CN103035908A - 一种动力型铅酸蓄电池用负极板铅膏配制方法 - Google Patents

一种动力型铅酸蓄电池用负极板铅膏配制方法 Download PDF

Info

Publication number
CN103035908A
CN103035908A CN2012105370171A CN201210537017A CN103035908A CN 103035908 A CN103035908 A CN 103035908A CN 2012105370171 A CN2012105370171 A CN 2012105370171A CN 201210537017 A CN201210537017 A CN 201210537017A CN 103035908 A CN103035908 A CN 103035908A
Authority
CN
China
Prior art keywords
storage battery
negative electrode
acid storage
electrode plate
lead
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012105370171A
Other languages
English (en)
Inventor
赵志坚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Sacred Sun Power Sources Co Ltd
Original Assignee
SHANDONG SACRED SUN POWER SUPPLY TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG SACRED SUN POWER SUPPLY TECHNOLOGY Co Ltd filed Critical SHANDONG SACRED SUN POWER SUPPLY TECHNOLOGY Co Ltd
Priority to CN2012105370171A priority Critical patent/CN103035908A/zh
Publication of CN103035908A publication Critical patent/CN103035908A/zh
Pending legal-status Critical Current

Abstract

一种动力型铅酸蓄电池用负极板铅膏配制方法，涉及铅酸蓄电池。目前，国内铅酸蓄电池在技术上面临比能量低、寿命短的困境。一种动力型铅酸蓄电池用负极板铅膏配制方法，其特征在于负极板铅膏配方是：铅粉100kg、短纤维0.05kg、硫酸钡0.8kg、乙炔黑0.5kg、活性炭1.5kg、酚-苯胺磺酸-甲醛缩合物0.3kg、导电石墨0.2kg、气相二氧化硅粉末100g、去离子水1.1kg、硫酸1.30-1.40g/cm3(25℃)的硫酸6000-8000ml、羧甲基纤维素钠(CMC)6-15g、聚四氟乙烯乳液(PTFE)20-60ml。本发明的有益效果是：本发明一种动力型铅酸蓄电池用负极板铅膏配制方法，存在比能量高、大电流放电能力强、循环寿命长的优点。

Description

一种动力型铅酸蓄电池用负极板铅膏配制方法
技术领域
本发明涉及铅酸蓄电池，更具体的为一种动力型铅酸蓄电池用负极板铅膏配制方法。
背景技术
目前，基于国内新能源的需求性和发展潮流，铅酸蓄电池的应用方式由常规的备用和小电流、低功率应用方式转变为大电流、大功率的应用方式，铅酸蓄电池的技术要求面临比能量低、寿命短的困境。目前国内提高铅酸蓄电池的比能量和寿命的常用方法有：1、减薄电极以提高电极比表面积，但是这种方法存在生产控制质量成本高、效率低下的缺点；2、添加可溶性添加剂并提高电池前期的比表面性，但是这种方法存在不能持续保持电池容量的缺点；3、提高电解液浓度，但是这种方法存在加快极板硫酸盐化的缺点；4、添加导电性物质以提高放电深度，但是这种方法存在成本过高的缺点。
发明内容
本发明的目的是提供一种动力型铅酸蓄电池用负极板铅膏配制方法，具有比能量高、大电流放电能力强、循环寿命长的特点。
本发明是通过如下方式实现的：一种动力型铅酸蓄电池用负极板铅膏配制方法，其特征在于负极板铅膏配方是：铅粉100kg、短纤维0.05kg、硫酸钡0.8kg、乙炔黑0.5kg、活性炭1.5kg、酚-苯胺磺酸-甲醛缩合物0.3kg、导电石墨0.2kg、气相二氧化硅粉末100g、去离子水1.1kg、硫酸1.30-1.40g/cm3(25℃)的硫酸6000-8000ml、羧甲基纤维素钠(CMC)6-15g、聚四氟乙烯乳液(PTFE)20-60ml。
配制时，先将羧甲基纤维素钠(CMC)、聚四氟乙烯乳液(PTFE)和水混合搅拌制成分散均匀的乳浊液，作粘结、分散剂静置待用；然后将铅粉、活性炭、酚-苯胺磺酸-甲醛缩合物、导电石墨、气相二氧化硅粉、硫酸钡、短纤维混合搅拌10-15分钟；在1-3分钟内加入去离子水以及羧甲基纤维素钠(CMC)、聚四氟乙烯乳液(PTFE)和水混合搅拌制成的分散、均匀乳浊液，继续搅拌10分钟；在10-15分钟内均匀加入浓度为1.3-1.4g/cm3(25℃)的硫酸，继续搅拌不低于10分钟至均匀，整个过程内温度控制在20-60℃以内；最后用去离子水微调，控制出料前铅膏的密度为3.0-3.8g/cm3。
本发明的有益效果是：本发明一种动力型铅酸蓄电池用负极板铅膏配制方法，存在比能量高、大电流放电能力强、循环寿命长的优点。
具体实施方式
首先准备铅膏配方，成份所占的重量比为：铅粉100kg、短纤维0.05kg、硫酸钡0.8kg、乙炔黑0.5kg、活性炭1.5kg、酚-苯胺磺酸-甲醛缩合物0.3kg、导电石墨0.2kg、气相二氧化硅粉末100g、去离子水1.1kg、硫酸1.30-1.40g/cm3(25℃)的硫酸6000-8000ml、羧甲基纤维素钠(CMC)6-15g、聚四氟乙烯乳液(PTFE)20-60ml。配制时，先将羧甲基纤维素钠(CMC)、聚四氟乙烯乳液(PTFE)和水混合搅拌制成分散、均匀乳浊液，作粘结、分散剂静置待用；然后将铅粉、活性炭、酚-苯胺磺酸-甲醛缩合物、导电石墨、气相二氧化硅粉、硫酸钡、短纤维混合搅拌10-15分钟；在1-3分钟内加入去离子水以及羧甲基纤维素钠(CMC)、聚四氟乙烯乳液(PTFE)和水混合搅拌制成的分散、均匀乳浊液，继续搅拌10分钟；在10-15分钟内均匀加入浓度为1.3-1.4g/cm3(25℃)的硫酸，继续搅拌不低于10分钟至均匀，整个过程内温度控制在20-60℃以内；最后用去离子水微调，控制出料前铅膏的密度为3.0-3.8g/cm3。

Claims (2)

1.一种动力型铅酸蓄电池用负极板铅膏配制方法，其特征在于负极板铅膏配方是：铅粉100kg、短纤维0.05kg、硫酸钡0.8kg、乙炔黑0.5kg、活性炭1.5kg、酚-苯胺磺酸-甲醛缩合物0.3kg、导电石墨0.2kg、气相二氧化硅粉末100g、去离子水1.1kg、硫酸1.30-1.40g/cm3(25℃)的硫酸6000-8000ml、羧甲基纤维素钠(CMC)6-15g、聚四氟乙烯乳液(PTFE)20-60ml。
2.如权利要求1所述的一种动力型铅酸蓄电池用正极板铅膏配制方法，其特征在于整个过程内温度应控制在20-60℃以内。
CN2012105370171A 2012-12-04 2012-12-04 一种动力型铅酸蓄电池用负极板铅膏配制方法 Pending CN103035908A (zh)