CN103172352A - Manufacturing method of imitation pearl diamond decorative furnishing art porcelain - Google Patents
Manufacturing method of imitation pearl diamond decorative furnishing art porcelain Download PDFInfo
- Publication number
- CN103172352A CN103172352A CN201310057933XA CN201310057933A CN103172352A CN 103172352 A CN103172352 A CN 103172352A CN 201310057933X A CN201310057933X A CN 201310057933XA CN 201310057933 A CN201310057933 A CN 201310057933A CN 103172352 A CN103172352 A CN 103172352A
- Authority
- CN
- China
- Prior art keywords
- porcelain
- pearl
- diamond
- imitative
- selecting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method of an imitation pearl diamond decorative furnishing art porcelain. The manufacturing method specifically comprises the following five steps: selecting porcelain clay, processing a porcelain biscuit, selecting an imitation pearl material, selecting diamonds and using the imitation pearl material and the diamonds to decorate the protein biscuit. The furnishing art porcelain manufactured by adopting the method has the advantages of superior product quality, and exquisite and beautiful appearance, and can simultaneously change waste into a valuable thing, save energy, reduce energy consumption and protect an environment.
Description
Technical field
The present invention relates to a kind of manufacture method of ceramics, be specifically related to a kind of manufacture method of imitative pearl diamond setting decorative furnishing artistic porcelain, belong to the porcelain manufacture technology field.
Background technology
The ceramics surface be unable to do without to be decorated, high-caliber decoration plays a very important role quality and the class that improves goods, industrial art is combined in ceramic ornament is integrated, increase exactly the technique class as the purpose of painting, painting in gold, applique etc. being decorated.In conjunction with the fashionable element of current popular, integrate collocation as clothes, headwear, footwear, furniture etc., meet American-European technique fan's aesthetic standard, be also the requisite exhibit of house ornamentation.
Imitative pearl and diamond are everybody decorative products of looking at of parent always, and luster effect is good, and is ornamental strong, good marketable value and economic benefit are arranged, imitative pearl and diamond are used for decorative furnishing artistic porcelain, product is high-grade, exquisite attractive in appearance, meet the development of world trends, market outlook are wide.
Summary of the invention
The objective of the invention is to overcome deficiency of the prior art; a kind of manufacture method of imitative pearl diamond setting decorative furnishing artistic porcelain is provided, and it can make product have colourful texture, and the technique class is high; exquisite attractive in appearance, turn waste into wealth again simultaneously, save energy, reduction energy consumption, protection of the environment.
In order to address the above problem, the technical solution adopted in the present invention is:
A kind of manufacture method of imitative pearl diamond setting decorative furnishing artistic porcelain comprises the following steps:
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, formed by the per-cent component of following weight part: SiO
262 ~ 68%, Al
2O
322 ~ 26%, Fe
2O
30.16 ~ 0.20%, MgO 0.20 ~ 0.38%, TiO
20.02 ~ 0.04%, CaO 0.2 ~ 0.4%, K
2O 3.0 ~ 4.8%, Na
2O 1.6 ~ 2.0% and IL 3.0 ~ 6.0%, the water ratio of porcelain mud are 25 ~ 26%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is respectively by weight percentage: porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 1.8 ~ 2 hours with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, dry rear the burning in ceramic kiln knot made porcelain blank, and sintering temperature is controlled at 1250 ~ 1280 ℃, sintering time 6 ~ 7 hours;
(3) processing of imitative pearl: the matrix material recycling that the pearl material selection is discarded, to process together in conjunction with the powder that pearl is worn into, the product that obtains is commonly called as imitative pearl, and its luster effect is good, and is ornamental strong;
(4) selecting of diamond: select real crystal drilling diamond, being processed into diameter is the diamond goods of 3 ~ 6mm;
(5) with the material in above step (3) and (4), porcelain blank is decorated: with white paint, white is painted on the biscuit surface according to design requirements, again water soluble adhesive is evenly coated in Liquid Paraffin after 20 ~ 40 minutes and paints face; After 10 ~ 30 minutes, pearl is pressed design requirements, discharging is covered with successively; The crystal diamond that is diameter 3 ~ 6mm with super glue at last is embedded in pearl and joins in the space, and all spaces are inlayed full crystal drilling and got final product.
Described water soluble adhesive is water soluble glue or super glue.
Porcelain of the present invention is adapted at the public place and private Interior Display uses, and is particularly suitable for the countries and regions such as America and Europe, the Middle East.
The invention has the beneficial effects as follows:
(1) the present invention utilizes discarded matrix material to make imitative pearl decorative porcelain, turns waste into wealth, saves production cost, and reduces energy consumption, protection of the environment.
(2) the display art pottery of the present invention's production, the technique class is high, and is exquisite attractive in appearance.
Embodiment:
Below by embodiment, the present invention is described in further details, these embodiment only are used for illustrating the present invention, do not limit the scope of the invention.
Embodiment 1
The whole surface manufacture method of imitative pearl diamond setting porcelain vase
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, formed by the per-cent component of following weight part: SiO
265%, Al
2O
324%, Fe
2O
30.18%, MgO 0.29%, TiO
20.03%, CaO 0.3%, K
2O 3.9%, Na
2O1.8% and IL 4.5%, the water ratio of porcelain mud are 26%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is respectively by weight percentage: porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 2 hours with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, dry rear the burning in ceramic kiln knot made porcelain blank, and sintering temperature is controlled at 1265 ℃, sintering time 6.5 hours;
(3) processing of imitative pearl: the matrix material recycling that the pearl material selection is discarded, to process together in conjunction with the powder that pearl is worn into, the product that obtains is commonly called as imitative pearl, and its luster effect is good, and is ornamental strong;
(4) selecting of diamond: select real crystal drilling diamond, being processed into diameter is the masonry goods of 6mm;
(5) with the material in above step (3) and (4), porcelain blank is decorated: with white paint, white is painted on the biscuit surface according to design requirements, again water soluble glue is evenly coated in Liquid Paraffin after 40 minutes and paints face; After 10 minutes, pearl is pressed design requirements, discharging is covered with successively; The crystal diamond that is diameter 6mm with super glue at last is embedded in pearl and joins in the space, and all spaces are inlayed full crystal drilling and got final product;
Make the display art pottery with aforesaid method, can improve the ceramic process class, strengthen the display china aesthetics.
Embodiment 2
The whole surface manufacture method of imitative pearl diamond setting porcelain vase
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, formed by the per-cent component of following weight part: SiO
262%, Al
2O
322%, Fe
2O
30.16%, MgO 0.20%, TiO
20.02%, CaO 0.2%, K
2O 3.0%, Na
2O 1.6% and IL 3.0%, the water ratio of porcelain mud are 26%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is respectively by weight percentage: porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 1.8 hours with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, dry rear the burning in ceramic kiln knot made porcelain blank, and sintering temperature is controlled at 1280 ℃, sintering time 6 hours;
(3) processing of imitative pearl: the matrix material recycling that the pearl material selection is discarded, to process together in conjunction with the powder that pearl is worn into, the product that obtains is commonly called as imitative pearl, and its luster effect is good, and is ornamental strong;
(4) selecting of diamond: select real crystal drilling diamond, being processed into diameter is the masonry goods of 3mm;
(5) with the material in above step (3) and (4), porcelain blank is decorated: with white paint, white is painted on the biscuit surface according to design requirements, again water soluble glue is evenly coated in Liquid Paraffin after 20 minutes and paints face; After 30 minutes, pearl is pressed design requirements, discharging is covered with successively; The crystal diamond that is diameter 6mm with super glue at last is embedded in pearl and joins in the space, and all spaces are inlayed full crystal drilling and got final product;
Make the display art pottery with aforesaid method, can improve the ceramic process class, strengthen the display china aesthetics.
Embodiment 3
The whole surface manufacture method of imitative pearl diamond setting porcelain vase
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, formed by the per-cent component of following weight part: SiO
264%, Al
2O
323%, Fe
2O
30.17%, MgO 0.25%, TiO
20.02%, CaO 0.2%, K
2O 3.5%, Na
2O 1.7% and IL 3.5%, the water ratio of porcelain mud are 25.8%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is respectively by weight percentage: porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 1.9 hours with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, dry rear the burning in ceramic kiln knot made porcelain blank, and sintering temperature is controlled at 1260 ℃, sintering time 7 hours;
(3) processing of imitative pearl: the matrix material recycling that the pearl material selection is discarded, to process together in conjunction with the powder that pearl is worn into, the product that obtains is commonly called as imitative pearl, and its luster effect is good, and is ornamental strong;
(4) selecting of diamond: select real crystal drilling diamond, being processed into diameter is the masonry goods of 4mm;
(5) with the material in above step (3) and (4), porcelain blank is decorated: with white paint, white is painted on the biscuit surface according to design requirements, again water soluble adhesive is evenly coated in Liquid Paraffin after 25 minutes and paints face; After 15 minutes, pearl is pressed design requirements, discharging is covered with successively; The crystal diamond that is diameter 4mm with super glue at last is embedded in pearl and joins in the space, and all spaces are inlayed full crystal drilling and got final product.
Embodiment 4
The whole surface manufacture method of imitative pearl diamond setting porcelain vase
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, formed by the per-cent component of following weight part: SiO
266%, Al
2O
325%, Fe
2O
30.19%, MgO 0.35%, TiO
20.3%, CaO 0.3%, K
2O 4.5%, Na
2O 1.9% and IL 5.0%, the water ratio of porcelain mud are 25.5%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is respectively by weight percentage: porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 2 hours with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, dry rear the burning in ceramic kiln knot made porcelain blank, and sintering temperature is controlled at 1270 ℃, sintering time 6 hours;
(3) processing of imitative pearl: the matrix material recycling that the pearl material selection is discarded, to process together in conjunction with the powder that pearl is worn into, the product that obtains is commonly called as imitative pearl, and its luster effect is good, and is ornamental strong;
(4) selecting of diamond: select real crystal drilling diamond, being processed into diameter is the masonry goods of 5mm;
(5) with the material in above step (3) and (4), porcelain blank is decorated: with white paint, white is painted on the biscuit surface according to design requirements, again water soluble adhesive is evenly coated in Liquid Paraffin after 35 minutes and paints face; After 25 minutes, pearl is pressed design requirements, discharging is covered with successively; The crystal diamond that is diameter 5mm with super glue at last is embedded in pearl and joins in the space, and all spaces are inlayed full crystal drilling and got final product.
Embodiment 5
The part surface manufacture method of imitative pearl diamond setting porcelain vase
In order to satisfy different clients to the demand of decorative artistic porcelain, the surface portion of decorative artistic porcelain is decorated with imitative pearl diamond setting, and another part is decorated with other trailings such as color-painting method.Part surface is as follows with the manufacture method of the porcelain vase that color-painting method is decorated with imitative pearl diamond setting decoration, part:
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, formed by the per-cent component of following weight part: SiO
268%, Al
2O
326%, Fe
2O
30.20%, MgO 0.38%, TiO
20.04%, CaO 0.4%, K
2O 4.8%, Na
2O 2.0% and IL 6.0%, the water ratio of porcelain mud are 25%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is respectively by weight percentage: porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 1.8 hours with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, dry rear the burning in ceramic kiln knot made porcelain blank, and sintering temperature is controlled at 1250 ℃, sintering time 7 hours;
(3) processing of imitative pearl: the matrix material recycling that the pearl material selection is discarded, to process together in conjunction with the powder that pearl is worn into, the product that obtains is commonly called as imitative pearl, and its luster effect is good, and is ornamental strong;
(4) selecting of diamond: select real crystal drilling diamond, being processed into diameter is the masonry goods of 5mm;
(5) with white paint, the biscuit part surface is painted white according to design requirements, after 30 minutes, again water soluble glue is evenly coated in Liquid Paraffin and paints face after 20 minutes, pearl is pressed design requirements, discharging is covered with white paint part successively, the crystal diamond that is diameter 5mm with super glue at last is embedded in pearl and joins in the space, and between all pearls, the space is inlayed full crystal drilling and got final product;
Increase step (6): be in harmonious proportion out the urushoil of required color with nitro colored paint and Tianna solution by the weight ratio of 2:1, will be with the colored face of the part biscuit color drawing for curved surface of body of colored drawing, then be sprayed on picture as sealer coat with polyurethane varnish with urushoil on the paintbrush libation at an ancient wedding ceremony.Often add color picture, repeat this step, until colored drawing is completed.
Claims (2)
1. the manufacture method of an imitative pearl diamond setting decorative furnishing artistic porcelain is characterized in that: comprise following step:
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, formed by the per-cent component of following weight part: SiO
262 ~ 68%, Al
2O
322 ~ 26%, Fe
2O
30.16 ~ 0.20%, MgO 0.20 ~ 0.38%, TiO
20.02 ~ 0.04%, CaO 0.2 ~ 0.4%, K
2O 3.0 ~ 4.8%, Na
2O 1.6 ~ 2.0% and IL 3.0 ~ 6.0%, the water ratio of porcelain mud are 25 ~ 26%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is (% by weight percentage): porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 1.8-2 hour with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, carry out sintering after drying in ceramic kiln, make porcelain blank, sintering temperature is controlled at 1250 ℃-1280 ℃, sintering time 6-7 hour;
(3) processing of imitative pearl: the matrix material recycling that the pearl material selection is discarded, to process together in conjunction with the powder that pearl is worn into, the product that obtains is commonly called as imitative pearl;
(4) selecting of diamond: select real crystal drilling diamond, being processed into diameter is the diamond goods of 3 ~ 6mm;
(5) with the material in above step (3) and (4), porcelain blank is decorated: with white paint, white is painted on the biscuit surface according to design requirements, again water soluble adhesive is evenly coated in Liquid Paraffin after 20 ~ 40 minutes and paints face; After 10 ~ 30 minutes, pearl is pressed design requirements, discharging is covered with successively; The crystal diamond that is diameter 3 ~ 6mm with water soluble adhesive at last is embedded in pearl and joins in the space, and all spaces are inlayed full crystal drilling and got final product.
2. the manufacture method of a kind of imitative pearl diamond setting decorative furnishing artistic porcelain according to claim 1, it is characterized in that: the described water soluble adhesive of step (5) is water soluble glue or super glue.