CN103088532A - Method for manufacturing split type fiber knitted wiping cloth - Google Patents
Method for manufacturing split type fiber knitted wiping cloth Download PDFInfo
- Publication number
- CN103088532A CN103088532A CN2012103221948A CN201210322194A CN103088532A CN 103088532 A CN103088532 A CN 103088532A CN 2012103221948 A CN2012103221948 A CN 2012103221948A CN 201210322194 A CN201210322194 A CN 201210322194A CN 103088532 A CN103088532 A CN 103088532A
- Authority
- CN
- China
- Prior art keywords
- cloth
- wiping cloth
- splittable
- fiber knitted
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a wiping cloth manufacturing method, in particular to a method for manufacturing split type fiber knitted wiping cloth. By using orange slice type polyester and nylon composite filaments as raw materials, the method for manufacturing the split type fiber knitted wiping cloth comprises the following processes of: a) weaving; b) de-oiling treatment; c) alkali peeling splitting; d) sizing; and e) cutting and cleaning. By adoption of the method, the technical problems of non-uniformity in splitting and low shrinkage of the conventional wiping cloth are solved.
Description
Technical field
The present invention relates to a kind of manufacture method of cleaning wiping cloth, relate in particular to the manufacture method of the fiber knitted cleaning wiping cloth of a kind of Splittable.
Background technology
The Splittable fiber be with two kinds fully different on chemical constitution, mutual exclusive polymer makes it be the composite fibre that tangerine flap alternate configurations is made in the cross section by the composite spinning method each other, complex form is different, splits from horizontal interface shape and the thickness of rear fiber also different.
The raw material of dacron ultrafine fiber capable of being used as wiping cloth." textile industry adjustment and development planning " clearly proposes " will accelerate research and development and the application and development of textile product one continuous line multi-functional, compound fibre in differentiation ", dacron ultrafine fiber is as the high-end product in differential high-performance fiber, being a kind of textile raw material of high-quality, high-tech, is that chemical fibre is to the Typical Representative of the shin-gosen of high-tech, high emulation future development.The fabric of dacron ultrafine fiber has that the surface is fine and soft, drapability good, soft characteristics, has again good perspire, leads wet effect, and warmth retention property, ABRASION RESISTANCE are good in addition, and waterproof and breathable ability and very high cleaning capacity, dirt-removing power are arranged.So dacron ultrafine fiber can be made Silk, imitative peach skin, imitative chamois leather, ultra-fine towel, high-efficiency cleaning cloth and industrial cloth product, range of application is very wide.
Dacron ultrafine fiber has remarkable capillary effect, and becoming dry fast is one of its remarkable characteristic.High-intensity synthetic fiber, not easy fracture.A thick filament is as having become its fine hundreds of root dacron ultrafine fiber in addition, and during so as cleaning wiping cloth, the comparable general cleaning wiping cloth of dacron ultrafine fiber cleaning wiping cloth has the multiple effect of striking off; General fiber is because of thicker, and flexural rigidity is large, so fabric floating-point and object contact area are little, otherwise the little softness again of dacron ultrafine fiber bending stiffness so fabric floating-point and object contact area are large, is wiped away clean power strong; The dacron ultrafine fiber cleaning wiping cloth is after the wiping dirt, and dirt can be the effect that peel off inside along the capillary channel of fiber toward outside migration, and so dirt can not remain in the cleaning wiping cloth surface, therefore just can not cause the product of scratch precision.According to the technique of processing, this project is selected both devillicates of tangerine lobe composite short fiber.In this fiber, two kinds of polymer are connected not separated in spinning process, taking suitable minute fine technique that it is not separately linked in the process of knitting post processing.
High performance wiping cloth is as the mainstream product in the dacron ultrafine fiber goods, it has many characteristics, as dustless property, water imbibition and wipe clean property, why high performance wiping cloth has the cleaning capacity of height, because it has than specific area and the micropore of common fabric height without several times, thus this kind fabric have very large receive dirt, deoil, dirt-removing power, and scrubbing is fast and thoroughly, be difficult for falling hair, reusable after washing.All has purposes widely at aspects such as precision optical machinery, optical instrument, microelectronics, dust free rooms.Cleaning wiping cloth can be divided into four classes substantially according to institutional framework:
(1) woven fabric class: structure is generally tightr, and fabric is thinner, mostly adopts plain weave construction;
(2) knitted fabric class: mostly be greatly through compiling or weft-knitted knop cloth, generally thicker, loose, soft, water absorbing properties is good;
(3) non-woven dry goods: general structure is more loose, has good water imbibition, and structure is various, can adapt to different purposes;
(4) other types: can adopt the compound composition of multiple different structure, as three-layer composite structure etc.
At present, high performance cleaning wiping cloth generally adopts the woven fabric plain weave, is characterized in that close structure, intensity are high, good endurance, is difficult for falling hair and causes and wiped object and pollute.In order to obtain desirable appearance effect, fabric often adopts two-sided sanding sand washing.It is equal tight that knitting principle of readjustment, restructuring, consolidation and improvement makes cloth cover and woven fabric have apart from, cotton wool structure, has high-intensity characteristic, and the rear whole sanding Sand Wash Process of having removed from saves production cost, and increases economic efficiency.
Based on above dacron ultrafine fiber and the principle of readjustment, restructuring, consolidation and improvement many characteristics apart from knitted cotton felt, those skilled in the art are devoted to develop the fiber knitted cleaning wiping cloth of a kind of Splittable, are intended to fill up that knitting principle of readjustment, restructuring, consolidation and improvement is blank apart from the research of cleaning wiping cloth in the world, certainly will have profound significance.
Summary of the invention
The manufacture method that the purpose of this invention is to provide the fiber knitted cleaning wiping cloth of a kind of Splittable is opened the technical problem fine irregular, that shrinkage is poor to solve existing cleaning wiping cloth, realizes allowing knitting cleaning cloth also can reach the same characteristics of woven fabric.
The present invention solves above-mentioned technical problem by the following technical programs.
The manufacture method of the fiber knitted cleaning wiping cloth of a kind of Splittable is washed bright and beautiful bicomponent filament yarn as raw material take tangerine lobe type, comprises following operation:
A) weaving process; B) treatment process of deoiling; C) the alkali decrement is opened fine operation; D) shaping process; E) cutting matting.
When the present invention specifically implemented, preferably, the regulated and controled parameter of described weaving process was as follows: line length is the 8.4-10.0cm/50 coil, and linear speed is 12.6-14r/min; It is the happy interlock machine of moral of E40 or E50 that described weaving process adopts plane No..
In the preferred embodiment of the present invention, the described treatment process of deoiling is carried out on overflow dyeing machine, specifically comprise the following steps: grey cloth was immersed in 60-65 ℃ of water wetting 20-30 minute, then carry out 80-95 ℃ of processing 20-45min after adding deoil yarn agent 1.5-3g/L, smooth agent 1.5-3g/L and NaOH 0.8-1g/L, use successively again 60-80 ℃ of hot water wash 20-45min, 10-25 ℃ of cold wash 10-30min; Wherein, the bath raio during washing is 1: 15-20, cloth speed is 180-200m/min.
In the specific embodiment of the present invention, the yarn agent TF-115B that deoils of the preferred development of evil in febrile disease of the yarn agent Group Co.,Ltd of deoiling; Smooth agent BT-44 in the bath of the preferred Shanghai of smooth agent Chinese Song textile technology Co., Ltd.
When the present invention specifically implemented, preferably, described alkali decrement was opened fine operation and is carried out on overflow dyeing machine, the concentration of the NaOH that adopts when opening fibre is 14-20g/L, opens fibre and carries out under 90-130 ℃, and the time is 30-60 minute, cloth speed 180-220m/min, bath raio is 1: 15-20.More preferably, the concentration of NaOH is 14-18g/L, opens fibre and carries out under 90-120 ℃, and the time is 30-45 minute, cloth speed 180-200m/min, and bath raio is 1: 15-20.
When the present invention specifically implemented, preferably, the regulated and controled parameter of described shaping process was as follows: temperature is 130-150 ℃, and overfeeding is 30%-40%, and the speed of a motor vehicle is 10-15m/min.
In another preferred embodiment of the present invention, described cutting matting comprises the following steps: with laser type and ultrasonic wave cut, hot cutter edge sealing; And whole process is cleaned, is dried at dust free room.Wherein, the selection of multiple cutting mode is in order to prevent that effectively four limit soft flocks are scattered.In cutting matting of the present invention, the method for cleaning, drying at dust free room is the general method in this area.
Beneficial effect of the present invention is as follows:
1, by experiment, wash bright and beautiful bicomponent filament yarn as the knitting cleaning cloth of raw material take tangerine lobe type, the optimised process of making is: the employing plane No. is the happy interlock machine of moral of E40, E50, woven cotton hair knot structure knitted fabric, deoil and fiber opening process through the knitting piece dyeing of optimizing again, the properties of the knitting cleaning cloth of producing is reached: open fine rate 90%, strength loss rate 1.3%, washing shrinkage 2.5%.
2, do not open fine grey cloth feel coarse, the roughly the same pure dacron product of wiping effect can not brought into play the advantage of polyamide composite filaments.For this reason, the present invention takes the method for alkali decrement to overcome the above problems.Referring to Fig. 1, Fig. 2, after opening fibre, originally be the composite fibre surface appearance fission that the tangerine flap is arranged, between lobe and lobe, the space appears, and spatial accommodation increases, and wiping properties strengthens again greatly.The present invention has captured existing cleaning wiping cloth and has opened fine irregular, the difficult problem such as shrinkage is poor, and the fine rate of opening of product of the present invention reaches 85～90%, and washing shrinkage can be controlled at ± and 2.5%.
3, compare with the production technology of present high performance wiping cloth, the present invention has removed the sanding Sand Wash Process from, saves production cost, and increases economic efficiency.
4, the cleaning wiping cloth that obtains by method of the present invention has the characteristics such as softness, moisture absorption, easy dirt-removing functions, has filled up the research blank of the fiber knitted cleaning wiping cloth of Splittable in the world.
Below the technique effect of design of the present invention, concrete technology and generation is described further so that those skilled in the art understands purpose of the present invention, feature and effect fully.
Description of drawings
Fig. 1 is the microscope picture of the cross section of polyester-nylon superthin fiber, amplifies 1000 times.
Fig. 2 is the microscope picture of the cross section after the polyester-nylon superthin fiber detaching, amplifies 1000 times, and in figure, arrow points is opened fine position.
The specific embodiment
The manufacture method of the fiber knitted cleaning wiping cloth of a kind of Splittable is washed bright and beautiful bicomponent filament yarn as raw material take tangerine lobe type, according to the fineness of Splittable superfine fibre, yam count, the index optimization yarns such as yarn twist.Tangerine lobe type is washed bright and beautiful bicomponent filament yarn dividing of 36 lobes, 24 lobes, 16 lobes, 6 lobes etc., may be used to the present invention.
The manufacture method of the fiber knitted cleaning wiping cloth of Splittable of the present invention comprises following operation:
A) weaving process; The employing plane No. is the happy interlock machine woven cotton of the moral hair knot structure knitted fabric (hereinafter to be referred as grey cloth) of E40, E50, optimizes weaving process, makes every effort to weave style smooth, the fabric of degree of tightness appropriateness; The customized parameter of concrete weaving process is as follows: line length is the 8.4-10.0cm/50 coil, linear speed 12.6-14r/min.
B) treatment process of deoiling; Carry out on overflow dyeing machine, comprise the following steps: grey cloth was immersed in 60-65 ℃ of water wetting 20-30 minute, then adding deoil yarn agent 1.5-3g/L, smooth agent 1.5-3g/L and purity is that the NaOH 0.8-1g/L of 98wt% carries out 80-95 ℃ and processes 20-45min, use again 60-80 ℃ of hot water wash 20-45min, 10-25 ℃ of cold wash 10-30min; Wherein, the water washing bath ratio is 1: 15-20, cloth speed is 180-200m/min.
C) the alkali decrement is opened fine operation; The alkali decrement is opened fine operation and is carried out on overflow dyeing machine, employing to open fine formula be 14-20g/L for the concentration of NaOH, open finely to carry out under 90-130 ℃, the time is 30-60 minute, the fast 180-220m/min of cloth, bath raio is 1: 15-20.
D) shaping process: the regulated and controled parameter of shaping process is as follows: temperature is 130-150 ℃, and overfeeding is 30%-40%, and the speed of a motor vehicle is 10-15m/min.
E) cutting matting; The cutting matting comprise the following steps: with laser type and ultrasonic wave cut, hot cutter edge sealing; And whole process is cleaned, is dried at dust free room.
Wherein, to open concrete fiber opening process condition, step, the result of fine operation as follows for alkali decrement of the present invention:
(1) sample fabric: the tangerine lobe type that Shanghai Jialinjie Textile Co., Ltd produces is washed bright and beautiful compound 60D/24F DTY interlock fabric.
(2) test sample devices: overflow dyeing machine.
(3) sample auxiliary agent: the yarn agent of deoiling is the yarn agent TF-115B that deoils available from development of evil in febrile disease Group Co.,Ltd; Smooth agent is available from smooth agent BT-44 in the bath of Shanghai Chinese Song textile technology Co., Ltd; NaOH is for analyzing pure commercial goods.
(4) method of testing:
1, weight-loss ratio: calculate according to ISO 3801-1977 " mensuration of textiles woven fabric linear mass and mass area ratio " method, at first the mass area ratio G of the fine sample of processing is not opened in weighing
0, the mass area ratio G of the sample after same method weighing is processed, then calculate weight-loss ratio Δ G as follows:
2, the strong damage: at first calculate the bursting strength of specimen according to ASTM D3786-2006 " measuring the test method of textiles rupture strength with film breaks strength-testing machine method " method, wherein, the bursting strength of not opening the fine sample of processing is A
0, open the powerful A of being of fabric after fibre is processed, then calculate as follows and damage by force Δ A:
3, washing shrinkage: according to the test of ISO 6330-2000 " home washings and the drying program that adopt during textiles _ test " method.
4, open fine rate: at first by computer microscope, the cross section of composite fibre is observed, number goes out devillicate radical N and the total radical N of fiber
0, then calculate as follows and open fine rate S:
(5) fiber opening process condition: as shown in table 1 below, wherein bath raio is 1: 20;
Table 1
| NaOH(g/L) | Temperature (℃) | Time (min) | Cloth speed (m/min) |
| 20 | 120 | 45 | 200 |
| 18 | 100 | 30 | 200 |
| 14 | 120 | 45 | 180 |
(6) fiber opening process result: as shown in table 2 below;
Table 2
Can draw to draw a conclusion according to the fiber opening process result of table 2:
When 1, the concentration of the concentration of NaOH: NaOH is in the 14-18g/L scope, weight-loss ratio, damages by force, open fine rate and increase with the increase of NaOH concentration, but after the concentration of NaOH was higher than 18g/L, opening fine rate increased not obvious.
2, temperature: the fabric weight-loss ratio increases along with the rising of temperature, but after temperature was higher than 120 ℃, opening fine rate increased also not obvious.
3, the time: in the time, weight-loss ratio increases along with the prolongation of time at 30-60min, has carried out fully but opened fibre in the time of 45 minutes.
4, cloth speed: in 180-220m/min cloth speed, strong damage and washing shrinkage increase along with the increase of cloth speed, have carried out fully but open fibre when 200m/min cloth speed.
In specific embodiments of the invention, the yarn agent of deoiling is the TF-115B of development of evil in febrile disease Group Co.,Ltd; Smooth agent is smooth agent BT-44 in the bath of Shanghai Chinese Song textile technology Co., Ltd; NaOH is the pure commercial goods of the analysis of 98wt%.
Embodiment 1
The present embodiment is the embodiment that produces 80D/36F DTY interlock fabric.
Yarn count: 80D/36F DTY dacron ultrafine fiber reaches ultra-fine fabrics Co., Ltd without Sillim and produces;
" the happy interlock machine of I3P284 moral, the happy textile machinery of German moral factory produces loom: 40G/30.
The manufacture method of the fiber knitted cleaning wiping cloth of a kind of Splittable is washed bright and beautiful bicomponent filament yarn as raw material take tangerine lobe type, comprises following operation:
A) weaving process; Raw material: 80D/36F DTY dacron ultrafine fiber." rotating speed 14r/min strictly controls bouncing pilotage, hook yarn, cross road, vertical bar, different fibre and the situation such as sneaks into loom: 40G/30 in addition for the happy interlock machine of I3P284 moral, line length 10.0cm/50 coil, adopts 8 petal-shapedly to open fine yarn.
B) treatment process of deoiling; Carry out on overflow dyeing machine, idiographic flow is: grey cloth is passed in the water of 60 ℃ after wetting 20 minutes, add the yarn agent TF-115B 2g/L that deoils, then smooth agent BT-442g/L and 98wt%NaOH 1g/L in bath process 30min (described processing refers to that grey cloth gets final product in being immersed in water) at 80 ℃, clean 30min with 70 ℃ of hot water afterwards, and 20 ℃ of cold water clean 10min, wherein, the bath raio during washing is 1: 15, and cloth speed is 200m/min.
C) the alkali decrement is opened fine operation; The alkali decrement is opened fine operation and is carried out on overflow dyeing machine, and the fine formula of opening of employing is 98wt%NaOH 16g/L, and bath raio is 1: 20, opens finely to carry out under 95 ℃, and the time is 40 minutes, and cloth speed is 200m/min.
D) shaping process; Temperature is 130 ℃, and overfeeding is 30%, and the speed of a motor vehicle is 15m/min.
E) cutting matting; At first, adopt laser type and ultrasonic wave cuts, hot cutter edge sealing; Then, adopt the 18 ultrapure water quality of megaohm, clean with dustless purpose-built washing equipment, oven dry makes product noresidue material, and reaches the highest dustless rank.This cleaning operation whole process is carried out at the class-10 dust free room, after the specialty oven dry, carries out the packing of product at packing shop, namely gets the fiber knitted cleaning wiping cloth of Splittable of the present invention.
This knitting cleaning cloth open the polyester-nylon superthin fiber before and after fine cross section the microscope picture as shown in Figure 1 and Figure 2.Its weight-loss ratio is 22% after testing, and opening fine rate is 92%, and strong the damage is 2.0%, and washing shrinkage is 2.2%.
Embodiment 2
The present embodiment is the embodiment that produces 75D/24F DTY interlock fabric.
Yarn count: 75D/24F DTY dacron ultrafine fiber reaches ultra-fine fabrics Co., Ltd without Sillim and produces;
" the happy interlock machine of I3P284 moral, the happy textile machinery of German moral factory produces loom: 40G/30.
The manufacture method of the fiber knitted cleaning wiping cloth of a kind of Splittable is washed bright and beautiful bicomponent filament yarn as raw material take tangerine lobe type, comprises following operation:
A) weaving process; Raw material: 75D/24FDTY dacron ultrafine fiber." rotating speed 14r/min strictly controls bouncing pilotage, hook yarn, cross road, vertical bar, different fibre and the situation such as sneaks into loom: 40G/30 in addition for the happy interlock machine of I3P284 moral, line length 10.0cm/50 coil, adopts 8 petal-shapedly to open fine yarn.
B) treatment process of deoiling; Carry out on overflow dyeing machine, idiographic flow is: grey cloth is passed in the water of 60 ℃ after wetting 20 minutes, add the yarn agent TF-115B 1.5g/L that deoils, smooth agent BT-441.5g/L and 98wt%NaOH 0.8g/L in bath, then process 30min (described processing refers to that grey cloth gets final product in being immersed in water) at 80 ℃, clean 30min with 60 ℃ of hot water afterwards, 10 ℃ of cold water clean 30min, cloth speed during cleaning is 180m/min, and bath raio is 1: 20.
C) the alkali decrement is opened fine operation; The alkali decrement is opened fine operation and is carried out on overflow dyeing machine, and the fine formula of opening of employing is 98wt%NaOH 14g/L, and bath raio is 1: 15, opens finely to carry out under 110 ℃, and the time is 60 minutes, and cloth speed is 180m/min.
D) shaping process: temperature is 130 ℃, and overfeeding is 30%, and the speed of a motor vehicle is 15m/min.
E) cutting matting; At first, adopt the cutting of laser type and ultrasonic wave, hot cutter edge sealing; Then, adopt the 18 ultrapure water quality of megaohm, clean with dustless purpose-built washing equipment, oven dry makes product noresidue material, and reaches the highest dustless rank.This cleaning operation whole process is carried out at the class-10 dust free room, after the specialty oven dry, carries out the packing of product at packing shop, namely gets the fiber knitted cleaning wiping cloth of Splittable of the present invention.
The weight-loss ratio of this knitting cleaning cloth is 18% after testing, and opening fine rate is 95%, and strong the damage is 1.3%, and washing shrinkage is-2.5%.
Embodiment 3
The present embodiment is the embodiment that produces 60D/24F DTY interlock fabric.
Yarn count: the 60D/24FDTY dacron ultrafine fiber reaches ultra-fine fabrics Co., Ltd without Sillim and produces;
" the happy interlock machine of I3P284 moral, the happy textile machinery of German moral factory produces loom: 50G/30.
A) weaving process; Raw material: 60D/24F DTY dacron ultrafine fiber." rotating speed 12.6r/min strictly controls bouncing pilotage, hook yarn, cross road, vertical bar, different fibre and the situation such as sneaks into loom: 50G/30 in addition for the happy interlock machine of I3P284 moral, line length 8.4cm/50 coil, adopts 8 petal-shapedly to open fine yarn.
B) treatment process of deoiling; Carry out on overflow dyeing machine, idiographic flow is: grey cloth is passed in the water of 60 ℃ after wetting 20 minutes, add the yarn agent TF-115B 3g/L that deoils, smooth agent BT-443g/L and 98wt%NaOH 1g/L in bath, then process 30min (described processing refers to that grey cloth gets final product in being immersed in water) at 95 ℃, clean 30min with 60 ℃ of hot water afterwards, and 10 ℃ of cold water clean 30min, wherein the water washing bath ratio is 1: 15, and cloth speed is 180m/min.
C) the alkali decrement is opened fine operation; The alkali decrement is opened fine operation and is carried out on overflow dyeing machine, and the fine formula of opening of employing is 98wt%NaOH 20g/L, and bath raio is 1: 20, opens finely to carry out under 130 ℃, and the time is 30 minutes, and cloth speed is 200m/min.
D) shaping process: temperature is 130 ℃, and overfeeding is 30%, and the speed of a motor vehicle is 15m/min.
E) cutting matting; At first, adopt laser type and ultrasonic wave cuts, hot cutter edge sealing; Then, adopt the 18 ultrapure water quality of megaohm, clean with dustless purpose-built washing equipment, oven dry makes product noresidue material, and reaches the highest dustless rank.This cleaning operation whole process is carried out at the class-10 dust free room, after the specialty oven dry, carries out the packing of product at packing shop, namely gets and cuts apart the fiber type knitting cleaning cloth.
The weight-loss ratio of this knitting cleaning cloth is 28% after testing, and opening fine rate is 95%, and strong the damage is 3.5%, and washing shrinkage is-2.5%.
More than describe preferred embodiment of the present invention in detail.The ordinary skill that should be appreciated that this area need not creative work and just can design according to the present invention make many modifications and variations.Therefore, all technical staff in the art all should be in the determined protection domain by claims under this invention's idea on the basis of existing technology by the available technical scheme of logical analysis, reasoning, or a limited experiment.
Claims (7)
1. the manufacture method of the fiber knitted cleaning wiping cloth of Splittable, is characterized in that, washs bright and beautiful bicomponent filament yarn as raw material take tangerine lobe type, comprises following operation:
A) weaving process;
B) treatment process of deoiling;
C) the alkali decrement is opened fine operation;
D) shaping process;
E) cutting matting.
2. the manufacture method of the fiber knitted cleaning wiping cloth of Splittable as claimed in claim 1, is characterized in that, the parameter of described weaving process is as follows: line length is the 8.4-10.0cm/50 coil, and linear speed is 12.6-14r/min; It is the happy interlock machine of moral of E40 or E50 that described weaving process adopts plane No..
3. the manufacture method of the fiber knitted cleaning wiping cloth of Splittable as claimed in claim 1, it is characterized in that, the described treatment process of deoiling is carried out on overflow dyeing machine, comprise the following steps: grey cloth was immersed in 60-65 ℃ of water wetting 20-30 minute, after adding deoil yarn agent 1.5-3g/L, smooth agent 1.5-3g/L, NaOH 0.8-1g/L, process 20-45min for 80-95 ℃, then 60-80 ℃ of hot water wash 20-45min, 10-25 ℃ of cold wash 10-30min, wherein the water washing bath ratio is 1: 15-20, cloth speed is 180-200m/min.
4. the manufacture method of the fiber knitted cleaning wiping cloth of Splittable as claimed in claim 1, it is characterized in that, described alkali decrement is opened fine operation and is carried out on overflow dyeing machine, wherein, open fibre and carry out under 90-130 ℃, the time is 30-60 minute, and bath raio is 1: 15-20, cloth speed is 180-220m/min, and the concentration of the NaOH of employing is 14-20g/L.
5. the manufacture method of the fiber knitted cleaning wiping cloth of Splittable as claimed in claim 4, is characterized in that, the described fibre of opening carries out under 90-120 ℃, time is 30-45 minute; bath raio is 1: 15-20, and cloth speed is 180-200m/min, the concentration of the NaOH of employing is 14-18g/L.
6. the manufacture method of the fiber knitted cleaning wiping cloth of Splittable as claimed in claim 1, is characterized in that, the parameter of described shaping process is as follows: temperature is 130-150 ℃, and overfeeding is 30-40%, and the speed of a motor vehicle is 10-15m/min.
7. the manufacture method of the fiber knitted cleaning wiping cloth of Splittable as claimed in claim 1, is characterized in that, the step of described cutting matting comprises with the cutting of laser type and ultrasonic wave, hot cutter edge sealing; And dustless cleaning, drying.