CN103320893B - 有色丙锦复合超细纤维的生产方法 - Google Patents

有色丙锦复合超细纤维的生产方法 Download PDF

Info

Publication number
CN103320893B
CN103320893B CN201310195783.9A CN201310195783A CN103320893B CN 103320893 B CN103320893 B CN 103320893B CN 201310195783 A CN201310195783 A CN 201310195783A CN 103320893 B CN103320893 B CN 103320893B
Authority
CN
China
Prior art keywords
nylon
fibre
composite
modification
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310195783.9A
Other languages
English (en)
Other versions
CN103320893A (zh
Inventor
余三川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongxiang Laidaobao Home Textile Co., Ltd.
Original Assignee
NINGBO SANBANG HOME PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO SANBANG HOME PRODUCTS CO Ltd filed Critical NINGBO SANBANG HOME PRODUCTS CO Ltd
Priority to CN201310195783.9A priority Critical patent/CN103320893B/zh
Publication of CN103320893A publication Critical patent/CN103320893A/zh
Application granted granted Critical
Publication of CN103320893B publication Critical patent/CN103320893B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种有色丙锦复合超细纤维的生产方法，其采用着色超细丙锦复合纤维为原料，所述的超细丙锦复合纤维是以超细丙纶纤维为芯线，外包覆改性尼龙纤维层组成，所述超细丙纶纤维的芯线直径在1.5微米至0.5微米，包覆后的复合纤维直径在4微米至1微米，所述改性尼龙是在尼龙6的熔体中含有氧化铈纳米粉体材料。本发明提供的有色丙锦复合超细纤维，既具有丙纶的良好纤维特性，具有的良好回弹力，伸长率18%时的弹性回复率在90%以上；又具有锦纶的良好着色特性，特别是在尼龙6中加入氧化铈纳米粉体材料，使尼龙6在着色时，极大提高了染料的活性，提高了其着色牢固度，进一步提高了尼龙6对多种染料的染色性。

Description

有色丙锦复合超细纤维的生产方法
技术领域
本发明涉及一种纤维的生产技术，特别是一种有色丙锦复合超细纤维的生产方法。
背景技术
目前丙锦复合超细纤维都是采用超细丙纶纤维和超细锦纶纤维简单加捻而成，这种简单加捻的复合纤维，由于纤维性能的不同，给后处理带来了一定的难度，特别是丙纶和锦纶的着色性能完全不同，给复合纤维的染色带来的很大的难题。
发明内容
本发明的目的是为了解决上述现有技术的不足而提供一种着色均匀，色牢度大的有色丙锦复合超细纤维的生产方法。
为了实现上述目的，本发明提供的一种有色丙锦复合超细纤维，它包括着色超细丙锦复合纤维，所述的超细丙锦复合纤维是以超细丙纶纤维为芯线，外包覆改性尼龙纤维层组成，所述超细丙纶纤维的芯线直径在1.5微米至0.5微米，包覆后的复合纤维直径在4微米至1微米，所述改性尼龙是在按重量计的100份尼龙6的熔体中含有氧化铈纳米粉体材料0.01份至0.1份。
一种有色丙锦复合超细纤维的生产方法，包括采用有色丙锦复合超细纤维为原料，所述改性尼龙是在按重量计的100份尼龙6的熔体中加入重量份的氧化铈纳米粉体材料0.01份至0.1份，充分分散均匀后，在235℃至250℃保持0.5小时至1小时而得到；改性尼龙与丙纶熔体同步拉丝，并将改性尼龙包覆在丙纶纤维外形成复合纤维；拉丝过程中，丙纶纤维的芯线直径控制在1.5微米至0.5微米，丙纶纤维的芯线纺丝温度控制在320℃,改性尼龙的纺丝温度控制在260℃，包覆后的复合纤维直径控制在4微米至1微米，成丝后通过酸性染料或分散性染料或其它尼龙6着色染料着色成为有色丙锦复合超细纤维。
在此，所述的超细纤维是指纤度0.3旦（直径5微米）以下的纤维。
本发明提供的有色丙锦复合超细纤维的生产方法所得到的有色丙锦复合超细纤维，通过对内外包覆结构的设置，复合纤维既具有丙纶的良好纤维特性，具有的良好回弹力，伸长率18%时的弹性回复率在90%以上；又具有锦纶的良好着色特性，特别是在尼龙6中加入氧化铈纳米粉体材料，使尼龙6在着色时，极大提高了染料的活性，提高了其着色牢固度，进一步提高了尼龙6对多种染料的染色性。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1：
本实施例提供的一种有色丙锦复合超细纤维，它包括着色超细丙锦复合纤维，所述的超细丙锦复合纤维是以超细丙纶纤维为芯线，外包覆改性尼龙纤维层组成，所述超细丙纶纤维的芯线直径在1.5微米至0.5微米，包覆后的复合纤维直径在4微米至1微米，所述改性尼龙是在按重量计的100份尼龙6的熔体中含有氧化铈纳米粉体材料0.01份；所述的纳米粉体材料是粉体粒径达到D90＜0.1um的纳米级粉体材料。
一种有色丙锦复合超细纤维的生产方法，包括采用上述的有色丙锦复合超细纤维，所述改性尼龙是在按重量计的100份尼龙6的熔体中加入重量份的氧化铈纳米粉体材料0.01份，充分分散均匀后，在235℃至250℃保持0.5小时至1小时而得到；改性尼龙与丙纶熔体同步拉丝，并将改性尼龙包覆在丙纶纤维外形成复合纤维；拉丝过程中，丙纶纤维的芯线直径控制在1.5微米至0.5微米，丙纶纤维的芯线纺丝温度控制在320℃,改性尼龙的纺丝温度控制在260℃，包覆后的复合纤维直径控制在4微米至1微米，成丝后通过酸性染料着色成为有色丙锦复合超细纤维。
通过测试，本发明提供的有色丙锦复合超细纤维，伸长率18%时的弹性回复率在90%以上；通过对不洗涤样品、洗涤30次、50次、100次比较后未色着变化。
实施例2：
本实施例提供的有色丙锦复合超细纤维，所述改性尼龙是在按重量计的100份尼龙6的熔体中含有氧化铈纳米粉体材料0.1份；生产方法同实施例1,成丝后采用分散性染料染色成有色丙锦复合超细纤维。
通过测试，本发明提供的有色丙锦复合超细纤维，伸长率18%时的弹性回复率在90%以上；通过对不洗涤样品、洗涤30次、50次、100次比较后未色着变化。
实施例3：
本实施例提供的有色丙锦复合超细纤维，所述改性尼龙是在按重量计的100份尼龙6的熔体中含有氧化铈纳米粉体材料0.5份；生产方法同实施例1。
通过测试，本发明提供的有色丙锦复合超细纤维，伸长率18%时的弹性回复率在90%以上；通过对不洗涤样品、洗涤30次、50次、100次比较后未色着变化。

Claims (1)

1.一种有色丙锦复合超细纤维的生产方法，采用着色超细丙锦复合纤维为原料，所述的超细丙锦复合纤维是以超细丙纶纤维为芯线，外包覆改性尼龙纤维层组成，所述超细丙纶纤维的芯线直径在1.5微米至0.5微米，包覆后的复合纤维直径在4微米至1微米，所述改性尼龙是在按重量计的100份尼龙6的熔体中含有氧化铈纳米粉体材料0.01份至0.1份，其特征是所述改性尼龙是在按重量计的100份尼龙6的熔体中加入重量份的氧化铈纳米粉体材料0.01份至0.1份，充分分散均匀后，在235℃至250℃保持0.5小时至1小时而得到；改性尼龙与丙纶熔体同步拉丝，并将改性尼龙包覆在丙纶纤维外形成复合纤维；拉丝过程中，丙纶纤维的芯线直径控制在1.5微米至0.5微米，丙纶纤维的芯线纺丝温度控制在320℃,改性尼龙的纺丝温度控制在260℃，包覆后的复合纤维直径控制在4微米至1微米，成丝后通过酸性染料或分散性染料或其它尼龙6着色染料着色成为有色丙锦复合超细纤维。
CN201310195783.9A 2013-05-24 2013-05-24 有色丙锦复合超细纤维的生产方法 Active CN103320893B (zh)