CN103159497A - Jinyongdong stone polished tile and production method for same - Google Patents
Jinyongdong stone polished tile and production method for same Download PDFInfo
- Publication number
- CN103159497A CN103159497A CN 201110408094 CN201110408094A CN103159497A CN 103159497 A CN103159497 A CN 103159497A CN 201110408094 CN201110408094 CN 201110408094 CN 201110408094 A CN201110408094 A CN 201110408094A CN 103159497 A CN103159497 A CN 103159497A
- Authority
- CN
- China
- Prior art keywords
- clay
- jinyongdong
- albite
- sand
- stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a Jinyongdong stone polished tile and a production method for the same. The Jinyongdong stone polished tile is characterized by being composed of a basic surface material and a crystalline grain material, wherein the basic surface material is composed of potassium feldspar sand A, potassium feldspar sand B, soda feldspar A, soda feldspar B, soda feldspar C, potassium-soda feldspar A, pyrophyllite, talcum, flint clay, clay A, clay B and pigment; and the crystalline grain material is composed of potassium feldspar sand 1, soda feldspar 1, soda feldspar 2, pyrophyllite, talcum, clay A, clay B and clay C. The production method for the Jinyongdong stone polished tile comprises the working procedures of raw material selection, powder preparation, material distribution, press-forming, drying, roller kiln once-firing, edging, polishing and the like. The Jinyongdong stone polished tile disclosed by the invention deduces the dynamic state of changing via an external environment and geologic features of natural stone, thus achieving the exaggerated artistic effect of natural straight lines, perfectly showing the textures of natural lines, soft colour and same exterior and interior, and glowing an extreme noble quality from inside to outside.
Description
Technical field
the present invention relates to a kind of vitrified tile and preparation method thereof, the gold that particularly relates to a kind of artificial grantie gushes hole stone polished brick and preparation method thereof.
Background technology
natural cavity stone is a kind of emerging import Decorative Building Stone, because its distinctive color and decorative pattern enjoy people to favor, hole stone is that the formal name used at school of its stone material is travertine or Tufa because there are many holes on the surface of stone material and gain the name, commercial, it is classified as to the marble class.The tone of hole stone is in the majority with cream colour, makes again the people feel gentle, rich texture, and clear-cut texture, impel the buildings of decoration that strong culture and historical charm are often arranged, and hole stone is mainly used in decorating outer wall of building and indoor floor, wall fitting.Existing natural cavity stone hole distribution is uneven, deep mixed, have aberration, intensity is poor, easily cracked, and the higher shortcoming of price, on market, starts in recent years artificial burrow stone imitation ceramic tile to have occurred, is characterized in that intensity is good, easily arranges, and price is more cheap.For example, the Chinese invention patent application that publication number is CN101016213 " natural cavity stone imitation ceramic tile ", by bed material and fabric respectively through ball milling, homogenizing, granulation, old, dry, burn till after, by bed material and fabric compression moulding and make, it is characterized in that, the composition that contains following weight parts in fabric is as foamed material: ball clay class: 8～15 parts of albite classes: 18～30 parts of lithium feldspars: 30～45 parts of Wingdales: 12～20 parts of polishing slags: 3～15 parts are burnt talcums: 0～1 part.
Summary of the invention
the object of the invention is to solve the technical bottleneck of this series products of domestic production, and the gold of having developed a kind of artificial grantie gushes hole stone polished brick and preparation method thereof.It is the evolution process according to rock that this gold of the present invention's exploitation gushes the hole stone polished brick, courageously make dynamically large straight burr, from springing up of magma, change, condensation, the whole process of petrochemical industry, deduce the dynamic form that lithotome changes via outside atmosphere and geologic feature, reached the effect of the art of natural straight burr exaggeration.Perfection shows natural lines completely, color is soft, and the texture of thinking and acting in one and the same way is being shone ultimate attainment honorable makings from inside to outside.
technical solution of the present invention is: this gold gushes the hole stone polished brick, basal plane material and crystal grain material, consists of, and is characterized in:
the composition of basal plane material and weight percent thereof are:
a potassium felspar sand sand 19-23%,
b potassium felspar sand sand 6-7%,
a albite 9-15%,
the long 15-19% of B sodium,
c albite 3-6%,
a potassium albite 4-8%,
agalmatolite 19-24%,
talcum 1.5-3.5%,
flint clay 5-8%,
a clay 19-22%,
b clay 5-6%,
colorant 1.6-3.00%;
the composition of crystal grain material and per-cent thereofweight is:
potassium felspar sand sand 1 19-25%;
albite 1 39-49%;
albite 2 11-16%;
agalmatolite 17-19%;
talcum 2.5-4.0%;
a clay 7-9%;
b clay 4-8%;
c clay 9-15%;
the chemical constitution that this gold that the present invention provides gushes the hole stone polished brick is:
the Chemical Composition of basal plane material and content thereof are:
SiO2 61.00--65.00％；
AL2O3 11.00-17.00％；
Fe2O3 <2.50％；
TiO3 <2.25％；
CaO <2.50％；
MgO 1.5-2.8％；
K2O 2.80-4.30％；
Na2O 3.90-5.60％；
I.L <2.8％。
the Chemical Composition of crystal grain material and content thereof are:
SiO
2
58.00--65.00％；
AL
2
O
3
20.00-29.00％；
Fe
2
O
3
<2.50％；
TiO
3
<1.25％；
CaO <2.50％；
MgO 0.5-1.0％；
K
2
O 1.1-1.5％；
Na
2
O 3.40-4.0％；
I.L <4.0％。
the preparation method that this gold that the present invention provides gushes the hole stone polished brick:
by operations such as picking of raw material, preparation, cloth, press forming, drying, roller kiln once-firing, edging, polishings, formed, use magic subregion Strand Feeding Technique and crystal grain Strand Feeding Technique, be characterized in: the base powder is when the end place by conveying belt sends into roll squeezer, directly continuously with striated spreading pigment, make base powder and pigment common roll be pressed into pie, then become the pellet of certain particle size through the crushed machine particle, the feeding harder, dry method is pressed into base, enter the klining knot, through polishing, warehouse-in is made finished product;
described magic subregion Strand Feeding Technique: different powders is transferred in proportion in the subregion grid and delivers in mould and be pressed;
described crystal grain Strand Feeding Technique: utilize two rollers to be distributed into two or more blocky-shaped particles in grid, make two or more blocky-shaped particle self-assembling formation particle bands, then spreading one deck or multilayer micro mist, finally be distributed into the micro mist pattern fabrics to fill up grid; Mix dexterously low-temperature transparent material and high temperature decorating colour, the startup of cloth, operation, unemployed time all calculate accurately through science, make closely and in an orderly manner alternate collocation of different material, stock yard border transition nature, clean mark easily is shown in, restores meticulously the true skin texture of lithotome.
compared with prior art, the invention has the beneficial effects as follows:
1, the texture that possesses lithotome: the large straight burr effect of hole texture and natural cavity stone.Reproduced the forming process of natural rock, caught the dynamic of magma racing current, the brick body is more bright penetrating, and color and luster is soft, and sense of touch is splendid.
2, than the advantage of natural cavity stone: use unrestrictedly, resistant is easy clean, and environmental protection is radiationless.3, tangible exclusive quality: the honorable gracefulness of color makings, decorate classical grade.4, than domestic same specification vitrified tile: high, the easy clean environmental protection of density, penetrating nature.
Embodiment
Embodiment
gold gushes the basal plane material add-on of hole stone polished brick:
a potassium felspar sand sand 20%, B potassium felspar sand sand 6%, A albite 12%, B sodium is long by 16%,
c albite 4%, A potassium albite 6%, agalmatolite 20%, talcum 2%, flint clay 5%,
colorant 2%, the clay surplus.
the Chemical Composition of basal plane material and content thereof:
AL2O3 14.00％，Fe2O3 2.00％，TiO3 2.00％，CaO 2.00％，
mgO 1.5%, and K2O 3%, and Na2O 4.50%; I.L 2.00%, the SiO2 surplus.
gold gushes the crystalline substance material add-on of hole stone polished brick:
albite 1 39%, albite 2 11%, agalmatolite 17%, talcum 3%,
clay surplus %.
chemical Composition and the content thereof of brilliant material:
AL
2
O
3
25.0％， Fe
2
O
3
2.0％，TiO
3
1.0％，CaO 2.0％，
MgO 0.8％，K
2
O 1.5％，Na
2
O 3.6％，I.L 3.0％，
siO
2
surplus.
each component add-on fragmentation of basal plane material is mixed into to the base powder, different powders is transferred in proportion in the subregion grid and delivers in mould and be pressed, when sending into roll squeezer directly continuously with striated spreading pigment, make base powder and pigment common roll be pressed into pie, then become the pellet of certain particle size through the crushed machine particle, utilize two rollers to be distributed into the blocky-shaped particle of two or more brilliant material in grid, make the blocky-shaped particle self-assembling formation particle band of two or more brilliant material, then spreading one deck or multilayer micro mist, finally the micro mist pattern fabrics is distributed into and fills up grid, the feeding harder, dry method is pressed into base, enter the klining knot, through polishing, warehouse-in is made finished product.
the technical indicator that this gold that the present invention provides gushes the hole stone polished brick sees the following form:
the technical indicator contrast table
Claims (3)
1. a gold gushes the hole stone polished brick, basal plane material and crystal grain material, consists of, and it is characterized in that:
The composition of basal plane material and weight percent thereof are:
A potassium felspar sand sand 19-23%,
B potassium felspar sand sand 6-7%,
A albite 9-15%,
The long 15-19% of B sodium,
C albite 3-6%,
A potassium albite 4-8%,
Agalmatolite 19-24%,
Talcum 1.5-3.5%,
Flint clay 5-8%,
A clay 19-22%,
B clay 5-6%,
Colorant 1.6-3.00%;
The composition of crystal grain material and weight percent thereof are:
Potassium felspar sand sand 1 19-25%;
Albite 1 39-49%;
Albite 2 11-16%;
Agalmatolite 17-19%;
Talcum 2.5-4.0%;
A clay 7-9%;
B clay 4-8%;
C clay 9-15%.
2. gold according to claim 1 gushes the hole stone polished brick, it is characterized in that the chemical constitution that described gold gushes the hole stone polished brick is:
The Chemical Composition of basal plane material and content thereof are:
SiO2 61.00--65.00％；
AL2O3 11.00-17.00％；
Fe2O3 <2.50％；
TiO3 <2.25％；
CaO <2.50％；
MgO 1.5-2.8％；
K2O 2.80-4.30％；
Na2O 3.90-5.60％；
I.L <2.8％；
The Chemical Composition of crystal grain material and content thereof are:
SiO
2 58.00--65.00％；
AL
2O
3 20.00-29.00％；
Fe
2O
3 <2.50％；
TiO
3 <1.25％；
CaO <2.50％；
MgO 0.5-1.0％；
K
2O 1.1-1.5％；
Na
2O 3.40-4.0％；
I.L <4.0％。
3. the preparation method that gold gushes the hole stone polished brick according to claim 1, by picking of raw material, preparation, cloth, press forming, dry, the roller kiln once-firing, edging, the operations such as polishing form, use magic subregion Strand Feeding Technique and crystal grain Strand Feeding Technique, it is characterized in that: the base powder is when the end place by conveying belt sends into roll squeezer, directly continuously with striated spreading pigment, make base powder and pigment common roll be pressed into pie, then become the pellet of certain particle size through the crushed machine particle, the feeding harder, dry method is pressed into base, enter the klining knot, through polishing, warehouse-in is made finished product,
Described magic subregion Strand Feeding Technique: different powders is transferred in proportion in the subregion grid and delivers in mould and be pressed;
Described crystal grain Strand Feeding Technique: utilize two rollers to be distributed into two or more blocky-shaped particles in grid, make two or more blocky-shaped particle self-assembling formation particle bands, then spreading one deck or multilayer micro mist, finally be distributed into the micro mist pattern fabrics to fill up grid.