CN103965999B - 一种硬质合金用长效拉丝液 - Google Patents
一种硬质合金用长效拉丝液 Download PDFInfo
- Publication number
- CN103965999B CN103965999B CN201410126163.4A CN201410126163A CN103965999B CN 103965999 B CN103965999 B CN 103965999B CN 201410126163 A CN201410126163 A CN 201410126163A CN 103965999 B CN103965999 B CN 103965999B
- Authority
- CN
- China
- Prior art keywords
- wire drawing
- drawing liquid
- stir
- wimet
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种拉丝液,具体涉及一种硬质合金用长效拉丝液,本发明拉丝液由以下重量份的原料制成:环烷油25-28、钛酸四丁酯4-5、季戊四醇油酸酯15-20、葡萄糖酸钠1-2、聚乙二醇6000双硬脂酸酯10-12、脂肪醇聚氧乙烯醚硫酸钠5-6、二溴二甲基乙内酰脲1-2、植酸1-2、助剂4-5、去离子水800-1000;本发明拉丝液以环烷油、季戊四醇油酸酯混合作为基础油,并以植酸、葡萄糖酸钠等原料作为螯合、缓蚀、防锈、抗菌添加剂,有效的保护合金线材表面,提高清净力,延长拉丝液储存寿命,本发明拉丝液耐极压抗磨,能够降低硬质合金在拉丝过程中的摩擦力,减少模具及线材的损耗,拉丝效率得到提高。
Description
技术领域
本发明涉及一种拉丝液,具体涉及一种硬质合金用长效拉丝液及其制备工艺。
背景技术
拉丝工艺是一种金属加工工艺,是指金属线材在压力作用下强行通过模具,获得所要求的截面积形状和尺寸的技术加工方法,而拉丝液则是拉丝工艺中必不可少的辅助剂,它主要的作用是在多种铜丝、铝丝多种线材的中拉、小拉、微细拉等拉丝、拉线工艺过程中起润滑作用,兼具保护线材、模具,达到良好的拉丝效果,拉丝液的品质直接影响到拉丝效果,性能优良的拉丝液可以很好的保护模具,减少线材断头、模具磨损现象,兼具防锈、冷却、清洗等作用,反之,则会严重影响拉丝质量;随着拉丝工艺的应用逐渐广泛,市场对拉丝液的品质需求越来越高,现有的拉丝液主要存在乳液稳定性差、腐蚀金属线材、能耗高、不易清洗等问题,制约着拉丝、拉拔质量,急需改进其配方和工艺,使其更为高效环保。
发明内容
本发明的目的在于,提供一种硬质合金用长效拉丝液,延长使用寿命,改善拉丝效率,为了实现上述目的,本发明采用的技术方案如下:
一种硬质合金用长效拉丝液,其特征在于,本发明材料由以下重量份的原料制成:环烷油25-28、钛酸四丁酯4-5、季戊四醇油酸酯15-20、葡萄糖酸钠1-2、聚乙二醇6000双硬脂酸酯10-12、脂肪醇聚氧乙烯醚硫酸钠5-6、二溴二甲基乙内酰脲1-2、植酸1-2、助剂4-5、去离子水800-1000;
所述的助剂由以下重量份的原料制成:环氧大豆油12-15、叶蜡石2-3、聚异丁烯基丁二酰亚胺3-4、三聚磷酸钠0.02-0.05、聚丙烯酸钠0.1-0.2、硅烷偶联剂KH5500.01-0.02、氯化石蜡421-2、聚甘油脂肪酸酯1-2、去离子水12-15,制备方法为:先将叶蜡石在750-800℃下高温煅烧2-3h,冷却后研磨成300目粉体,粉体与硅烷偶联剂KH550混合,球磨10-15min后,与三聚磷酸钠、聚丙烯酸钠一起加入去离子水中,以500-600转/分钟的转速搅拌20-30min,随后对溶液进行喷雾干燥,得到的粉体与其它剩余物料混合,加热至40-50℃,继续搅拌40-50min,搅拌结束冷却至室温,即得浆料。
所述的一种硬质合金用长效拉丝液,其制备工艺为:
(1)先将去离子水加热至50-60℃,加入葡萄糖酸钠、二溴二甲基乙内酰脲、植酸,充分搅拌至物料完全溶解分散,再加入聚乙二醇6000双硬脂酸酯、脂肪醇聚氧乙烯醚硫酸钠,继续搅拌20-30min,混合溶液保温备用;
(2)将环烷油、季戊四醇油酸酯混合加热至50-60℃,加入钛酸四丁酯,以1200-1500转/分钟的转速搅拌20-30min,然后继续一边搅拌,一边缓慢加入步骤(1)所得物料,搅拌40-50min,最后再加入其它剩余物料,搅拌20-30min,搅拌结束后溶液静置2-3h,即得成品。
本发明制备的拉丝液优点在于:以环烷油、季戊四醇油酸酯混合作为基础油,热稳定性好,高温润滑性能优良,添加的植酸、葡萄糖酸钠等原料具有螯合、缓蚀、防锈、抗菌等功能,有效的保护合金线材表面,提高清净力,延长拉丝液储存寿命,再结合聚乙二醇6000双硬脂酸酯、钛酸四丁酯等原料,使得本发明拉丝液的抗极压性得到提高,润滑性能更为优良,能够降低硬质合金在拉丝过程中的摩擦力,减少模具及线材的损耗,提高了拉丝效率。
具体实施方式
实施例
本实施例拉丝液由以下重量份(公斤)的原料制成:环烷油25-28、钛酸四丁酯4-5、季戊四醇油酸酯15-20、葡萄糖酸钠1-2、聚乙二醇6000双硬脂酸酯10-12、脂肪醇聚氧乙烯醚硫酸钠5-6、二溴二甲基乙内酰脲1-2、植酸1-2、助剂4-5、去离子水800-1000;
助剂由以下重量份的原料制成:环氧大豆油12、叶蜡石3、聚异丁烯基丁二酰亚胺4、三聚磷酸钠0.05、聚丙烯酸钠0.1、硅烷偶联剂KH5500.02、氯化石蜡422、聚甘油脂肪酸酯2、去离子水15,制备方法为:先将叶蜡石在750-800℃下高温煅烧3h,冷却后研磨成300目粉体,粉体与硅烷偶联剂KH550混合,球磨15min后,与三聚磷酸钠、聚丙烯酸钠一起加入去离子水中,以600转/分钟的转速搅拌30min,随后对溶液进行喷雾干燥,得到的粉体与其它剩余物料混合,加热至40-50℃,继续搅拌50min,搅拌结束冷却至室温,即得浆料。
所述的一种硬质合金用长效拉丝液,其制备工艺为:
(1)先将去离子水加热至50-60℃,加入葡萄糖酸钠、二溴二甲基乙内酰脲、植酸,充分搅拌至物料完全溶解分散,再加入聚乙二醇6000双硬脂酸酯、脂肪醇聚氧乙烯醚硫酸钠,继续搅拌30min,混合溶液保温备用;
(2)将环烷油、季戊四醇油酸酯混合加热至50-60℃,加入钛酸四丁酯,以1500转/分钟的转速搅拌20min,然后继续一边搅拌,一边缓慢加入步骤(1)所得物料,搅拌50min,最后再加入其它剩余物料,搅拌30min,搅拌结束后溶液静置3h,即得成品。
本发明拉丝液在常温下可贮存至少18个月以上,换液周期延长至12个月以上,拉丝时不易断线,线材表面光洁无划痕,塔轮走线通畅,其具体测试性能指标如下:
项目 | 指标 |
运动粘度(50℃) | ≤100mm2/s |
凝点 | ≤-5℃ |
pH值 | 8.8 |
乳化液腐蚀(55±2)℃,全浸铜片1h | 合格 |
乳化液稳定性(15-35℃)1h | 无分层,无沉淀,无皂、油析出 |
消泡性(55±2℃,5min) | ≤4mL |
Claims (1)
1.一种硬质合金用长效拉丝液,其特征在于,该拉丝液由以下重量份的原料制成:环烷油25-28、钛酸四丁酯4-5、季戊四醇油酸酯15-20、葡萄糖酸钠1-2、聚乙二醇6000双硬脂酸酯10-12、脂肪醇聚氧乙烯醚硫酸钠5-6、二溴二甲基乙内酰脲1-2、植酸1-2、助剂4-5、去离子水800-1000;
所述的助剂由以下重量份的原料制成:环氧大豆油12-15、叶蜡石2-3、聚异丁烯基丁二酰亚胺3-4、三聚磷酸钠0.02-0.05、聚丙烯酸钠0.1-0.2、硅烷偶联剂KH5500.01-0.02、氯化石蜡421-2、聚甘油脂肪酸酯1-2、去离子水12-15,制备方法为:先将叶蜡石在750-800℃下高温煅烧2-3h,冷却后研磨成300目粉体,粉体与硅烷偶联剂KH550混合,球磨10-15min后,与三聚磷酸钠、聚丙烯酸钠一起加入去离子水中,以500-600转/分钟的转速搅拌20-30min,随后对溶液进行喷雾干燥,得到的粉体与其它剩余物料混合,加热至40-50℃,继续搅拌40-50min,搅拌结束冷却至室温,即得浆料;
所述一种硬质合金用长效拉丝液的制备工艺如下:
(1)先将去离子水加热至50-60℃,加入葡萄糖酸钠、二溴二甲基乙内酰脲、植酸,充分搅拌至物料完全溶解分散,再加入聚乙二醇6000双硬脂酸酯、脂肪醇聚氧乙烯醚硫酸钠,继续搅拌20-30min,混合溶液保温备用;
(2)将环烷油、季戊四醇油酸酯混合加热至50-60℃,加入钛酸四丁酯,以1200-1500转/分钟的转速搅拌20-30min,然后继续一边搅拌,一边缓慢加入步骤(1)所得物料,搅拌40-50min,最后再加入其它剩余物料,搅拌20-30min,搅拌结束后溶液静置2-3h,即得成品。