CN102965814A - 双色双抗双面料及其生产方法 - Google Patents

双色双抗双面料及其生产方法 Download PDF

Info

Publication number
CN102965814A
CN102965814A CN2012104857984A CN201210485798A CN102965814A CN 102965814 A CN102965814 A CN 102965814A CN 2012104857984 A CN2012104857984 A CN 2012104857984A CN 201210485798 A CN201210485798 A CN 201210485798A CN 102965814 A CN102965814 A CN 102965814A
Authority
CN
China
Prior art keywords
cloth
fabric
looped pile
teeth
speed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012104857984A
Other languages
English (en)
Inventor
刘桂芬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Shenli Enterprise Co Ltd
Original Assignee
Jiangsu Shenli Enterprise Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Shenli Enterprise Co Ltd filed Critical Jiangsu Shenli Enterprise Co Ltd
Priority to CN2012104857984A priority Critical patent/CN102965814A/zh
Publication of CN102965814A publication Critical patent/CN102965814A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种双色双抗双面料及其生产方法，所述双色双抗双面料由100D/36F的平针线圈和单色的75D/144FCD阳离子丝的拉长沉降弧的毛圈线圈和单色的150D/96F的拉长沉降弧的毛圈线圈经过纬编依次串套而成，所述75D/144FCD阳离子丝的拉长沉降弧的毛圈线圈的涤纶为70%改性阳离子涤纶，先将平针线圈层和拉长沉降弧的毛圈线圈层经过纬编依次串套成面料，在对面料进行染色和烘干后，将面料进行后处理，最后在面料上附着保暖剂，本发明经过后整理，舒适柔软占色度牢，同时具有保暖功能，穿在身上舒适得体。

Description

双色双抗双面料及其生产方法
技术领域
本发明涉及纺织领域，尤其是一种双色双抗双面料及其生产方法。
背景技术
随着人们生活水平的提高，人们对穿着的服装也提出了更高的要求，现有的面料由涤纶纱线经过十字编织法编织而成，保暖性差，穿在身上也不美观舒适。
发明内容
本发明针对上述的不足提供了一种双色双抗双面料及其生产方法。
本发明为实现这一目的，所采用的方法是：一种双色双抗双面料，所述双色双抗双面料由100D/36F的平针线圈和单色的75D/144FCD阳离子丝的拉长沉降弧的毛圈线圈和单色的150D/96F的拉长沉降弧的毛圈线圈经过纬编依次串套而成，所述双色双抗双面料上附着有保暖剂，所述75D/144FCD阳离子丝的拉长沉降弧的毛圈线圈中的涤纶为70%改性阳离子涤纶。
一种双色双抗双面料的生产方法，步骤如下：
将所述平针线圈层和拉长沉降弧的毛圈线圈层经过大圆机纬编依次串套成布匹；
将布匹采用分散阳离子染料染色，其中染料的助剂为冰醋酸0.8g/L，高温匀染剂1.2g/L，醋酸钠0.5 g/L，进布后升温到130℃,保温30分钟，浴比为1：12，PH值为5，然后将面料取出采用还原清洗，在清洗液中加入保险粉1.5g/L，烧碱2.5g/L，浴比为1：12，升温80℃，保温20分钟，再对布匹进行中和水洗，在清洗液中加入冰醋酸1g/L，浴比为1:12，升温60℃，保温15min，最后将布匹放入烘干机温度为130℃，布速20m/min；
将布匹的上下面的毛圈均进行拉毛处理，小毛圈拉3次，大毛圈拉3次，齿轮小毛圈拉毛力度为51牙、47牙、44牙，齿轮大毛圈的拉毛力度为52牙、48牙、45牙，然后将布匹放入刷毛机进行刷毛，毛刷转速为1200r/min，车速为20m/min，然后对布匹进行剪毛，布速25m/min，滚刀速度1200r/min、再将布匹在60℃温度下干滚30分钟进行摇粒，最后对布匹进行定型处理，温度为150℃，布速为30m/min，风速为1000m/s；
将面料在最后一道定型处理时采用一浸一轧法,浸轧时加入保暖剂,带液率为80%，将面料在130℃的高温下烘干，在150℃的高温下焙烘2分钟。
本发明的有益效果是：该面料经过拉毛、刷毛、剪毛和摇粒和定型处理，然后浸入药剂，使得面料舒适柔软占色度牢，同时具有保暖功能，穿在身上舒适得体。
附图说明
图1是本发明的结构示意图。
如图所示1-平针线圈、2-拉长沉降弧的毛圈线圈、3-拉长沉降弧的毛圈线圈。
具体实施方式
本说明书中公开的所有特征，或公开的所有方法或过程中的步骤，除了互相排斥的特征和/或步骤以外，均可以以任何方式组合。
如图1所示一种双色双抗双面料及其生产方法，所述双色双抗双面料由100D/36F的平针线圈1和单色的75D/144FCD阳离子丝的拉长沉降弧的毛圈线圈2和单色的150D/96F的拉长沉降弧的毛圈线圈3经过纬编依次串套而成，所述75D/144FCD阳离子丝的拉长沉降弧的毛圈线圈2中的涤纶为70%改性阳离子涤纶。将所述平针线圈层和拉长沉降弧的毛圈线圈层经过大圆机纬编依次串套成布匹，将布匹采用分散阳离子染料染色，其中染料的助剂为冰醋酸0.8g/L，高温匀染剂1.2g/L，醋酸钠0.5 g/L，进布后升温到130℃,保温30分钟，浴比为1：12，PH值为4.5，然后将面料取出采用还原清洗，在清洗液中加入保险粉1.5g/L，烧碱2.5g/L，浴比为1：12，升温80℃，保温20分钟，再对布匹进行中和水洗，在清洗液中加入冰醋酸1g/L，浴比为1:12，升温60℃，保温15min，最后将布匹放入烘干机温度为130℃，布速20m/min，将布匹的上下面的毛圈均进行拉毛处理，小毛圈拉3次，大毛圈拉3次，齿轮小毛圈拉毛力度为51牙、47牙、44牙，齿轮大毛圈的拉毛力度为52牙、48牙、45牙，然后将布匹放入刷毛机进行刷毛，毛刷转速为1200r/min，车速为20m/min，然后对布匹进行剪毛，布速25m/min，滚刀速度1200r/min、再将布匹在60℃温度下干滚30分钟进行摇粒，最后对布匹进行定型处理，温度为150℃，布速为30m/min，风速为1000m/s，将面料在最后一道定型处理时采用一浸一轧法,浸轧时加入保暖剂,带液率为80%，将面料在130℃的高温下烘干，在150℃的高温下焙烘2分钟。
实施例1
所述保暖剂为德国拓纳的HOT2药剂，使用量为3%（O.W.F）。
本发明并不局限于前述的具体实施方式。本发明扩展到任何在本说明书中披露的新特征或任何新的组合，以及披露的任一新的方法或过程的步骤或任何新的组合。

Claims (2)

1.一种双色双抗双面料，其特征在于：所述双色双抗双面料由100D/36F的平针线圈（1）和单色的75D/144FCD阳离子丝的拉长沉降弧的毛圈线圈（2）和单色的150D/96F的拉长沉降弧的毛圈线圈（3）经过纬编依次串套而成，所述双色双抗双面料上附着有保暖剂，所述75D/144FCD阳离子丝的拉长沉降弧的毛圈线圈（2）中的涤纶为70%改性阳离子涤纶。
2.一种双色双抗双面料的生产方法，其特征在于，所述生产步骤如下：
将所述平针线圈层和拉长沉降弧的毛圈线圈层经过大圆机纬编依次串套成布匹；
将布匹采用分散阳离子染料，其中染料的助剂为冰醋酸0.8g/L，高温匀染剂1.2g/L，醋酸钠0.5 g/L，进布后升温到130℃,保温30分钟，浴比为1：12，PH值为5，然后将面料取出采用还原清洗，在清洗液中加入保险粉1.5g/L，烧碱2.5g/L，浴比为1：12，升温80℃，保温20分钟，再对布匹进行中和水洗，在清洗液中加入冰醋酸1g/L，浴比为1:12，升温60℃，保温15min，最后将布匹放入烘干机温度为130℃，布速20m/min；
将布匹的上下面的毛圈均进行拉毛处理，小毛圈拉3次，大毛圈拉3次，齿轮小毛圈拉毛力度为51牙、47牙、44牙，齿轮大毛圈的拉毛力度为52牙、48牙、45牙，然后将布匹放入刷毛机进行刷毛，毛刷转速为1200r/min，车速为20m/min，然后对布匹进行剪毛，布速25m/min，滚刀速度1200r/min、再将布匹在60℃温度下干滚30分钟进行摇粒，最后对布匹进行定型处理，温度为150℃，布速为30m/min，风速为1000m/s；
将面料在最后一道定型处理时采用一浸一轧法,浸轧时加入保暖剂,带液率为80%，将面料在130℃的高温下烘干，在150℃的高温下焙烘2分钟。
CN2012104857984A 2012-11-26 2012-11-26 双色双抗双面料及其生产方法 Pending CN102965814A (zh)