CN103073274A - Manufacturing method for tiny mosaic electroplated decoration display artistic ceramic - Google Patents
Manufacturing method for tiny mosaic electroplated decoration display artistic ceramic Download PDFInfo
- Publication number
- CN103073274A CN103073274A CN2013100579679A CN201310057967A CN103073274A CN 103073274 A CN103073274 A CN 103073274A CN 2013100579679 A CN2013100579679 A CN 2013100579679A CN 201310057967 A CN201310057967 A CN 201310057967A CN 103073274 A CN103073274 A CN 103073274A
- Authority
- CN
- China
- Prior art keywords
- mosaic
- porcelain
- manufacture method
- mud
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method for tiny mosaic electroplated decoration display artistic ceramic. The manufacturing method comprises the steps of selecting petuntse, processing china biscuit, processing and treating mosaic, decorating the china biscuit by using tiny mosaic and the like. The display artistic ceramic manufactured by the method is formed by recycling waste materials discarded in the market, so that the display artistic ceramic is lower in cost but has strong fashionable breath.
Description
Technical field
The present invention relates to a kind of manufacture method of ceramics, be specifically related to a kind of manufacture method of small glass Mosaic electroplated decoration decorative artistic porcelain; The present invention also can decorate in conjunction with different types of material artwork, combines such as artworks such as woodwork, resin product, iron skills, is combined into the household decorations with modern trend breath.
Background technology
The ceramics surface be unable to do without to be decorated, and high-caliber decoration plays a very important role quality and the class that improves goods.The decoration of ceramic relates to a plurality of fields such as material, technique, the fine arts, and the surface decorating method of ceramic has glazing decoration, illuminated (such as over-glaze decoration, under glazed, in-glaze decoration, stamp applique) and liquid pigment (such as Jinsui River, rainbow material, ooze colored pigment) to decorate etc. traditionally.But aforesaid method all be difficult to form have native texture, tone enriches active effect, be difficult to adapt to the especially aesthetic psychology of American-European countries's pottery fan uphold nature of society, and material cost is higher, it is also more to consume energy.
Summary of the invention
The objective of the invention is to overcome deficiency of the prior art, a kind of manufacture method of small mosaic electroplated decoration decorative artistic porcelain is provided, it can make product have the modern trend breath.
The present invention is achieved in that
A kind of manufacture method of small mosaic electroplated decoration decorative artistic porcelain, the method comprises the steps:
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, its composition comprises (by weight percentage %): SiO
262-68, Al
2O
322-26, Fe
2O
30.16-0.20, MgO0.20-0.38, TiO
20.02-0.04, CaO0.2-0.4, K
2O3.0-4.8, Na
2O1.6-2.0 and IL3.0-6.0, the water ratio of porcelain mud are 25-26%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is (by weight percentage %): porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 1.8-2 hour with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, in ceramic kiln, burn after dry knot, make porcelain blank, sintering temperature is controlled at 1250 ℃-1280 ℃, sintering time 6-7 hour, again base substrate is coated ceramic insulating powder, then burn to 600 ℃, firing time 3 hours is wiped clean the porcelain surface again, be placed in the baking oven and dry, be placed on again and electroplate electroplating cost body in the kiln;
(3) processing of mosaic: the mosaic making is become thickness 1mm, twill tangent line specification 3mm * 3mm;
(4) with the material of step (3) biscuit of ceramics that step (2) obtains is decorated: after the biscuit of ceramics that will decorate sprays with silver color minute surface lacquer, reach mirror effect, mosaic with step (3) gained sticks on the biscuit of ceramics surface with the water soluble adhesive original state again, evenly is coated with at last last layer varnish as sealer coat.
Described water soluble adhesive is powerful water soluble glue, and described varnish is zapon varnish or polyester varnish.
Porcelain of the present invention is adapted at the public place and private Interior Display uses, and is particularly suitable for the countries and regions such as America and Europe, the Middle East.
The invention has the beneficial effects as follows:
(1) economic benefits utilizes discarded mosaic to reclaim the processing recycling;
(2) turn waste into wealth, save energy is conducive to protection of the environment.
Embodiment
Below by example the present invention is described in further details, these examples only are used for illustrating the present invention, do not limit the scope of the invention.
Embodiment 1
The manufacture method of porcelain vase is electroplated on whole surface with small glass Mosaic
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, its composition comprises (by weight percentage %): SiO
265, Al
2O
324, Fe
2O
30.18, MgO0.29, TiO
20.03, CaO0.3, K
2O3.9, Na
2O1.8 and IL4.5, the water ratio of porcelain mud are 26%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is (by weight percentage %): porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 2 hours with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, in ceramic kiln, carry out sintering after dry, make porcelain blank, sintering temperature is controlled at 1250 ℃, and sintering time 6.5 hours is made the porcelain vase biscuit, again base substrate is coated ceramic insulating powder, then burn to 600 ℃, firing time 3 hours, re-plating becomes body.
(3) processing of glass Mosaic: the glass Mosaic specification varies, and different moulding and various combinations of patterns can be arranged.We adopt is a kind of screen of ultra-thin, ultra-small dimension.Existing market is strong to blank field curiosity, and technical difficulty is large, the cullet recycling that utilizes market to abandon, and making becomes thickness 1mm, twill tangent line specification 3mm * 3mm;
(4) electroplating good base substrate (gold, silver color or other color), be coated with first the last layer super glue, according to design needs sticking glass mosaic, plug the gap to flat with ashes after waiting for half hour, reach at last that brightness is attractive in appearance, the finished product of good visual effect gets final product.
Can make with aforesaid method and to have that brightness is attractive in appearance, the decorative artistic porcelain of the small glass Mosaic electroplated decoration of good visual effect.
Embodiment 2
Part surface is electroplated the manufacture method of porcelain vase with small glass Mosaic
In order to satisfy different clients to the demand of decorative artistic porcelain, the surface portion of decorative artistic porcelain is decorated with glass Mosaic, and another part is decorated with other trailings such as color-painting method.Part surface is as follows with the manufacture method of the porcelain vase that color-painting method is decorated with glass Mosaic decoration, part:
Step (1), (2), (3) are with example 1.
Step (4): electroplating good base substrate (gold, silver color or other color), partly be coated with the last layer super glue according to the design needs, the sticking glass mosaic, after waiting for half hour with ashes fill up pasted glass Mosaic the part space to flat, reach at last that brightness is attractive in appearance, the finished product of good visual effect gets final product.
Increase step (5): be in harmonious proportion out the urushoil of required color with nitro colored paint and Tianna solution by the weight ratio of 2:1, will with the colored face of the part biscuit color drawing for curved surface of body of colored drawing, be sprayed on picture as sealer coat with polyurethane varnish again with urushoil on the paintbrush libation at an ancient wedding ceremony.Whenever add color picture, repeat this step, until colored drawing is finished.
Embodiment 3
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, its composition comprises (by weight percentage %): SiO
268, Al
2O
322, Fe
2O
30.18 MgO 0.29, TiO
20.03 CaO 0.3, K
2O 3.9, Na
2O 1.8 and IL5.5, the water ratio of porcelain mud are 26%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is (by weight percentage %): porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 1.8 hours with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, in ceramic kiln, carry out sintering after dry, make porcelain blank, sintering temperature is controlled at 1280 ℃, and sintering time 6.0 hours is made the porcelain vase biscuit, again base substrate is coated ceramic insulating powder, then burn to 600 ℃, firing time 3 hours, re-plating becomes body.
(3) processing of wooden mosaic: the mosaic specification varies, different moulding and various combinations of patterns can be arranged, existing market is strong to blank field curiosity, technical difficulty is large, the waste wood that utilizes market to abandon mosaic recycling processed, making becomes thickness 1mm, twill tangent line specification 3mm * 3mm;
(4) electroplating good base substrate (gold, silver color or other color), be coated with first the last layer super glue, paste wooden mosaic according to the design needs, plug the gap to flat with ashes after waiting for half hour, reach at last that brightness is attractive in appearance, the finished product of good visual effect gets final product.
Embodiment 4
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, its composition comprises (by weight percentage %): SiO
262, Al
2O
324.5, Fe
2O
30.18 MgO 0.29, TiO
20.03 CaO 0.2, K
2O 4.8, Na
2O 2.0 and IL6.0, the water ratio of porcelain mud are 25%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is (by weight percentage %): porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 1.8 hours with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, in ceramic kiln, carry out sintering after dry, make porcelain blank, sintering temperature is controlled at 1260 ℃, and sintering time 7.0 hours is made the porcelain vase biscuit, again base substrate is coated ceramic insulating powder, then burn to 600 ℃, firing time 3 hours, re-plating becomes body.
(3) processing of metal mosaic: the mosaic specification varies, different moulding and various combinations of patterns can be arranged, existing market is strong to blank field curiosity, technical difficulty is large, the scrap metal mosaic recycling that utilizes market to abandon, making becomes thickness 1mm, twill tangent line specification 3mm * 3mm;
(4) electroplating good base substrate (gold, silver color or other color), be coated with first the last layer super glue, paste metal mosaic according to the design needs, plug the gap to flat with ashes after waiting for half hour, reach at last that brightness is attractive in appearance, the finished product of good visual effect gets final product.
Claims (5)
1. the manufacture method of a small mosaic electroplated decoration decorative artistic porcelain is characterized in that: comprise the following steps:
(1) selecting of porcelain mud: select common middle temperature to burn till porcelain mud, its composition comprises (by weight percentage %): SiO
262-68, Al
2O
322-26, Fe
2O
30.16-0.20, MgO 0.20-0.38, TiO
20.02-0.04, CaO 0.2-0.4, K
2O 3.0-4.8, Na
2O 1.6-2.0 and IL3.0-6.0, the water ratio of porcelain mud are 25-26%;
(2) processing of porcelain blank: porcelain mud is added entry, water glass and sodium humate, the ratio that adds is (by weight percentage %): porcelain mud: water: water glass: sodium humate=94: 0.8: 5: 0.2, then stirred 1.8-2 hour with stirrer, cross 100 order vibratory screening apparatuss; Get the gypsum mold injection forming ready, in ceramic kiln, burn after dry knot, make porcelain blank, sintering temperature is controlled at 1250 ℃-1280 ℃, sintering time 6-7 hour, again base substrate is coated ceramic insulating powder, then burn to 600 ℃, firing time 3 hours is wiped clean the porcelain surface again, be placed in the baking oven and dry, be placed on again and electroplate electroplating cost body in the kiln;
(3) processing of mosaic: the mosaic making is become thickness 1mm, twill tangent line specification 3mm * 3mm;
(4) with the material of step (3) biscuit of ceramics that step (2) obtains is decorated: after the biscuit of ceramics that will decorate sprays with the minute surface lacquer, reach mirror effect, mosaic with step (3) gained sticks on the biscuit of ceramics surface with the water soluble adhesive original state again, evenly is coated with at last last layer varnish as sealer coat.
2. the manufacture method of decorative artistic porcelain according to claim 1, it is characterized in that: described water soluble adhesive is powerful water soluble glue.
3. the manufacture method of decorative artistic porcelain according to claim 1, it is characterized in that: described varnish is zapon varnish or polyester varnish.
4. the manufacture method of decorative artistic porcelain according to claim 1, it is characterized in that: described mosaic is wooden mosaic, resin mosaic or metal mosaic.
5. the manufacture method of decorative artistic porcelain according to claim 1 is characterized in that: described minute surface lacquer is silver color, gold or other colors.