CN103205060B - 一种改善加工性能的橡胶 - Google Patents

一种改善加工性能的橡胶 Download PDF

Info

Publication number
CN103205060B
CN103205060B CN201310139207.2A CN201310139207A CN103205060B CN 103205060 B CN103205060 B CN 103205060B CN 201310139207 A CN201310139207 A CN 201310139207A CN 103205060 B CN103205060 B CN 103205060B
Authority
CN
China
Prior art keywords
parts
rubber
processing characteristics
elastomeric material
mass fraction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310139207.2A
Other languages
English (en)
Other versions
CN103205060A (zh
Inventor
吴喜林
吕晓刚
华伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Jituo Rubber Technologies Co Ltd
Original Assignee
Wuhu Jituo Rubber Technologies Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Jituo Rubber Technologies Co Ltd filed Critical Wuhu Jituo Rubber Technologies Co Ltd
Priority to CN201310139207.2A priority Critical patent/CN103205060B/zh
Publication of CN103205060A publication Critical patent/CN103205060A/zh
Application granted granted Critical
Publication of CN103205060B publication Critical patent/CN103205060B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种改善加工性能的橡胶，包括如下质量份数的组分：三元乙丙橡胶93～105份、氯化聚乙烯8～11份、炭黑90～110份、石蜡油40～45份、氧化锌7～12份、硬脂酸0.5～2份、1,2-聚丁二烯15～25份、硫磺8～10份、四硫化双戊撑秋兰姆1～3份、N-叔丁基-2-苯并噻唑次黄酰胺1～3份、二正丁基二硫代氨基甲酸锌1～3份、氧化钙5～8份。本发明所提供的改善加工性能的橡胶，能够降低用于制造汽车零部件的邵氏A硬度90度以上的橡胶材料的门尼粘度，从而提高橡胶材料的可塑性和用该材料制成的汽车零部件的性能。

Description

一种改善加工性能的橡胶
技术领域
本发明涉及橡胶加工技术领域，具体涉及一种改善加工性能的橡胶。
技术背景
现有技术中，用于制造汽车零部件的邵氏A硬度90度以上的橡胶材料存在门尼粘度较高的情况，导致使用橡胶材料制造汽车零部件的可塑性较低，从而影响了汽车零部件的生产合格率和产品性能。因此，需要在现有技术的基础上对现有的橡胶材料作出改进，以降低其门尼粘度，从而提高橡胶材料的可塑性和用该材料制成的汽车零部件的性能。
发明内容
本发明的目的在于提供一种改善加工性能的橡胶，能够降低用于制造汽车零部件的邵氏A硬度90度以上的橡胶材料的门尼粘度，从而提高橡胶材料的可塑性和用该材料制成的汽车零部件的性能。
为了实现上述目的，本发明提出的技术方案是：
一种改善加工性能的橡胶，包括如下质量份数的组分：
三元乙丙橡胶93～105份、
氯化聚乙烯8～11份、
炭黑90～110份、
石蜡油40～45份、
氧化锌7～12份、
硬脂酸0.5～2份、
1,2-聚丁二烯15～25份、
硫磺8～10份、
四硫化双戊撑秋兰姆1～3份、
N-叔丁基-2-苯并噻唑次黄酰胺1～3份、
二正丁基二硫代氨基甲酸锌1～3份、
氧化钙5～8份。
作为本发明进一步优化的改善加工性能的橡胶，包括如下质量份数的组分：
三元乙丙橡胶100份、
氯化聚乙烯10份、
炭黑100份、
石蜡油42份、
氧化锌10份、
硬脂酸0.7份、
1,2-聚丁二烯20份、
硫磺8份、
四硫化双戊撑秋兰姆1.5份、
N-叔丁基-2-苯并噻唑次黄酰胺2份、
二正丁基二硫代氨基甲酸锌1份、
氧化钙6份。
本发明所提供的改善加工性能的橡胶，能够降低用于制造汽车零部件的邵氏A硬度90度以上的橡胶材料的门尼粘度，从而提高橡胶材料的可塑性和用该材料制成的汽车零部件的性能。
具体实施方式
为了加深对本发明的理解，下面将结合实施例对本发明做进一步详细描述，该实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
实施例一
本实施例提供的改善加工性能的邵氏A硬度为90度的橡胶材料，包括如下质量份数的组分：
三元乙丙橡胶100份、
氯化聚乙烯10份、
炭黑100份、
石蜡油42份、
氧化锌10份、
硬脂酸0.7份、
1,2-聚丁二烯20份、
硫磺8份、
四硫化双戊撑秋兰姆1.5份、
N-叔丁基-2-苯并噻唑次黄酰胺2份、
二正丁基二硫代氨基甲酸锌1份、
氧化钙6份。
将上述质量份数的三元乙丙橡胶、氯化聚乙烯、炭黑、石蜡油、氧化锌、硬脂酸保持80℃混炼180秒，再加入上述质量份数的1,2-聚丁二烯、硫磺、四硫化双戊撑秋兰姆、N-叔丁基-2-苯并噻唑次黄酰胺、二正丁基二硫代氨基甲酸锌、氧化钙保持110℃混炼40秒即可。
实施例二
本实施例提供的改善加工性能的邵氏A硬度为90度的橡胶材料，包括如下质量份数的组分：
三元乙丙橡胶93份、
氯化聚乙烯8份、
炭黑90份、
石蜡油40份、
氧化锌7份、
硬脂酸0.5份、
1,2-聚丁二烯15份、
硫磺9份、
四硫化双戊撑秋兰姆1份、
N-叔丁基-2-苯并噻唑次黄酰胺3份、
二正丁基二硫代氨基甲酸锌2份、
氧化钙5份。
混炼方法同实施例一。
实施例三
本实施例提供的改善加工性能的邵氏A硬度为90度的橡胶材料，包括如下质量份数的组分：
三元乙丙橡胶105份、
氯化聚乙烯11份、
炭黑110份、
石蜡油45份、
氧化锌12份、
硬脂酸2份、
1,2-聚丁二烯25份、
硫磺10份、
四硫化双戊撑秋兰姆3份、
N-叔丁基-2-苯并噻唑次黄酰胺1份、
二正丁基二硫代氨基甲酸锌3份、
氧化钙8份。
混炼方法同实施例一。
对比实施例
根据现有技术的配方，本实施例提供的邵氏A硬度为90度的橡胶材料，包括如下质量份数的组分：
三元乙丙橡胶100份、
炭黑100份、
石蜡油40份、
氧化锌10份、
硬脂酸1份、
硫磺5份、
二硫化四甲基秋兰姆1份、
N-叔丁基-2-苯并噻唑次黄酰胺2份、
二正丁基二硫代氨基甲酸锌1份、
氧化钙6份。
将上述质量份数的三元乙丙橡胶、炭黑、石蜡油、氧化锌、硬脂酸保持80℃混炼180秒，再加入上述质量份数的硫磺、二硫化四甲基秋兰姆、N-叔丁基-2-苯并噻唑次黄酰胺、二正丁基二硫代氨基甲酸锌、氧化钙保持110℃混炼40秒即可。
上述实施例提供的橡胶材料加工性能测试结果如表1所示：
表1
通过上述实验数据可知，实施例一至三的加工性能明显优于对比实施例，其中以实施例一的加工性能最优。

Claims (2)

1.一种改善加工性能的橡胶，其特征在于，包括如下质量份数的组分：
三元乙丙橡胶93～105份、
氯化聚乙烯8～11份、
炭黑90～110份、
石蜡油40～45份、
氧化锌7～12份、
硬脂酸0.5～2份、
1,2-聚丁二烯15～25份、
硫磺8～10份、
四硫化双戊撑秋兰姆1～3份、
N-叔丁基-2-苯并噻唑次黄酰胺1～3份、
二正丁基二硫代氨基甲酸锌1～3份、
氧化钙5～8份。
2.根据权利要求1所述的改善加工性能的橡胶，其特征在于,包括如下质量份数的组分：
三元乙丙橡胶100份、
氯化聚乙烯10份、
炭黑100份、
石蜡油42份、
氧化锌10份、
硬脂酸0.7份、
1,2-聚丁二烯20份、
硫磺8份、
四硫化双戊撑秋兰姆1.5份、
N-叔丁基-2-苯并噻唑次黄酰胺2份、
二正丁基二硫代氨基甲酸锌1份、
氧化钙6份。
CN201310139207.2A 2013-04-19 2013-04-19 一种改善加工性能的橡胶 Active CN103205060B (zh)