CN103012642A - 一种树脂的制备方法 - Google Patents

一种树脂的制备方法 Download PDF

Info

Publication number
CN103012642A
CN103012642A CN 201110288891 CN201110288891A CN103012642A CN 103012642 A CN103012642 A CN 103012642A CN 201110288891 CN201110288891 CN 201110288891 CN 201110288891 A CN201110288891 A CN 201110288891A CN 103012642 A CN103012642 A CN 103012642A
Authority
CN
China
Prior art keywords
temperature
preparation
resin
reaction
methyl methacrylate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110288891
Other languages
English (en)
Inventor
许瑞君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201110288891 priority Critical patent/CN103012642A/zh
Publication of CN103012642A publication Critical patent/CN103012642A/zh
Pending legal-status Critical Current

Abstract

一种树脂的制备方法属于化工技术领域，更具体的说，是涉及一种树脂的制备方法。本发明提供了一种外观优良、抗冲击强度大、流动性好的树脂的制备方法。本发明的制备步骤为：将聚乙烯醇、十二烷基苯磺酸钠、磷酸钙加入三口瓶中，将三口瓶置于水浴箱内，通入氮气进行保护，打开搅拌装置，装置，封住剩余的开口，调节搅拌速度，保持水浴温度为95℃，搅拌0.5h，活化分散剂；然后降水温至85～90℃时，采用一次投料方式，加入单体(甲基丙烯酸甲酯∶苯乙烯＝15∶20～15∶3)和引发剂过氧化二苯甲酰0.5～0.7g，恒温85～90℃，氮气保护，反应0.3～6h；反应后升水温至95℃，熟化2h，结束反应。

Description

一种树脂的制备方法
技术领域：
本发明属于化工技术领域，更具体的说，是涉及一种树脂的制备方法。
背景技术：
合成树脂是由人工合成的一类高分子聚合物。合成树脂最重要的应用是制造塑料。为便于加工和改善性能，常添加助剂，有时也直接用于加工成形，故常是塑料的同义语。合成树脂还是制造合成纤维、涂料、胶粘剂、绝缘材料等的基础原料。合成树脂种类繁多，其中聚乙烯(PE)、聚氯乙烯(PVC)、聚苯乙烯(PS)、聚丙烯(PP)和ABS树脂为五大通用树脂，是应用最为广泛的合成树脂材料。
按树脂合成反应可将树脂分为加聚物和缩聚物。加聚物是指由加成聚合反应制得的聚合物，其链节结构的化学式与单体的分子式相同，如聚乙烯、聚苯乙烯、聚四氟乙烯等；缩聚物是指由缩合聚合反应制得的聚合物，其结构单元的化学式与单体的分子式不同，如酚醛树脂、聚酯树脂、聚酰胺树脂等。
甲基丙烯酸甲酯(MMA)是一种重要的有机化工原料，可在光热或催化剂存在下自聚或与其它单体共聚生成甲基丙烯酸甲酯树脂和塑料。产品具有透明度高、耐候性好、光学性能优良等特点，广泛用作广告牌、照明材料、建筑材料、汽车零件等。近来，在1T行业相关领域如液晶显示屏光导板、DVD光盘等的需求也快速增长。MMA具有低毒性，且可以回收，因而是有利于环保的材料。
由甲基丙烯酸甲酯自身聚合而得的均聚物为聚甲基丙烯酸甲酯(PMMA)，存在性脆和不耐冲击等缺陷。
发明内容：
本发明就是针对上述问题，提供了一种外观优良、抗冲击强度大、流动性好的树脂的制备方法。
为了实现本发明的上述目的，本发明的制备步骤为：将聚乙烯醇、十二烷基苯磺酸钠、磷酸钙加入三口瓶中，将三口瓶置于水浴箱内，通入氮气进行保护，打开搅拌装置，装置，封住剩余的开口，调节搅拌速度，保持水浴温度为95℃，搅拌0.5h，活化分散剂；然后降水温至85～90℃时，采用一次投料方式，加入单体(甲基丙烯酸甲酯∶苯乙烯＝15∶20～15∶3)和引发剂过氧化二苯甲酰0.5～0.7g，恒温85～90℃，氮气保护，反应0.3～6h；反应后升水温至95℃，熟化2h，结束反应；静置后倾出上层清液，用HCl/H2O(2∶1)洗涤，用大量的蒸馏水洗至中性，过滤，真空干燥，筛分，得到透明珠状产物，称重，计算产率。
本发明的有益效果：
1.本发明具有良好的透明度和光泽度；
2.本发明具有较高的抗冲击强度，而且在加工成型时，熔融粘度不大，流动性较好。
具体实施方式：
本发明利用悬浮聚合法合成了苯乙烯-甲基丙烯酸甲酯树脂，本发明的制备步骤为：将聚乙烯醇、十二烷基苯磺酸钠、磷酸钙加入三口瓶中，将三口瓶置于水浴箱内，通入氮气进行保护，打开搅拌装置，装置，封住剩余的开口，调节搅拌速度，保持水浴温度为95℃，搅拌0.5h，活化分散剂；然后降水温至85～90℃时，采用一次投料方式，加入单体(甲基丙烯酸甲酯∶苯乙烯＝15∶20～15∶3)和引发剂过氧化二苯甲酰0.5～0.7g，恒温85～90℃，氮气保护，反应0.3～6h；反应后升水温至95℃，熟化2～3h，结束反应；静置后倾出上层清液，用HCl/H2O(2∶1)洗涤，用大量的蒸馏水洗至中性，过滤，真空干燥，筛分，得到透明珠状产物，称重，计算产率。本发明选择单体中甲基丙烯酸甲酯和苯乙烯的质量比、反应时间作为影响树脂性质的因素，可见表1、表2。
表1  单体投料比对树脂外观及粒径的影响
Figure BSA00000581323800031
表2  反应时间对树脂性质的影响
Figure BSA00000581323800032
作为一种优选方案，本发明的制备步骤为：甲基丙烯酸甲酯和苯乙烯的质量比为15∶4.1，酯化温度为88℃，引发剂为0.5％，聚合时间为4h，熟化时间为2h。

Claims (2)

1.一种树脂的制备方法，其特征在于，本发明的制备步骤为：将聚乙烯醇、十二烷基苯磺酸钠、磷酸钙加入三口瓶中，将三口瓶置于水浴箱内，通入氮气进行保护，打开搅拌装置，装置，封住剩余的开口，调节搅拌速度，保持水浴温度为95℃，搅拌0.5h，活化分散剂；然后降水温至85～90℃时，采用一次投料方式，加入单体(甲基丙烯酸甲酯∶苯乙烯＝15∶20～15∶3)和引发剂过氧化二苯甲酰0.5～0.7g，恒温85～90℃，氮气保护，反应0.3～6h；反应后升水温至95℃，熟化2h，结束反应；静置后倾出上层清液，用HCl/H2O(2∶1)洗涤，用大量的蒸馏水洗至中性，过滤，真空干燥，筛分，得到透明珠状产物，称重，计算产率。
2.根据权利要求1所述的一种树脂的制备方法，其特征在于，本发明的制备步骤为：甲基丙烯酸甲酯和苯乙烯的质量比为15∶4.1，酯化温度为88℃，引发剂为0.5％，聚合时间为4h，熟化时间为2h。
CN 201110288891 2011-09-27 2011-09-27 一种树脂的制备方法 Pending CN103012642A (zh)