CN103351506A - 一种绝缘电缆料及其制备方法 - Google Patents

一种绝缘电缆料及其制备方法 Download PDF

Info

Publication number
CN103351506A
CN103351506A CN201310242705XA CN201310242705A CN103351506A CN 103351506 A CN103351506 A CN 103351506A CN 201310242705X A CN201310242705X A CN 201310242705XA CN 201310242705 A CN201310242705 A CN 201310242705A CN 103351506 A CN103351506 A CN 103351506A
Authority
CN
China
Prior art keywords
minute
cable material
density polyethylene
mixing
insulated cable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310242705XA
Other languages
English (en)
Other versions
CN103351506B (zh
Inventor
胡必林
蔡飞
李健
刘丽
胡程
胡豪杰
李星
焦长庚
胡涓涓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Star Cable Technology Co. Ltd.
Original Assignee
ANHUI TIANXING OPTICAL FIBER COMMUNICATION EQUIPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI TIANXING OPTICAL FIBER COMMUNICATION EQUIPMENT Co Ltd filed Critical ANHUI TIANXING OPTICAL FIBER COMMUNICATION EQUIPMENT Co Ltd
Priority to CN201310242705.XA priority Critical patent/CN103351506B/zh
Publication of CN103351506A publication Critical patent/CN103351506A/zh
Application granted granted Critical
Publication of CN103351506B publication Critical patent/CN103351506B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种绝缘电缆料及其制备方法，其特征在于由下列重量份的原料制成：高密度聚乙烯34-37、EVA12-15、十八烷醇基聚氧乙烯醚3-4、聚-1-丁烯8-10、线性低密度聚乙烯24-27、碳化硅粉1-2、二月桂酸二丁基锡2-3、氧化锌2-3、铝矾土35-39、膨润土23-26、促进剂DTDM1-2、乙烯基三(β-甲氧基乙氧基)硅烷2-3、丙烯酸乙酯4-6、炭黑N33915-20、N660炭黑23-26、抗氧剂10351-2、改性硅藻土6-8。本发明配方合理，提供的电缆料具有优越的耐温性能，柔软性能，耐油性能。

Description

一种绝缘电缆料及其制备方法
技术领域
本发明属于电缆料技术领域，更具体地说，是涉及一种绝缘电缆料及其制备方法。
背景技术
电线电缆料，主要由树脂料、填充料、增塑剂、防老剂、阻燃剂、抗氧剂等混合制成，配方原料主要集中于一些常用成分，由此导致电缆料技术指标不高或成本高等问题，比如体积电阻率偏低、耐高温、耐低温、阻燃性、绝缘性等不能满足电缆厂家对绝缘级护套料更高电性能的要求。
发明内容
本发明的目的是提供一种绝缘电缆料及其制备方法。
本发明所采用的技术方案是：
一种绝缘电缆料，其特征在于由下列重量份的原料制成:高密度聚乙烯34-37、EVA12-15、十八烷醇基聚氧乙烯醚3-4、聚-1-丁烯8-10、线性低密度聚乙烯24-27、碳化硅粉1-2、二月桂酸二丁基锡2-3、氧化锌2-3、铝矾土35-39、膨润土23-26、促进剂DTDM1-2、乙烯基三(β-甲氧基乙氧基)硅烷2-3、丙烯酸乙酯4-6、炭黑N339 15-20、N660炭黑23-26、抗氧剂1035 1-2、改性硅藻土6-8。
所述的改性硅藻土由以下方法制得：
将硅藻土放入460-480℃下煅烧3-4小时，取出，冷却，放入10-12%氢氧化钠溶液中浸泡2-3小时，取出，用纯净水洗净，烘干研成粉末；再加入相当于硅藻土重量35-40%的氮化铝、3-4%的二茂铁、2-3%的氟化锆、3-4%的氧化锌、5-6%的促进剂PZ，混合研磨30-40分钟，然后再喷入相当于硅藻土重量6-8%的异丙基二硬脂酰氧基铝酸酯，在13000-16000转/分下搅拌60-70分钟，即得。
所述的绝缘电缆料的制备方法，其特征在于包括以下步骤：将EVA、十八烷醇基聚氧乙烯醚、聚-1-丁烯、线性低密度聚乙烯、碳化硅粉、二月桂酸二丁基锡、氧化锌、铝矾土、膨润土、促进剂DTDM在90-125℃下混合12-16分钟，得到混合料A；将其它物料混合，在125-145℃下混合12-16分钟，得到混合料B；将混合料A、B存放18-24小时后混合，在110-135℃下混合10-15分钟，送入双螺杆挤出机在125-145℃下挤出造粒，即得。
本发明配方合理，提供的电缆料具有优越的耐温性能，柔软性能，耐油性能。
具体实施方式
一种绝缘电缆料，由下列重量份（公斤）的原料制成：
高密度聚乙烯37、EVA（醋酸乙烯40%） 15、十八烷醇基聚氧乙烯醚4、聚-1-丁烯10、线性低密度聚乙烯24、碳化硅粉2、二月桂酸二丁基锡3、氧化锌3、铝矾土39、膨润土23、促进剂DTDM 2、乙烯基三(β-甲氧基乙氧基)硅烷3、丙烯酸乙酯6、炭黑N339 15、N660炭黑26、抗氧剂1035 1、改性硅藻土8。
所述的改性硅藻土由以下方法制得：
将硅藻土放入460-480℃下煅烧3-4小时，取出，冷却，放入10-12%氢氧化钠溶液中浸泡2-3小时，取出，用纯净水洗净，烘干研成粉末；再加入相当于硅藻土重量40%的氮化铝、4%的二茂铁、3%的氟化锆、4%的氧化锌、6%的促进剂PZ，混合研磨30-40分钟，然后再喷入相当于硅藻土重量8%的异丙基二硬脂酰氧基铝酸酯，在13000-16000转/分下搅拌60-70分钟，即得。
绝缘电缆料的制备，包括以下步骤：将EVA、十八烷醇基聚氧乙烯醚、聚-1-丁烯、线性低密度聚乙烯、碳化硅粉、二月桂酸二丁基锡、氧化锌、铝矾土、膨润土、促进剂DTDM在90-125℃下混合12-16分钟，得到混合料A；将其它物料混合，在125-145℃下混合12-16分钟，得到混合料B；将混合料A、B存放18-24小时后混合，在110-135℃下混合10-15分钟，送入双螺杆挤出机在125-145℃下挤出造粒，即得。
本发明的电缆料性能：
项         目 单     位 本发明电缆料
原始拉伸强度 MPa  不小于 17.00
原始断裂伸长率 %  不小于 470
耐158℃×168h老化后    
断裂强度 MPa  不小于 15
断裂伸长率 %  不小于 450
20℃体积电阻率 Ω·m 1.0×1014
200℃热稳定时间 Min 60

Claims (2)

1.一种绝缘电缆料，其特征在于由下列重量份的原料制成：高密度聚乙烯34-37、EVA12-15、十八烷醇基聚氧乙烯醚3-4、聚-1-丁烯8-10、线性低密度聚乙烯24-27、碳化硅粉1-2、二月桂酸二丁基锡2-3、氧化锌2-3、铝矾土35-39、膨润土23-26、促进剂DTDM1-2、乙烯基三(β-甲氧基乙氧基)硅烷2-3、丙烯酸乙酯4-6、炭黑N339 15-20、N660炭黑23-26、抗氧剂1035 1-2、改性硅藻土6-8；
所述的改性硅藻土由以下方法制得：
将硅藻土放入460-480℃下煅烧3-4小时，取出，冷却，放入10-12%氢氧化钠溶液中浸泡2-3小时，取出，用纯净水洗净，烘干研成粉末；再加入相当于硅藻土重量35-40%的氮化铝、3-4%的二茂铁、2-3%的氟化锆、3-4%的氧化锌、5-6%的促进剂PZ，混合研磨30-40分钟，然后再喷入相当于硅藻土重量6-8%的异丙基二硬脂酰氧基铝酸酯，在13000-16000转/分下搅拌60-70分钟，即得。
2.根据权利要求1所述的绝缘电缆料的制备方法，其特征在于包括以下步骤：将EVA、十八烷醇基聚氧乙烯醚、聚-1-丁烯、线性低密度聚乙烯、碳化硅粉、二月桂酸二丁基锡、氧化锌、铝矾土、膨润土、促进剂DTDM在90-125℃下混合12-16分钟，得到混合料A；将其它物料混合，在125-145℃下混合12-16分钟，得到混合料B；将混合料A、B存放18-24小时后混合，在110-135℃下混合10-15分钟，送入双螺杆挤出机在125-145℃下挤出造粒，即得。
CN201310242705.XA 2013-06-19 2013-06-19 一种绝缘电缆料及其制备方法 Active CN103351506B (zh)