CN103333541B - 一种防锈抗紫外线氧化铁黑的生产方法 - Google Patents
一种防锈抗紫外线氧化铁黑的生产方法 Download PDFInfo
- Publication number
- CN103333541B CN103333541B CN201310227937.8A CN201310227937A CN103333541B CN 103333541 B CN103333541 B CN 103333541B CN 201310227937 A CN201310227937 A CN 201310227937A CN 103333541 B CN103333541 B CN 103333541B
- Authority
- CN
- China
- Prior art keywords
- iron oxide
- black iron
- rust
- light absorber
- aluminium triphosphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种防锈抗紫外线氧化铁黑的生产方法，采用氢氧化钠氧化法制得的氧化铁黑，加入相当于氧化铁黑滤饼重量3-6%的三聚磷酸铝、0.2-0.3%的紫外线吸收剂UV-327、0.4-0.5%的双(二辛氧基焦磷酸酯基)乙撑钛酸和0.5-1%的去离子水，2500-3000rpm高速研磨10-20分钟，取出烘干后加入适量的水打浆20-30分钟，制成浓度为55-65%的浆液。本发明在先添加三聚磷酸铝、紫外线吸收剂UV-327、双(二辛氧基焦磷酸酯基)乙撑钛酸和去离子水进行研磨处理，通过钛酸酯桥接三聚磷酸铝与紫外线吸收剂，包覆在氧化铁黑表面，不易分离脱落。
Description
技术领域
本发明涉及一种防锈抗紫外线氧化铁黑的生产方法，属于化工颜料领域。
背景技术
铁系颜料作为重要的无机彩色颜料,其年产量居无机彩色颜料之首。由于世界环保意识的加强,无机铁系颜料以其无毒、无嗅、无污染等特点不断取代有机颜料及红丹、铅铬黄等铅系列、铬系列有毒的无机颜料。氧化铁黑由于化学成分简单,无毒无污染，化学稳定性强,广泛应用于建筑行业油漆涂料中。但是现有的氧化铁黑在容易发生褪色、变色等现象，抗紫外线差，防锈能力差，从而限制了氧化铁黑的使用范围。
发明内容
本发明的目的在于针对现有技术的不足，提供一种防锈抗紫外线氧化铁黑的生产方法。该生产方法生产的氧化铁黑是集防锈、抗紫外线、成膜于一体功能化材料。
本发明采用的技术方案如下：
一种防锈抗紫外线氧化铁黑的生产方法，采用氢氧化钠氧化法制得的氧化铁黑，直接使用未烘干的氧化铁黑滤饼，加入相当于氧化铁黑滤饼重量3-6%的三聚磷酸铝、0.2-0.3%的紫外线吸收剂UV-327、0.4-0.5%的双(二辛氧基焦磷酸酯基)乙撑钛酸酯和0.5-1%的去离子水，2500-3000rpm高速研磨10-20分钟，取出烘干后加入适量的水打浆20-30分钟，制成浓度为55-65%的浆液，并加入浆液重量0.15-0.25%的纳米二氧化硅、0.2-0.3%的柠檬酸铵、0.2-0.3%的儿茶酚，搅拌15-25分钟，再通过胶体磨磨浆至粒径小于50μm，将浆液烘干打粉即为成品。
本发明的有益效果：
本发明在先添加三聚磷酸铝、紫外线吸收剂UV-327、双(二辛氧基焦磷酸酯基)乙撑钛酸和去离子水进行研磨处理，通过钛酸酯桥接三聚磷酸铝与紫外线吸收剂，包覆在氧化铁黑表面，不易分离脱落，可以在氧化铁黑表面形成一层防锈膜，使其具有防锈作用以及提高其抗紫外线性能。
具体实施方式
一种防锈抗紫外线氧化铁黑的生产方法，采用氢氧化钠氧化法制得的氧化铁黑，直接使用未烘干的氧化铁黑滤饼，加入相当于氧化铁黑滤饼重量5%的三聚磷酸铝、0.25%的紫外线吸收剂UV-327、0.4%的双(二辛氧基焦磷酸酯基)乙撑钛酸和0.6%的去离子水，2500rpm高速研磨20分钟，取出烘干后加入适量的水打浆30分钟，制成浓度为60%的浆液，并加入浆液重量0.2%的纳米二氧化硅、0.3%的柠檬酸铵、0.2%的儿茶酚，搅拌20分钟，再通过胶体磨磨浆至粒径小于50μm，将浆液烘干打粉即为成品。
本发明在先添加三聚磷酸铝、紫外线吸收剂UV-327、双(二辛氧基焦磷酸酯基)乙撑钛酸和去离子水进行研磨处理，通过钛酸酯桥接三聚磷酸铝与紫外线吸收剂，包覆在氧化铁黑表面，不易分离脱落，使其具有防锈作用以及提高其抗紫外线性能。
本实施例生产出来的氧化铁黑产品性能分析数据如下表：
| 项目 | 指标 | 检测结果 |
| Fe2O3含量（%） | ≥85 | 89.8 |
| 105℃挥发物（%） | ≤1.0 | 0.74 |
| 吸油量（%） | 15-25 | 21.9 |
| 着色强度（%） | 95-105 | 98.2 |
| 耐200℃/30min （△E） | ≤1.0 | 0.72 |
Claims (1)
1.一种防锈抗紫外线氧化铁黑的生产方法，其特征在于：采用氢氧化钠氧化法制得的氧化铁黑，直接使用未烘干的氧化铁黑滤饼，加入相当于氧化铁黑滤饼重量3-6%的三聚磷酸铝、0.2-0.3%的紫外线吸收剂UV-327、0.4-0.5%的双(二辛氧基焦磷酸酯基)乙撑钛酸酯和0.5-1%的去离子水，2500-3000rpm高速研磨10-20分钟，取出烘干后加入适量的水打浆20-30分钟，制成浓度为55-65%的浆液，并加入浆液重量0.15-0.25%的纳米二氧化硅、0.2-0.3%的柠檬酸铵、0.2-0.3%的儿茶酚，搅拌15-25分钟，再通过胶体磨磨浆至粒径小于50μm，将浆液烘干打粉即为成品。