CN103102123A - Environmentally-friendly interior wall putty powder and preparation method thereof - Google Patents
Environmentally-friendly interior wall putty powder and preparation method thereof Download PDFInfo
- Publication number
- CN103102123A CN103102123A CN2012105479545A CN201210547954A CN103102123A CN 103102123 A CN103102123 A CN 103102123A CN 2012105479545 A CN2012105479545 A CN 2012105479545A CN 201210547954 A CN201210547954 A CN 201210547954A CN 103102123 A CN103102123 A CN 103102123A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- putty powder
- sealing compound
- environmentally
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides environmentally-friendly interior wall putty powder and a preparation method thereof. The putty powder is prepared from the following raw materials in parts by weight: 700 to 750 parts of calcium carbonate powder, 180 to 220 parts of white portland cement, 1 to 3 parts of water-retaining agents, 3 to 7 parts of polyvinyl alcohol, 1 to 5 parts of emulsion powder, 40 to 60 parts of bentonite and 1 to 3 parts of wood fibers. Compared with the prior art, the putty powder provided by the invention has the beneficial effects that the scraping resistance, polishing property, fineness, cracking resistance, later-phase hardness and construction tolerance of the putty powder are superior to those of the traditional putty powder; and the putty powder is nontoxic and environmentally-friendly and is free of containing formaldehyde and benzene, thereby being beneficial to the body health of a constructor. In addition, the putty powder is long in service life and can be stably proportioned and mixed on a construction site, so that theoretical consumption of the putty powder is reduced in a definite degree.
Description
Technical field
The present invention relates to a kind of inner wall environmentally-friendly sealing compound powder and preparation method thereof.
Background technology
Putty carries out pretreated a kind of Surface filling material to construction surface before being the construction of paint class, and main purpose is the curve deviation of filling the hole of construction surface and correcting construction surface, lays a solid foundation for obtaining even, level and smooth lacquer painting.
Tradition putty is generally glue and talcum powder, wherein contains too much objectionable impurities, and especially formaldehyde and benzene, therefore after metope has been criticized putty, have and make people's foreign odor; Also will use sodium cellulosate in traditional technology, it needs could use after the long-time bubble of water, and its result probably causes damage to indoor environment.Because it is also a kind of tamanori, inevitably to overflow when modulating with talcum powder, the working-yard will become dirty like this.If at the finishing in summer, its scene will be apparent.In addition, winter, sodium cellulosate was difficult to bubble open, and bonding effect just reduces greatly like this.
Summary of the invention
The present invention proposes a kind of inner wall environmentally-friendly sealing compound powder and preparation method thereof, overcome deficiency of the prior art, not only performance is better than traditional putty, asepsis environment-protecting, preservation period limit for length, working-yard modulation is stable, and the working-yard can keep neatly, totally.
Technical scheme of the present invention is achieved in that a kind of inner wall environmentally-friendly sealing compound powder, it is made by the raw material of following weight part: dry powder: 700-750 part, white portland cement: 180-220 part, water-holding agent: 1-3 part, polyvinyl alcohol: 3-7 part, latex powder: 1-5 part, wilkinite: 40-60 part, wood fibre: 1-3 part.
Further, it is made by the raw material of following weight part: dry powder: 720-730 part, white portland cement: 190-210 part, water-holding agent: 1.5-2.5 part, polyvinyl alcohol: 4-6 part, latex powder: 2-4 part, wilkinite: 45-55 part, wood fibre: 1.5-2.5 part.
Further, it is made by the raw material of following weight part: dry powder: 725 parts, and white portland cement: 200 parts, water-holding agent: 2.0 parts, polyvinyl alcohol: 5 parts, latex powder: 3 parts, wilkinite: 50 parts, wood fibre: 2 parts.
Further, described water-holding agent is acrylamide-acrylicacid salt crosslinking copolymerization thing.
The preparation method of above-mentioned inner wall environmentally-friendly sealing compound powder is: first dry powder is poured in production unit and stirred, then stir in again white portland cement, water-holding agent, polyvinyl alcohol, latex powder, wilkinite and wood fibre being joined production unit in proportion under the condition that stirs, wait the rear pack that stirs.
Further, to pour the churning time in production unit into be 9-11min to described dry powder.
Further, to pour the churning time in production unit into be 10min to described dry powder.
Further, the churning time of described whole production process is 28-32min.
Further, the churning time of described whole production process is 30min.
Compared with prior art, the invention has the beneficial effects as follows: batch the scraping property of the inner wall environmentally-friendly sealing compound powder in the present invention, grinability, fineness, cracking resistance, late hardness, construction tolerance all are better than traditional putty; And asepsis environment-protecting, do not contain formaldehyde and benzene, useful to workmen's health; Preservation period limit for length, the working-yard modulation is stable, has improved working efficiency; Because unit brushing area is large, also reduced to a certain extent theoretical consumption, saved material; Its performance can keep 20 years not mouldy, non-yellowing.
Embodiment
The below is clearly and completely described the technical scheme in the present invention, and obviously, described embodiment is only several embodiment wherein of the present invention, rather than whole embodiment.Based on the embodiment in the present invention, those of ordinary skills belong to the scope of protection of the invention not making the every other embodiment that obtains under the creative work prerequisite.
Embodiment 1:
A kind of inner wall environmentally-friendly sealing compound powder, it is made by the raw material of following weight part: dry powder: 745 parts, white portland cement: 185 parts, water-holding agent: 2.5 parts, polyvinyl alcohol: 4 parts, latex powder: 4 parts, wilkinite: 55 parts, wood fibre: 1.5 parts; In the present embodiment, what described water-holding agent used is polyacrylamide-polyacrylamide.
The consumption of producing concrete each raw material that uses of inner wall environmentally-friendly sealing compound powder of 2000kg is: dry powder: 1494.5Kg, white portland cement: 371.1Kg, polyacrylamide-polyacrylamide: 5.0Kg, polyvinyl alcohol: 8.0Kg, latex powder: 8.0Kg, wilkinite: 110.3Kg, wood fibre: 3.0Kg.
Its preparation method is: first dry powder is poured into and stirred 9min in production unit, then stir in again white portland cement, polyacrylamide-polyacrylamide, polyvinyl alcohol, latex powder, wilkinite and wood fibre being joined production unit in proportion under the condition that stirs, wait the rear pack that stirs; Pour production unit into from dry powder and stir production unit to whole raw materials, the whole production process time used is 28min.
Embodiment 2
A kind of inner wall environmentally-friendly sealing compound powder, it is made by the raw material of following weight part: dry powder: 700 parts, white portland cement: 210 parts, water-holding agent: 1.5 parts, polyvinyl alcohol: 6 parts, latex powder: 2 parts, wilkinite: 40 parts, wood fibre: 2.5 parts; In the present embodiment, what described water-holding agent used is sodium polyacrylate-sodium polyacrylate.
The consumption of producing concrete each raw material that uses of inner wall environmentally-friendly sealing compound powder of 2000kg is: dry powder: 1455.2Kg, white portland cement: 436.6Kg, sodium polyacrylate-sodium polyacrylate: 3.1Kg, polyvinyl alcohol: 12.5Kg, latex powder: 4.2Kg, wilkinite 83.2Kg, wood fibre: 5.2Kg.
Its preparation method is: first dry powder is poured into and stirred 11min in production unit, then stir in again white portland cement, sodium polyacrylate-sodium polyacrylate, polyvinyl alcohol, latex powder, wilkinite and wood fibre being joined production unit in proportion under the condition that stirs, wait the rear pack that stirs; Pour production unit into from dry powder and stir production unit to whole raw materials, the whole production process time used is 32min.
Embodiment 3
A kind of inner wall environmentally-friendly sealing compound powder, it is made by the raw material of following weight part: dry powder: 725 parts, white portland cement: 200 parts, water-holding agent: 2.0 parts, polyvinyl alcohol: 5 parts, latex powder: 3 parts, wilkinite: 50 parts, wood fibre: 2 parts; In the present embodiment, what described water-holding agent used is sodium polyacrylate-sodium polyacrylate.
The consumption of producing concrete each raw material that uses of inner wall environmentally-friendly sealing compound powder of 2000kg is: dry powder: 1469.0Kg, white portland cement: 405.3Kg, sodium polyacrylate-sodium polyacrylate: 4.1Kg, polyvinyl alcohol: 10.1Kg, latex powder: 6.1Kg, wilkinite 101.3Kg, wood fibre: 4.1Kg.
Its preparation method is: first dry powder is poured into and stirred 10min in production unit, then stir in again white portland cement, sodium polyacrylate-sodium polyacrylate, polyvinyl alcohol, latex powder, wilkinite and wood fibre being joined production unit in proportion under the condition that stirs, wait the rear pack that stirs; Pour production unit into from dry powder and stir production unit to whole raw materials, the whole production process time used is 30min.
The performance of the inner wall environmentally-friendly sealing compound powder for preparing in the above-mentioned Preparation Example 1-3 performance with traditional putty is compared as following table:
Can find out from the form of above-mentioned contrast: batch the scraping property of the inner wall environmentally-friendly sealing compound powder in the present invention, grinability, fineness, cracking resistance, late hardness, construction tolerance all are better than traditional putty; And asepsis environment-protecting, do not contain formaldehyde and benzene, useful to workmen's health; Preservation period limit for length, the working-yard modulation is stable; Also reduced to a certain extent theoretical consumption.
The above is only preferred embodiment of the present invention, and is in order to limit the present invention, within the spirit and principles in the present invention not all, any modification of doing, is equal to replacement, improvement etc., within all should being included in protection scope of the present invention.
Claims (9)
1. inner wall environmentally-friendly sealing compound powder, it is characterized in that: it is made by the raw material of following weight part: dry powder: 700-750 part, white portland cement: 180-220 part, water-holding agent: 1-3 part, polyvinyl alcohol: 3-7 part, latex powder: 1-5 part, wilkinite: 40-60 part, wood fibre: 1-3 part.
2. inner wall environmentally-friendly sealing compound powder according to claim 1, it is characterized in that: it is made by the raw material of following weight part: dry powder: 720-730 part, white portland cement: 190-210 part, water-holding agent: 1.5-2.5 part, polyvinyl alcohol: 4-6 part, latex powder: 2-4 part, wilkinite: 45-55 part, wood fibre: 1.5-2.5 part.
3. inner wall environmentally-friendly sealing compound powder according to claim 2, it is characterized in that: it is made by the raw material of following weight part: dry powder: 725 parts, white portland cement: 200 parts, water-holding agent: 2.0 parts, polyvinyl alcohol: 5 parts, latex powder: 3 parts, wilkinite: 50 parts, wood fibre: 2 parts.
4. inner wall environmentally-friendly sealing compound powder according to claim 3, it is characterized in that: described water-holding agent is acrylamide-acrylicacid salt crosslinking copolymerization thing.
5. the preparation method of the described inner wall environmentally-friendly sealing compound powder of any one according to claim 1-4, it is characterized in that: first dry powder is poured in production unit and stirred, then stir in again white portland cement, water-holding agent, polyvinyl alcohol, latex powder, wilkinite and wood fibre being joined production unit in proportion under the condition that stirs, wait the rear pack that stirs.
6. the preparation method of inner wall environmentally-friendly sealing compound powder according to claim 5, it is characterized in that: the churning time that described dry powder is poured in production unit is 9-11min.
7. the preparation method of inner wall environmentally-friendly sealing compound powder according to claim 6, it is characterized in that: the churning time that described dry powder is poured in production unit is 10min.
8. the preparation method of inner wall environmentally-friendly sealing compound powder according to claim 5, it is characterized in that: the churning time of described whole production process is 28-32min.
9. the preparation method of inner wall environmentally-friendly sealing compound powder according to claim 8, it is characterized in that: the churning time of described whole production process is 30min.