CN106565212A - Manufacturing method of multicolor ceramic vase and multicolor ceramic vase - Google Patents
Manufacturing method of multicolor ceramic vase and multicolor ceramic vase Download PDFInfo
- Publication number
- CN106565212A CN106565212A CN201611017684.1A CN201611017684A CN106565212A CN 106565212 A CN106565212 A CN 106565212A CN 201611017684 A CN201611017684 A CN 201611017684A CN 106565212 A CN106565212 A CN 106565212A
- Authority
- CN
- China
- Prior art keywords
- kiln
- bake
- moulded pottery
- pattern
- firing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a manufacturing method of a multicolor ceramic vase and the multicolor ceramic vase. The manufacturing method of the multicolor ceramic vase comprises the following steps: refining mud, preparing a blank, performing trimming, performing engraving, and blowing a cobalt blue material namely performing cobalt blue material blowing treatment on the engraved mud blank by using a blowing tool; removing the cobalt blue material from patterns, namely scraping off the cobalt blue material attached to the patterns on the mud blank by using a tool; performing painting and pattern separation, namely performing painting treatment on parts except the patterns on the mud blank by using a painting needle, and performing pattern separation treatment on the patterns to ensure that the patterns have a three-dimensional sense; and performing biscuit firing to form a transparent glaze after firing. The manufacturing method disclosed by the invention can solve the technical problems of how to enable the vase to have three-dimensional patterns, achieve a painting effect on a vase body and enable the colors of part of three-dimensional patterns to be inconsistent with that of the other three-dimensional patterns.
Description
The application is the applying date to be on December 01st, 2015, and Application No. 2015108587352 is entitled " colorful
The divisional application of the manufacture method of ceramic vase and colorful ceramic vase ".
Technical field
The present invention relates to have the colorful ceramic vase that two kinds of patterns are combined on a kind of porcelain, also there is protrusion on the vase
Pattern.
Background technology
Current ceramic vase is usually that multiple color glaze is directly drawn on moulded pottery not yet put in a kiln to bake, then fires and obtains colorful Ceramic flower
Bottle, without raised pattern from without solid layer feeling, and the coloured glaze on moulded pottery not yet put in a kiln to bake also only has one layer to this vase, does not have
Two kinds of coloured glazes are combined with each other, so pattern expression is more single, in addition, not taking off floral pattern on moulded pottery not yet put in a kiln to bake, only have pattern,
So that whole bottle does not take off colored aesthetic feeling.There is a kind of vase at present, there is space pattern, but space pattern on the bottle
Color and other positions of bottle solid colour, be combined with each other without two kinds of coloured glazes, so pattern expression is more single,
In addition, not taking off floral pattern on moulded pottery not yet put in a kiln to bake, only there is pattern, so that whole bottle does not take off colored aesthetic feeling.
The content of the invention
It is an object of the invention to provide a kind of manufacture method of colorful ceramic vase, solves how to make having solid on vase
Pattern and on body have take off colored effect and make part isometric pattern color and other space patterns color it is inconsistent
Technical problem.
It is a further object to provide a kind of colorful ceramic vase, solves how to make having space pattern on vase
And there is the inconsistent technology of color of color and other space patterns taken off colored effect and make part isometric pattern on body
Problem.
The manufacture method of colorful ceramic vase：Comprise the steps：
1st, pugging：Moulded pottery not yet put in a kiln to bake is filtered, dried, is put in air compressor and is refined so as to being not in air inside moulded pottery not yet put in a kiln to bake
Bubble and occur splitting base phenomenon；
2nd, make base：Moulded pottery not yet put in a kiln to bake after pugging is put in base making machine carries out molding or offhand；
3rd, repaired biscuit：The moulded pottery not yet put in a kiln to bake of molding is repaired with repaired biscuit instrument；
4th, carve：Moulded pottery not yet put in a kiln to bake after repaired biscuit is carried out into hand engraving using instrument, the pattern on moulded pottery not yet put in a kiln to bake with protrusion is made；
5th, blue and white material is blown：The moulded pottery not yet put in a kiln to bake carved is carried out blowing blue and white material process using material instrument is blown；
6th, pattern removes blue and white material：The blue and white material that will be attached on the pattern on moulded pottery not yet put in a kiln to bake is wiped off using instrument；
7th, flower and potted flower are taken off：Position on moulded pottery not yet put in a kiln to bake in addition to pattern carries out taking off colored process using floricome is taken off, and carries out on pattern point
Flower is processed, and makes pattern have solid layer feeling；
8th, biscuiting：Moulded pottery not yet put in a kiln to bake after taking off flower and potted flower is put in kiln carries out biscuiting, moulded pottery not yet put in a kiln to bake is facilitated sucking and is prevented sucking
During curling；
9th, blowing can form the glaze of transparent color after firing：Partial pattern on moulded pottery not yet put in a kiln to bake after biscuiting is carried out to fill out high temperature coloured glaze
Process, and blown moulded pottery not yet put in a kiln to bake whole position the glaze process that transparent color can be formed after firing；
10th, glaze firing forms finished product：Moulded pottery not yet put in a kiln to bake in step 9 is carried out into glaze firing and forms finished product.
The ceramic vase either appreciates bottle either Guan yin vase or beautiful tall bottle with spout for vault-of-Heaven vase.
The high temperature coloured glaze is high temperature Tao beauty's color glaze.
The glaze that transparent color can be formed after firing is celadon glaze either blue and white glaze or celeste glaze.
The step of biscuiting is：After moulded pottery not yet put in a kiln to bake loading of kiln, then light a fire, wicket is opened during igniting, air pressure is adjusted to
0.15Pa, the purpose of igniting of opening the door is the liquefied gas and moisture content for excluding residual in kiln, and firing temperature is 300-350 degree Celsius, is burnt
1-2 hours processed drain moisture substantially to moulded pottery not yet put in a kiln to bake；Wicket is closed, air pressure is adjusted to into 0.2Pa, intensification can not be too fast, firing temperature
For 550-650 degree Celsius, 1-2 hours are fired；Use oxidizing flame firing instead, and air pressure in kiln is adjusted to into 0.25Pa, temperature reaches
When 800-850 degree Celsius, kept for 30-50 minutes, then temperature is burnt to 850-900 degree Celsius, fire 1-2 hours.
The step of glaze firing is：After glazed body loading of kiln, by the biscuiting step firing temperature 950-1000 degree Celsius is reached
When, 0.5-1 hours are incubated, use reducing flame firing instead, air pressure is adjusted to 0.8-1.2Pa, and temperature reaches 1280-1300 degree Celsius, burns
9-11 hours processed；After truce, wicket is opened, naturally cool to 1000-1100 degree Celsius, shut wicket, natural cooling 10-12
Hour.
Colorful ceramic vase, is made by described manufacture method and is obtained.
The ceramic vase either appreciates bottle either Guan yin vase or beautiful tall bottle with spout for vault-of-Heaven vase.
The invention has the beneficial effects as follows：Have on the body of the present invention and take off flower process, so have taking off colored effect；On body
Partial pattern removes in the former color material for having sprayed for the first time, then fills the coloured glaze of particular color and carries out potted flower, so makes
There are the different pattern obtained on bottle different color tables to reach.
Specific embodiment
Embodiment 1
As a example by the present embodiment is to make vault-of-Heaven vase.
Pugging：Moulded pottery not yet put in a kiln to bake is filtered, dried, is put in air compressor and is refined so as to being not in sky inside moulded pottery not yet put in a kiln to bake
Gas bubble and occur splitting base phenomenon.
Make base：Moulded pottery not yet put in a kiln to bake after pugging is put in base making machine carries out molding or offhand so as to be shaped as vault-of-Heaven vase
Shape.Repaired biscuit：The moulded pottery not yet put in a kiln to bake of molding is repaired with repaired biscuit instrument.
Engraving：Moulded pottery not yet put in a kiln to bake after repaired biscuit is carried out into hand engraving using instrument, the Flos Nelumbinises and Folium Nelumbinis on moulded pottery not yet put in a kiln to bake with protrusion are made
Pattern.
Blow blue and white material：The moulded pottery not yet put in a kiln to bake carved is carried out blowing at blue and white material using material instrument is blown to the whole positions in body outside
Reason.
Pattern removes blue and white material：The blue and white material that will be attached on the Flos Nelumbinises on moulded pottery not yet put in a kiln to bake and Folium Nelumbinis pattern is scraped using instrument
Fall.
Take off flower and potted flower：Position on moulded pottery not yet put in a kiln to bake in addition to pattern carries out taking off colored process using floricome is taken off, and is needing potted flower
Potted flower process is carried out on pattern, makes pattern that there is solid layer feeling, the such as inside potted flower in Folium Nelumbinis goes out the vein reason of Folium Nelumbinis.
Biscuiting：After moulded pottery not yet put in a kiln to bake loading of kiln, then light a fire, wicket is opened during igniting, air pressure is adjusted to 0.15Pa, igniting of opening the door
Purpose is the liquefied gas and moisture content for excluding residual in kiln, and firing temperature is 300 degrees Celsius, and firing is drained for 1 hour substantially to moulded pottery not yet put in a kiln to bake
Moisture；Wicket is closed, air pressure is adjusted to into 0.2Pa, intensification can not be too fast, firing temperature is 550 degrees Celsius, is fired 1 hour；Change
Fired with oxidizing flame, and air pressure in kiln is adjusted to into 0.25Pa, when temperature reaches 800 degrees Celsius, kept for 30 minutes, then by temperature
Burn to 850 degrees Celsius, fire 1 hour.
Blow high temperature Tao beauty's color glaze：The process of raising temperature Tao beauty color glaze is carried out to the Flos Nelumbinises pattern on the moulded pottery not yet put in a kiln to bake after biscuiting,
And moulded pottery not yet put in a kiln to bake whole position is carried out blowing celadon glaze process；
Glaze firing：After glazed body loading of kiln, during by the biscuiting step firing temperature up to 950 degrees Celsius, 0.5 hour is incubated, is used instead also
Former flame is fired, and air pressure is adjusted to 0.8Pa, and temperature is fired 9 hours up to 1280 degrees Celsius；After truce, wicket is opened, it is naturally cold
But to 1000 degrees Celsius, wicket, natural cooling 10 hours are shut.
Embodiment 2
As a example by the present embodiment is to make reward bottle.
Pugging：Moulded pottery not yet put in a kiln to bake is filtered, dried, is put in air compressor and is refined so as to being not in sky inside moulded pottery not yet put in a kiln to bake
Gas bubble and occur splitting base phenomenon.
Make base：Moulded pottery not yet put in a kiln to bake after pugging is put in base making machine carries out molding or offhand makes moulded pottery not yet put in a kiln to bake into the shape of reward bottle
Shape.
Repaired biscuit：The moulded pottery not yet put in a kiln to bake of molding is repaired with repaired biscuit instrument.
Engraving：Moulded pottery not yet put in a kiln to bake after repaired biscuit is carried out into hand engraving using instrument, the pattern on moulded pottery not yet put in a kiln to bake with protrusion, these figures are made
Case includes Flos Mume and prunus mume (sieb.) sieb.et zucc. branch.
Blow blue and white material：The moulded pottery not yet put in a kiln to bake carved is carried out blowing blue and white material process using material instrument is blown.
Pattern removes blue and white material：The blue and white material that will be attached on Flos Mume and prunus mume (sieb.) sieb.et zucc. branch pattern is wiped off using instrument.
Take off flower and potted flower：Position on moulded pottery not yet put in a kiln to bake in addition to Flos Mume and prunus mume (sieb.) sieb.et zucc. branch pattern carries out taking off colored process using floricome is taken off,
Potted flower process is carried out on Flos Mume and prunus mume (sieb.) sieb.et zucc. branch pattern, makes Flos Mume and prunus mume (sieb.) sieb.et zucc. branch pattern that there is solid layer feeling.
Biscuiting：After moulded pottery not yet put in a kiln to bake loading of kiln, then light a fire, wicket is opened during igniting, air pressure is adjusted to 0.15Pa, igniting of opening the door
Purpose is the liquefied gas and moisture content for excluding residual in kiln, and firing temperature is 350 degrees Celsius, and firing is drained for 2 hours substantially to moulded pottery not yet put in a kiln to bake
Moisture；Wicket is closed, air pressure is adjusted to into 0.2Pa, intensification can not be too fast, firing temperature is 650 degrees Celsius, is fired 2 hours；Change
Fired with oxidizing flame, and air pressure in kiln is adjusted to into 0.25Pa, when temperature reaches 850 degrees Celsius, kept for 50 minutes, then by temperature
Burn to 900 degrees Celsius, fire 2 hours.
Blow blue and white glaze：The process of raising temperature fancy glaze is carried out to the plum blossom design on the moulded pottery not yet put in a kiln to bake after biscuiting, and to moulded pottery not yet put in a kiln to bake whole portion
Position carries out blowing blue and white glaze process.
Glaze firing：After glazed body loading of kiln, during by the biscuiting step firing temperature up to 1000 degrees Celsius, 1 hour is incubated, is used instead
Reducing flame is fired, and air pressure is adjusted to 1.2Pa, and temperature is fired 11 hours up to 1300 degrees Celsius；After truce, wicket is opened, it is natural
1100 degrees Celsius are cooled to, wicket, natural cooling 12 hours is shut.
Embodiment 3
As a example by the present embodiment is to make Guan yin vase.
Pugging：Moulded pottery not yet put in a kiln to bake is filtered, dried, is put in air compressor and is refined so as to being not in sky inside moulded pottery not yet put in a kiln to bake
Gas bubble and occur splitting base phenomenon.
Make base：Moulded pottery not yet put in a kiln to bake after pugging is put in base making machine to carry out molding or offhand and makes it into Guan yin vase.
Repaired biscuit：The moulded pottery not yet put in a kiln to bake of molding is repaired with repaired biscuit instrument.
Engraving：Moulded pottery not yet put in a kiln to bake after repaired biscuit is carried out into hand engraving using instrument, the Folium Salicis Babylonicae and Ramulus Salicis Babylonicae on moulded pottery not yet put in a kiln to bake with protrusion is made
Pattern.
Blow blue and white material：The moulded pottery not yet put in a kiln to bake carved is carried out blowing blue and white material process using material instrument is blown.
Pattern removes blue and white material：The blue and white material that will be attached on the Folium Salicis Babylonicae on moulded pottery not yet put in a kiln to bake and Ramulus Salicis Babylonicae pattern is scraped using instrument
Fall.
Take off flower and potted flower：Position on moulded pottery not yet put in a kiln to bake in addition to Folium Salicis Babylonicae and Ramulus Salicis Babylonicae pattern carries out taking off colored process using floricome is taken off,
Potted flower process is carried out on Folium Salicis Babylonicae and Ramulus Salicis Babylonicae pattern, makes pattern that there is solid layer feeling.
Biscuiting：After moulded pottery not yet put in a kiln to bake loading of kiln, then light a fire, wicket is opened during igniting, air pressure is adjusted to 0.15Pa, igniting of opening the door
Purpose is the liquefied gas and moisture content for excluding residual in kiln, and firing temperature is 325 degrees Celsius, and firing is arranged for 1.5 hours substantially to moulded pottery not yet put in a kiln to bake
Solid carbon dioxide point；Wicket is closed, air pressure is adjusted to into 0.2Pa, intensification can not be too fast, firing temperature is 600 degrees Celsius, fires 1.5 little
When；Use oxidizing flame firing instead, and air pressure in kiln is adjusted to into 0.25Pa, when temperature reaches 825 degrees Celsius, kept for 40 minutes, then
Temperature is burnt to 876 degrees Celsius, is fired 1.8 hours.
Blow celeste glaze：The process of raising temperature green glaze is carried out to the Folium Salicis Babylonicae pattern on the moulded pottery not yet put in a kiln to bake after biscuiting, and to moulded pottery not yet put in a kiln to bake whole portion
Position carries out blowing celeste glaze process.
Glaze firing：After glazed body loading of kiln, during by the biscuiting step firing temperature up to 970 degrees Celsius, 0.6 hour is incubated, is changed
Fired with reducing flame, air pressure is adjusted to 0.8Pa, temperature is fired 10 hours up to 1290 degrees Celsius；After truce, wicket is opened, from
1050 degrees Celsius are so cooled to, wicket, natural cooling 11 hours is shut.
Embodiment 4
As a example by the present embodiment is to make beautiful tall bottle with spout.
Pugging：Moulded pottery not yet put in a kiln to bake is filtered, dried, is put in air compressor and is refined so as to being not in sky inside moulded pottery not yet put in a kiln to bake
Gas bubble and occur splitting base phenomenon.
Make base：Moulded pottery not yet put in a kiln to bake after pugging is put in base making machine to carry out molding or offhand and makes it into beautiful tall bottle with spout.
Repaired biscuit：The moulded pottery not yet put in a kiln to bake of molding is repaired with repaired biscuit instrument.
Engraving：Moulded pottery not yet put in a kiln to bake after repaired biscuit is carried out into hand engraving using instrument, the Fructus Mali pumilae and Fructus Mali pumilae on moulded pottery not yet put in a kiln to bake with protrusion is made
Branch pattern.
Blow blue and white material：The moulded pottery not yet put in a kiln to bake carved is carried out blowing blue and white material process using material instrument is blown.
Pattern removes blue and white material：The blue and white material that will be attached on the Fructus Mali pumilae on moulded pottery not yet put in a kiln to bake and Fructus Mali pumilae branch pattern is scraped using instrument
Fall.
Take off flower and potted flower：Position on moulded pottery not yet put in a kiln to bake in addition to Fructus Mali pumilae and Fructus Mali pumilae branch pattern carries out taking off colored process using floricome is taken off,
Potted flower process is carried out on Fructus Mali pumilae and Fructus Mali pumilae branch pattern, makes pattern that there is solid layer feeling.
Biscuiting：After moulded pottery not yet put in a kiln to bake loading of kiln, then light a fire, wicket is opened during igniting, air pressure is adjusted to 0.15Pa, igniting of opening the door
Purpose is the liquefied gas and moisture content for excluding residual in kiln, and firing temperature is 390 degrees Celsius, and firing is arranged for 1.9 hours substantially to moulded pottery not yet put in a kiln to bake
Solid carbon dioxide point；Wicket is closed, air pressure is adjusted to into 0.2Pa, intensification can not be too fast, firing temperature is 640 degrees Celsius, fires 1.8 little
When；Use oxidizing flame firing instead, and air pressure in kiln is adjusted to into 0.25Pa, when temperature reaches 840 degrees Celsius, kept for 45 minutes, then
Temperature is burnt to 880 degrees Celsius, is fired 1.4 hours.
Blow lime glaze：The process of raising fire stons ash glaze is carried out to the apple pattern on the moulded pottery not yet put in a kiln to bake after biscuiting, and to moulded pottery not yet put in a kiln to bake whole
Position carries out blowing lime glaze process.
Glaze firing：After glazed body loading of kiln, during by the biscuiting step firing temperature up to 970 degrees Celsius, 0.9 hour is incubated, is changed
Fired with reducing flame, air pressure is adjusted to 1.1Pa, temperature is fired 10.5 hours up to 1288 degrees Celsius；After truce, wicket is opened,
1009 degrees Celsius are naturally cooled to, wicket, natural cooling 11.7 hours is shut.
Claims (3)
1. the manufacture method of colorful ceramic vase：Comprise the steps：It is characterized in that：
A, pugging：Moulded pottery not yet put in a kiln to bake is filtered, dried, is put in air compressor and is refined so as to being not in air inside moulded pottery not yet put in a kiln to bake
Bubble and occur splitting base phenomenon；
B, make base：Moulded pottery not yet put in a kiln to bake after pugging is put in base making machine carries out molding or offhand；
C, repaired biscuit：The moulded pottery not yet put in a kiln to bake of molding is repaired with repaired biscuit instrument；
D, engraving：Moulded pottery not yet put in a kiln to bake after repaired biscuit is carried out into hand engraving using instrument, the pattern on moulded pottery not yet put in a kiln to bake with protrusion is made；
E, blow blue and white material：The moulded pottery not yet put in a kiln to bake carved is carried out blowing blue and white material process using material instrument is blown；
F, pattern remove blue and white material：The blue and white material that will be attached on the pattern on moulded pottery not yet put in a kiln to bake is wiped off using instrument；
G, take off flower and potted flower：Position on moulded pottery not yet put in a kiln to bake in addition to pattern carries out taking off colored process using floricome is taken off, and carries out on pattern point
Flower is processed, and makes pattern have solid layer feeling；
H, biscuiting：Moulded pottery not yet put in a kiln to bake after taking off flower and potted flower is put in kiln carries out biscuiting, moulded pottery not yet put in a kiln to bake is facilitated sucking and is prevented sucking
During curling；The step of biscuiting is：After moulded pottery not yet put in a kiln to bake loading of kiln, then light a fire, wicket is opened during igniting, air pressure is adjusted to
0.15Pa, the purpose of igniting of opening the door is the liquefied gas and moisture content for excluding residual in kiln, and firing temperature is 300-350 degree Celsius, is burnt
1-2 hours processed drain moisture substantially to moulded pottery not yet put in a kiln to bake；Wicket is closed, air pressure is adjusted to into 0.2Pa, intensification can not be too fast, firing temperature
For 550-650 degree Celsius, 1-2 hours are fired；Use oxidizing flame firing instead, and air pressure in kiln is adjusted to into 0.25Pa, temperature reaches
When 800-850 degree Celsius, kept for 30-50 minutes, then temperature is burnt to 850-900 degree Celsius, fire 1-2 hours；
J, blow the glaze that transparent color can be formed after firing：Partial pattern on moulded pottery not yet put in a kiln to bake after biscuiting is carried out to fill out high temperature coloured glaze
Process, and blown moulded pottery not yet put in a kiln to bake whole position the glaze process that transparent color can be formed after firing；
K, glaze firing form finished product：Moulded pottery not yet put in a kiln to bake in step 9 is carried out into glaze firing and forms finished product.
2. colorful ceramic vase, it is characterised in that made by the manufacture method described in claim 1 and obtained.
3. according to the colorful ceramic vase described in claim 2, it is characterised in that：The ceramic vase is vault-of-Heaven vase or reward
Bottle either Guan yin vase or beautiful kettle spring bottle.