CN107723967A - The dyeing and finishing processing method of T/R spandex four-side elasticity fabrics - Google Patents

The dyeing and finishing processing method of T/R spandex four-side elasticity fabrics Download PDF

Info

Publication number
CN107723967A
CN107723967A CN201711049716.0A CN201711049716A CN107723967A CN 107723967 A CN107723967 A CN 107723967A CN 201711049716 A CN201711049716 A CN 201711049716A CN 107723967 A CN107723967 A CN 107723967A
Authority
CN
China
Prior art keywords
dyeing
processing method
spandexs
finishing processing
side elasticity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201711049716.0A
Other languages
Chinese (zh)
Other versions
CN107723967B (en
Inventor
徐继盛
武光信
王洪明
唐凯
王红玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG WOYUAN NEW FASHIONED FABRIC CO Ltd
Original Assignee
SHANDONG WOYUAN NEW FASHIONED FABRIC CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG WOYUAN NEW FASHIONED FABRIC CO Ltd filed Critical SHANDONG WOYUAN NEW FASHIONED FABRIC CO Ltd
Priority to CN201711049716.0A priority Critical patent/CN107723967B/en
Publication of CN107723967A publication Critical patent/CN107723967A/en
Application granted granted Critical
Publication of CN107723967B publication Critical patent/CN107723967B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of dyeing and finishing processing method of fabric, and in particular to a kind of dyeing and finishing processing method of T/R spandexs four-side elasticity fabric.Described production technology, step are as follows:Allocate → dye jigger pre-treatment → mistake water drying → HTHP overflow dyeing machine kiering → pre-setting → singe → dyeing → dry → auxiliary agent sizing → decatizing → mistake water is shaped → examines clot to pack.The T/R spandex face fabrics produced by production technology of the present invention have the characteristics that:Soft, elasticity is good, and fabric is fluffy, fabric excellent size stability;The effective retraction problems for avoiding T/R spandex fabrics, make cloth cover more smooth bright and clean, substantially improve the pyrocondensation of fabric and wash the problem of shrinkage is big.

Description

The dyeing and finishing processing method of T/R spandex four-side elasticity fabrics
Technical field
The present invention relates to a kind of dyeing and finishing processing method of fabric, and in particular to a kind of dyeing and finishing of T/R spandexs four-side elasticity fabric Processing method.
Background technology
As living standard constantly improves, people are also more and more various for the fabric Functional Requirement of dress ornament.For Only there was only traditional water clothes of thermal effect, its too fat to move burden, the style of shortage new meaning have been difficult to meet consumer's Consumption concept, the common people, which more thirst for novel great-hearted new product fabric, to be occurred.Nowadays, the at home and abroad city of the fabric containing elastic polyurethane fiber All the fashion on field, this kind of product has higher shrinkage and excellent resilience, soft, comfortable and easy to wear and can appear Go out pretty figure, plus easy absorbing sweat, the reasons such as electrostatic will not be produced, it is commercially had very big advantage always.
The production technology of T/R spandex four-side elasticity fabrics, is the production that high value added product is turned to from conventional products, T/R ammonia Synthetic fibre stockinette market development potential is larger.Exist because the content of elastic polyurethane fiber yarn is typically less, and with the structure of covering yarn, Good contraction is difficult to obtain in the larger production procedure of tension force, causes the fabric elastic force produced little.This problem into Problem in production, in order to solve this problem, fabric is set to obtain good elasticity, a kind of processing method for finding such product is come Solve the above problems and be particularly important.
The content of the invention
In view of the shortcomings of the prior art, it is an object of the invention to provide a kind of dyeing and finishing of T/R spandexs four-side elasticity fabric processing Method, solve prior art in T/R spandex four-side elasticity fabric dyeing and finishing process because of tension force is big and occurs elastic small, feel The problem of plate, the fabric power of organization of production is strong, elastic good, dimensionally stable, the fluffy softness of feel.
Technical scheme of the invention for the use that solves the above problems, step are as follows:Allocate → dye jigger pre-treatment → mistake water Drying → HTHP overflow dyeing machine kiering → pre-setting → singe → dyeing → dry → auxiliary agent sizing → decatizing → mistake water Sizing → inspection clot packaging.
The dyeing and finishing processing method of T/R spandexs four-side elasticity fabric of the present invention, is comprised the following steps that:
(1) 800-1200 rice is allocated per cylinder;
(2) dye jigger pre-treatment:Using soda ash, degreaser to fabric carrying out washing treatment;
(3) water drying is crossed;
(4) HTHP overflow dyeing machine kiering:Use soda ash, refining agent processing;
(5) pre-setting:170-190 DEG C of temperature, speed 30-50m/min, overfeeding 10%;
(6) singe:Singed method using two forward one-reverses or a positive and a negative, speed of singing 24-30Hz;
(7) dye:Using disperse dyes and reactive dye respectively to fabric ingrain;
(8) dry:150 DEG C, speed 50-70m/min of temperature, overfeeding 10%;
(9) auxiliary agent is shaped:160-180 DEG C of temperature, speed 40-60m/min, softening agent 20-40g/L;
(10) decatizing:Steam pressure is 0.6bar, from inside to outside 60s, outside to inside 90s, takes out cool time 150s;
(11) water sizing is crossed:130-150 DEG C of temperature, speed 30-50m/min, overfeeding 5%;
(12) clot packaging is examined.
Wherein:
The concentration of soda ash described in step (2) is 5g/L.
Degreaser described in step (2) is spirit 101 of deoiling.Described degreaser alkali resistance, high temperature resistant.
The concentration of degreaser described in step (2) is 5g/L.
Described in step (3) cross water drying condition be:140-160 DEG C of temperature, padding machine pressure 3.0bar, speed 30- 50m/min。
The concentration of soda ash described in step (4) is 1.5g/L.
Refining agent described in step (4) is the refining degreaser DR-N6 of Zibo Dan Rui industrial and trading companies production.Described refining Agent alkali resistance, high temperature resistant, cleaning function are strong.
The concentration of refining agent described in step (4) is 1g/L.
Softening agent described in step (9) stands for highly concentrated the softening agent DR-69A and Jiangsu lattice of the production of Zibo Dan Rui industrial and trading companies The refreshing bullet finishing agent 1472 of special auxiliary agent company production.
The concentration of described refreshing bullet finishing agent 1472 is 10g/L, and highly concentrated softening agent DR-69A concentration is 10g/L.
Compared with prior art, the invention has the advantages that:
1st, the T/R spandex face fabrics produced by production technology of the present invention have the characteristics that:It is soft, elasticity Good, fabric is fluffy, fabric excellent size stability.
2nd, due to the characteristic of spandex, to there is wrinkle strip phenomenon when preventing HTHP overflow dyeing machine kiering, in preceding processing Before increased water drying it is most important, can effectively prevent the quality problems caused by contraction.
3rd, this technique effectively avoids the retraction problems of T/R spandex fabrics, makes cloth cover more smooth bright and clean, substantially improves The problem of pyrocondensation of fabric and washing shrinkage big.
Embodiment
With reference to embodiment, the present invention will be further described, but does not limit the present invention.
All raw materials used in embodiment are purchased in market unless otherwise specified.
Experiment material, experimental facilities and the test medicine used in embodiment is as follows:
Experiment material:
The T/R spandexs four-side elasticity fabric used is glued as 32 sun using warp-wise and glued with the twisting of 40D spandex threads and 32 sun of broadwise It is raw material to be twisted with 75DDTY and 40D spandexs, grammes per square metre 338g/m2, door width 180cm.
Experimental facilities:
Dye jigger, forming machine, gassing frame, HTHP overflow dyeing machine, tank steam machine, coiler.
Test medicine:
Soda ash, refining agent, degreaser, disperse dyes, reactive dye, water softener, glacial acetic acid, glauber salt, high temperature levelling agent, Soaping agent 535, softening agent.
Described degreaser is spirit 101 of deoiling.
Described refining agent is the refining degreaser DR-N6 of Zibo Dan Rui industrial and trading companies production.
Described softening agent is the highly concentrated softening agent DR-69A and Jiangsu Ge Lite auxiliary agents of Zibo Dan Rui industrial and trading companies production The refreshing bullet finishing agent 1472 of company's production.
Embodiment 1
The dyeing and finishing processing method of described T/R spandex four-side elasticity fabrics, is comprised the following steps that:
(1) allocate:950 meters of meter number is allocated per cylinder.
(2) dye jigger pre-treatment:Soda ash 5g/L, degreaser 5g/L, 95 DEG C of insulation 60min.Cloth feeding is smooth, and winding is closely knit.
(3) water drying is crossed:150 DEG C of temperature, padding machine pressure 3.0bar, speed 40m/min, cropping door width 165cm.
(4) HTHP overflow dyeing machine kiering:Soda ash 1.5g/L, refining agent 1g/L, 120 DEG C of temperature, processing time 30min。
(5) pre-setting:180 DEG C, speed 40m/min of temperature, overfeeding 10%, cropping door width 155cm.
(6) singe:Singed method using a positive and a negative according to cloth cover situation, speed of singing 26Hz.
(7) dye:
Dispersion dyeing technology preparation is:
Disperse blue F-L 2.1%
Disperse orange F-C 0.42%
Disperse red F-H 0.1%
Glacial acetic acid 0.8g/L
Levelling agent 1g/L
Water softener 1g/L
Process conditions:130℃×40min;
Activity staining procedure prescription:
Process conditions:60℃×40min+95℃×30min.
(8) dry:150 DEG C, speed 60m/min of temperature, overfeeding 10%.
(9) auxiliary agent is shaped:160 DEG C, speed 45m/min of temperature, the 10g/L of softening agent 1472, softening agent 69A 10g/L, falls Cloth door width 152cm.
(10) decatizing:Steam pressure P is 0.6bar, from inside to outside 60s, and 90s, takes out cool time 150s outside to inside.
(11) water sizing is crossed:130 DEG C, speed 40m/min of temperature, overfeeding 5%, cropping door width 150cm.
(12) clot packaging is examined.
Embodiment 2
The dyeing and finishing processing method of described T/R spandex four-side elasticity fabrics, is comprised the following steps that:
(1) 1200 meters are allocated per cylinder;
(2) dye jigger pre-treatment:Soda ash 5g/L, degreaser 5g/L, 95 DEG C of insulation 60min.Cloth feeding is smooth, and winding is closely knit.
(3) water drying is crossed:160 DEG C of temperature, padding machine pressure 3.0bar, speed 50m/min, cropping door width 165cm.
(4) HTHP overflow dyeing machine kiering:Soda ash 1.5g/L, refining agent 1g/L, 120 DEG C of temperature, processing time 30min。
(5) pre-setting:170 DEG C, speed 30m/min of temperature, overfeeding 10%;
(6) singe:Singed method using two forward one-reverses, speed of singing 30Hz;
(7) dye:Using disperse dyes and reactive dye respectively to fabric ingrain;
Dyeing prescription and process conditions are the same as embodiment 1.
(8) dry:150 DEG C, speed 50m/min of temperature, overfeeding 10%;
(9) auxiliary agent is shaped:170 DEG C, speed 60m/min of temperature, softening agent 1472 20g/L, softening agent 69A 20g/L;
(10) decatizing:Steam pressure is 0.6bar, from inside to outside 60s, outside to inside 90s, takes out cool time 150s;
(11) water sizing is crossed:140 DEG C, speed 30m/min of temperature, overfeeding 5%;
(12) clot packaging is examined.
Embodiment 3
The dyeing and finishing processing method of described T/R spandex four-side elasticity fabrics, is comprised the following steps that:
(1) 800 meters are allocated per cylinder;
(2) dye jigger pre-treatment:Soda ash 5g/L, degreaser 5g/L, 95 DEG C of insulation 60min.Cloth feeding is smooth, and winding is closely knit.
(3) water drying is crossed:140 DEG C of temperature, padding machine pressure 3.0bar, speed 50m/min, cropping door width 165cm;
(4) HTHP overflow dyeing machine kiering:Use soda ash, refining agent processing;
(5) pre-setting:190 DEG C, speed 50m/min of temperature, overfeeding 10%;
(6) singe:Singed method using a positive and a negative, speed of singing 24Hz;
(7) dye:Using disperse dyes and reactive dye respectively to fabric ingrain;
Dyeing prescription and process conditions are the same as embodiment 1.
(8) dry:150 DEG C, speed 70m/min of temperature, overfeeding 10%;
(9) auxiliary agent is shaped:180 DEG C, speed 60m/min of temperature, softening agent 1472 15g/L, softening agent 69A 15g/L;
(10) decatizing:Steam pressure is 0.6bar, from inside to outside 60s, outside to inside 90s, takes out cool time 150s;
(11) water sizing is crossed:150 DEG C, speed 50m/min of temperature, overfeeding 5%;
(12) clot packaging is examined.
Comparative example 1
Described production technology, is comprised the following steps that:
The dyeing and finishing processing method of described T/R spandex four-side elasticity fabrics, is comprised the following steps that:
(1) allocate:950 meters of meter number is allocated per cylinder.
(2) HTHP overflow dyeing machine kiering:Soda ash 1.5g/L, refining agent 1g/L, 120 DEG C of temperature, processing time 30min。
(3) pre-setting:180 DEG C, speed 40m/min of temperature, overfeeding 10%, cropping door width 155cm.
(4) singe:Singed method using a positive and a negative according to cloth cover situation, speed of singing 26Hz.
(5) dye:
Dispersion dyeing technology preparation is:
Disperse blue F-L 2.1%
Disperse orange F-C 0.42%
Disperse red F-H 0.1%
Glacial acetic acid 0.8g/L
Levelling agent 1g/L
Water softener 1g/L
Process conditions:130℃×40min;
Activity staining procedure prescription:
Process conditions:60℃×40min+95℃×30min.
(6) dry:150 DEG C, speed 60m/min of temperature, overfeeding 10%.
(7) auxiliary agent is shaped:160 DEG C, speed 45m/min of temperature, the 10g/L of softening agent 1472, softening agent 69A10g/L, falls Cloth door width 152cm.
(8) decatizing:Steam pressure P is 0.6bar, from inside to outside 60s, and 90s, takes out cool time 150s outside to inside.
(9) water sizing is crossed:130 DEG C, speed 40m/min of temperature, overfeeding 5%, cropping door width 150cm.
(10) clot packaging is examined.
Performance test is carried out to embodiment 1-3 and the product of comparative example 1, test event is as follows, and test result is shown in Table 1:
Fastness to wet rubbing, with reference to GB/T3920-2008《Textile color stability tests colour fastness to rubbing》Measure, with evaluation Change colour gray card grading.
Washing fastness, by GB/3921.3《Textile color stability tests color fastness to washing:Experiment 3》Evaluation, changed colour with evaluation Graded with gray card.
Ultimate strength, according to GB/T3923.1-1997《Low 1 portion fractures of textile fabric tensile property and extension at break The measure of rate》.
The test result of table 1
Fastness to wet rubbing Washing fastness Ultimate strength
Embodiment 1 3 grades 4 grades 948N
Embodiment 2 2-3 levels 3-4 levels 926N
Embodiment 3 2-3 levels 4 grades 946N
Comparative example 1 2 grades 3 grades 890N

Claims (10)

  1. A kind of 1. dyeing and finishing processing method of T/R spandexs four-side elasticity fabric, it is characterised in that:Comprise the following steps that:
    (1) 800-1200 rice is allocated per cylinder;
    (2) dye jigger pre-treatment:Using soda ash, degreaser to fabric carrying out washing treatment;
    (3) water drying is crossed;
    (4) HTHP overflow dyeing machine kiering:Use soda ash, refining agent processing;
    (5) pre-setting:170-190 DEG C of temperature, speed 30-50m/min, overfeeding 10%;
    (6) singe:Singed method using two forward one-reverses or a positive and a negative, speed of singing 24-30Hz;
    (7) dye:Using disperse dyes and reactive dye respectively to fabric ingrain;
    (8) dry:150 DEG C, speed 50-70m/min of temperature, overfeeding 10%;
    (9) auxiliary agent is shaped:160-180 DEG C of temperature, speed 40-60m/min, softening agent 20-40g/L;
    (10) decatizing:Steam pressure is 0.6bar, from inside to outside 60s, outside to inside 90s, takes out cool time 150s;
    (11) water sizing is crossed:130-150 DEG C of temperature, speed 30-50m/min, overfeeding 5%;
    (12) clot packaging is examined.
  2. 2. the dyeing and finishing processing method of T/R spandexs four-side elasticity fabric according to claim 1, it is characterised in that:Step (2) institute The concentration for the soda ash stated is 5g/L.
  3. 3. the dyeing and finishing processing method of T/R spandexs four-side elasticity fabric according to claim 1, it is characterised in that:Step (2) institute The degreaser stated is spirit 101 of deoiling.
  4. 4. the dyeing and finishing processing method of T/R spandexs four-side elasticity fabric according to claim 1, it is characterised in that:Step (2) institute The concentration for the degreaser stated is 5g/L.
  5. 5. the dyeing and finishing processing method of T/R spandexs four-side elasticity fabric according to claim 1, it is characterised in that:Step (3) institute That states, which crosses the condition of water drying, is:140-160 DEG C of temperature, padding machine pressure 3.0bar, speed 30-50m/min.
  6. 6. the dyeing and finishing processing method of T/R spandexs four-side elasticity fabric according to claim 1, it is characterised in that:Step (4) institute The concentration for the soda ash stated is 1.5g/L.
  7. 7. the dyeing and finishing processing method of T/R spandexs four-side elasticity fabric according to claim 1, it is characterised in that:Step (4) institute The refining agent stated is DR-N6.
  8. 8. the dyeing and finishing processing method of T/R spandexs four-side elasticity fabric according to claim 1, it is characterised in that:Step (4) institute The concentration for the refining agent stated is 1g/L.
  9. 9. the dyeing and finishing processing method of T/R spandexs four-side elasticity fabric according to claim 1, it is characterised in that:Step (9) institute The softening agent stated is highly concentrated softening agent DR-69A and refreshing bullet finishing agent 1472.
  10. 10. the dyeing and finishing processing method of T/R spandexs four-side elasticity fabric according to claim 9, it is characterised in that:Described is refreshing The concentration for playing finishing agent 1472 is 10g/L, and highly concentrated softening agent DR-69A concentration is 10g/L.
CN201711049716.0A 2017-10-31 2017-10-31 Dyeing and finishing processing method of T/R spandex four-side stretch fabric Active CN107723967B (en)