CN107503132A - A kind of method for being knitted fabric post processing - Google Patents
A kind of method for being knitted fabric post processing Download PDFInfo
- Publication number
- CN107503132A CN107503132A CN201710810002.0A CN201710810002A CN107503132A CN 107503132 A CN107503132 A CN 107503132A CN 201710810002 A CN201710810002 A CN 201710810002A CN 107503132 A CN107503132 A CN 107503132A
- Authority
- CN
- China
- Prior art keywords
- parts
- knitting fabric
- pretreatment liquid
- aftertreatment fluid
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of method for being knitted fabric post processing, including following operating procedure：（1）Knitting fabric is put into pretreatment liquid after the 80min of immersion treatment 60, takes out, pretreatment liquid is cleaned with clear water；（2）Knitting fabric is put into aftertreatment fluid, immersion treatment 35 hours；（3）Step will be passed through（2）After the knitting fabric of processing uses the 40min of ultrasonication 30, using oven for drying, it is then placed in 170 180 DEG C of baking oven, bakes sizing, finished product.The method of knitting fabric post processing provided by the invention, simple to operate, green, obtained knitting fabric, pliability is good, and crock fastness is high, especially after repeatedly washing, still has preferably elasticity, greatly improves the quality of knitting fabric.
Description
Technical field
The invention belongs to be knitted fabric preparing technical field, and in particular to a kind of method for being knitted fabric post processing.
Background technology
It is that the fabric being formed by connecting mutually is worn by coil to be knitted fabric, is a big kind of fabric.Knitting fabric has
Preferably elasticity, moisture absorption are breathed freely, comfortable warming, are the most popular fabrics of children's garment, and raw material is mainly that linen-cotton silk hair etc. is natural
Fiber, also there is the change of the chemical fibre such as polyamide fibre, acrylic fibers, terylene knitted fabric tissue to enrich, various in style, outward appearance does not have feature, mistake
Go to be used for underwear, T-shirt etc., now, with the development of hosiery trade and the birth of new finishing technique, the taking of knitted fabric
Can greatly it take on a new look.But knitting fabric is during use, still there is multiple washing after, its pliability, elasticity can be tight
The phenomenon declined again, cause the service life for being knitted fabric shorter.
The content of the invention
In order to solve the above-mentioned technical problem, the present invention provides a kind of method for being knitted fabric post processing.
The present invention is achieved by the following technical solutions.
A kind of method for being knitted fabric post processing, including following operating procedure：
（1）Knitting fabric is put into pretreatment liquid after immersion treatment 60-80min, takes out, pretreatment liquid is cleaned with clear water, its
Middle pretreatment liquid is made up of the component of following parts by weight：Methylpropene sodium sulfonate 9-13 parts, 1,2- 1,2-diaminocyclohexane tetraacetic acids 6-12
Part, sodium phosphate 18-23 parts, water 250-300 parts；
（2）Will knitting fabric be put into aftertreatment fluid, immersion treatment 3-5 hours, wherein aftertreatment fluid by following parts by weight group
Divide and be made：Lauryl amine 12-19 parts, bromoacetaldehyde condensed ethandiol 14-20 parts, methyl Adipoyl Chloride 10-15 parts, sodium hexafluoro phosphate 7-
12 parts, 3- oxo octanoic acid glyceride 11-16 parts, ethyl acetate 200-250 parts；
（3）Step will be passed through（2）After the knitting fabric of processing uses ultrasonication 30-40min, using oven for drying, then
It is put into 170-180 DEG C of baking oven, bakes sizing, finished product.
Specifically, above-mentioned steps（1）Temperature during middle pretreatment liquid immersion is 45-50 DEG C.
Specifically, above-mentioned aftertreatment fluid is made of following methods：Respectively by lauryl amine, bromoacetaldehyde condensed ethandiol, first
Base Adipoyl Chloride, sodium hexafluoro phosphate, 3- oxo octanoic acid glyceride are added into ethyl acetate, are continued using 300r/min rotating speed
Stirring, feeding interval 2min, after the completion of charging, continue after stirring 10min, aftertreatment fluid is made.
Specifically, above-mentioned steps（3）During middle ultrasonication, the frequency of ultrasonic wave is 32-35kHz.
Specifically, above-mentioned steps（3）In, the temperature of oven for drying processing is 88-95 DEG C, and the time of drying and processing is 140-
160min。
Technical scheme more than, the beneficial effects of the invention are as follows：
The method of knitting fabric post processing provided by the invention, simple to operate, green, obtained knitting fabric, pliability
Good, crock fastness is high, especially after repeatedly washing, still has preferably elasticity, greatly improves knitting fabric
Quality.Wherein, pretreatment liquid provided by the invention, can effectively remove the greasy dirt that may be infected with knitting fabric, and and can has
The permeability of the lift pins knitted fabric of effect, and then improve the action effect of aftertreatment fluid；Aftertreatment fluid provided by the invention, can
The water soak resistance energy of effective lift pins knitted fabric so that knitting fabric is after repeatedly washing, still with excellent elasticity
And pliability, greatly extend the quality for being knitted fabric.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, following examples are carried out to the present invention
It is further described.It should be appreciated that specific embodiment party example described herein is not used to limit only to explain the present invention
The fixed present invention.
Embodiment 1
A kind of method for being knitted fabric post processing, including following operating procedure：
（1）Knitting fabric is put into pretreatment liquid after immersion treatment 60min, takes out, pretreatment liquid is cleaned with clear water, wherein before
Treatment fluid is made up of the component of following parts by weight：9 parts of methylpropene sodium sulfonate, 6 parts of 1,2- 1,2-diaminocyclohexane tetraacetic acids, sodium phosphate 18
Part, 250 parts of water；
（2）Will knitting fabric be put into aftertreatment fluid, immersion treatment 3 hours, wherein aftertreatment fluid by following parts by weight component
It is made：12 parts of lauryl amine, 14 parts of bromoacetaldehyde condensed ethandiol, 10 parts of methyl Adipoyl Chloride, 7 parts of sodium hexafluoro phosphate, 3- oxos are pungent
11 parts of acid glyceride, 200 parts of ethyl acetate；
（3）Step will be passed through（2）After the knitting fabric of processing uses ultrasonication 30min, using oven for drying, it is then placed in
In 170 DEG C of baking oven, sizing, finished product are baked.
Specifically, above-mentioned steps（1）Temperature during middle pretreatment liquid immersion is 45 DEG C.
Specifically, above-mentioned aftertreatment fluid is made of following methods：Respectively by lauryl amine, bromoacetaldehyde condensed ethandiol, first
Base Adipoyl Chloride, sodium hexafluoro phosphate, 3- oxo octanoic acid glyceride are added into ethyl acetate, are continued using 300r/min rotating speed
Stirring, feeding interval 2min, after the completion of charging, continue after stirring 10min, aftertreatment fluid is made.
Specifically, above-mentioned steps（3）During middle ultrasonication, the frequency of ultrasonic wave is 32kHz.
Specifically, above-mentioned steps（3）In, the temperature of oven for drying processing is 88 DEG C, and the time of drying and processing is 140min.
Embodiment 2
A kind of method for being knitted fabric post processing, including following operating procedure：
（1）Knitting fabric is put into pretreatment liquid after immersion treatment 70min, takes out, pretreatment liquid is cleaned with clear water, wherein before
Treatment fluid is made up of the component of following parts by weight：11 parts of methylpropene sodium sulfonate, 8 parts of 1,2- 1,2-diaminocyclohexane tetraacetic acids, sodium phosphate
20 parts, 280 parts of water；
（2）Will knitting fabric be put into aftertreatment fluid, immersion treatment 4 hours, wherein aftertreatment fluid by following parts by weight component
It is made：15 parts of lauryl amine, 16 parts of bromoacetaldehyde condensed ethandiol, 13 parts of methyl Adipoyl Chloride, 10 parts of sodium hexafluoro phosphate, 3- oxos are pungent
13 parts of acid glyceride, 230 parts of ethyl acetate；
（3）Step will be passed through（2）After the knitting fabric of processing uses ultrasonication 35min, using oven for drying, it is then placed in
In 175 DEG C of baking oven, sizing, finished product are baked.
Specifically, above-mentioned steps（1）Temperature during middle pretreatment liquid immersion is 48 DEG C.
Specifically, above-mentioned aftertreatment fluid is made of following methods：Respectively by lauryl amine, bromoacetaldehyde condensed ethandiol, first
Base Adipoyl Chloride, sodium hexafluoro phosphate, 3- oxo octanoic acid glyceride are added into ethyl acetate, are continued using 300r/min rotating speed
Stirring, feeding interval 2min, after the completion of charging, continue after stirring 10min, aftertreatment fluid is made.
Specifically, above-mentioned steps（3）During middle ultrasonication, the frequency of ultrasonic wave is 34kHz.
Specifically, above-mentioned steps（3）In, the temperature of oven for drying processing is 90 DEG C, and the time of drying and processing is 150min.
Embodiment 3
A kind of method for being knitted fabric post processing, including following operating procedure：
（1）Knitting fabric is put into pretreatment liquid after immersion treatment 80min, takes out, pretreatment liquid is cleaned with clear water, wherein before
Treatment fluid is made up of the component of following parts by weight：13 parts of methylpropene sodium sulfonate, 12 parts of 1,2- 1,2-diaminocyclohexane tetraacetic acids, sodium phosphate
23 parts, 300 parts of water；
（2）Will knitting fabric be put into aftertreatment fluid, immersion treatment 5 hours, wherein aftertreatment fluid by following parts by weight component
It is made：19 parts of lauryl amine, 20 parts of bromoacetaldehyde condensed ethandiol, 15 parts of methyl Adipoyl Chloride, 12 parts of sodium hexafluoro phosphate, 3- oxos are pungent
16 parts of acid glyceride, 250 parts of ethyl acetate；
（3）Step will be passed through（2）After the knitting fabric of processing uses ultrasonication 40min, using oven for drying, it is then placed in
In 180 DEG C of baking oven, sizing, finished product are baked.
Specifically, above-mentioned steps（1）Temperature during middle pretreatment liquid immersion is 50 DEG C.
Specifically, above-mentioned aftertreatment fluid is made of following methods：Respectively by lauryl amine, bromoacetaldehyde condensed ethandiol, first
Base Adipoyl Chloride, sodium hexafluoro phosphate, 3- oxo octanoic acid glyceride are added into ethyl acetate, are continued using 300r/min rotating speed
Stirring, feeding interval 2min, after the completion of charging, continue after stirring 10min, aftertreatment fluid is made.
Specifically, above-mentioned steps（3）During middle ultrasonication, the frequency of ultrasonic wave is 35kHz.
Specifically, above-mentioned steps（3）In, the temperature of oven for drying processing is 95 DEG C, and the time of drying and processing is 160min.
Knitting fabric is made with each embodiment respectively, then chooses the commercially available common knitting with phase same material in embodiment
Fabric, puts it into water after soaking 7 days, carries out elastic recovery test to it using electronic fabric strength tester, stretches
Long rate=(extended length-original length)/original length × 100%, response rate=(extended length-reply length)/(extended length-
Original length) × 100%, test result is as shown in table 1：
Table 1 is knitted fabric elasticity performance test
| Project | Elongation, %（Radially） | Response rate, %（Radially） |
| Embodiment 1 | 43.7 | 98.4 |
| Embodiment 2 | 44.1 | 99.1 |
| Embodiment 3 | 44.9 | 99.3 |
| Control group | 29.5 | 88.4 |
As shown in Table 1, knitting fabric produced by the present invention, after being soaked for a long time in water, still there is higher elasticity, explanation
The water resistance for being knitted fabric is excellent.
It should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted.Although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the technology of invention
Scheme is modified or equivalent substitution, and without departing from the scope of technical solution of the present invention, it all should cover the power in the present invention
In sharp claimed range.
Claims (5)
- A kind of 1. method for being knitted fabric post processing, it is characterised in that including following operating procedure：（1）Knitting fabric is put into pretreatment liquid after immersion treatment 60-80min, takes out, pretreatment liquid is cleaned with clear water, its Middle pretreatment liquid is made up of the component of following parts by weight：Methylpropene sodium sulfonate 9-13 parts, 1,2- 1,2-diaminocyclohexane tetraacetic acids 6-12 Part, sodium phosphate 18-23 parts, water 250-300 parts；（2）Will knitting fabric be put into aftertreatment fluid, immersion treatment 3-5 hours, wherein aftertreatment fluid by following parts by weight group Divide and be made：Lauryl amine 12-19 parts, bromoacetaldehyde condensed ethandiol 14-20 parts, methyl Adipoyl Chloride 10-15 parts, sodium hexafluoro phosphate 7- 12 parts, 3- oxo octanoic acid glyceride 11-16 parts, ethyl acetate 200-250 parts；（3）Step will be passed through（2）After the knitting fabric of processing uses ultrasonication 30-40min, using oven for drying, then It is put into 170-180 DEG C of baking oven, bakes sizing, finished product.
- 2. the method post-processed according to a kind of knitting fabric described in claim 1, it is characterised in that above-mentioned steps（1）In Temperature when pretreatment liquid soaks is 45-50 DEG C.
- 3. the method post-processed according to a kind of knitting fabric described in claim 1, it is characterised in that above-mentioned aftertreatment fluid is adopted It is made using the following method：It is respectively that lauryl amine, bromoacetaldehyde condensed ethandiol, methyl Adipoyl Chloride, sodium hexafluoro phosphate, 3- oxos is pungent Acid glyceride is added into ethyl acetate, is persistently stirred using 300r/min rotating speed, feeding interval 2min, and charging is completed Afterwards, continue after stirring 10min, aftertreatment fluid is made.
- 4. the method post-processed according to a kind of knitting fabric described in claim 1, it is characterised in that above-mentioned steps（3）In During ultrasonication, the frequency of ultrasonic wave is 32-35kHz.
- 5. the method post-processed according to a kind of knitting fabric described in claim 1, it is characterised in that above-mentioned steps（3）In, The temperature of oven for drying processing is 88-95 DEG C, and the time of drying and processing is 140-160min.