CN103073295A - Er3+和Tm3+共掺的氧化镧钇闪烁透明陶瓷材料的制备方法 - Google Patents
Er3+和Tm3+共掺的氧化镧钇闪烁透明陶瓷材料的制备方法 Download PDFInfo
- Publication number
- CN103073295A CN103073295A CN2013100165688A CN201310016568A CN103073295A CN 103073295 A CN103073295 A CN 103073295A CN 2013100165688 A CN2013100165688 A CN 2013100165688A CN 201310016568 A CN201310016568 A CN 201310016568A CN 103073295 A CN103073295 A CN 103073295A
- Authority
- CN
- China
- Prior art keywords
- powder
- ball
- milling
- ceramic material
- sintering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种Er3+和Tm3+共掺的氧化镧钇闪烁透明陶瓷材料的制备方法,属特种陶瓷制造工艺技术领域。本发明采用高纯Y2O3,Er2O3,Tm2O3,La2O3粉体为原料,采用传统陶瓷制备工艺在较低的温度条件下,通过合适的烧结制度,固相烧结法制备了Er3+-Tm3+共掺后的氧化镧钇透明陶瓷材料。经实验测定,添加Tm3+离子后,Er3+/Tm3+共掺氧化镧钇透明陶瓷可以获得更强的2.7um发光。因此,Er3+和Tm3+共掺氧化镧钇透明陶瓷材料在3um激光领域有着广泛的应用前景。
Description
技术领域
本发明涉及一种Er3+和Tm3+共掺的氧化镧钇闪烁透明陶瓷材料的制备方法,属于特种陶瓷制造工艺技术领域。
背景技术
近年来,3um激光材料受到国内外的高度重视。3um波段的激光位于大气的2个传输窗口(1-3um,3-5um)内,并且覆盖了许多重要的分子特征谱线。因此,在遥感、测距、环境监测、生物工程和医疗等领域有着广泛的应用。军事上,3um波段激光的大气传输特性好,对战场烟雾穿透能力强,保密性好,对人眼也极为安全,可实现激光二极管泵浦小型化,因此这种激光器在军事上有重要的应用前景。同时,2um激光器具有量子缺损小,转换效率高的特点,是获得3-5um光学参数震荡器最适宜的抽运源,因此在激光制导、激光定向红外干扰、激光通讯等方面的应用而显得越来越重要。3um波段激光在医疗上也有广泛的应用。值得一提的是Er3+离子在3um附近激光被称为皮肤科、外科、牙科的黄金激光。因为生物组织70%以上为水分,水分对2.8um激光的吸收是2.1um激光的两百倍,是1.06um激光的一万倍。基于该特点,利用它可以进行极为精确的切割和软组织切除手术,对邻近组织的热扩散和机械损伤极小。
Y2O3属立方晶系,无双折射现象,热导率高,为YAG(钇铝石榴石)的两倍多,是一种优良的固体闪烁基质材料。因此,Er3+:Y2O3被广泛的用在3um激光发射等领域。但是由于Y2O3的熔点高达2430℃,且在2280℃附近会发生立方相向六方相的多晶转变,因而难以生长出大尺寸和高光学质量的Y2O3单晶。随着陶瓷制备技术及纳米制粉技术的发展,Y2O3透明陶瓷的烧结温度可降低为1700℃左右。此外,由于La2O3的加入,可以加速气孔的排除,降低透明陶瓷烧结温度并且有效抑制陶瓷晶粒过分长大,因此Er3+掺杂的氧化镧钇透明陶瓷是一种性能优良的闪烁材料。
此外,由于Er3+与Tm3+之间存在有效的能量传递,可以使Er3+的2.7um荧光输出更加高效。所以Er3+-Tm3+共掺的材料得到广泛的研究,尤其在Er3+-Tm3+共掺的碲酸盐和磷酸盐玻璃中,Er3+的2.7um荧光输出明显增强。由于在Y2O3基质中,Er3+与Tm3+之间的有效能量转,使得2.7um荧光输出明显增强。目前,Er3+-Tm3+共掺的材料应用比较广泛的是玻璃和晶体。但是,由于玻璃的受激发射界面较小,热导率和热损伤阈值也很小,限制其连续使用,对于晶体,其荧光寿命(2-4ms)相对较短,晶体生长困难,难以加工成大尺寸,制备成本高。
发明内容
针对现有技术存在的缺陷,本发明的目的是提供一种Er3+和Tm3+共掺的氧化镧钇闪烁透明陶瓷材料的制备方法,采用固相烧结法制备Er3+-Tm3+共掺的氧化镧钇透明陶瓷材料。
为达到上述目的,本发明采用如下技术方案:
一种Er3+和Tm3+共掺的氧化镧钇闪烁透明陶瓷材料的制备方法,具有以下的工艺过程和步骤:
a.采用高纯99.99%Y2O3,99.99%Er2O3,99.99%Tm2O3和99.99%La2O3为原料,四者的摩尔比按化学式(Tm0.02Er0.02Y0.86La0.1)2O3进行称量配料;
b.将按上述配方配制好的Y2O3,Er2O3,Tm2O3,La2O3混合粉料放入球磨罐中进行球磨,球料比为2:1,溶剂乙醇与粉体的质量比为4:1,球磨罐转速为50转/分,球磨时间为5h;
c.将球磨好的粉体在烘箱内烘干,然后将混合粉体在马弗炉中进行煅烧,1200℃保温10h,自然冷却,得到(Tm0.02Er0.02Y0.86La0.1)2O3粉体;
d.再次将粉体放入球磨罐中进行球磨,球料比为2:1,溶剂乙醇与粉体的质量比为4:1,球磨罐转速为50转/分,球磨时间为5h;
e.将球磨好的粉体在烘箱内烘干,将粉料进行造粒,过40目筛;
f.将造粒后的粉料干压成型,随后在200MP冷等静压下压成片状试样;
g.将上述试样放在氢气炉中烧结,烧结温度范围1450-1650℃,烧结时间45个小时最终得到致密的(Tm0.02Er0.02Y0.86La0.1)2O3陶瓷。
与现有技术相比,本发明具有如下的突出的有点:
本发明制备的致密的(Tm0.02Er0.02Y0.86La0.1)2O3透明陶瓷,具有良好的光学性能,在中红外激光领域有着广泛的应用前景。本发明的材料制备工艺简单,制造成本低,有利于实现工业规模化生产。
附图说明
图1为本发明中(Tm0.02Er0.02Y0.86La0.1)2O3陶瓷的显微结构图。
图2为本发明中(Tm0.02Er0.02Y0.86La0.1)2O3陶瓷的荧光光谱。
具体实施方式
现将本发明的具体实施例结合附图叙述于后。
一种Er3+和Tm3+共掺的氧化镧钇闪烁透明陶瓷材料的制备方法,具有以下的工艺过程和步骤:
a.采用高纯99.99%Y2O3,99.99%Er2O3,99.99%Tm2O3和99.99%La2O3为原料,四者的摩尔比按化学式(Tm0.02Er0.02Y0.86La0.1)2O3进行称量配料;
b.将按上述配方配制好的Y2O3,Er2O3,Tm2O3,La2O3混合粉料放入球磨罐中进行球磨,球料比为2:1,溶剂乙醇与粉体的质量比为4:1,球磨罐转速为50转/分,球磨时间为5h;
c.将球磨好的粉体在烘箱内烘干,然后将混合粉体在马弗炉中进行煅烧,1200℃保温10h,自然冷却,得到(Tm0.02Er0.02Y0.86La0.1)2O3粉体;
d.再次将粉体放入球磨罐中进行球磨,球料比为2:1,溶剂乙醇与粉体的质量比为4:1,球磨罐转速为50转/分,球磨时间为5h;
e.将球磨好的粉体在烘箱内烘干,将粉料进行造粒,过40目筛;
f.将造粒后的粉料干压成型,随后在200MP冷等静压下压成片状试样;
g.将上述试样放在氢气炉中烧结,烧结温度范围1450-1650℃,烧结时间45个小时最终得到致密的(Tm0.02Er0.02Y0.86La0.1)2O3陶瓷。
所制得的透明陶瓷样品的显微结构图通过金相显微镜测得,荧光光谱通过分光光度计(FP-6300,JASCO,Japan)检测。图1是(Tm0.02Er0.02Y0.86La0.1)2O3透明陶瓷的显微结构图,由图可知样品晶粒尺寸均匀,晶界几乎无气孔存在,晶粒尺寸在20um左右,结构比较致密。图2是(Tm0.02Er0.02Y0.86La0.1)2O3透明陶瓷样品的荧光光谱图,由图可知,添加Tm3+离子以后,样品2.7um处的荧光强度明显增强。表明,Tm3+的掺杂有利于增强Er3+2.7um发光强度。因此,Er3+和Tm3+共掺氧化镧钇透明陶瓷材料在中红外激光领域有着广泛的应用前景。
Claims (1)
1.一种Er3+和Tm3+共掺的氧化镧钇闪烁透明陶瓷材料的制备方法,其特征在于,具有以下的工艺过程和步骤:
a. 采用高纯99.99%Y2O3,99.99%Er2O3,99.99%Tm2O3和99.99%La2O3为原料,四者的摩尔比按化学式(Tm0.02Er0.02Y0.86La0.1)2O3进行称量配料;
b. 将按上述配方配制好的Y2O3,Er2O3,Tm2O3,La2O3混合粉料放入球磨罐中进行球磨,球料比为2:1,溶剂乙醇与粉体的质量比为4:1,球磨罐转速为50转/分,球磨时间为5h;
c.将球磨好的粉体在烘箱内烘干,然后将混合粉体在马弗炉中进行煅烧,1200℃保温10h,自然冷却,得到(Tm0.02Er0.02Y0.86La0.1)2O3粉体;
d.再次将粉体放入球磨罐中进行球磨,球料比为2:1,溶剂乙醇与粉体的质量比为4:1,球磨罐转速为50转/分,球磨时间为5h;
e.将球磨好的粉体在烘箱内烘干,将粉料进行造粒,过40目筛;
f.将造粒后的粉料干压成型,随后在200MP冷等静压下压成片状试样;
g.将上述试样放在氢气炉中烧结,烧结温度范围1450-1650℃,烧结时间45个小时最终得到致密的(Tm0.02Er0.02Y0.86La0.1)2O3陶瓷。