CN102975453A - 一种环保型耐高温pvc硬挺复合布及其生产工艺 - Google Patents
一种环保型耐高温pvc硬挺复合布及其生产工艺 Download PDFInfo
- Publication number
- CN102975453A CN102975453A CN2012105550780A CN201210555078A CN102975453A CN 102975453 A CN102975453 A CN 102975453A CN 2012105550780 A CN2012105550780 A CN 2012105550780A CN 201210555078 A CN201210555078 A CN 201210555078A CN 102975453 A CN102975453 A CN 102975453A
- Authority
- CN
- China
- Prior art keywords
- pvc
- environment
- cloth
- temperature
- friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及PVC复合布技术领域,具体地说是一种环保型耐高温PVC硬挺复合布及其生产工艺,包括上层布料、下层布料及中层PVC塑料,中层PVC塑料的主要成分按重量百分比为:聚氯乙烯树脂42-55%、碳酸钙18-28%、聚己二醇0.5-1%、PVC稳定剂0.6-1.8%、邻苯二甲酸二壬酯(DINP)8-18%、环保增塑剂5-15%及有机锡稳定剂1-2%放入搅拌机中,搅拌成为糊状的浆料,置于20-30℃的常温室中20-30小时,将浆料均匀地涂在上层布料和下层布料之间,放入刮塑机经过150-200℃的高温滚压、烘干,烘干温度为160-180℃,最后得成品;本发明不仅非常环保,具有耐酸碱、极耐高温、高强度、安全性能可靠等优点,且由于上层布料和下层布料均经过添加有草酸的清水清洗,并脱干、烘干、冷却及拉幅定型而成,从而制得的PVC硬挺复合布外形轻巧,颜色白皙,非常美观。
Description
[技术领域]
本发明涉及PVC复合布技术领域,具体地说是一种环保型耐高温PVC硬挺复合布及其生产工艺。
[背景技术]
PVC是一种乙烯基的聚合物质,作为世界上产量最大的聚合物之一,其在实际的加工过程中,经常添加一定量的各种加工助剂,然后打粉混合,挤出造粒,最后通过多种加工工艺,制造出具有独特性价比的不同PVC制品。加工助剂主要有热稳定剂、增塑剂、润滑剂、色母料、辅助加工剂、抗冲击剂及其它添加剂等等。其中,热稳定剂主要用于吸收PVC受热加工时分解出来的游离氯,增塑剂用于使PVC制品具有一定的柔韧性,润滑剂用于使得PVC制品在造粒时更易于挤出,色母料用于使PVC制品具有各种颜色。由于制成的PVC制品具有不易燃性、高强度、耐气侯变化性以及优良的几何稳定性,且对氧化剂、还原剂和强酸都有很强的抵抗力,目前已被广泛应用于各种行业。
PVC硬挺复合布是在两层布料之间涂上含有pvc的塑料层,使其表面更加光滑,防水性能更好,且具有优异的防霉性、良好的低温柔软性、强度高、拉力强、相对轻等特点。目前,现有的PVC硬挺复合布的中层PVC塑料在加工过程中所添加的增塑剂主要为:DEHA(DOA),中文化学名称为:己二酸二(2-乙基己)酯;DEHP(DOP),中文化学名称为:邻苯二甲酸二(2-乙基己)酯以及DBP,中文化学名称为:邻苯二甲酸二丁酯,这些增塑剂均属于有害化学物质。国内、外早已对DOP、DBP等邻苯二甲酸酯类在PVC制品进行限制,其主要原因是其对人体有危害,如有致癌性、容易造成内分泌紊乱、对生殖毒性较大等。欧洲政府陆续出台了对DOP等有害化学物质的限制令,要求在PVC成品中DEHP(DOP),BBP,DNHP,DBP,DIDP的含量要低于0.06%。而目前市场的PVC硬挺复合布的中层PVC塑料所含的DOP等有害化学物质均已超标。
另外,采用现有的PVC硬挺复合布生产工艺所制造出的PVC硬挺复合布,其具有如下不足之处:一方面,耐高温性差,生产过程中还会产生有害环境的物质,不够环保;另一方面,所制得的PVC硬挺复合布表面极易出现如黄色印迹等污痕,且表面颜色泛黄,不够美观,如此造成不良率高,增大了PVC硬挺复合布厂家的成本。
[发明内容]
本发明的目的就是要解决上述的不足而提供一种环保型耐高温PVC硬挺复合布及其生产工艺,由于中层PVC塑料在加工过程中所添加的增塑剂采用UN488复合环保增塑剂,从而非常环保,极耐高温,而且制成的PVC硬挺复合布既轻巧、美观,又结实、安全,能满足各种场合的需求。
为实现上述目的设计一种环保型耐高温PVC硬挺复合布,包括上层布料、下层布料及中层PVC塑料,其特征在于:所述中层PVC塑料的主要成分按重量百分比为:聚氯乙烯树脂42-55%、碳酸钙18-28%、聚己二醇0.5-1%、PVC稳定剂0.6-1.8%、邻苯二甲酸二壬酯(DINP)8-18%、环保增塑剂5-15%及有机锡稳定剂1-2%。
所述中层PVC塑料的主要成分按重量百分比为:聚氯乙烯树脂48%、碳酸钙24%、聚己二醇0.6%、PVC稳定剂1.2%、邻苯二甲酸二壬酯(DINP)15%、环保增塑剂10%及有机锡稳定剂1.2%。
所述环保增塑剂采用UN488复合环保增塑剂,所述有机锡稳定剂采用甲基硫酸有机锡稳定剂。
一种环保型耐高温PVC硬挺复合布的生产工艺,包括以下步骤:
1)将布料浸入清洗槽中的清水中,向清洗槽内添加适量的草酸,清洗水温为60-90℃;
2)清洗后,对布料进行冲洗,将布料中的草酸残留物冲洗干净;
3)取出冲洗干净的布料,先脱干,再烘干,冷却后,拉幅定型;
4)按权利要求1所述重量百分比将聚氯乙烯树脂、碳酸钙、聚己二醇、PVC稳定剂、邻苯二甲酸二壬酯(DINP)、环保增塑剂及有机锡稳定剂放入搅拌机中,搅拌15-25分钟,使其成为糊状的浆料;
5)将浆料置于20-30℃的常温室中20-30小时;
6)将浆料均匀地涂在经步骤1)至步骤3)处理过的上层布料和下层布料之间,并放入刮塑机经过150-200℃的高温滚压、烘干,烘干温度为160-180℃,最后得成品。
本发明同现有技术相比,由于将中层PVC塑料在加工过程中所添加的增塑剂使用不含DIDP的DINP来替换DOP,以及UN488来替换DBP,因此非常环保,利用这种PVC硬挺复合布所制成的劳动防护用品不仅穿戴柔软、舒适,且具有耐酸碱、极耐高温、高强度、安全性能可靠的优点;另外,由于该PVC硬挺复合布的上层布料和下层布料均经过添加有草酸的清水清洗,并反复冲洗干净,然后脱干、烘干、冷却及拉幅定型而成,从而避免了PVC硬挺复合布表面颜色泛黄的现象发生,使得制得的PVC硬挺复合布外形轻巧,颜色白皙,非常美观;此外,本发明所述的生产工艺流程设计合理,操作简单方便,且成本低,可适用于其他纺织面料投放市场,具有广阔的应用前景,值得推广应用。
[具体实施方式]
实施例1:
1)向清洗槽中放入1.2吨清水,将布料浸入清洗槽中的清水中,向清洗槽内添加7公斤草酸,清洗水温为80℃;
2)清洗后,对布料进行二道冲洗,每道三遍,直至将布料中的草酸残留物冲洗干净;
3)取出冲洗干净的布料,先脱干,再烘干,冷却后,夹子拉幅,定型,下机门幅为90公分;
4)将重量百分比分别为聚氯乙烯树脂48%、碳酸钙24%、聚己二醇0.6%、PVC稳定剂1.2%、邻苯二甲酸二壬酯(DINP)15%、环保增塑剂10%及有机锡稳定剂1.2%放入搅拌机中,搅拌20分钟,使其成为糊状的浆料,环保增塑剂采用UN488复合环保增塑剂,有机锡稳定剂采用甲基硫酸有机锡稳定剂;
5)将浆料置于25℃的常温室中25小时;
6)将浆料均匀地涂在经步骤1)至步骤3)处理过的上层布料和下层布料之间,并放入刮塑机经过180℃的高温滚压、烘干,烘干温度为170℃,最后得成品PVC硬挺复合布。
实施例2:
1)向清洗槽中放入1吨清水,将布料浸入清洗槽中的清水中,向清洗槽内添加6公斤草酸,清洗水温为60℃;
2)清洗后,对布料进行二道冲洗,每道三遍,直至将布料中的草酸残留物冲洗干净;
3)取出冲洗干净的布料,先脱干,再烘干,冷却后,夹子拉幅,定型,下机门幅为90公分;
4)将重量百分比分别为聚氯乙烯树脂42%、碳酸钙22%、聚己二醇0.8%、PVC稳定剂1.2%、邻苯二甲酸二壬酯(DINP)18%、环保增塑剂15%及有机锡稳定剂1%放入搅拌机中,搅拌15分钟,使其成为糊状的浆料,环保增塑剂采用UN488复合环保增塑剂,有机锡稳定剂采用甲基硫酸有机锡稳定剂;
5)将浆料置于20℃的常温室中20小时;
6)将浆料均匀地涂在经步骤1)至步骤3)处理过的上层布料和下层布料之间,并放入刮塑机经过150℃的高温滚压、烘干,烘干温度为160℃,最后得成品PVC硬挺复合布。
实施例3:
1)向清洗槽中放入1.5吨清水,将布料浸入清洗槽中的清水中,向清洗槽内添加8公斤草酸,清洗水温为90℃;
2)清洗后,对布料进行二道冲洗,每道三遍,直至将布料中的草酸残留物冲洗干净;
3)取出冲洗干净的布料,先脱干,再烘干,冷却后,夹子拉幅,定型,下机门幅为90公分;
4)将重量百分比分别为聚氯乙烯树脂55%、碳酸钙28%、聚己二醇1%、PVC稳定剂1%、邻苯二甲酸二壬酯(DINP)8%、环保增塑剂5%及有机锡稳定剂2%放入搅拌机中,搅拌25分钟,使其成为糊状的浆料,环保增塑剂采用UN488复合环保增塑剂,有机锡稳定剂采用甲基硫酸有机锡稳定剂;
5)将浆料置于30℃的常温室中30小时;
6)将浆料均匀地涂在经步骤1)至步骤3)处理过的上层布料和下层布料之间,并放入刮塑机经过200℃的高温滚压、烘干,烘干温度为180℃,最后得成品PVC硬挺复合布。
本发明中的布料采用市布或墙布,该市布或墙布为21支/2股×10支,下机门幅为90公分;草酸采用山东元丰公司制造的丰元牌草酸;刮塑机下机后,取样做水渍测试,160-180℃烘干后,水渍不明显。
本发明并不受上述实施方式的限制,其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化,均应为等效的置换方式,都包含在本发明的保护范围之内。
Claims (4)
1.一种环保型耐高温PVC硬挺复合布,包括上层布料、下层布料及中层PVC塑料,其特征在于:所述中层PVC塑料的主要成分按重量百分比为:聚氯乙烯树脂42-55%、碳酸钙18-28%、聚己二醇0.5-1%、PVC稳定剂0.6-1.8%、邻苯二甲酸二壬酯(DINP)8-18%、环保增塑剂5-15%及有机锡稳定剂1-2%。
2.如权利要求1所述的环保型耐高温PVC硬挺复合布,其特征在于:所述中层PVC塑料的主要成分按重量百分比为:聚氯乙烯树脂48%、碳酸钙24%、聚己二醇0.6%、PVC稳定剂1.2%、邻苯二甲酸二壬酯(DINP)15%、环保增塑剂10%及有机锡稳定剂1.2%。
3.如权利要求2所述的环保型耐高温PVC硬挺复合布,其特征在于:所述环保增塑剂采用UN488复合环保增塑剂,所述有机锡稳定剂采用甲基硫酸有机锡稳定剂。
4.一种如权利要求1所述PVC硬挺复合布的生产工艺,其特征在于,包括以下步骤:
1)将布料浸入清洗槽中的清水中,向清洗槽内添加适量的草酸,清洗水温为60-90℃;
2)清洗后,对布料进行冲洗,将布料中的草酸残留物冲洗干净;
3)取出冲洗干净的布料,先脱干,再烘干,冷却后,拉幅定型;
4)按权利要求1所述重量百分比将聚氯乙烯树脂、碳酸钙、聚己二醇、PVC稳定剂、邻苯二甲酸二壬酯(DINP)、环保增塑剂及有机锡稳定剂放入搅拌机中,搅拌15-25分钟,使其成为糊状的浆料;
5)将浆料置于20-30℃的常温室中20-30小时;
6)将浆料均匀地涂在经步骤1)至步骤3)处理过的上层布料和下层布料之间,并放入刮塑机经过150-200℃的高温滚压、烘干,烘干温度为160-180℃,最后得成品。