CN103408800B - 一种色母料用高分散性改性碳酸钙及其制备方法 - Google Patents

一种色母料用高分散性改性碳酸钙及其制备方法 Download PDF

Info

Publication number
CN103408800B
CN103408800B CN201310275907.4A CN201310275907A CN103408800B CN 103408800 B CN103408800 B CN 103408800B CN 201310275907 A CN201310275907 A CN 201310275907A CN 103408800 B CN103408800 B CN 103408800B
Authority
CN
China
Prior art keywords
calcium carbonate
parts
modified calcium
speed
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310275907.4A
Other languages
English (en)
Other versions
CN103408800A (zh
Inventor
陈永忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd
Original Assignee
QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd filed Critical QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd
Priority to CN201310275907.4A priority Critical patent/CN103408800B/zh
Publication of CN103408800A publication Critical patent/CN103408800A/zh
Application granted granted Critical
Publication of CN103408800B publication Critical patent/CN103408800B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种色母料用高分散性改性碳酸钙，由下列重量份的原料组分制备而成：重质碳酸钙95-100、扩散剂NNO0.1-0.3、二茂铁0.1-0.3、双酚A型聚碳酸酯0.2-0.4、金红石型二氧化钛1-2、滑石粉0.4-0.6、白油0.1-0.2、甲基苯基硅油乙撑双油酸酰胺0.5-1、高密度线型聚乙烯1-2、硬脂酸0.3-0.4、石蜡1-2、异丙基三（二辛基焦磷酸酰氧基）钛酸酯 2-3。先将部分物料混合，再将碳酸钙干燥，然后混合，再将其它原料按比例按次序分次加入其中，在高速搅拌机里充分混合，干燥研磨，即可。本发明获得的改性碳酸钙具有分散性好，应用于各种色母料中，能降低成本，同时提高了色母的分散性和遮光性。

Description

一种色母料用高分散性改性碳酸钙及其制备方法
技术领域
本发明涉及无机填料领域，具体涉及一种色母料用高分散性改性碳酸钙及其制备方法。
背景技术
重质碳酸钙是一种常用无机填料，因来源广、价格便宜等，广泛用于橡胶、塑料、涂料等领域。但重质碳酸钙表面亲水疏油、比表面积大、表面能高、颗粒间极易团聚，当直接或大量填充有机基体材料中时，不但难以均匀地分散，且与基体的结合力很弱，导致两相界面缺陷、复合材料的某些性能下降。因此，为了拓宽其应用领域，必须对重质碳酸钙表面进行改性，使其表面亲油疏水，增强与有机基体的相容性，提高在有机基体中的分散性，改善和提高复合材料的性能。
发明内容
本发明提供一种色母料用高分散性改性碳酸钙及其制备方法。
本发明采用的技术方案如下：
一种色母料用高分散性改性碳酸钙，其特征在于，由下列重量份的原料组分制备而成：
重质碳酸钙95-100、 扩散剂NNO0.1-0.3、二茂铁0.1-0.3、双酚A型聚碳酸酯0.2-0.4、金红石型二氧化钛1-2、滑石粉0.4-0.6、白油0.1-0.2、甲基苯基硅油乙撑双油酸酰胺0.5-1、高密度线型聚乙烯1-2、硬脂酸0.3-0.4、石蜡1-2、异丙基三（二辛基焦磷酸酰氧基）钛酸酯2-3。
2、根据权利要求1所述的色母料用高分散性改性重质碳酸钙的制备方法，其特征在于：具体操作为：
首先将重质碳酸钙在90-100℃下干燥至水份0.5%以下，然后加入高速搅拌机里；按配方比例将扩散剂NNO、二茂铁、双酚A型聚碳酸酯、金红石型二氧化钛、滑石粉、白油，加入高速搅拌机里，在80-95℃下，以800-1000转/分的速度高速搅拌3-5分钟；再将甲基苯基硅油乙撑双油酸酰胺、高密度线型聚乙烯、硬脂酸、石蜡、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，按配方比例依次加入到高速混合机中，以1000-1200转/分的速度高速搅拌8-10分钟， 停止搅拌，自然冷却到室温，干燥、研磨成纳米粉末，即可。
本发明的有益效果：
本发明在现有重质碳酸钙改性的基础上添加了多种表面处理剂及功能助剂，所得的改性碳酸钙具有粒径小于0.1um，粒子大小均匀，比表面积大，应用性能大大优于普通碳酸钙的特点、得到的改性碳酸钙在生产天花板原料中分散性和相容性好，可以提高填料的加入量，降低原材料成本；在改性时通过添加少量的金红石型二氧化钛、滑石粉、白油、甲基苯基硅油乙撑双油酸酰胺、高密度线型聚乙烯，大大提高了色母的遮光率，同时改善了色母在体系中的分散性和染色性。
具体实施方式
一种色母料用高分散性改性碳酸钙的制备方法，
首先按重量（kg）称取重质碳酸钙100、扩散剂NNO 0.3、二茂铁0.2、双酚A型聚碳酸酯0.3、金红石型二氧化钛1、滑石粉0.5、白油0.1、甲基苯基硅油乙撑双油酸酰胺0.6、高密度线型聚乙烯1、硬脂酸0.3、石蜡1、异丙基三（二辛基焦磷酸酰氧基）钛酸酯 3，按下列步骤制备：
首先将重质碳酸钙在90-100℃下干燥至水份0.5%以下，然后加入高速搅拌机里；按配方比例将扩散剂NNO、二茂铁、双酚A型聚碳酸酯、金红石型二氧化钛、滑石粉、白油，加入高速搅拌机里，在80-95℃下，以800-1000转/分的速度高速搅拌3-5分钟；再将甲基苯基硅油乙撑双油酸酰胺、高密度线型聚乙烯、硬脂酸、石蜡、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，按配方比例依次加入到高速混合机中，以1000-1200转/分的速度高速搅拌8-10分钟， 停止搅拌，自然冷却到室温，干燥、研磨成纳米粉末，即可。
试验数据：
参照以下标准：
GB/T1040—92塑料拉伸试验方法；
GB/T9341—2000塑料弯曲性能试验方法；
GB/T1043—93塑料简支梁冲击试验方法
将改性好的碳酸钙和未改性的重质碳酸钙分别按30％的比例加入到树脂中，制成样条，分别测试两者的力学性能，对比结果见下表1。
表1
由表1可以看出，改性后的碳酸钙的松散堆积密度变小，说明碳酸钙分体充分分散，加入到其它材料中发生团聚现象越小，分散性好，说明改性效果好；还可以看出改性后碳酸钙的各项力学性能都得到提高。

Claims (1)

1.一种色母料用高分散性改性碳酸钙，其特征在于，由下列重量份的原料组分制备而成：
重质碳酸钙95-100、扩散剂NNO 0.1-0.3、二茂铁 0.1-0.3、双酚A型聚碳酸酯0.2-0.4、金红石型二氧化钛1-2、滑石粉0.4-0.6、白油0.1-0.2、甲基苯基硅油和乙撑双油酸酰胺0.5-1、高密度线型聚乙烯1-2、硬脂酸0.3-0.4、石蜡1-2、异丙基三（二辛基焦磷酸酰氧基）钛酸酯 2-3；
所述的色母料用高分散性改性重质碳酸钙的制备方法，具体操作为：
首先将重质碳酸钙在90-100℃下干燥至水份0.5%以下，然后加入高速搅拌机里；按配方比例将扩散剂NNO、二茂铁、双酚A型聚碳酸酯、金红石型二氧化钛、滑石粉、白油，加入高速搅拌机里，在80-95℃下，以800-1000转/分的速度高速搅拌3-5分钟；再将甲基苯基硅油、乙撑双油酸酰胺、高密度线型聚乙烯、硬脂酸、石蜡、异丙基三（二辛基焦磷酸酰氧基）钛酸酯，按配方比例依次加入到高速混合机中，以1000-1200转/分的速度高速搅拌8-10分钟， 停止搅拌，自然冷却到室温，干燥、研磨成纳米粉末，即可。
CN201310275907.4A 2013-07-03 2013-07-03 一种色母料用高分散性改性碳酸钙及其制备方法 Active CN103408800B (zh)