CN103436074B - 一种水性导电墨的制备方法 - Google Patents

一种水性导电墨的制备方法 Download PDF

Info

Publication number
CN103436074B
CN103436074B CN201310334861.9A CN201310334861A CN103436074B CN 103436074 B CN103436074 B CN 103436074B CN 201310334861 A CN201310334861 A CN 201310334861A CN 103436074 B CN103436074 B CN 103436074B
Authority
CN
China
Prior art keywords
dispersion
parts
carbon nanotube
water
printing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310334861.9A
Other languages
English (en)
Other versions
CN103436074A (zh
Inventor
孙晓刚
杨湘杰
李颖毅
吴毅强
姚军
曹宏辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henan Calway Nano Carbon Materials Co Ltd
Original Assignee
Nanchang University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanchang University filed Critical Nanchang University
Priority to CN201310334861.9A priority Critical patent/CN103436074B/zh
Publication of CN103436074A publication Critical patent/CN103436074A/zh
Application granted granted Critical
Publication of CN103436074B publication Critical patent/CN103436074B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种水性导电墨的制备方法，其特征是按步骤如下：（1）先将碳纳米管石墨化处理；然后将碳纳米管微波处理；（2）处理后的碳纳米管加入到去离子水中球磨分散24小时后，再高速剪切分散10小时；（3）初步分散的碳纳米管分散液中加入适量的分散剂超声分散12小时；（4）加入适量水性粘结剂搅拌2h，再超声分散12小时；其组分按重量份数为：导电功能体5~50份；粘结剂5-50份；分散剂0.5~10份；去离子水100份。发明水性导电墨可用于印刷电子领域，在基体上印刷或打印导电薄膜或电子电路，用于打印RFID天线、护照、身份识别卡、商品电子标签；用于锂离子电池导电剂，打印晶体管等。在透明基体PET薄膜上印刷上碳纳米管导电薄膜可制成透明导电薄膜替代ITO玻璃。

Description

一种水性导电墨的制备方法
技术领域
本发明涉及一种纳米导电流体碳纳米管导电墨水的制备方法。
背景技术
碳纳米管是由碳构成的一维晶态结构纳米材料，具有极高的强度和优异的导电导热性能，在基体材料中添加少量碳纳米管，经充分分散后就能构成三维到电网络，从而极大提高基体材料的导电和导热性能。但传统工艺合成的碳纳米管非常弯曲，相互缠绕严重，分散困难。一般需要通过强酸处理，表面接枝官能团来提高可分散性。晶须状碳纳米管的合成成功，彻底改变了碳纳米管相互缠绕，难于分散的难题。晶须状碳纳米管为直线型一维材料，相互之间不缠绕，易于分散。由于不需要强酸处理，因此不会改变碳纳米管的表面结构，碳纳米管导电性能得以充分发挥，为导电墨水的制造提供了了良好基础。
发明内容
本发明的目的是提出一种水性导电墨的制备方法，以晶须状碳纳米管为导电功能体，碳纳米管经热处理后分散在去离子水中制成悬浮液，成为导电墨水。
本发明是通过以下技术方案实现的。
（1）先将碳纳米管石墨化处理；然后将碳纳米管微波处理。
（2）处理后的碳纳米管加入到去离子水中球磨分散24小时后，再高速剪切分散10小时。
（3）初步分散的碳纳米管分散液中加入适量的分散剂超声分散12小时。
（4）加入适量水性粘结剂搅拌2h，再超声分散12小时。
其组分按重量份数为：导电功能体5~50份；粘结剂5-50份；分散剂0.5~10份；去离子水100份。
所述的导电功能体是碳纳米管、碳纳米管与石墨烯复合体或碳纳米管与导电炭黑的复合体。
所述的粘结剂为羧甲基纤维素、羟丙基甲基纤维素、聚苯乙烯磺酸钠或聚乙烯吡咯烷酮中的一种或两种以上。
所述的分散剂为十二烷基苯磺酸纳、十二烷基硫酸钠中的一种或两种。
发明水性导电墨可用于印刷电子领域，根据产品对电导率的要求可调节导电墨的电导率，通过印刷方式或使用喷墨打印机，在基体上印刷或打印导电薄膜或电子电路，可用于打印RFID（电子标签）天线，用于护照，身份识别卡，商品电子标签。也可用于锂离子电池导电剂，打印晶体管等。在透明基体PET薄膜上印刷上碳纳米管导电薄膜可制成透明导电薄膜用于替代ITO玻璃。
具体实施方式
实施例1。
(1)称取5g碳纳米管放入真空石墨化炉中，升温到3000℃后保温一小时，然后自然冷却。
将石墨化的碳纳米管放入微波炉中，微波照射10分钟，然后取出。
(2)将热处理后的碳纳米管放入100ml的去离子水中在球磨机中球磨分散24h,取出后再用高速剪切机分散处理10h。
(3)碳纳米管分散液中加入1g十二烷基苯磺酸纳，超声处理12h。
(4)上述分散液再加入5g羧甲基纤维素,边搅拌变均匀加入，然后再超声分散12h。
实施例2。
(1)称取5g碳纳米管放入真空石墨化炉中，升温到2800℃后保温一小时，然后自然冷却。
将石墨化的碳纳米管放入微波炉中，微波照射20分钟，然后取出。
(2)将热处理后的碳纳米管放入100ml的去离子水中在球磨机中球磨分散24h,取出后再用高速剪切机分散处理10h。
(3)碳纳米管分散液中加入2g十二烷基硫酸纳，超声处理12h。
(4)上述分散液再加入5g羟丙基甲基纤维素,边搅拌变均匀加入，然后再超声分散12h。
实施例3。
(1)称取5g碳纳米管放入真空石墨化炉中，升温到2800℃后保温一小时，然后自然冷却。
将石墨化的碳纳米管放入微波炉中，微波照射5分钟，然后取出。
(2)将热处理后的碳纳米管放入100ml的去离子水中在球磨机中球磨分散24h,取出后再用高速剪切机分散处理10h。
(3)碳纳米管分散液中加入3g十二烷基硫酸纳，超声处理12h。
(4)上述分散液再加入5g聚乙烯吡咯烷酮,边搅拌变均匀加入，然后再超声分散12h。

Claims (3)

1.一种水性导电墨的制备方法，其特征是按步骤如下：
（1）先将导电功能体石墨化处理；然后将碳纳米管微波处理；
（2）处理后的导电功能体加入到去离子水中球磨分散24小时后，再高速剪切分散10小时；
（3）初步分散的导电功能体分散液中加入适量的分散剂超声分散12小时；
（4）加入适量水性粘结剂搅拌2h，再超声分散12小时；
其组分按重量份数为：导电功能体5~50份；粘结剂5-50份；分散剂0.5~10份；去离子水100份；
所述的导电功能体是碳纳米管、碳纳米管与石墨烯复合体或碳纳米管与导电炭黑的复合体。
2.根据权利要求1所述的制备方法，其特征是所述的粘结剂为羧甲基纤维素、羟丙基甲基纤维素、聚苯乙烯磺酸钠或聚乙烯吡咯烷酮中的一种或两种以上。
3.根据权利要求1所述的制备方法，其特征是所述的分散剂为十二烷基苯磺酸纳、十二烷基硫酸钠中的一种或两种。
CN201310334861.9A 2013-08-05 2013-08-05 一种水性导电墨的制备方法 Active CN103436074B (zh)