墨有厚膜色浆和树脂型两种。前者是以玻璃料为黏合剂的高温烧成型,后者是以合成树脂为黏合剂的低温干燥或辐射(UV、EB)固化型的丝网油墨。
发明内容
解决的技术问题:针对油墨导电性、附着力、印刷适应性差等弊端,提供一种导电性优良、附着力、印刷适性和耐溶剂性好的导电性油墨。
技术方案:一种导电性油墨,以质量份计含有以下成分:丙烯酸树脂M109为25~40质量份,二醇型柔性凸版导电油墨连结料60~70质量份,乙二醇10~20质量份,氯化橡胶液15~18质量份,尿素10~15质量份,三乙醇胺5~10质量份,一缩二乙二醇10~20质量份,硬脂酸铝0.1~0.4质量份,一乙醇胺0.5~1质量份,气相二氧化硅1~4质量份,导电炭黑25~30质量份。
作为本发明的一种优选技术方案:一种导电性油墨,以质量份计含有以下成分:丙烯酸树脂M109为30质量份,二醇型柔性凸版导电油墨连结料65质量份,乙二醇15质量份,氯化橡胶液17质量份,尿素12.5质量份,三乙醇胺8质量份,一缩二乙二醇15质量份,硬脂酸铝0.2质量份,一乙醇胺0.8质量份,气相二氧化硅2质量份,导电炭黑28质量份。
有益效果:本发明提供的导电性油墨,导电性优良、附着力、印刷适性和耐溶剂性好,适用于QB/T2023-1994规定的标准,黏度30000mPa·s/25℃,酸值120mgKOH/g,细度≤20微米,流动度35mm/25℃。
具体实施方式
实施例1
本实施例提供一种导电性油墨,以质量份计含有以下成分:丙烯酸树脂M109为25质量份,二醇型柔性凸版导电油墨连结料60质量份,乙二醇10质量份,氯化橡胶液15质量份,尿素10质量份,三乙醇胺5质量份,一缩二乙二醇10质量份,硬脂酸铝0.1质量份,一乙醇胺0.5质量份,气相二氧化硅1质量份,导电炭黑25质量份。
实施例2
本实施例提供一种导电性油墨,以质量份计含有以下成分:丙烯酸树脂M109为40质量份,二醇型柔性凸版导电油墨连结料70质量份,乙二醇20质量份,氯化橡胶液18质量份,尿素15质量份,三乙醇胺10质量份,一缩二乙二醇20质量份,硬脂酸铝0.4质量份,一乙醇胺1质量份,气相二氧化硅4质量份,导电炭黑30质量份。
实施例3
本实施例提供一种导电性油墨,以质量份计含有以下成分:丙烯酸树脂M109为30质量份,二醇型柔性凸版导电油墨连结料65质量份,乙二醇15质量份,氯化橡胶液17质量份,尿素12.5质量份,三乙醇胺8质量份,一缩二乙二醇15质量份,硬脂酸铝0.2质量份,一乙醇胺0.8质量份,气相二氧化硅2质量份,导电炭黑28质量份。
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (2)
1.一种导电性油墨,其特征在于以质量份计含有以下成分:丙烯酸树脂M109为25~40质量份,二醇型柔性凸版导电油墨连结料60~70质量份,乙二醇10~20质量份,氯化橡胶液15~18质量份,尿素10~15质量份,三乙醇胺5~10质量份,一缩二乙二醇10~20质量份,硬脂酸铝0.1~0.4质量份,一乙醇胺0.5~1质量份,气相二氧化硅1~4质量份,导电炭黑25~30质量份。
2.根据权利要求1所述的一种导电性油墨,其特征在于以质量份计含有以下成分:丙烯酸树脂M109为30质量份,二醇型柔性凸版导电油墨连结料65质量份,乙二醇15质量份,氯化橡胶液17质量份,尿素12.5质量份,三乙醇胺8质量份,一缩二乙二醇15质量份,硬脂酸铝0.2质量份,一乙醇胺0.8质量份,气相二氧化硅2质量份,导电炭黑28质量份。