CN103421281B - Pet/petg的增韧增温剂 - Google Patents

Pet/petg的增韧增温剂 Download PDF

Info

Publication number
CN103421281B
CN103421281B CN201310151310.9A CN201310151310A CN103421281B CN 103421281 B CN103421281 B CN 103421281B CN 201310151310 A CN201310151310 A CN 201310151310A CN 103421281 B CN103421281 B CN 103421281B
Authority
CN
China
Prior art keywords
parts
pet
petg
grafted
maleic anhydride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310151310.9A
Other languages
English (en)
Other versions
CN103421281A (zh
Inventor
彭朕财
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Xin Hengli Science And Technology Ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310151310.9A priority Critical patent/CN103421281B/zh
Publication of CN103421281A publication Critical patent/CN103421281A/zh
Application granted granted Critical
Publication of CN103421281B publication Critical patent/CN103421281B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种PET/PETG的增韧增温剂，其特征在于所述PET/PETG的增韧增温剂按下列原料的质量份数配制而成：1，4-环己二甲醇:66～87份；热塑性弹性体SEBS:15～30份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:10～15份；丁苯橡胶接枝马来酸酐合成的成核物:10～15份；苯甲酸钠:10～15份；抗氧剂1010:3～8份。通过本发明所述技术方案，可以配制成液体PET/PETG的增韧增温剂，可以增加透明PET(PETG)的韧性的同时提高热变型温度。

Description

PET/PETG的增韧增温剂
技术领域
本发明涉及塑料添加剂的技术领域，具体说是PET/PETG的增韧增温剂的技术。
背景技术
聚对苯二甲酸乙二醇酯(PET)是一种热塑性工程塑料，具有较好的力学性能、电绝缘性、耐热性和耐化学试剂性，因而广泛用于纤维、薄膜以及饮料瓶领域。
在通常应用的加工模温下，PET的结晶速率太慢而造成结晶不完善和不均匀，致使模塑周期延长，制品易粘附在模具上，并有翘曲、表面粗糙无光泽、耐冲击性和耐湿热性差等缺点。
PET工程化的关键问题在于如何提高PET树脂的结晶速率，相应提高PET的抗冲击性和机械强度。现有的成核剂以及结晶促进剂出现较多新问题。如易引起PET降解，特别是在加工过程中使分子质量下降，影响力学强度，对熔体具有增稠效应，难于得到高分子质量的PET，这将对材料的力学性能产生负面影响，耐候性差，硬度大，影响工程塑料力学性能。
发明内容
本发明的目的是提供一种PET/PETG的增韧增温剂，有效降低成本，PET/PETG的力学性能效果改善显著，增强韧性的同时提高热变型温度。
本发明通过以下技术方案来实现。
一种PET/PETG的增韧增温剂，其特征在于所述PET/PETG的增韧增温剂按下列原料的质量份数配制而成：1，4-环己二甲醇:66～87份；热塑性弹性体SEBS:15～30份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:10～15份；丁苯橡胶接枝马来酸酐合成的成核物:10～15份；苯甲酸钠:10～15份；抗氧剂1010:3～8份。
具体如下：所述1，4-环己二甲醇:66份；热塑性弹性体SEBS:15份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:10份；丁苯橡胶接枝马来酸酐合成的成核物:10份；苯甲酸钠:10份；抗氧剂1010:3份。
或者所述1，4-环己二甲醇:67份；热塑性弹性体SEBS:18份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:10份；丁苯橡胶接枝马来酸酐合成的成核物:10份；苯甲酸钠:10份；抗氧剂1010:5份。
或者所述1，4-环己二甲醇:75份；热塑性弹性体SEBS:20份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:12份；丁苯橡胶接枝马来酸酐合成的成核物:12份；苯甲酸钠:12份；抗氧剂1010:5份。
或者所述1，4-环己二甲醇:80份；热塑性弹性体SEBS:25份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:13份；丁苯橡胶接枝马来酸酐合成的成核物:13份；苯甲酸钠:13份；抗氧剂1010:6份。
或者所述1，4-环己二甲醇:85份；热塑性弹性体SEBS:20份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:15份；丁苯橡胶接枝马来酸酐合成的成核物:13份；苯甲酸钠:12份；抗氧剂1010:7份。
或者所述1，4-环己二甲醇:87份；热塑性弹性体SEBS:30份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:15份；丁苯橡胶接枝马来酸酐合成的成核物:15份；苯甲酸钠:15份；抗氧剂1010:8份。
或者所述1，4-环己二甲醇:86份；热塑性弹性体SEBS:15份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:14份；丁苯橡胶接枝马来酸酐合成的成核物:15份；苯甲酸钠:15份；抗氧剂1010:7份。
本发明与现有技术相比具有以下优点。
1)PET是由对苯二甲酸(TPA)(或对苯二甲酸二甲酯(DMT))与乙二醇(EG)缩聚而成的。在PET的聚合过程中加入CHDM即1，4-环己二甲醇，进行共缩聚制得ET/CT共聚酯P(ET/CT)。可见，共聚酯在聚合过程中，除PET的基本单体之外，增加了第三单体CHDM，使大分子结构发生变化，以达到改善其物理、化学性质的目的。CHDM的加入，使P(ET/CT)共聚酯具有强的韧性和高的冲击强度。
2)热塑性弹性体SEBS，在聚对苯二甲酸乙二醇酯即PET中分散不均匀，团聚现象严重，加入相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:就可以降低界面张力，促进连续相PET和分散相SEBS的粘结，使SEBS颗粒尺寸明显减小，起到分散作用。SEBS的添加能够提高材料的缺口冲击韧性，SEBS含量增加，材料缺口冲击强度随之增加。
3)复合成核剂苯甲酸钠的加入使PET的结晶峰温、结晶放热焓和结晶速率常数与纯PET相比分别相应增加，据试验，分别增加48.6℃、30.14J/R和3.93，而半结晶时间减小，据试验，减小了1min。
4)丁苯橡胶接枝马来酸酐合成的成核物与PET共混就能使冲击性能大大提高。据试验，100份PET中掺混15份接枝率为0.6％的SBRG即丁苯橡胶接枝马来酸酐使复合物的冲击强度比纯PET提高了2.5倍。
本发明按照上述配方，可以配制成液体PET/PETG的增韧增温剂，可以增加透明PET/PETG的韧性的同时提高热变型温度。
具体实施方式
一种PET/PETG的增韧增温剂，其特征在于所述PET/PETG的增韧增温剂按下列原料的质量份数配制而成：1，4-环己二甲醇:66～87份；热塑性弹性体SEBS:15～30份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:10～15份；丁苯橡胶接枝马来酸酐合成的成核物:10～15份；苯甲酸钠:10～15份；抗氧剂1010:3～8份。
下面是各配方的实施例：
实施例一：1，4-环己二甲醇:66份；热塑性弹性体SEBS:15份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:10份；丁苯橡胶接枝马来酸酐合成的成核物:10份；苯甲酸钠:10份；抗氧剂1010:3份。
实施例二：1，4-环己二甲醇:67份；热塑性弹性体SEBS:18份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:10份；丁苯橡胶接枝马来酸酐合成的成核物:10份；苯甲酸钠:10份；抗氧剂1010:5份。
实施例三：1，4-环己二甲醇:75份；热塑性弹性体SEBS:20份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:12份；丁苯橡胶接枝马来酸酐合成的成核物:12份；苯甲酸钠:12份；抗氧剂1010:5份。
实施例四：1，4-环己二甲醇:80份；热塑性弹性体SEBS:25份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:13份；丁苯橡胶接枝马来酸酐合成的成核物:13份；苯甲酸钠:13份；抗氧剂1010:6份。
实施例五：1，4-环己二甲醇:85份；热塑性弹性体SEBS:20份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:15份；丁苯橡胶接枝马来酸酐合成的成核物:13份；苯甲酸钠:12份；抗氧剂1010:7份。
实施例六：1，4-环己二甲醇:87份；热塑性弹性体SEBS:30份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:15份；丁苯橡胶接枝马来酸酐合成的成核物:15份；苯甲酸钠:15份；抗氧剂1010:8份。
实施例七：1，4-环己二甲醇:86份；热塑性弹性体SEBS:15份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯:14份；丁苯橡胶接枝马来酸酐合成的成核物:15份；苯甲酸钠:15份；抗氧剂1010:7份。
在本发明中，按照上述配方，可以配制成液体PET/PETG的增韧增温剂，可以增加透明PET(PETG)的韧性的同时提高热变型温度。

Claims (8)

1.一种PET/PETG的增韧增温剂，其特征在于所述PET/PETG的增韧增温剂按下列原料的质量份数配制而成：
 1，4-环己二甲醇：66～87份；
 热塑性弹性体SEBS：15～30份；
 相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯：10～15份；
 丁苯橡胶接枝马来酸酐合成的成核物：10～15份；
 苯甲酸钠：10～15份；
 抗氧剂1010：3～8份。
2.根据权利要求1所述的PET/PETG的增韧增温剂，其特征在于：所述1，4-环己二甲醇66份；热塑性弹性体SEBS：15份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯：10份；丁苯橡胶接枝马来酸酐合成的成核物：10份；苯甲酸钠：10份；抗氧剂1010：3份。
3.根据权利要求1或2所述的PET/PETG的增韧增温剂，其特征在于：所述1，4-环己二甲醇67份；热塑性弹性体SEBS：18份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯：10份；丁苯橡胶接枝马来酸酐合成的成核物：10份；苯甲酸钠：10份；抗氧剂1010：5份。
4.根据权利要求1或2所述的PET/PETG的增韧增温剂，其特征在于：所述1，4-环己二甲醇75份；热塑性弹性体SEBS：20份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯：12份；丁苯橡胶接枝马来酸酐合成的成核物：12份；苯甲酸钠：12份；抗氧剂1010：5份。
5.根据权利要求1或2所述的PET/PETG的增韧增温剂，其特征在于：所述1，4-环己二甲醇80份；热塑性弹性体SEBS：25份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯：13份；丁苯橡胶接枝马来酸酐合成的成核物：13份；苯甲酸钠：13份；抗氧剂1010：6份。
6.根据权利要求1或2所述的PET/PETG的增韧增温剂，其特征在于：所述1，4-环己二甲醇85份；热塑性弹性体SEBS：20份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯：15份；丁苯橡胶接枝马来酸酐合成的成核物：13份；苯甲酸钠：12份；抗氧剂1010：7份。
7.根据权利要求1或2所述的PET/PETG的增韧增温剂，其特征在于：所述1，4-环己二甲醇87份；热塑性弹性体SEBS：30份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯：15份；丁苯橡胶接枝马来酸酐合成的成核物：15份；苯甲酸钠：15份；抗氧剂1010：8份。
8.根据权利要求1或2所述的PET/PETG的增韧增温剂，其特征在于：所述1，4-环己二甲醇86份；热塑性弹性体SEBS：15份；相容剂乙烯-甲基丙烯酸缩水廿油酯接枝聚苯乙烯：14份；丁苯橡胶接枝马来酸酐合成的成核物：15份；苯甲酸钠：15份；抗氧剂1010：7份。
CN201310151310.9A 2013-04-26 2013-04-26 Pet/petg的增韧增温剂 Expired - Fee Related CN103421281B (zh)