CN103214779B - 一种合成树脂材料代替部分铜材生产行进号的方法 - Google Patents
一种合成树脂材料代替部分铜材生产行进号的方法 Download PDFInfo
- Publication number
- CN103214779B CN103214779B CN201310133493.1A CN201310133493A CN103214779B CN 103214779 B CN103214779 B CN 103214779B CN 201310133493 A CN201310133493 A CN 201310133493A CN 103214779 B CN103214779 B CN 103214779B
- Authority
- CN
- China
- Prior art keywords
- advancing
- produce
- synthetic resins
- mixture
- resin material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种树脂材料代替部分铜材生产行进号的方法，利用合成树脂材料生产行进号的喇叭口管，然后将其与铜制发音管组合安装。该合成树脂材料发音效果与铜材相同，环保安全，并可以减轻行进号的重量，节约成本。
Description
技术领域
本发明涉及乐器生产技术领域，尤其涉及一种合成树脂材料代替部分铜材生产行进号的方法。
背景技术
传统的行进号生产中，管体使用材料为铜材，存在着抗碰撞、抗冲击性能差，易划伤，受外力冲击后不能回弹恢复原样，表面涂漆因使用油漆和电镀镍、银，长时间后易氧化生锈的缺点。而且铜材成分中含有重金属铅，焊接采用钎焊方法，不能达到对人体无害的要求。
发明内容
本发明的目的在于提供一种合成树脂材料代替部分铜材生产行进号的方法，该合成树脂材料发音效果与铜材相同，环保安全，并可以减轻进行号的重量，节约成本。
为了实现上述目的，本发明提供了一种合成树脂材料代替部分铜材生产行进号的方法，本发明是通过以下技术方案的：
利用合成树脂材料生产行进号的喇叭口管，然后将其与铜制发音管组合安装；
利用合成树脂材料生产行进号的喇叭口管的具体方法如下：
1）提供一种合成树脂复合物，按重量百分比，由以下组分的原料混合制成：
丙烯腈-丁二烯-苯乙烯共聚物颗粒 30-70%；
玻璃纤维混合物 10-30%；
无机银持久抗菌剂1-10%；
氢氧化铝5-15%；
水杨酸脂5-15%；
非离子型抗静电剂 1-3%；
混合挤出切粒制得；
2）将步骤1）的混合料加入到磨具中加热到140-180℃，成型；
3）采用电晕放电式除静电器除静电；
4）涂装：将上述步骤的产品被涂物做阳极，涂料喷口为阴极并施以负电压，雾化后的涂料液滴，带着负电荷飞向带正电荷的塑料制品进行涂装。
作为本发明的进一步改进，所述非离子型抗静电剂为脂肪醇、环氧氯丙烷、单乙醇胺混合剂。
作为本发明的进一步改进，其中步骤1）中各组分原料的重量百分比为：
丙烯腈-丁二烯-苯乙烯共聚物颗粒 50%；
玻璃纤维混合物 23%；
无机银持久抗菌剂5%；
氢氧化铝10%；
水杨酸脂10%；
非离子型抗静电剂 2%。
本发明所取得的有益效果：
本发明所提供的一种合成树脂材料代替部分铜材生产行进号的方法，由于管体采用了合成树脂，其特性为抗碰撞、抗冲击力性能好，长久保持不变形，即有轻微变形也能很快恢复原样，表面平整、漂亮，不氧化，无锈蚀现象。另外，合成树脂不含铅等重金属，且含有抑菌剂使用安全环保。本发明所提供的合成材料可以增加树脂强度，降低铸件收缩率25%。用合成树脂替代铜材，可以降低成本，且能够减少行进号的重量。以JYTU—E278进行号为例，每只行进号的重量由10.78千克减少为7.17千克，节约成本289元/只。
【具体实施方式】
实施例1
一种合成树脂材料代替部分铜材生产行进号的方法：包括利用合成树脂材料生产行进号的喇叭口管，然后将其与铜制发音管组合安装；
利用合成树脂材料生产行进号的喇叭口管的具体方法如下：
1）提供一种合成树脂复合物，按重量百分比，由以下组分的原料混合制成：
丙烯腈-丁二烯-苯乙烯共聚物颗粒 50%；
玻璃纤维混合物 23%；
无机银持久抗菌剂5%；
氢氧化铝10%；
水杨酸脂10%；
脂肪醇、环氧氯丙烷、单乙醇胺混合剂 2%。
混合挤出切粒制得；
2）将步骤1）的混合料加入到磨具中加热到140℃，成型；
3）采用电晕放电式除静电器除静电；
4）涂装：将上述步骤的产品被涂物做阳极，涂料喷口为阴极并施以负电压，雾化后的涂料液滴，带着负电荷飞向带正电荷的塑料制品进行涂装。
实施例2
一种合成树脂材料代替部分铜材生产行进号的方法：包括利用合成树脂材料生产行进号的喇叭口管，然后将其与铜制发音管组合安装；
利用合成树脂材料生产行进号的喇叭口管的具体方法如下：
1）提供一种合成树脂复合物，按重量百分比，由以下组分的原料混合制成：
丙烯腈-丁二烯-苯乙烯共聚物颗粒 30%；
玻璃纤维混合物30%；
无机银持久抗菌剂10%；
氢氧化铝15%；
水杨酸脂12%；
脂肪醇、环氧氯丙烷、单乙醇胺混合剂3%；
混合挤出切粒制得；
2）将步骤1）的混合料加入到磨具中加热到180℃，成型；
3）采用电晕放电式除静电器除静电；
4）涂装：将上述步骤的产品被涂物做阳极，涂料喷口为阴极并施以负电压，雾化后的涂料液滴，带着负电荷飞向带正电荷的塑料制品进行涂装。
实施例3
一种合成树脂材料代替部分铜材生产行进号的方法：包括利用合成树脂材料生产行进号的喇叭口管，然后将其与铜制发音管组合安装；
利用合成树脂材料生产行进号的喇叭口管的具体方法如下：
1）提供一种合成树脂复合物，按重量百分比，由以下组分的原料混合制成：
丙烯腈-丁二烯-苯乙烯共聚物颗粒70%；
玻璃纤维混合物 10%；
无机银持久抗菌剂7%；
氢氧化铝5%；
水杨酸脂5%；
非离子型抗静电剂3%；
混合挤出切粒制得；
2）将步骤1）的混合料加入到磨具中加热到160℃，成型；
3）采用电晕放电式除静电器除静电；
4）涂装：将上述步骤的产品被涂物做阳极，涂料喷口为阴极并施以负电压，雾化后的涂料液滴，带着负电荷飞向带正电荷的塑料制品进行涂装。
本发明中使用的脂肪醇、环氧氯丙烷、单乙醇胺混合剂为乙很有效的抗静电剂，即使是在相对湿度低的情况下亦然，而且长期有效。脂肪醇、环氧氯丙烷、单乙醇胺的质量比为1：0.1-7:0.5-4。
由于本发明中使用了阻燃剂氢氧化铝，保证了制作过程的安全，另外在制备中容易产生静电，因此需要再涂装之前一步先进行除静电操作，本发明采用电晕放电式除静电器，摩擦产生不均匀电荷，产生与塑料表面相反的电荷中和。
以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的精神和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (3)
1.一种树脂材料代替部分铜材生产行进号的方法，其特征在于，利用合成树脂材料生产行进号的喇叭口管，然后将其与铜制发音管组合安装；
利用合成树脂材料生产行进号的喇叭口管的具体方法如下：
1）提供一种合成树脂复合物，按重量百分比，由以下组分的原料混合制成：
丙烯腈-丁二烯-苯乙烯共聚物颗粒 30-70%；
玻璃纤维混合物 10-30%；
无机银持久抗菌剂1-10%；
氢氧化铝5-15%；
水杨酸酯5-15%；
非离子型抗静电剂 1-3%；
混合挤出切粒制得；
2）将步骤1）的混合料加入到磨具中加热到140-180℃，成型；
3）采用电晕放电式除静电器除静电；
4）涂装：将上述步骤的产品被涂物做阳极，涂料喷口为阴极并施以负电压，雾化后的涂料液滴，带着负电荷飞向带正电荷的塑料制品进行涂装。
2.如权利要求1所述的一种树脂材料代替部分铜材生产行进号的方法，其特征在于，所述非离子型抗静电剂为脂肪醇、环氧氯丙烷、单乙醇胺混合剂。
3.如权利要求1所述的一种树脂材料代替部分铜材生产行进号的方法，其特征在于，步骤1）中各组分原料的重量百分比为：
丙烯腈-丁二烯-苯乙烯共聚物颗粒 50%；
玻璃纤维混合物 23%；
无机银持久抗菌剂5%；
氢氧化铝10%；
水杨酸酯10%；
非离子型抗静电剂 2%。