CN103408971B - 一种抗老化油漆-乳胶漆用改性碳酸钙及其制备方法 - Google Patents

一种抗老化油漆-乳胶漆用改性碳酸钙及其制备方法 Download PDF

Info

Publication number
CN103408971B
CN103408971B CN201310276397.2A CN201310276397A CN103408971B CN 103408971 B CN103408971 B CN 103408971B CN 201310276397 A CN201310276397 A CN 201310276397A CN 103408971 B CN103408971 B CN 103408971B
Authority
CN
China
Prior art keywords
calcium carbonate
parts
paint
modified calcium
speed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310276397.2A
Other languages
English (en)
Other versions
CN103408971A (zh
Inventor
陈永忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd
Original Assignee
QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd filed Critical QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd
Priority to CN201310276397.2A priority Critical patent/CN103408971B/zh
Publication of CN103408971A publication Critical patent/CN103408971A/zh
Application granted granted Critical
Publication of CN103408971B publication Critical patent/CN103408971B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种抗老化油漆-乳胶漆用改性碳酸钙，由下列重量份的原料组分制备而成：800目重质碳酸钙95-100、油酸聚氧乙烯酯1-3、聚乙烯蜡0.5-0.8、苯乙烯1-2、氮化铝粉0.3-0.5、亚磷酸三苯酯1-3、氮丙啶交联剂XR-1000.2-0.4、聚乙烯醇0.1-0.3、硅烷偶联剂KH550 2-3、苯丙乳液0.3-0.5、乳化剂OP-10 2-3、 氧化铝0.4-0.6、纳米二氧化硅（VK-SP30）1-2、环氧大豆油1-2、聚磷酸铵0.5-0.6、锌粉0.8-1.2。先将碳酸钙干燥，然后将其它原料按比例按次序分次加入其中，在高速搅拌机里充分混合，干燥研磨，即可。本发明获得的改性碳酸钙具有分散性好，耐磨性能好，应用于油漆材中，能降低成本，同时提高了油漆的施工性能，漆膜光泽度高。

Description

一种抗老化油漆-乳胶漆用改性碳酸钙及其制备方法
技术领域
本发明涉及无机填料领域，具体涉及一种抗老化油漆-乳胶漆用改性碳酸钙及其制备方法。
背景技术
重质碳酸钙是一种常用无机填料，因来源广、价格便宜等，广泛用于橡胶、塑料、涂料等领域。但重质碳酸钙表面亲水疏油、比表面积大、表面能高、颗粒间极易团聚，当直接或大量填充有机基体材料中时，不但难以均匀地分散，且与基体的结合力很弱，导致两相界面缺陷、复合材料的某些性能下降。因此，为了拓宽其应用领域，必须对重质碳酸钙表面进行改性，使其表面亲油疏水，增强与有机基体的相容性，提高在有机基体中的分散性，改善和提高复合材料的性能。
发明内容
本发明提供一种抗老化油漆-乳胶漆用改性碳酸钙及其制备方法。
本发明采用的技术方案如下：
一种抗老化油漆-乳胶漆用改性重质碳酸钙，其特征在于，由下列重量份的原料组分制备而成： 800目重质碳酸钙95-100、油酸聚氧乙烯酯1-3、聚乙烯蜡0.5-0.8、苯乙烯1-2、氮化铝粉0.3-0.5、亚磷酸三苯酯1-3、氮丙啶交联剂XR-1000.2-0.4、聚乙烯醇0.1-0.3、硅烷偶联剂KH550 2-3、苯丙乳液0.3-0.5、乳化剂OP-10 2-3、 氧化铝0.4-0.6、纳米二氧化硅（VK-SP30）1-2、环氧大豆油1-2、聚磷酸铵0.5-0.6、锌粉0.8-1.2。
所述的抗老化油漆-乳胶漆用改性碳酸钙的制备方法，其特征在于：具体操作为：
首先将重质碳酸钙在90-95℃下烘干至水份0.5%以下，然后加入到高速混合机中，在将油酸聚氧乙烯酯、聚乙烯蜡、苯乙烯、氮化铝粉、亚磷酸三苯酯、氮丙啶交联剂XR-100、聚乙烯醇、硅烷偶联剂KH550、按配方比例混合，然后加入到碳酸钙里，升温到95-100℃高速搅拌4-5分钟， 再按比例依次加入苯丙乳液、乳化剂OP-10、氧化铝、纳米二氧化硅（VK-SP30）、环氧大豆油、聚磷酸铵、锌粉，以800-1000转/分的速度高速搅拌5-6分钟后，再以1200-1300转/分的速度高速搅拌10-15分钟， 然后干燥，得到改性碳酸钙。
本发明的有益效果：
本发明在现有重质碳酸钙改性的基础上添加了多种表面处理剂及功能助剂，所得的改性碳酸钙具有粒径小于0.1um，粒子大小均匀，比表面积大，应用性能大大优于普通碳酸钙的特点、得到的改性碳酸钙在油漆中分散性和相容性好，可以提高填料的加入量，降低原材料成本；在改性时通过添加少量的亚磷酸三苯酯、纳米二氧化硅（VK-SP30）大大提高了油漆的抗老化、同时提高了漆膜的表面光泽度，改善了体系的流动性及加工性能，所得油漆耐磨擦，且施工方便。
具体实施方式
一种抗老化油漆-乳胶漆用改性重质碳酸钙，
首先按重量（kg）称取800目重质碳酸钙100、油酸聚氧乙烯酯2、聚乙烯蜡0.6、苯乙烯1、氮化铝粉0.4、亚磷酸三苯酯2、氮丙啶交联剂XR-100 0.3、聚乙烯醇0.2、硅烷偶联剂KH550 2、苯丙乳液0.4、乳化剂OP-10 2、氧化铝0.5、纳米二氧化硅（VK-SP30）1、环氧大豆油2、聚磷酸铵0.5、锌粉0.9，
首先将重质碳酸钙在90-95℃下烘干至水份0.5%以下，然后加入到高速混合机中，在将油酸聚氧乙烯酯、聚乙烯蜡、苯乙烯、氮化铝粉、亚磷酸三苯酯、氮丙啶交联剂XR-100、聚乙烯醇、硅烷偶联剂KH550、按配方比例混合，然后加入到碳酸钙里，升温到95-100℃高速搅拌4-5分钟， 再按比例依次加入苯丙乳液、乳化剂OP-10、氧化铝、纳米二氧化硅（VK-SP30）、环氧大豆油、聚磷酸铵、锌粉，以800-1000转/分的速度高速搅拌5-6分钟后，再以1200-1300转/分的速度高速搅拌10-15分钟， 然后干燥，得到改性碳酸钙。
试验数据：
对本发明的改性碳酸钙和普通碳酸钙的性能检测比较如下：
检测标准：
GB/T1040—92塑料拉伸试验方法；
GB/T9341—2000塑料弯曲性能试验方法；
GB/T1043—93塑料简支梁冲击试验方法；
首先测量改性前、后碳酸钙的堆积密度，然后将改性好的碳酸钙和未改性的重质碳酸钙分别按30％的比例加入到树脂中，制成样条，分别测试两者的力学性能，对比结果见下表1。
表1
由表1可以看出，改性后的碳酸钙的松散堆积密度变小，说明碳酸钙分体充分分散，加入到其它材料中发生团聚现象越小，分散性好，说明改性效果好；从表1中可以看出改性后碳酸钙的各项力学性能都得到很大的提高。

Claims (2)

1.一种抗老化油漆-乳胶漆用改性重质碳酸钙，其特征在于，由下列重量份的原料组分制备而成： 800目重质碳酸钙95-100、油酸聚氧乙烯酯1-3、聚乙烯蜡0.5-0.8、苯乙烯1-2、氮化铝粉0.3-0.5、亚磷酸三苯酯1-3、氮丙啶交联剂XR-100 0.2-0.4、聚乙烯醇0.1-0.3、硅烷偶联剂KH550 2-3、苯丙乳液0.3-0.5、乳化剂OP-10 2-3、 氧化铝0.4-0.6、纳米二氧化硅VK-SP30  1-2、环氧大豆油1-2、聚磷酸铵0.5-0.6、锌粉0.8-1.2。
2.根据权利要求1所述的抗老化油漆-乳胶漆用改性重质碳酸钙的制备方法，其特征在于：具体操作为：
首先将重质碳酸钙在90-95℃下烘干至水份0.5%以下，然后加入到高速混合机中，再将油酸聚氧乙烯酯、聚乙烯蜡、苯乙烯、氮化铝粉、亚磷酸三苯酯、氮丙啶交联剂XR-100、聚乙烯醇、硅烷偶联剂KH550、按配方比例混合，然后加入到碳酸钙里，升温到95-100℃高速搅拌4-5分钟， 再按比例依次加入苯丙乳液、乳化剂OP-10、氧化铝、纳米二氧化硅VK-SP30、环氧大豆油、聚磷酸铵、锌粉，以800-1000转/分的速度高速搅拌5-6分钟后，再以1200-1300转/分的速度高速搅拌10-15分钟， 然后干燥，得到改性重质碳酸钙。
CN201310276397.2A 2013-07-03 2013-07-03 一种抗老化油漆-乳胶漆用改性碳酸钙及其制备方法 Active CN103408971B (zh)