CN109081583A - A kind of processing technology of sauce red glaze dark color lines pottery - Google Patents
A kind of processing technology of sauce red glaze dark color lines pottery Download PDFInfo
- Publication number
- CN109081583A CN109081583A CN201811076125.7A CN201811076125A CN109081583A CN 109081583 A CN109081583 A CN 109081583A CN 201811076125 A CN201811076125 A CN 201811076125A CN 109081583 A CN109081583 A CN 109081583A
- Authority
- CN
- China
- Prior art keywords
- pottery
- glaze
- parts
- slurry
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to the production technologies for having textured pottery, more particularly to a kind of processing technology of sauce red glaze dark color lines pottery, glaze includes the first pottery glaze and the second pottery glaze, body color of first glaze as pottery, second glaze high temperature has expansion effect, for filling the lines or pattern on pottery surface, after the completion of the surface pattern of pottery element tire is portrayed, manually it is polished into mellow and full state, conducive to glazing, after the completion of textured portion glazing, one layer of first pottery glaze of painting is integrally covered to pottery carries out pre-burned, then the first pottery of dip-coating glaze, kiln temperature is finally controlled according to the time, it processes sauce red glaze colours and there is the pottery of dark lines, though the pottery is the inclined modernization color of red sauce, but there is simple and unsophisticated thick and heavy atmosphere sense, with very big ornamental value.
Description
Technical field
The present invention relates to the specially treated production technologies that surface has textured pottery, and in particular to a kind of sauce red glaze is dark
The processing technology of lines pottery.
Background technique
Pottery is originated in the Eastern Han Dynasty, is one of five big kiln porcelain of Song Dynasty, the treasure in Chinese tradition technology in producing porcelain.Pottery with
Its unique transmutation is artistic and is world-famous for, and the title of " the valuable an ancient unit of weight of gold is priceless " is known as, by its simple and unsophisticated moulding, consummate work
Skill, the complicated emperorship transmutation with glaze, " it is color to enter kiln kiln discharge ten thousand of the same colour ", the beautiful scenery of lakes and mountains, rosy clouds fog, people's beast flower, bird, insect, and fish etc. become
Change infinite figure color and marvellous charm, is known as first of Chinese " five big porcelain ".The glaze colours transmutation artistic effect of pottery
Inartificial, self-assembling formation at a high temperature of stove fire in kiln, it is no any color that pottery, which enters kiln, and one is plain,
The gorgeous color and natural picture that pottery surface is formed are formed in kiln in sintering procedure, and principle is exactly glaze mine
The physical chemical phenomenon of object colour generation at high temperature, transmutation phenomenon be temperature, glaze, fire position and stove quality etc. it is a variety of because
The combination of element, transmutation have today of suitable awareness and understanding, transmutation knot in people the result is that self-assembling formation to transmutation phenomenon
What fruit also and was non-fully grasped, often not next, the unexpected encounter of trick, this adds the stirring glamour of pottery art significantly,
So the formation of every a piece of china all somethings can only be found by accident, and not through seeking.
Summary of the invention
It is an object of the present invention to provide a kind of processing method of sauce red glaze dark color lines pottery, to plain tire surface portray lines or
Person's pattern applies the second glaze at this, and entire surface part applies the first glaze, though it is sauce red that the product processed, which has,
The color of color modernized partially but has simple and unsophisticated thick and heavy atmosphere sense, has very big ornamental value.
Processing technology provided by the invention is a kind of processing technology of sauce red glaze dark color lines pottery, and glaze includes first an ancient unit of weight
Glaze and the second pottery glaze, according to weight ratio, the first pottery glaze include 38-45 parts of potassium feldspar, 48-54 parts of albite,
10-13 parts of kaolin, 6-9 parts of calcite, 4-9 parts of quartz, 2-5 parts of wood ash, 1-4 parts of iron oxide, 1-3 parts of zinc oxide, aluminium oxide
0.5-0.8 parts, 2-3 parts of glass powder, 2-5 parts of talcum and 1-2 parts of diopside, the second pottery glaze include 20-25 parts of potassium feldspar, sodium
23-29 parts of feldspar, 9-11 parts of kaolin, 10-18 parts of calcite, 10-20 parts of quartz, 4-9 parts of zircon, 2-3 parts of wood ash, black phosphorus
20-35 parts, 5-8 parts of alkali stone and 5-10 parts of iron ore.
Further, processing process the following steps are included:
Step 1: production pottery element tire, portrays lines or pattern on pottery element tire surface, weeded out using the detection of sonic detection instrument
There are crackle or the defective products of hole on surface;
Step 2: the first pottery glaze slurry and the second pottery glaze is respectively prepared in the first pottery glaze and the second pottery glaze
Slurry, wherein the second pottery glaze slurry uses preceding placement 10-18 hours;
Step 3: the lines of pottery element tire or pattern are faced upward, the second glaze slurry is sprayed on to the line on pottery element tire surface
At road or pattern, slurry adjusts pottery element tire direction after air-drying, and continues to spray the second glaze slurry, until pottery element tire surface line
The second glaze slurry is filled at road or pattern and slurry air-dries;
Step 3: pottery element tire is placed in glazing platform, the second glaze slurry is brushed at its surface pattern or pattern, slurry air-dries
Afterwards, it covers and applies the first pottery glaze slurry, the first pottery glaze slurry enters kiln progress pre-burned and obtains semi-finished product after air-drying;
Step 4: the semi-finished product after pre-burned are immersed in the first pottery glaze slurry, the first slurry of painting is covered after its slurry air-dries
Material, kiln-firing obtains finished product after air-drying again.
Further, after the completion of the lines or pattern on pottery element tire surface are portrayed in the step 1, also need to lines or
Pattern and pottery element tire surface transition position carry out manual polishing.
Further, the pre-burned time is 1 hour in the step 4, and pre-burned temperature is 100-200 DEG C, when pre-burned
Stove door opens 1-2 centimetres.
Further, in the step 4 in sintering procedure, the raising of furnace kiln temperature is divided into following several stages:
S1: furnace kiln temperature rises to 700 DEG C in 60 minutes;
S2: furnace kiln temperature rises to 1300 DEG C in 70 minutes;
S3: furnace kiln temperature is near 1100 DEG C in 60 minutes;
S4: furnace kiln temperature is maintained at 1050 DEG C -1130 DEG C in 40 minutes;
S5: furnace kiln temperature rises to 1200 DEG C in 10 minutes;
S6: furnace kiln temperature is stablized in 130 minutes at 1200 DEG C;
S7: furnace kiln temperature gradually reduces in 24 hours to room temperature, kiln discharge after near room temperature 3 hours.
Beneficial effect
1, the first pottery glaze plays protection and colour generation, the ferro element and zinc oxide of iron oxide pyroreaction be present it is partially light
Red reason, the viscosity, hardness and anti-pressure ability of glaze can be improved in aluminium oxide, moreover it is possible to prevent sagging, the amount of aluminium oxide
Increase to it is a certain amount of after glaze paint can be made to generate without light effect, so will form more dim red sauce;In second pottery glaze
Include zircon, black phosphorus, alkali stone and iron ore, the second pottery glaze slurry is placed 10 to 18 hours using preceding, concentration compared with
Height, the second pottery glaze slurry are mainly used at the pattern for filling pottery element tire surface, and iron ore, alkali stone and black phosphorus are at high temperature
Peony can be presented in reaction, and color and the red sauce on pottery surface have soft mistake after cooperating the zr element in zircon to react
It crosses, the second pottery glaze slurry can expand in lines and pattern, cover the first pottery glaze of painting after applying the second pottery glaze
Slurry material applies smooth applying the first pottery glaze slurry for surface and cover after pre-burned, and last pottery entirety colour generation is red sauce,
Textured portion is the kermesinus of soft transitions, while having modern sense and simple and unsophisticated heavy feeling.
2, a kind of processing technology of sauce red glaze dark color lines pottery of the present invention, it is preparatory on its surface in the production of pottery element tire
Lines or pattern are portrayed, pattern is the dark striped of finished product, and manual polishing after lines or pattern are portrayed guarantees and pottery element
Transition position is round and smooth as far as possible between tire surface or grain pattern, is conducive to glazing;Pottery element tire passes through detection after making and screens out it
In the defective products with crackle or hole, avoid influencing other products in sintering procedure, glaze is divided into as porcelain integral color
The first pottery glaze and filling grain pattern part the second slurry, the grain pattern of pottery element tire upward applies it
Second glaze slurry air-dries rear steering until having filled in grain pattern to it, covers to Pre-sintered porcelain body and apply the first pottery glaze slurry
Material carries out pre-burned, makes the second glaze slurry original shaping in grain pattern, and semi-finished product are then immersed the first pottery glaze
Glazing is carried out in slurry, final kiln-firing, the second glaze slurry expanded by heating is filled in lines or pattern, and the second glaze
Slurry color after pyroreaction is deeper, ultimately forms dark lines or pattern.
3, the second glaze slurry is using preceding placements a period of time, and it is dense that concentration compares the first pottery glaze slurry, glazed body
After pre-burned molding, enters kiln and kiln temperature is quickly increased to 700 DEG C, then heating rate, which slightly reduces, is warming up to 1300 DEG C of left sides
Then the right side is reduced to 1100 DEG C and is maintained at 1100 DEG C or so ranges, so that glaze is stablized reaction, be warming up to later to 1200 DEG C simultaneously
1200 DEG C are maintained at, makes the abundant stable reaction of multilayer glaze, avoids fast cooling after truce, it should be gradually stable by kiln temperature
It is reduced to extraneous room temperature, then kiln discharge after cooling placement minimum 24 hours, avoids environment cataclysm from influencing yield rate.
Specific embodiment
Embodiment 1
A kind of processing technology of sauce red glaze dark color lines pottery, glaze include include the first pottery glaze and the second pottery glaze,
According to weight ratio, the first pottery glaze includes 38 parts of potassium feldspar, 48 parts of albite, 10 parts of kaolin, 6 parts of calcite, quartz 4
Part, 2 parts of wood ash, 1 part of iron oxide, 1 part of zinc oxide, 0.5 part of aluminium oxide, 2 parts of glass powder, 2 parts of talcum and 1 part of diopside, second
Pottery glaze includes 20 parts of potassium feldspar, 23 parts of albite, 9 parts of kaolin, 10 parts of calcite, 10 parts of quartz, 4 parts of zircon, wood
2 parts of ash, 20 parts of black phosphorus, 5 parts of alkali stone and 5 parts of iron ore.
Process the following steps are included:
Step 1: production pottery element tire, portrays lines or pattern on pottery element tire surface, it is artificial to crossover position after the completion of portraying
Polishing, weeding out surface using the detection of sonic detection instrument later, there are crackle or the defective products of hole;
Step 2: by the first pottery glaze and the second pottery glaze, ball milling adds water and stirs and is uniformly made the first pottery glaze slurry respectively
Material and the second pottery glaze slurry, wherein the second pottery glaze slurry is placed 10 hours using preceding;
Step 3: the lines of pottery element tire or pattern are faced upward, the second glaze slurry is sprayed on to the line on pottery element tire surface
At road or pattern, slurry adjusts pottery element tire direction after air-drying, and continues to spray the second glaze slurry, until pottery element tire surface line
The second glaze slurry is filled at road or pattern and slurry air-dries;
Step 3: pottery element tire is placed in glazing platform, the second glaze slurry is brushed at its surface pattern or pattern, slurry air-dries
Afterwards, it covering and applies the first pottery glaze slurry, the first pottery glaze slurry enters kiln and obtains semi-finished product within pre-burned 1 hour at 100 DEG C after air-drying,
Stove door opens 1-2 centimetres when pre-burned;
Step 4: the semi-finished product after pre-burned are immersed in the first pottery glaze slurry, the first slurry of painting is covered after its slurry air-dries
Material, kiln-firing obtains finished product sauce red glaze dark color lines pottery after air-drying again, and in sintering procedure, furnace kiln temperature, which increases, to be divided
For following several stages:
S1: furnace kiln temperature rises to 700 DEG C in 60 minutes;
S2: furnace kiln temperature rises to 1300 DEG C in 70 minutes;
S3: furnace kiln temperature is near 1100 DEG C in 60 minutes;
S4: furnace kiln temperature is maintained at 1050 DEG C -1130 DEG C in 40 minutes;
S5: furnace kiln temperature rises to 1200 DEG C in 10 minutes;
S6: furnace kiln temperature is stablized in 130 minutes at 1200 DEG C;
S7: furnace kiln temperature gradually reduces in 24 hours to room temperature, kiln discharge after near room temperature 3 hours.
Embodiment 2
A kind of processing technology of sauce red glaze dark color lines pottery, glaze include the first pottery glaze and the second pottery glaze, according to
Weight ratio, the first pottery glaze include 45 parts of potassium feldspar, 54 parts of albite, 13 parts of kaolin, 9 parts of calcite, 9 parts of quartz, wood
5 parts of ash, 4 parts of iron oxide, 3 parts of zinc oxide, 0.8 part of aluminium oxide, 3 parts of glass powder, 5 parts of talcum and 2 parts of diopside, the second pottery glaze
Material includes 25 parts of potassium feldspar, 29 parts of albite, 11 parts of kaolin, 18 parts of calcite, quartzy 20 parts, 9 parts of zircon, 3 parts of wood ash,
35 parts of black phosphorus, 8 parts of alkali stone and 10 parts of iron ore.
Processing technology the following steps are included:
Step 1: production pottery element tire, portrays lines or pattern on pottery element tire surface, people is carried out to transition position after the completion of portraying
Work polishing, then weeding out surface using the detection of sonic detection instrument, there are crackle or the defective products of hole;
Step 2: by the first pottery glaze and the second pottery glaze, ball milling adds water and stirs and is uniformly made the first pottery glaze slurry respectively
Material and the second pottery glaze slurry, wherein the second pottery glaze slurry is placed 18 hours using preceding;
Step 3: the lines of pottery element tire or pattern are faced upward, the second glaze slurry is sprayed on to the line on pottery element tire surface
At road or pattern, slurry adjusts pottery element tire direction after air-drying, and continues to spray the second glaze slurry, until pottery element tire surface line
The second glaze slurry is filled at road or pattern and slurry air-dries;
Step 3: pottery element tire is placed in glazing platform, the second glaze slurry is brushed at its surface pattern or pattern, slurry air-dries
Afterwards, it covers and applies the first pottery glaze slurry, the first pottery glaze slurry enters kiln after air-drying, and to carry out pre-burned 1 under the conditions of 200 DEG C small
When obtain semi-finished product, during pre-burned stove door open 1-2 centimetres;
Step 4: the semi-finished product after pre-burned are immersed in the first pottery glaze slurry, the first slurry of painting is covered after its slurry air-dries
Material, kiln-firing obtains the sauce red glaze dark color lines pottery of finished product after air-drying again, and in sintering procedure, the raising of furnace kiln temperature is divided into
Following several stages:
S1: furnace kiln temperature rises to 700 DEG C in 60 minutes;
S2: furnace kiln temperature rises to 1300 DEG C in 70 minutes;
S3: furnace kiln temperature is near 1100 DEG C in 60 minutes;
S4: furnace kiln temperature is maintained at 1050 DEG C -1130 DEG C in 40 minutes;
S5: furnace kiln temperature rises to 1200 DEG C in 10 minutes;
S6: furnace kiln temperature is stablized in 130 minutes at 1200 DEG C;
S7: furnace kiln temperature gradually reduces in 24 hours to room temperature, kiln discharge after near room temperature 3 hours.
The above described is only a preferred embodiment of the present invention, be not intended to limit the present invention in any form, though
So the present invention has been disclosed as a preferred embodiment, and however, it is not intended to limit the invention, any technology people for being familiar with this profession
Member, without departing from the scope of the present invention, when the technology contents using the disclosure above make a little change or modification
It is right according to the technical essence of the invention for the equivalent embodiment of equivalent variations, but without departing from the technical solutions of the present invention
Any simple modification, equivalent change and modification made by above embodiments, all of which are still within the scope of the technical scheme of the invention.
Claims (5)
1. a kind of processing technology of sauce red glaze dark color lines pottery, it is characterised in that: glaze includes the first pottery glaze and second
Pottery glaze, according to weight ratio, the first pottery glaze includes 38-45 parts of potassium feldspar, 48-54 parts of albite, kaolin 10-13
Part, 6-9 parts of calcite, 4-9 parts of quartz, 2-5 parts of wood ash, 1-4 parts of iron oxide, 1-3 parts of zinc oxide, 0.5-0.8 parts of aluminium oxide, glass
2-3 parts of glass powder, 2-5 parts of talcum and 1-2 parts of diopside, the second pottery glaze include 20-25 parts of potassium feldspar, 23-29 parts of albite,
9-11 parts of kaolin, 10-18 parts of calcite, 10-20 parts of quartz, 4-9 parts of zircon, 2-3 parts of wood ash, 20-35 parts of black phosphorus, alkali stone
5-8 parts and iron ore 5-10 parts.
2. a kind of processing technology of sauce red glaze dark color lines pottery as described in claim 1, it is characterised in that: including following step
It is rapid:
Step 1: production pottery element tire, portrays lines or pattern on pottery element tire surface, weeded out using the detection of sonic detection instrument
There are crackle or the defective products of hole on surface;
Step 2: the first pottery glaze slurry and the second pottery glaze is respectively prepared in the first pottery glaze and the second pottery glaze
Slurry, wherein the second pottery glaze slurry uses preceding placement 10-18 hours;
Step 3: the lines of pottery element tire or pattern are faced upward, the second glaze slurry is sprayed on to the line on pottery element tire surface
At road or pattern, slurry adjusts pottery element tire direction after air-drying, and continues to spray the second glaze slurry, until pottery element tire surface line
The second glaze slurry is filled at road or pattern and slurry air-dries;
Step 3: pottery element tire is placed in glazing platform, the second glaze slurry is brushed at its surface pattern or pattern, slurry air-dries
Afterwards, it covers and applies the first pottery glaze slurry, the first pottery glaze slurry enters kiln progress pre-burned and obtains semi-finished product after air-drying;
Step 4: the semi-finished product after pre-burned are immersed in the first pottery glaze slurry, the first slurry of painting is covered after its slurry air-dries
Material, kiln-firing obtains finished product after air-drying again.
3. a kind of processing technology of sauce red glaze dark color lines pottery as claimed in claim 2, it is characterised in that: the step 1
After the completion of the lines or pattern on middle pottery element tire surface are portrayed, also need to lines or pattern and pottery element tire surface transition position into
Row manual polishing.
4. a kind of processing technology of sauce red glaze dark color lines pottery as claimed in claim 2, it is characterised in that: the step 4
The middle pre-burned time is 1 hour, and pre-burned temperature is 100-200 DEG C, and stove door opens 1-2 centimetres when pre-burned.
5. a kind of processing technology of sauce red glaze dark color lines pottery as claimed in claim 2, it is characterised in that: the step 4
In middle sintering procedure, the raising of furnace kiln temperature is divided into following several stages:
S1: furnace kiln temperature rises to 700 DEG C in 60 minutes;
S2: furnace kiln temperature rises to 1300 DEG C in 70 minutes;
S3: furnace kiln temperature is near 1100 DEG C in 60 minutes;
S4: furnace kiln temperature is maintained at 1050 DEG C -1130 DEG C in 40 minutes;
S5: furnace kiln temperature rises to 1200 DEG C in 10 minutes;
S6: furnace kiln temperature is stablized in 130 minutes at 1200 DEG C;
S7: furnace kiln temperature gradually reduces in 24 hours to room temperature, kiln discharge after near room temperature 3 hours.