CN103351928A - 一种不锈钢拉丝液组合物及其制备方法 - Google Patents
一种不锈钢拉丝液组合物及其制备方法 Download PDFInfo
- Publication number
- CN103351928A CN103351928A CN2013102436152A CN201310243615A CN103351928A CN 103351928 A CN103351928 A CN 103351928A CN 2013102436152 A CN2013102436152 A CN 2013102436152A CN 201310243615 A CN201310243615 A CN 201310243615A CN 103351928 A CN103351928 A CN 103351928A
- Authority
- CN
- China
- Prior art keywords
- parts
- coupling agent
- add
- stainless steel
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种不锈钢拉丝液组合物及其制备方法,其特征在于由下列重量份的原料制成:三异丙醇胺0.3-0.5、油酸1-2、聚乙烯醇6-8、丙二醇1-2、脂肪醇聚氧乙烯醚AEO-3 1-2、铝酸酯偶联剂DL-411 1-2、环氧油酸丁酯1-2、偶氮二异丁腈0.2-0.3、成膜助剂1-2、水100-120。本发明采用水基起到较好的散热作用,三异丙醇胺起到缓蚀作用,通过偶氮二异丁腈的引发反应,使得油酸、聚乙烯醇、丙二醇等成分之间形成保护膜,增加与水的相溶性,提高了拉丝组合物的保护效果。本发明采用硅烷偶联剂KH550起到桥接作用,增加了各组分分散性,防止存放时间长以后产生的沉淀分层现象。
Description
技术领域
本发明涉及不锈钢拉丝技术领域,是一种不锈钢拉丝液组合物及其制备方法。
背景技术
不锈钢丝通常由拉拔工艺制得,即将直径较大的金属丝如钢丝通过模具孔隙,在外力作用下拉拔使其截面积缩小形成所需直径的线材。
现有拉丝工艺中多采用润滑油作为拉丝介质,拉拔出的不锈钢丝表面圆润、细腻、光滑、透亮、无杂物滞留,断丝率降低,产品质量大大提高。但是润滑油散热慢,损毁模具,影响产品质量,同时高温易引燃油品或使油品蒸发冒烟导致现场环境恶化。
发明内容
本发明的目的是提供一种不锈钢拉丝液组合物及其制备方法,具有成膜性能好、润滑效果佳、冷却效果好、易清洗的特点。
本发明的技术方案如下:
一种不锈钢拉丝液组合物,其特征在于由下列重量份的原料制成:
三异丙醇胺0.3-0.5、油酸1-2、聚乙烯醇6-8、丙二醇1-2、脂肪醇聚氧乙烯醚AEO-3 1-2、铝酸酯偶联剂DL-411 1-2、环氧油酸丁酯1-2、偶氮二异丁腈0.2-0.3、成膜助剂1-2、水100-120;
所述的成膜助剂由下列重量份的原料制成:苯醌1-2、苯乙烯6-8、叔丁基过氧化氢0.1-0.2、衣康酸二正丁酯3-4、硅烷偶联剂KH550 1-2、1-羟乙基-2-油基咪唑啉2-3;制备方法是:将苯乙烯与衣康酸酯混合,搅拌,加入叔丁基过氧化氢、苯醌,搅拌反应45-60分钟,然后,加入1-羟乙基-2-油基咪唑啉,搅拌反应,反应2-3小时后,升温至125-130℃,加入硅烷偶联剂KH550,搅拌反应2-3小时;即得。
制备方法是:将三异丙醇胺、聚乙烯醇、油酸、脂肪醇聚氧乙烯醚AEO-3加入到水中,加热至85-90℃,搅拌30-40分钟,然后,加入偶氮二异丁腈、环氧油酸丁酯,搅拌反应1-2小时,然后,加入铝酸酯偶联剂DL-411等其它成分,继续反应1-2小时,即得。
本发明采用水基起到较好的散热作用,三异丙醇胺起到缓蚀作用,通过偶氮二异丁腈的引发反应,使得油酸、聚乙烯醇、丙二醇等成分之间形成保护膜,增加与水的相溶性,提高了拉丝组合物的保护效果。本发明采用硅烷偶联剂KH550起到桥接作用,增加了各组分分散性,防止存放时间长以后,产生的沉淀分层现象。
本发明具有优良的润滑性能、储存稳定性,成本低,冷却效果好,传热速度快,使用过程中温度升幅小,不易燃,易清洗。
具体实施方式
一种不锈钢拉丝液组合物,由下列重量份的原料(公斤)制成:
三异丙醇胺0.5、油酸2、聚乙烯醇6、丙二醇1、脂肪醇聚氧乙烯醚AEO-3 1、铝酸酯偶联剂DL-411 2、环氧油酸丁酯1、偶氮二异丁腈0.3、成膜助剂2、水100;
制备方法是:将三异丙醇胺、聚乙烯醇、油酸、脂肪醇聚氧乙烯醚AEO-3加入到水中,加热至85-90℃,搅拌30-40分钟,然后,加入偶氮二异丁腈、环氧油酸丁酯,搅拌反应1-2小时,然后,加入铝酸酯偶联剂DL-411等其它成分,继续反应2小时,即得。
所述的成膜助剂由下列重量份(公斤)的原料制成:苯醌1、苯乙烯6、叔丁基过氧化氢0.2、衣康酸二正丁酯3、硅烷偶联剂KH550 2、1-羟乙基-2-油基咪唑啉2;制备方法是:将苯乙烯与衣康酸酯混合,搅拌,加入叔丁基过氧化氢、苯醌,搅拌反应45-60分钟,然后,加入1-羟乙基-2-油基咪唑啉,搅拌反应,反应2-3小时后,升温至125-130℃,加入硅烷偶联剂KH550,搅拌反应2-3小时;即得。
使用本发明拉丝液,最高拉丝速度可达16m/sec。生产出的不锈钢丝工序间防锈时间在5天以上;集中油池换油周期为3 年,单机油池换油周期为8个月,减少了废液处理和排放,保护了环境。
Claims (2)
1.一种不锈钢拉丝液组合物,其特征在于由下列重量份的原料制成:
三异丙醇胺0.3-0.5、油酸1-2、聚乙烯醇6-8、丙二醇1-2、脂肪醇聚氧乙烯醚AEO-3 1-2、铝酸酯偶联剂DL-411 1-2、环氧油酸丁酯1-2、偶氮二异丁腈0.2-0.3、成膜助剂1-2、水100-120;
所述的成膜助剂由下列重量份的原料制成:苯醌1-2、苯乙烯6-8、叔丁基过氧化氢0.1-0.2、衣康酸二正丁酯3-4、硅烷偶联剂KH550 1-2、1-羟乙基-2-油基咪唑啉2-3;制备方法是:将苯乙烯与衣康酸酯混合,搅拌,加入叔丁基过氧化氢、苯醌,搅拌反应45-60分钟,然后,加入1-羟乙基-2-油基咪唑啉,搅拌反应,反应2-3小时后,升温至125-130℃,加入硅烷偶联剂KH550,搅拌反应2-3小时;即得。
2.根据权利要求1所述的不锈钢拉丝液组合物的制备方法,其特征在于包括以下步骤:将三异丙醇胺、聚乙烯醇、油酸、脂肪醇聚氧乙烯醚AEO-3加入到水中,加热至85-90℃,搅拌30-40分钟,然后,加入偶氮二异丁腈、环氧油酸丁酯,搅拌反应1-2小时,然后,加入铝酸酯偶联剂DL-411等其它成分,继续反应1-2小时,即得。