CN103274762A - Process for drawing traditional Chinese painting in Longquan celadon glaze - Google Patents

Process for drawing traditional Chinese painting in Longquan celadon glaze Download PDF

Info

Publication number
CN103274762A
CN103274762A CN2013101410954A CN201310141095A CN103274762A CN 103274762 A CN103274762 A CN 103274762A CN 2013101410954 A CN2013101410954 A CN 2013101410954A CN 201310141095 A CN201310141095 A CN 201310141095A CN 103274762 A CN103274762 A CN 103274762A
Authority
CN
China
Prior art keywords
celadon
glaze
longquan celadon
kiln
longquan
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101410954A
Other languages
Chinese (zh)
Other versions
CN103274762B (en
Inventor
吴新伟
吴艳芳
翁妙妙
许灵语
沈其旺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Jianzhen Longquan Ceramics Co. Ltd
Original Assignee
Lishui University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lishui University filed Critical Lishui University
Priority to CN201310141095.4A priority Critical patent/CN103274762B/en
Publication of CN103274762A publication Critical patent/CN103274762A/en
Application granted granted Critical
Publication of CN103274762B publication Critical patent/CN103274762B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a process for drawing traditional Chinese painting in Longquan celadon glaze. The process comprises a shaping step (1): preparing a mud blank of the Longquan celadon; a drying step (2): performing drying treatment on the prepared mud blank of the Longquan celadon; a fettling step (3): fettling the dried mud blank of the celadon; a biscuiting step (4): loading the dried and fettled blank of the Longquan celadon into a furnace, so as to obtain a biscuit of the Longquan celadon; a washing step (5): washing the surface of the biscuit of the Longquan celadon by dipping water with fine sponge; a glazing step (6): glazing the biscuit of the celadon; a drawing step (7): preparing high temperature raw materials and drawing decorative patterns of the traditional Chinese painting; a glazing step (8): spraying glaze on the blank body of the celadon; and a glaze firing step (9): loading the blank body of the Longquan celadon into the furnace to carry out secondary firing after the glaze layer of the Longquan celadon is dried, so that a well decorated Longquan celadon product glazed with the traditional Chinese painting is obtained. The traditional Chinese painting is drawn on the decorative part of the Longquan celadon, so that art celadon products with rich decoration and a better visible effect can be prepared.

Description

A kind of technique that traditional Chinese Painting is drawn in Longquan celadon glaze
Technical field
The invention belongs to Longquan celadon manufacture craft field, it is related to the technique that traditional Chinese Painting is drawn in a kind of Longquan celadon glaze.
Background technology
Decorated in Longquan celadon glaze except carving, drawing, in addition to the tradition design such as applique is main decoration technology, decoration decorative under glaze is simply simply just made of materials such as some iron oxide and cupric oxide.Along with Longquan celadon practitioner is in the shortcoming of the artistic abilities such as Chinese painting, cause time-honored Longquan celadon glaze Chinese painting decoration technology research and the upper relative blank of practice, directly affect celadon and decorate single artistic effect, be difficult to improve in artistic grade and cultural quality.In practice, the innovative technology of Longquan celadon glaze Chinese painting decoration makes, to Longquan celadon innovation and development and the great realistic meaning of product development.
The content of the invention
It is an object of the invention to provide a kind of Longquan celadon glaze Chinese painting draw craft, overcome blank of the Longquan celadon product in the drafting of glaze Chinese painting in existing decoration technology, drafting material is made with high temperature feedstock, traditional Chinese Painting drafting is carried out to imposing the decorative position after one layer of starved glaze after biscuiting, makes it that a kind of brand-new traditional Chinese Painting draw craft of Longquan celadon be presented after firing.
In order to realize above-mentioned purpose, the technical solution adopted in the present invention is：
A kind of Longquan celadon glaze Chinese painting draw craft, this method comprises the following steps：
1. it is molded：Required according to drawing design, make Longquan celadon moulded pottery not yet put in a kiln to bake；
2. dry：Processing is dried in the Longquan celadon moulded pottery not yet put in a kiln to bake made, dry degree is reached；
3. repaired biscuit：According to the technological requirement of drafting, dry celadon moulded pottery not yet put in a kiln to bake is repaired, then polished with the fine sandpaper of 800 ~ 1500 mesh, moulded pottery not yet put in a kiln to bake surface reaches smooth without particle pore-free shape；
4. biscuiting：The Longquan celadon carcass after finishing will be dried and put into kiln, fire 5 ~ 8 hours, kiln temperature is gradually increased to 750 ~ 800 DEG C from normal temperature, be then further continued for insulation 30 ~ 60 minutes, natural cooling after stopping working obtains Longquan celadon biscuiting tire；
5. clean：Got wet cleaning Longquan celadon biscuiting tire surface with thin sponge, reaches more smooth without particle pore-free shape, and processing is dried；
6. glazing：After Longquan celadon tire reaches degree of drying, glaze is soaked to celadon biscuiting tire, glazed thickness is 0.5 ~ 0.8mm, and processing is dried；
7. draw：After Longquan celadon glaze layer reaches degree of drying, modulation high temperature feedstock draws Chinese painting ornamental pattern on glaze, and processing is dried；
8. glazing：After Longquan celadon glaze layer high temperature feedstock reaches degree of drying, glaze spraying is carried out to celadon carcass, nozzle diameter is 1 ~ 3mm, and glazed thickness reaches 4 ~ 5mm, processing is dried；
Glaze firing：Longquan celadon glaze layer is reached after degree of drying, kiln is put into and carries out twice firing, by the firing of 8 ~ 12 hours, kiln temperature is reached only fire cooling after 1280 DEG C, obtains glaze Chinese painting and decorate intact Longquan celadon product,.
Preferably, described step
Figure 389647DEST_PATH_IMAGE002
In shaping, be molded using hand throwing, high-pressure slip-casting, roll mud plate shaping make Longquan celadon moulded pottery not yet put in a kiln to bake.
Preferably, described step 3. in repaired biscuit, dry celadon moulded pottery not yet put in a kiln to bake finely repaired, moulded pottery not yet put in a kiln to bake surface pores is filled up, then progressively polished with the fine sandpaper of 800 ~ 1500 mesh, reached smooth without particle pore-free shape.
Preferably, described step 6. in, using by hand soak glaze method one layer of starved glaze is imposed to Longquan celadon biscuit, thickness is 0.5-0.8.
Preferably, described step 7. in, modulation high temperature feedstock include chromium oxide or oxidation iron formula, diluted with water, with Chinese painting brush instrument carry out traditional Chinese Painting pattern drafting.
Preferably, described step 8. in, shower nozzle is selected from 1 to 3mm respectively, using spray glazing to having painted celadon tire by thin to thick progress glazing.
Preferably, describedIn step, programming rate requirement is very slow between temperature reaches 1080 ~ 1200 DEG C, 1 DEG C/min of speed；Fire after being incubated 60 minutes after 1280 DEG C, using natural cooling, the kiln discharge after kiln temperature is cooled to 100-80 DEG C produces Longquan celadon glaze Chinese painting pattern finished product.
The present invention is as a result of above-mentioned technical scheme, realize the technological break-through of Longquan celadon glaze Chinese painting draw craft, and pass through the method for drafting, decorative position is subjected to traditional Chinese Painting drafting, it can produce and decorate the more preferably artistic celadon product of abundant, visual effect, the limitation innovated in Longquan celadon glaze without traditional Chinese Painting as decorative art is breached, is that directional beacon is found in the brand-new development of Longquan celadon decoration technology, lifts Longquan celadon cultural connotation.Art is valued for innovation, by Longquan celadon glaze Chinese painting draw craft, excavates Longquan celadon new manifestation mode and esthetic sentiment, allows Longquan celadon to play bigger effect and value in the development of contemporary ceramic art. 
Embodiment
The process technology scheme of the present invention is described in further detail below by specific embodiment.
Embodiment 1
Lotus bottle draw craft, comprises the following steps in a kind of Longquan celadon glaze：
Figure 488501DEST_PATH_IMAGE002
Shaping：Celadon moulded pottery not yet put in a kiln to bake is made using offhand, such as osculum round vase is fabricated to osculum round vase shape, diameter 18cm, high 25cm according to its rendering request.
Figure 631906DEST_PATH_IMAGE003
Dry：The celadon moulded pottery not yet put in a kiln to bake made is positioned over ventilation or temperature higher position is dried, certain carcass strength is made it have, takes more than 100 hours.
Repaired biscuit：Dry celadon moulded pottery not yet put in a kiln to bake is placed on repaired biscuit car, according to design original text requirement, carcass is subjected to refine using cutter, the refine at traditional Chinese Painting position is especially drawn to body, integrally polished with the fine sandpaper of 800-1000 mesh afterwards, then position is drawn with the sand papering of 1500 mesh, reached smooth without particle pore-free shape, finish the rear a diameter of 15cm of round vase body, high 23cm.
4. biscuiting：The Longquan celadon carcass after finishing will be dried and put into kiln, fire 8 hours, kiln temperature is gradually increased to 860 DEG C from normal temperature, be then further continued for insulation 60 minutes, natural cooling after stopping working obtains Longquan celadon biscuiting tire.
5. clean：Got wet cleaning biscuiting tire surface with thin sponge, reaches smooth without graininess, and processing is dried.
6. biscuiting：By dried celadon carcass and bedder loading of kiln, when firing makes the kiln temperature reach 750 DEG C for 5 hours, cooling of stopping working obtains celadon biscuiting tire.
7. glazing：After biscuiting tire reaches degree of drying, using glaze method is once soaked, glazed thickness is about 0.7mm, and drying process is carried out afterwards.
Draw：After glaze layer reaches degree of drying, modulate that high temperature feedstock is blackish green and red formulation, the blackish green lotus leaves one of completion from dense to light are drawn on glaze, three, lotus pole is drawn in the same way, it is another to take one-pen to draw the red lotus one from dense to light, partial desiccation processing is carried out, then lotus leaf passages through which vital energy circulates is sketched the contours with thick ink green, point pole and pistil, carry out drying process afterwards.
Figure 583177DEST_PATH_IMAGE001
Glazing：After lotus drafting portion reaches degree of drying in glaze layer, glaze spraying processing is carried out to celadon carcass, nozzle diameter is 2mm, and glazed thickness reaches about 4mm, and drying process is carried out afterwards.
Glaze firing：By dried osculum lotus it is bottled enter kiln carry out twice firing, its step includes：Drying stage：Heated up with 3 hours slow fires, kiln temperature is risen to 450 DEG C；B. oxidation stage：Kiln temperature is risen to 980 DEG C with 2 hours, steam is fully volatilized with oxidation Decomposition gaseous product；C. holding stage：It was incubated with 1 hour, makes kiln temperature stable at 980 DEG C, contribute to the discharge of gas in tire, glaze；D. strong reduction phase：Kiln temperature was set to rise to 1200 DEG C with 1.5 hours, kiln air pressure is enlarged to 0.04Mpa；E. weak reduction temperature rise period：Kiln temperature is risen to 1280 DEG C with 1 hour；F. holding stage：It is only fiery after kiln temperature control is incubated into 1 hour at 1280 DEG C；G. cooling stage：Using natural cooling, the kiln discharge after kiln temperature is cooled to 75 DEG C is fired and completed.
Embodiment 2
The Oujiang River small stream fish process is drawn in a kind of Longquan celadon cup glaze, is comprised the following steps：
Figure 875935DEST_PATH_IMAGE002
Molding：Make cup high pressure master mold（High 9cm, rim of a cup diameter 9cm, foot 6cm）, after checking accurately, turn over and high-pressure work mould be made.
Figure 301100DEST_PATH_IMAGE003
Shaping：Celadon cup moulded pottery not yet put in a kiln to bake is made using high-pressure slip-casting shaping, partial desiccation processing is carried out.
Figure 337189DEST_PATH_IMAGE004
Cleaning：By the celadon made cup moulded pottery not yet put in a kiln to bake moisturizing cleaning, press back processing is carried out.After it is completely dried, traditional Chinese Painting position is drawn to cup body and integrally polished with the fine sandpaper of 1000 mesh, surface reaches flat smooth shape.
4. biscuiting：Dried Longquan celadon carcass is put into kiln, fires 6 hours, kiln temperature is gradually increased to 800-900 DEG C from normal temperature, insulation 60 minutes is then further continued for, natural cooling after stopping working obtains Longquan celadon biscuiting tire.
5. clean：The plaster on biscuiting tire surface is handled with writing brush writing brush, is reached smooth without graininess.
6. glazing：After biscuiting tire reaches degree of drying, using glaze method is once soaked, glazed thickness is about 0.1-0.2mm, and drying process is carried out afterwards.
7. draw：After glaze layer reaches degree of drying, high temperature feedstock formula is modulated, the Oujiang River small stream fish two is drawn on glaze, fish body emphasizes the deep or light and withered wet change of color, finally with the eyes and face of heavy colour point fish.
Figure 432184DEST_PATH_IMAGE005
Glazing：After small stream fish drafting portion reaches degree of drying in glaze layer, glaze spraying processing is carried out to celadon carcass, is 1-2mm gradually glaze sprayings with nozzle diameter, glazed thickness reaches 3-4mm, and drying process is carried out afterwards.
Figure 163511DEST_PATH_IMAGE001
Glaze firing：Dried small stream fish cup is entered into kiln and carries out twice firing, its step includes：Drying stage：Heated up with 3 hours slow fires, kiln temperature is risen to 450 DEG C；B. oxidation stage：Kiln temperature is risen to 980 DEG C with 2 hours, steam is fully volatilized with oxidation Decomposition gaseous product；C. holding stage：It was incubated with 1.5 hours, makes kiln temperature stable at 980 DEG C, contribute to the discharge of gas in tire, glaze；D. strong reduction phase：Kiln temperature was set to rise to 1200 DEG C with 5 hours, kiln air pressure is enlarged to 1.15 0.04Mpa；E. weak reduction temperature rise period：Kiln temperature is risen to 1280 DEG C with 1 hour；F. holding stage：It is only fiery after kiln temperature control is incubated into 1 hour at 1280 DEG C；G. cooling stage：Using natural cooling, the kiln discharge after kiln temperature is cooled to 75 DEG C is fired and completed.
Embodiment 3
Traditional Chinese Painting the Oujiang River technique is drawn in a kind of Longquan celadon disk glaze, is comprised the following steps：
Figure 267733DEST_PATH_IMAGE002
Molding：Make plate high pressure master mold（High 3cm, disk mouthful diameter 23cm, foot 14.5cm）, after checking accurately, turn over and high-pressure work mould be made.
Figure 892750DEST_PATH_IMAGE003
Shaping：Celadon disk moulded pottery not yet put in a kiln to bake is made using high-pressure molding, partial desiccation processing is carried out.
Figure 424225DEST_PATH_IMAGE004
Cleaning：The celadon disk moulded pottery not yet put in a kiln to bake made is subjected to moulding mark processing.After it is completely dried, traditional Chinese Painting position is drawn to disk body and integrally polished with the fine sandpaper of 900-1000 mesh, card reaches flat smooth shape.
4. biscuiting：Dried Longquan celadon carcass is put into kiln, fires 7 hours, kiln temperature is gradually increased to 800 DEG C from normal temperature, insulation 30 minutes is then further continued for, natural cooling after stopping working obtains Longquan celadon disk biscuiting tire.
5. clean：The plaster in biscuiting placenta face is handled with writing brush writing brush, is reached smooth without graininess.
6. glazing：After biscuiting tire reaches degree of drying, using glaze method is once soaked, glazed thickness is about 0.2-0.3mm, and drying process is carried out afterwards.
7. draw：After glaze layer reaches and is completely dried, high temperature feedstock formula is modulated, the Oujiang River sailing boat, distant mountain, crescent moon are drawn on glaze to inscribe plain autumn money and draw side's red seal chapter, the deep or light and withered wet change of colourity is emphasized, the face of the line and distant mountain of focusing on sailing boat carries out contrast processing.
Figure 626536DEST_PATH_IMAGE005
Glazing：After reaching and be completely dried after drafting portion in glaze layer, glaze spraying processing is carried out to celadon carcass, is 2mm glaze sprayings with nozzle diameter, card glazed thickness reaches 3-4mm, and drying process is carried out afterwards. 
Figure 534450DEST_PATH_IMAGE001
Glaze firing：Dried celadon disk is put into kiln and carries out twice firing, its step includes：Drying stage：Heated up with 3 hours slow fires, kiln temperature is risen to 450 DEG C；B. oxidation stage：Kiln temperature is risen to 990 DEG C with 2 hours, steam is fully volatilized with oxidation Decomposition gaseous product；C. holding stage：It was incubated with 1.5 hours, makes kiln temperature stable at 990 DEG C, contribute to the discharge of gas in tire, glaze；D. strong reduction phase：Kiln temperature was set to rise to 1250 DEG C with 4 hours, kiln air pressure is enlarged to 1.15 0.04Mpa；E. weak reduction temperature rise period：Kiln temperature is risen to 1300 DEG C with 1 hour；F. holding stage：It is only fiery after kiln temperature control is incubated into 1 hour at 1300 DEG C；G. cooling stage：Using natural cooling, kiln is opened after kiln temperature is cooled to 100-120 DEG C,.

Claims (8)

1. the technique of traditional Chinese Painting is drawn in a kind of Longquan celadon glaze, it is characterised in that this method comprises the following steps：
1. it is molded：Required according to drawing design, make Longquan celadon moulded pottery not yet put in a kiln to bake；
2. dry：Processing is dried in the Longquan celadon moulded pottery not yet put in a kiln to bake made, dry degree is reached；
3. repaired biscuit：According to the technological requirement of drafting, dry celadon moulded pottery not yet put in a kiln to bake is repaired, then polished with the fine sandpaper of 800 ~ 1500 mesh, moulded pottery not yet put in a kiln to bake surface reaches smooth without particle pore-free shape；
4. biscuiting：The Longquan celadon carcass after finishing will be dried and put into kiln, fire 5 ~ 8 hours, kiln temperature is gradually increased to 750 ~ 800 DEG C from normal temperature, be then further continued for insulation 30 ~ 60 minutes, natural cooling after stopping working obtains Longquan celadon biscuiting tire；
5. clean：Got wet cleaning Longquan celadon biscuiting tire surface with thin sponge, reaches more smooth without particle pore-free shape, and processing is dried；
6. glazing：After Longquan celadon tire reaches degree of drying, glaze is soaked to celadon biscuiting tire, glazed thickness is 0.5 ~ 0.8mm, and processing is dried；
7. draw：After Longquan celadon glaze layer reaches degree of drying, modulation high temperature feedstock draws Chinese painting ornamental pattern on glaze, and processing is dried；
8. glazing：After Longquan celadon glaze layer high temperature feedstock reaches degree of drying, glaze spraying is carried out to celadon carcass, nozzle diameter is 1 ~ 3mm, and glazed thickness reaches 4 ~ 5mm, processing is dried；
Figure 2013101410954100001DEST_PATH_IMAGE002
Glaze firing：Longquan celadon glaze layer is reached after degree of drying, kiln is put into and carries out twice firing, by the firing of 8 ~ 12 hours, kiln temperature is reached only fire cooling after 1280 DEG C, obtains glaze Chinese painting and decorate intact Longquan celadon product,.
2. the technique of Chinese painting is drawn in Longquan celadon glaze according to claim 1, it is characterised in that：Described step
Figure 2013101410954100001DEST_PATH_IMAGE004
In shaping, be molded using hand throwing, high-pressure slip-casting, roll mud plate shaping make Longquan celadon moulded pottery not yet put in a kiln to bake.
3. the technique of Chinese painting is drawn in Longquan celadon glaze according to claim 1, it is characterised in that：Described step 3. in repaired biscuit, dry celadon moulded pottery not yet put in a kiln to bake finely repaired, moulded pottery not yet put in a kiln to bake surface pores is filled up, then progressively polished with the fine sandpaper of 800 ~ 1500 mesh, reached smooth without particle pore-free shape.
4. the technique of Chinese painting is drawn in Longquan celadon glaze according to claim 1, it is characterised in that：Described step 6. in, using by hand soak glaze method one layer of starved glaze is imposed to Longquan celadon biscuit, thickness is 0.5-0.8.
5. the technique of Chinese painting is drawn in Longquan celadon glaze according to claim 1, it is characterised in that：Described step 7. in, modulation high temperature feedstock include chromium oxide or oxidation iron formula, diluted with water, with Chinese painting brush instrument carry out traditional Chinese Painting pattern drafting.
6. the technique of Chinese painting is drawn in Longquan celadon glaze according to claim 1, it is characterised in that：Described step 8. in, shower nozzle is selected from 1 to 3mm respectively, using spray glazing to having painted celadon tire by thin to thick progress glazing.
7. the technique of Chinese painting is drawn in Longquan celadon glaze according to claim 1, it is characterised in that：Described
Figure 97255DEST_PATH_IMAGE002
In step, programming rate requirement is very slow between temperature reaches 1080 ~ 1200 DEG C, 1 DEG C/min of speed；Fire after being incubated 60 minutes after 1280 DEG C, using natural cooling, the kiln discharge after kiln temperature is cooled to 100-80 DEG C produces Longquan celadon glaze Chinese painting pattern finished product.
8. a kind of Longquan celadon, it is characterised in that：Prepared using the technique described in claim 1 ~ 7 any one claim.
CN201310141095.4A 2013-04-23 2013-04-23 Process for drawing traditional Chinese painting in Longquan celadon glaze Expired - Fee Related CN103274762B (en)