CN103247783A - 一种铅酸蓄电池用炭黑的添加方法 - Google Patents

一种铅酸蓄电池用炭黑的添加方法 Download PDF

Info

Publication number
CN103247783A
CN103247783A CN201310140245XA CN201310140245A CN103247783A CN 103247783 A CN103247783 A CN 103247783A CN 201310140245X A CN201310140245X A CN 201310140245XA CN 201310140245 A CN201310140245 A CN 201310140245A CN 103247783 A CN103247783 A CN 103247783A
Authority
CN
China
Prior art keywords
carbon black
mixed liquor
cream
lead
mins
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310140245XA
Other languages
English (en)
Inventor
杨广福
郭从乐
杨巨鹏
孙言行
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHAANXI LINGYUN ELECTRONICS GROUP CO Ltd
SHAANXI LINGYUN BATTERY CO Ltd
Original Assignee
SHAANXI LINGYUN ELECTRONICS GROUP CO Ltd
SHAANXI LINGYUN BATTERY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHAANXI LINGYUN ELECTRONICS GROUP CO Ltd, SHAANXI LINGYUN BATTERY CO Ltd filed Critical SHAANXI LINGYUN ELECTRONICS GROUP CO Ltd
Priority to CN201310140245XA priority Critical patent/CN103247783A/zh
Publication of CN103247783A publication Critical patent/CN103247783A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种铅酸蓄电池用炭黑的添加方法，即湿法添加法。其制作方法是先把炭黑添加到木素磺酸钠的水溶液中分散为炭黑混合液，再将炭黑混合液湿法添加至蓄电池负极铅膏中，提高了炭黑的均匀性。

Description

一种铅酸蓄电池用炭黑的添加方法
技术领域
本发明属于铅酸蓄电池制造技术领域，涉及铅酸蓄电池用炭黑的添加方法，具体涉及炭黑混合液的制作方法。
背景技术
炭黑(包括乙炔炭黑、混汽炭黑)是铅酸蓄电池制造过程必须的添加剂，其作用是增加铅膏的导电性，提高蓄电池的充电接受性能，防止蓄电池负极硫酸盐化。如果炭黑的添加量不合适、或添加后炭黑分散不均匀，就会引起蓄电池的充电接受性能降低或负极硫酸盐化，性能下降，影响使用寿命。
目前炭黑普遍采用干法添加，也就是将炭黑直接添加至铅粉中，搅拌混合。这种添加方式不能改变炭黑颗粒的大小，若添加前炭黑颗粒太大时将引起炭黑在铅膏和膏过程中分散不均匀；这种添加方式，在和膏过程，不但会造成正在添加的炭黑容易被除尘风机抽走而引起铅膏配方中的炭黑量不足，质量不稳定，还存在添加过程由于炭黑的扬尘飞散，造成操作者易吸入而危害身体健康。
发明内容
本发明的目的是克服炭黑在蓄电池铅膏中添加时所存在的前述缺陷，由于炭黑的憎水性，用纯水或去离子水分散时，炭黑的颗粒度较大，并且性能不稳定易沉降。采用木素磺酸钠的水溶液来分散炭黑，可利用木素磺酸钠的表面活性作用，改善了炭黑的表面张力，增加亲水性，使之分散为颗粒更小的炭黑混合液，能防止炭黑团聚或沉降。
在蓄电池负极板制作时，再将炭黑混合液添加至铅膏中和膏，即完成了铅酸蓄电池用炭黑的添加。
具体实施方式
按下述步骤进行实施：
(1)木素磺酸钠水溶液制备：将0.09kg～5kg木素磺酸钠在搅拌的条件下，在8min～12min时间均匀加入45kg纯水或去离子水中，制成百分比浓度为0.2％～10％的木素磺酸钠水溶液。
(2)炭黑混合液的制备：将5kg混汽炭黑或乙炔碳黑加入前述百分比浓度为0.2％～10％的木素磺酸钠水溶液中，在1000转/分～3000转/分的搅拌条件下搅拌2h～3h，制成百分比浓度为10％的炭黑混合液，备用。
特别的，在铅膏和膏时应先将炭黑混合液在1000转/分～3000转/分的条件，再搅拌10min～30min。
(3)和膏：在蓄电池负极制作时，将铅粉和干添加剂干混后，加入配方量的所需纯水搅拌1min～2min，再根据不同型式型号蓄电池负极性能所要求的炭黑量，将对应所含炭黑量的炭黑混合液添加至铅膏中和膏，制作成蓄电池负极。

Claims (7)

1.一种铅酸蓄电池用炭黑的添加方法，其特征在于，把炭黑添加到木素磺酸钠水溶液中分散，制成炭黑混合液，再将炭黑混合液加至铅膏中和膏。
2.如权利要求1所述的方法，其特征在于，添加的炭黑包括乙炔炭黑或混气炭黑。
3.如权利要求1所述的方法，其特征在于，木素磺酸钠水溶液的浓度为0.2％～10％。
4.如权利要求1所述的方法，其特征在于，炭黑混合液中炭黑的含量为10％。
5.如权利要求1所述的方法，其特征在于，炭黑的混合液制作的搅拌条件为搅拌速度1000转/分～3000转/分，搅拌时间2h～3h。
6.如权利要求1所述的方法，其特征在于，在和膏时，炭黑混合液在和膏前的搅拌条件为搅拌速度1000转/分～3000转/分，搅拌时间10min～30min。
7.如权利要求1所述的方法，其特征在于，在蓄电池负极制作和膏时，根据型式所要求的炭黑量，将对应含炭黑量的炭黑混合液添加至铅膏中和膏，制作成蓄电池负极。
CN201310140245XA 2013-04-10 2013-04-10 一种铅酸蓄电池用炭黑的添加方法 Pending CN103247783A (zh)