CN103071976A - 一种不锈钢仿铜件生产方法 - Google Patents

一种不锈钢仿铜件生产方法 Download PDF

Info

Publication number
CN103071976A
CN103071976A CN2012105965929A CN201210596592A CN103071976A CN 103071976 A CN103071976 A CN 103071976A CN 2012105965929 A CN2012105965929 A CN 2012105965929A CN 201210596592 A CN201210596592 A CN 201210596592A CN 103071976 A CN103071976 A CN 103071976A
Authority
CN
China
Prior art keywords
workpiece
stainless steel
copper
production method
moulding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105965929A
Other languages
English (en)
Other versions
CN103071976B (zh
Inventor
陈乾辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210596592.9A priority Critical patent/CN103071976B/zh
Publication of CN103071976A publication Critical patent/CN103071976A/zh
Application granted granted Critical
Publication of CN103071976B publication Critical patent/CN103071976B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种不锈钢仿铜件生产方法，其包括以下步骤：不锈钢弯花造型；造型后的工件经过正反两面冲压，点焊成型；型材与造型后的工件焊接组装成型；工件组装后进行表面处理；工件表面抛光处理后进行喷塑处理；喷塑处理后进行刷铜处理；所述弯花造型时不锈钢钢带经过折边机折叠加工成弯花扁钢，再按花型大小不同经过弯花机配套模具旋转不同的角度回转挤压成型；所述表面处理时首先用金钢纱布抛光、打磨、再进入除油灵浸泡2小时，出池后放入清水池1小时，再用高压水枪冲洗干净后进入烘箱烘干。本发明通过对不锈钢进行弯花造型、焊接、抛光、喷塑、刷铜、烘干等工艺处理，使不锈钢外表面具有铜涂层，涂层附着力强，无污染更环保。

Description

一种不锈钢仿铜件生产方法
技术领域
本发明涉及一种生产方法，尤其是指一种不锈钢仿铜件生产方法。
背景技术
家居建材产品随着房地产行业的蓬勃发展种类越来越多，而彰显人们生活品质的高档户外装修材料也越来越受到热捧，庭院大门、栏杆等现在广泛使用的是不锈钢材料，不锈钢材料较铸铁大门来讲不容易生锈，不需要定期保养维护成本较低，深受消费者喜欢，但是不锈钢的颜色较为单一，在强光下不锈钢容易反光，使人炫目，不锈钢刷漆改变色彩存在的问题是油漆与不锈钢的粘合度不好，风吹日晒油漆容易剥落影响美观；彩钢的成本太高，不适宜进行大面积的庭院装修使用，因此需要一种既美观大方又价廉的产品来满足人们对高品质生活的追求。
本发明提供一种不锈钢仿铜工件的制作方法，以满足人们的生活需求。
发明内容
本发明的目的在于提供一种不锈钢仿铜件生产方法。
为实现上述技术目的，本发明采用的技术方案如下：一种不锈钢仿铜件生产方法，其包括以下步骤：不锈钢弯花造型；造型后的工件经过正反两面冲压，点焊成型；型材与造型后的工件焊接组装成型；工件组装后进行表面处理；工件表面抛光处理后进行喷塑处理；喷塑处理后进行刷铜处理；所述弯花造型时不锈钢钢带经过折边机折叠加工成弯花扁钢，再按花型大小不同经过弯花机配套模具旋转不同的角度回转挤压成型；所述表面处理时首先用金钢纱布抛光、打磨、再进入除油灵浸泡2小时，出池后放入清水池1小时，再用高压水枪冲洗干净后进入烘箱烘干。
进一步，所述点焊成型时，焊接点与连接处需打磨平整，再由喷砂设备配套100码金钢砂连接旋转喷枪对工件进行表面喷砂处理。
进一步，所述焊接为氩弧焊，焊接时型材与工件必须在同一平面，组装成型后对工件进行垂直度与平面的校正。
进一步，所述弯花机配套模具旋转角度为180度、36度及260度。
进一步，工件烘干后在常温状态下进入喷塑台，接8公升气压，380伏旋转风机，220伏电源机箱，工件需接静电，调整雾化0.1kg/m2，硫化0.3kg/m2，使喷枪匀速喷涂工件表面，喷涂后出喷塑台进入烘箱200°高温烘烤。
进一步，工件出烘箱冷却后刷铜，刷铜后成品放入烘箱烘干。
本发明与现有技术相比，具有如下有益效果：通过对不锈钢进行弯花造型、焊接、抛光、喷塑、刷铜、烘干等工艺处理，使不锈钢外表面具有铜涂层，涂层附着力强，无污染更环保。
具体实施方式：
以下对本发明做进一步描述。
本发明一种不锈钢仿铜件生产方法，其包括以下步骤：
不锈钢弯花造型；用25mm*1.5mm不锈钢带经过折边机折叠加工成15mm*3mm的弯花扁钢，再按花型大小的要求，经过专用弯花机配套模具旋转180°、36°、260°等回转挤压配套手工校正成型，再经过专用喷砂设备强化表面喷砂处理。
造型后的工件经过正反两面冲压，点焊成型；所述点焊成型时，焊接点与连接处需打磨平整，再由喷砂设备配套100码金钢砂连接旋转喷枪对工件进行表面喷砂处理。标准型材的表面喷砂要定制的喷砂设备，型材放进机器后，自动匀速移动使型材表面喷砂颗粒度一致，能保证喷涂后的附着力增强。
型材与造型后的工件焊接组装成型；所述焊接为氩弧焊，焊接时型材与工件必须在同一平面，组装成型后对工件进行垂直度与平面的校正。
工件组装后进行表面处理；产品制作成型后，首先用金钢纱布抛光、打磨、再进入除油灵浸泡2小时，出池后放入清水池1小时，再用高压水枪冲洗干净后进入烘箱150°烘干。
工件表面抛光处理后进行喷塑处理；工件烘干后在常温状态下进入喷塑台，接8公升气压，380伏旋转风机，220伏电源机箱，同时工件需接静电，调整雾化0.1kg/m2，硫化0.3kg/m2，使喷枪匀速喷涂工件表面，反复2次，出喷塑台后连接滑轮台匀速进入烘箱，经过200°高温烘烤。
喷塑处理后进行刷铜处理；所述工件出烘箱待其冷却后放置于刷铜工作台按要求配置铜粉比例，搅拌均匀后用羊毛刷轻拭工件表面，漏黑底托铜漆刷第一遍，再由精粽刷弹刷第二遍成品，将成品放入烘箱烘干。

Claims (6)

1.一种不锈钢仿铜件生产方法，其特征在于，包括以下步骤：不锈钢弯花造型；造型后的工件经过正反两面冲压，点焊成型；型材与造型后的工件焊接组装成型；工件组装后进行表面处理；工件表面抛光处理后进行喷塑处理；喷塑处理后进行刷铜处理；所述弯花造型时不锈钢钢带经过折边机折叠加工成弯花扁钢，再按花型大小不同经过弯花机配套模具旋转不同的角度回转挤压成型；所述表面处理时首先用金钢纱布抛光、打磨、再进入除油灵浸泡2小时，出池后放入清水池1小时，再用高压水枪冲洗干净后进入烘箱烘干。
2.如权利要求1所述的不锈钢仿铜件生产方法，其特征在于：所述点焊成型时，焊接点与连接处需打磨平整，再由喷砂设备配套100码金钢砂连接旋转喷枪对工件进行表面喷砂处理。
3.如权利要求2所述的不锈钢仿铜件生产方法，其特征在于：所述焊接为氩弧焊，焊接时型材与工件必须在同一平面，组装成型后对工件进行垂直度与平面的校正。
4.如权利要求3所述的不锈钢仿铜件生产方法，其特征在于：所述弯花机配套模具旋转角度为180度、36度及260度。
5.如权利要求3或4所述的不锈钢仿铜件生产方法，其特征在于：所述工件烘干后在常温状态下进入喷塑台，接8公升气压，380伏旋转风机，220伏电源机箱，工件需接静电，调整雾化0.1kg/m2，硫化0.3kg/m2，使喷枪匀速喷涂工件表面，喷涂后出喷塑台进入烘箱200°高温烘烤。
6.如权利要求5所述的不锈钢仿铜件生产方法，其特征在于：工件出烘箱冷却后刷铜，刷铜后成品放入烘箱烘干。
CN201210596592.9A 2012-12-24 2012-12-24 一种不锈钢仿铜件生产方法 Active CN103071976B (zh)