CN102977320A - 一种端羟基聚丁二烯改性水性聚氨酯的方法 - Google Patents

一种端羟基聚丁二烯改性水性聚氨酯的方法 Download PDF

Info

Publication number
CN102977320A
CN102977320A CN2012104496416A CN201210449641A CN102977320A CN 102977320 A CN102977320 A CN 102977320A CN 2012104496416 A CN2012104496416 A CN 2012104496416A CN 201210449641 A CN201210449641 A CN 201210449641A CN 102977320 A CN102977320 A CN 102977320A
Authority
CN
China
Prior art keywords
hydroxy
performed polymer
terminated polybutadienes
aqueous polyurethane
dmba
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012104496416A
Other languages
English (en)
Inventor
苏建丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Wenchuang Technology Co Ltd
Original Assignee
Qingdao Wenchuang Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Wenchuang Technology Co Ltd filed Critical Qingdao Wenchuang Technology Co Ltd
Priority to CN2012104496416A priority Critical patent/CN102977320A/zh
Publication of CN102977320A publication Critical patent/CN102977320A/zh
Pending legal-status Critical Current

Abstract

一种端羟基聚丁二烯改性水性聚氨酯的方法，是以IPDI、N220、DEG、DMBA为原料制备预聚体，加入HTPB改性预聚体，加入三乙胺进行中和反应生成盐，加入乙二胺的水溶液进行乳化扩链，制得水性聚氨酯乳液。本发明得到的聚氨酯涂膜具有较好的贮存稳定性、低温柔韧性和力学性能。

Description

一种端羟基聚丁二烯改性水性聚氨酯的方法
技术领域
本发明涉及一种端羟基聚丁二烯改性水性聚氨酯的方法，属化工领域。
技术背景        
水性聚氨酯以水作为分散介质，具有不燃、无毒等优点，随着其性能的不断完善，已被广泛应用，是一种具有很大发展前景的绿色环保材料。目前普遍采用聚酯或聚醚二元醇来制备水性聚氨酯，制备的水性聚氨酯存在机械性能不好、耐水性差、耐溶剂性不好等缺点，因而对水性聚氨酯在结构上进行改性成为水性聚氨酯发展的重要途径。
本专利采用端羟基聚丁二烯对水性聚氨酯改性，端羟基聚丁二烯是液体橡胶的一种，具有较长的非极性碳链，采用其改性水性聚氨酯，是通过强疏水性的烯键，提高水性聚氨酯的耐水性，同时利用橡胶材料优异的弹性和柔韧性，可以很好的改善水性聚氨酯的低温柔韧性，最终制备出的水性聚氨酯具有良好的贮存稳定性、低温柔韧性和力学性能。
发明内容
本发明的目的是提供一种端羟基聚丁二烯改性水性聚氨酯的方法，得到的聚氨酯涂膜具有良好的贮存稳定性、低温柔韧性和力学性能。
为实现以上目的，本发明的一种端羟基聚丁二烯改性水性聚氨酯的方法，其步骤具体为：
(1) 异佛尔酮二异氰酸酯(IPDI)、聚醚二元醇(N220)、一缩二乙二醇(DEG)、二羟甲基丁酸(DMBA)为原料制备预聚体，反应2h。
(2) 加入端羟基聚丁二烯(HTPB)对预聚体改性，反应1h。
(3) 降温至40℃，加入三乙胺进行中和反应生成盐，反应3-5min。
(4) 加入乙二胺(EA)的水溶液进行乳化扩链1h，得到端羟基聚丁二烯改性的水性聚氨酯乳液。
步骤(1)中预聚体原料的配比为：IPDI与N220、DEG、DMBA的摩尔比为1.3:1-1.4:1，DEG占预聚体质量的2%-3%，DMBA占预聚体质量的5%-6%。
步骤(2)中端羟基聚丁二烯的用量为预聚体质量的0.2%。
步骤(3)中三乙胺的物质的量与DMBA的物质的量相同。
步骤(4)中乙二胺(EA)的用量为预聚体质量的0.1%，水的用量为预聚体总质量的2倍。
本发明产生的有益效果为，本专利采用端羟基聚丁二烯对水性聚氨酯改性，端羟基聚丁二烯是液体橡胶的一种，具有较长的非极性碳链，采用其改性水性聚氨酯，是通过强疏水性的烯键，提高水性聚氨酯的耐水性，同时利用橡胶材料优异的弹性和柔韧性，可以很好的改善水性聚氨酯的低温柔韧性，最终制备出的水性聚氨酯具有良好的贮存稳定性、低温柔韧性和力学性能。
实施例
实施例1：
异佛尔酮二异氰酸酯(IPDI)、聚醚二元醇(N220)、一缩二乙二醇(DEG)、二羟甲基丁酸(DMBA)为原料制备预聚体，反应2h，IPDI与N220、DEG、DMBA的摩尔比为1.3:1，DEG占预聚体质量的2%，DMBA占预聚体质量的5%。加入端羟基聚丁二烯(HTPB)对预聚体改性，反应1h，端羟基聚丁二烯的用量为预聚体质量的0.2%。降温至40℃，加入三乙胺进行中和反应生成盐，反应3min，三乙胺的物质的量与DMBA的物质的量相同。加入乙二胺(EA)的水溶液进行乳化扩链1h，乙二胺(EA)的用量为预聚体质量的0.1%，水的用量为预聚体总质量的2倍，得到端羟基聚丁二烯改性的水性聚氨酯乳液。
实施例2：
异佛尔酮二异氰酸酯(IPDI)、聚醚二元醇(N220)、一缩二乙二醇(DEG)、二羟甲基丁酸(DMBA)为原料制备预聚体，反应2h，IPDI与N220、DEG、DMBA的摩尔比为1.35:1，DEG占预聚体质量的3%，DMBA占预聚体质量的5%。加入端羟基聚丁二烯(HTPB)对预聚体改性，反应1h，端羟基聚丁二烯的用量为预聚体质量的0.15%。降温至40℃，加入三乙胺进行中和反应生成盐，反应3min，三乙胺的物质的量与DMBA的物质的量相同。加入乙二胺(EA)的水溶液进行乳化扩链1h，乙二胺(EA)的用量为预聚体质量的0.1%，水的用量为预聚体总质量的2倍，得到端羟基聚丁二烯改性的水性聚氨酯乳液。

Claims (6)

1.一种端羟基聚丁二烯改性水性聚氨酯的方法，其特征在于：步骤如下：
(1) 异佛尔酮二异氰酸酯(IPDI)、聚醚二元醇(N220)、一缩二乙二醇(DEG)、二羟甲基丁酸(DMBA)为原料制备预聚体，反应2h；
(2) 加入端羟基聚丁二烯(HTPB)对预聚体改性，反应1h；
(3) 降温至40℃，加入三乙胺进行中和反应生成盐，反应3-5min；
(4) 加入乙二胺(EA)的水溶液进行乳化扩链1h，得到端羟基聚丁二烯改性的水性聚氨酯乳液。
2.如权利要求1所述的一种端羟基聚丁二烯改性水性聚氨酯的方法，其特征在于：所述的步骤(1)中预聚体原料的配比为：IPDI与N220、DEG、DMBA的摩尔比为1.3:1-1.4:1，DEG占预聚体质量的2%-3%，DMBA占预聚体质量的5%-6%。
3.如权利要求1所述的一种端羟基聚丁二烯改性水性聚氨酯的方法，其特征在于：所述的步骤(2)中端羟基聚丁二烯的用量为预聚体质量的0.2%。
4.如权利要求1所述的一种端羟基聚丁二烯改性水性聚氨酯的方法，其特征在于：所述的步骤(3)中三乙胺的物质的量与DMBA的物质的量相同。
5.如权利要求1所述的一种端羟基聚丁二烯改性水性聚氨酯的方法，其特征在于：所述的步骤(4)中乙二胺(EA)的用量为预聚体质量的0.1%。
6.如权利要求1所述的一种端羟基聚丁二烯改性水性聚氨酯的方法，其特征在于：所述的步骤(4)中水的用量为预聚体总质量的2倍。
CN2012104496416A 2012-11-12 2012-11-12 一种端羟基聚丁二烯改性水性聚氨酯的方法 Pending CN102977320A (zh)