CN102887730A - Production method of tape-casting glazed ceramic vase - Google Patents
Production method of tape-casting glazed ceramic vase Download PDFInfo
- Publication number
- CN102887730A CN102887730A CN 201210428744 CN201210428744A CN102887730A CN 102887730 A CN102887730 A CN 102887730A CN 201210428744 CN201210428744 CN 201210428744 CN 201210428744 A CN201210428744 A CN 201210428744A CN 102887730 A CN102887730 A CN 102887730A
- Authority
- CN
- China
- Prior art keywords
- vase
- ceramic
- weight parts
- production method
- ceramic vase
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of a tape-casting glazed ceramic vase. The production method is characterized by comprising the following production steps of: (1) taking and putting triphane, quartz, feldspar, calcium carbonate, steatite and kaolin in a ball mill, and then, adding clear water to carry out ball milling and sieving to prepare a ceramic glaze for later use; (2) producing a ceramic vase biscuit with a height of 60-120 cm; and (3) uniformly coating the ceramic glaze for later use on a surface in a spray coating way from a vase neck of the ceramic vase biscuit to the middle part of a vase body within 20-30 seconds to form a glaze layer which has a thickness of 1-2 mm, then placing the ceramic vase biscuit in a kiln, firstly carrying out low-temperature sintering for 10-15 minutes at 120-140 DEG C, and then, heating to 1100-1120 DEG C for sintering for 4-5 hours so as to prepare a finished product. The tape-casting glaze is formed on the surface of the vase produced by the invention; the vase has natural and random appearance; a unique and novel aesthetic feeling is generated; and the design style of the conventional product is broken through.
Description
Technical field
The present invention relates to ceramic field, specifically a kind of production method of curtain coating shape glazed ceramic vase.
Background technology
The tradition vase is to adopt applique or colored drawing to decorate on its surface mostly, and pattern is tradition simply, lacks new meaning, can't attract the human consumer.
Summary of the invention
For overcoming above-mentioned deficiency, the invention provides a kind of production method of curtain coating shape glazed ceramic vase.
The production method of curtain coating shape glazed ceramic vase of the present invention is characterized in that, comprises following production stage:
(1), gets triphane 10 weight parts, quartzy 12 weight parts, feldspar 44 weight parts, calcium carbonate 18 weight parts, talcum 20 weight parts, kaolin 5 weight parts and put into ball mill, the clear water that adds weight again and be blended stock 30% carries out ball milling and crosses 240 mesh sieves, and it is for subsequent use to make enamel;
(2), produce the high ceramic vase of 60～120cm element carcass (namely be to form through moulding, sintering, but without the plain tire of surperficial glazing) by ceramic product traditional mode of production mode;
(3), above-mentioned enamel for subsequent use was sprayed on equably ceramic vase element carcass bottleneck in 20～30 seconds to the surface at body middle part, the glaze layer thickness is 1～2mm, then place in the kiln, carrying out easy fired 10～15 minutes prior to 120～140 ℃ (makes enamel down condense on the curtain coating limit in this temperature bottom, form unique curtain coating shape, be unlikely to again to flow to vase bottom), and then be warming up to 1100～1120 ℃ and burnt till 4～5 hours, product of the present invention made.
The vase surface that the present invention makes has formed the glaze of curtain coating shape, has the random outward appearance of nature, has produced the aesthetic feeling of unique novelty, has broken through the design style of traditional product.
Embodiment
The present invention will be described in detail by the following examples.
Get triphane 10 weight parts, quartzy 12 weight parts, feldspar 44 weight parts, calcium carbonate 18 weight parts, talcum 20 weight parts, kaolin 5 weight parts and put into ball mill, the clear water that adds weight again and be blended stock 30% carries out ball milling and crosses 240 mesh sieves, and it is for subsequent use to make enamel;
Produce the high ceramic vase element carcass of 100cm by ceramic product traditional mode of production mode;
Above-mentioned enamel for subsequent use was sprayed on ceramic vase element carcass bottleneck equably to the surface at body middle part in 25 seconds, the glaze layer thickness is 2mm, then places in the kiln, carries out easy fired 12 minutes prior to 130 ℃, and then be warming up to 1110 ℃ and burnt till 5 hours, make product.
Product surface has formed the glaze of many curtain coating shapes, and enamel minimum allowable distance vase bottom 3.7cm has produced the aesthetic feeling of unique novelty, has broken through the design style of traditional product.
Claims (1)
1. the production method of curtain coating shape glazed ceramic vase is characterized in that, comprises following production stage:
(1), gets triphane 10 weight parts, quartzy 12 weight parts, feldspar 44 weight parts, calcium carbonate 18 weight parts, talcum 20 weight parts, kaolin 5 weight parts and put into ball mill, the clear water that adds weight again and be blended stock 30% carries out ball milling and crosses 240 mesh sieves, and it is for subsequent use to make enamel;
(2), produce the high ceramic vase element carcass of 60～120cm by ceramic product traditional mode of production mode;
(3), above-mentioned enamel for subsequent use was sprayed on equably ceramic vase element carcass bottleneck in 20～30 seconds to the surface at body middle part, the glaze layer thickness is 1～2mm, then place in the kiln, carried out easy fired 10～15 minutes prior to 120～140 ℃, and then be warming up to 1100～1120 ℃ and burnt till 4～5 hours, make product.