CN103351917A - 一种全合成铝合金拉丝液及其制备方法 - Google Patents
一种全合成铝合金拉丝液及其制备方法 Download PDFInfo
- Publication number
- CN103351917A CN103351917A CN2013102434886A CN201310243488A CN103351917A CN 103351917 A CN103351917 A CN 103351917A CN 2013102434886 A CN2013102434886 A CN 2013102434886A CN 201310243488 A CN201310243488 A CN 201310243488A CN 103351917 A CN103351917 A CN 103351917A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring reaction
- preparation
- add
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种全合成铝合金拉丝液及其制备方法,其特征在于由下列重量份的原料制成:甲基苯并三氮唑1.2-1.5、亚磷酸二正丁酯2-3、2,6-苯并异噻唑啉酮0.6-0.8、十二烷基苯磺酸钠1-2、菜籽油6-8、苯基三乙氧基硅烷1-2、偏硅酸钠1-2、成膜助剂2-3、水150-160。本发明具有优异的润滑性能、清洗性和铝防护性能。良好的润滑性能够满足加工精度要求,良好的清洗性,保证工件在进行下一道工序时能够迅速清洗干净,不影响操作,良好的铝防护性能则保证工件的光亮度要求。
Description
技术领域
本发明涉及铝导线拉丝技术领域,是一种全合成铝合金拉丝液及其制备方法。
背景技术
铜线( 丝)、铝线( 丝) 是电力行业输送电的主要传输导线,通常由拉拔工艺制得,即将直径较大的金属丝如钢丝通过模具孔隙,在外力作用下拉拔使其截面积缩小形成所需直径的线材。
现有拉丝工艺中多采用润滑油作为拉丝介质,拉拔出的导线表面圆润、细腻、光滑、透亮、无杂物滞留,断丝率降低,产品质量大大提高。但是润滑油散热慢,损毁模具,影响产品质量,同时高温易引燃油品或使油品蒸发冒烟导致现场环境恶化。
发明内容
本发明的目的是提供一种全合成铝合金拉丝液及其制备方法,具有成膜性能好、润滑效果佳、稳定性高、传热速度快、冷却效果好、易清洗的特点。
本发明的技术方案如下:
一种全合成铝合金拉丝液,,其特征在于由下列重量份的原料制成:
甲基苯并三氮唑1.2-1.5、亚磷酸二正丁酯2-3、2,6-苯并异噻唑啉酮0.6-0.8、十二烷基苯磺酸钠1-2、菜籽油6-8、苯基三乙氧基硅烷1-2、偏硅酸钠1-2、成膜助剂2-3、水150-160。
所述的成膜助剂由下列重量份的原料制成:苯醌1-2、苯乙烯6-8、叔丁基过氧化氢0.1-0.2、衣康酸二正丁酯3-4、硅烷偶联剂KH550 1-2、1-羟乙基-2-油基咪唑啉2-3;制备方法是:将苯乙烯与衣康酸酯混合,搅拌,加入叔丁基过氧化氢、苯醌,搅拌反应45-60分钟,然后,加入1-羟乙基-2-油基咪唑啉,搅拌反应,反应2-3小时后,升温至125-130℃,加入硅烷偶联剂KH550,搅拌反应2-3小时;即得。
制备方法:将甲基苯并三氮唑、亚磷酸二正丁酯、2,6-苯并异噻唑啉酮、十二烷基苯磺酸钠、菜籽油加入水中,加热至90-97℃,搅拌反应60-90分钟,然后,加入苯基三乙氧基硅烷、偏硅酸钠搅拌反应30-40分钟,再加入其它剩余成分,搅拌反应1-2小时,即得。
本发明具有优异的润滑性能、清洗性和铝防护性能。良好的润滑性能够满足加工精度要求,良好的清洗性,保证工件在进行下一道工序时能够迅速清洗干净,不影响操作,良好的铝防护性能则保证工件的光亮度要求。
具体实施方式
一种全合成铝合金拉丝液,,由下列重量份的原料(公斤)制成:
甲基苯并三氮唑1.2、亚磷酸二正丁酯3、2,6-苯并异噻唑啉酮0.8、十二烷基苯磺酸钠1、菜籽油8、苯基三乙氧基硅烷1、偏硅酸钠2、成膜助剂2、水160;
制备方法是:将甲基苯并三氮唑、亚磷酸二正丁酯、2,6-苯并异噻唑啉酮、十二烷基苯磺酸钠、菜籽油加入水中,加热至90-97℃,搅拌反应60-90分钟,然后,加入苯基三乙氧基硅烷、偏硅酸钠搅拌反应30-40分钟,再加入其它剩余成分,搅拌反应1-2小时,即得。
所述的成膜助剂由下列重量份(公斤)的原料制成:苯醌1、苯乙烯6、叔丁基过氧化氢0.2、衣康酸二正丁酯3、硅烷偶联剂KH550 2、1-羟乙基-2-油基咪唑啉2;制备方法是:将苯乙烯与衣康酸酯混合,搅拌,加入叔丁基过氧化氢、苯醌,搅拌反应45-60分钟,然后,加入1-羟乙基-2-油基咪唑啉,搅拌反应,反应2-3小时后,升温至125-130℃,加入硅烷偶联剂KH550,搅拌反应2-3小时;即得。
使用本发明拉丝液,最高铝合金导线拉丝速度可达21m/sec。生产出的铜丝工序间防锈时间在5天以上;集中油池换油周期为2年,单机油池换油周期为8个月,减少了废液处理和排放,保护了环境。
Claims (2)
1.一种全合成铝合金拉丝液,,其特征在于由下列重量份的原料制成:
甲基苯并三氮唑1.2-1.5、亚磷酸二正丁酯2-3、2,6-苯并异噻唑啉酮0.6-0.8、十二烷基苯磺酸钠1-2、菜籽油6-8、苯基三乙氧基硅烷1-2、偏硅酸钠1-2、成膜助剂2-3、水150-160;
所述的成膜助剂由下列重量份的原料制成:苯醌1-2、苯乙烯6-8、叔丁基过氧化氢0.1-0.2、衣康酸二正丁酯3-4、硅烷偶联剂KH550 1-2、1-羟乙基-2-油基咪唑啉2-3;制备方法是:将苯乙烯与衣康酸酯混合,搅拌,加入叔丁基过氧化氢、苯醌,搅拌反应45-60分钟,然后,加入1-羟乙基-2-油基咪唑啉,搅拌反应,反应2-3小时后,升温至125-130℃,加入硅烷偶联剂KH550,搅拌反应2-3小时;即得。
2.根据权利要求1所述的全合成铝合金拉丝液的制备方法,其特征在于包括以下步骤:将甲基苯并三氮唑、亚磷酸二正丁酯、2,6-苯并异噻唑啉酮、十二烷基苯磺酸钠、菜籽油加入水中,加热至90-97℃,搅拌反应60-90分钟,然后,加入苯基三乙氧基硅烷、偏硅酸钠搅拌反应30-40分钟,再加入其它剩余成分,搅拌反应1-2小时,即得。