CN105310378B - 一种纤丝绒拉舍尔毛毯的生产工艺 - Google Patents

一种纤丝绒拉舍尔毛毯的生产工艺 Download PDF

Info

Publication number
CN105310378B
CN105310378B CN201510724070.6A CN201510724070A CN105310378B CN 105310378 B CN105310378 B CN 105310378B CN 201510724070 A CN201510724070 A CN 201510724070A CN 105310378 B CN105310378 B CN 105310378B
Authority
CN
China
Prior art keywords
floss
fibril
rachael blanket
finished product
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510724070.6A
Other languages
English (en)
Other versions
CN105310378A (zh
Inventor
毛青山
陈玉霜
郑其明
孟波
毛森贤
厉巽巽
吴明贤
俞宏斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Truelove Blanket Industry Technology Co Ltd
Original Assignee
Zhejiang Truelove Blanket Industry Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Truelove Blanket Industry Technology Co Ltd filed Critical Zhejiang Truelove Blanket Industry Technology Co Ltd
Priority to CN201510724070.6A priority Critical patent/CN105310378B/zh
Publication of CN105310378A publication Critical patent/CN105310378A/zh
Application granted granted Critical
Publication of CN105310378B publication Critical patent/CN105310378B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种纤丝绒拉舍尔毛毯的生产工艺,包括以下步骤:1)纱线选择;2)编织;3)前整理;4)染色;5)后整理。本发明对整个生产工艺进行了优化改进,通过提高正面烫光温度,以增加毛毯的蓬松性;在染色过程中选用了环保的染料助剂,绝对绿色环保,该产品顺应国际纺织产业绿色、环保、生态的发展趋势,达到了天然、环保、舒适的效果,项目的实施有着良好的经济效益和社会效益。

Description

一种纤丝绒拉舍尔毛毯的生产工艺
技术领域
本发明涉及功能性拉舍尔毛毯生产技术领域,尤其是涉及一种环保,具有手感滑爽、吸湿透气性好、色泽亮丽、毯面丰满圆滑、保暖性好纤丝绒拉舍尔毛毯的生产工艺。
背景技术
随着人类对地球保护意识、能源枯竭意识、安全意识和纺织卫生意识的增强,追求时尚,生态、环保、健康逐渐成为主流意识。浙江真爱毯业科技有限公司研制开发的纤丝绒拉舍尔毛毯,所用原料纤丝绒是多孔超细旦涤纶丝,纤细如天然羽绒,具有极佳的手感和保暖性,纤细致密的纤维层能锁定空气,产生稳定的静止空气层,起到保暖防寒的功效,纤维长期使用后也不会相互缠结,保持优良的蓬松性,在保暖性能和蓬松性与天然羽绒媲美的同时,它的化学纤维的本性又赋予它不霉变生螨,易水洗易储存的优势。
咖啡碳纤维是利用喝完咖啡后剩下的咖啡渣,经煅烧后制成晶体,再研磨成纳米粉体,加入到涤纶纤维中,生产出一种功能性涤纶基纤维-咖啡碳纤维,其具有抑菌除臭、发散负离子和抗紫外线、蓄热保温、低碳环保的功能和特色。
中国专利公开号CN 1661151 A,公开日2005年8月31日,名称为莫代尔棉拉舍尔毛毯,该申请案公开了一种莫代尔棉拉舍尔毛毯,以莫代尔和面替代腈纶,由下述重量百分比的原料配制:莫代尔35-50%、棉30-40%、涤纶15-30%,制作方法为,涤纶长丝整经,莫代尔和棉混纺后的毛纱整经,编织,剖绒,检验,入半成品仓库。其不足之处在于,莫代尔和棉的混纺纱属于棉型纱,只适合做薄型毛毯,光泽黯淡,手感较差,且没有保健功能。
发明内容
本发明的目的在于为了解决现有制作的毛毯光泽黯淡,手感较差,且没有保健功能的缺陷而提供一种环保,具有手感滑爽、吸湿透气性好、色泽亮丽、毯面丰满圆滑、保暖性好纤丝绒拉舍尔毛毯的生产工艺。
为了实现上述目的,本发明采用以下技术方案:
一种纤丝绒拉舍尔毛毯的生产工艺,其特征在于,包括以下步骤:
1)纱线选择:以多孔超细旦涤纶丝与咖啡碳纤维变形丝作为毛绒纱,涤纶牵伸丝作为地纱,多孔超细旦涤纶丝与咖啡碳纤维变形丝的质量比为2:1;
2)编织:在双针床经编机上对毛绒纱和地纱进行编织、剖绒,得纤丝绒拉舍尔毛毯半成品;
3)前整理:将步骤2)得到的纤丝绒拉舍尔毛毯半成品进行定型、刷毛、烫光、打卷;
4)染色:将染色液pH调节至5.8-6.8后,将纤丝绒拉舍尔毛毯半成品置于染色液中进行染色,之后用还原清洗液对染色后的纤丝绒拉舍尔毛毯半成品进行还原清洗,再用质量百分浓度为0.5-0.6%的醋酸溶液中和,水洗出缸,之后烘干,对烘干后的纤丝绒拉舍尔毛毯半成品进行蒸化,蒸化后用柔软液进行柔软平滑处理,最后再烘干;
5)后整理:对染色后的纤丝绒拉舍尔毛毯半成品依次进行烘干定型、正面烫光、正面刷毛、正面烫剪、背面起毛、背面刷毛、背面烫光、背面抓剪、复定型、正面烫剪、背面烫剪、切条缝合,即得纤丝绒拉舍尔毛毯成品,最后将成品检验后包装后入库。
在本技术方案中,本发明以150D/72F多孔超细旦涤纶丝作为毛绒纱,150D/36F FDY涤纶牵伸丝作为编链、衬纬纱在 HDR5DPLM30拉舍尔经编机上织造, 整经过程中通过减小纱线张力,利用H40-21NC电脑控制(CNC)拷贝整经机的优良性能,保证纱线张力均匀一致;在织造过程,通过控制车间的相对温湿度,结合HDR5DPLM30拉舍尔经编机的性能,设计出符合其特性的上机组织。对剖绒后的白坯布先进行预定型和烫光处理,使染色前的毯面绒毛卷曲度降低,毛束散松有利于染色、柔软处理及后整理加工。
作为优选,多孔超细旦涤纶丝的规格为150D/72F,咖啡碳纤维变形丝的规格为140D/70F-160D/150F,涤纶牵伸丝的规格为150D/36F。
作为优选,步骤(2)中编织的具体工艺为:在机号为16-20,型号为E2291A的双针床经编机上,前后针床隔距为12mm,编织速度为430-450转/分;用1、6号梳栉在前后针床分别编织3针衬纬组织,2、5号梳栉在前后针床分别编织开口编链组织,3、4号梳栉在前后针床编织闭口编链组织毛绒。
作为优选,步骤3)定型时,将纤丝绒拉舍尔毛毯半成品在室温下浸入处理液中,处理液以2℃/min的速率升温至50℃,然后保温45min,以3℃/min的速率降温至室温后将纤丝绒拉舍尔毛毯半成品取出水洗,处理液中含有以下物质:硅酸钠0.3g/L、元明粉2g/L、硅酸铝0.22g/L、甲壳素1.2g/L与渗透剂0.5g/L,浴比1:20。
作为优选,步骤4)中,染色液pH用醋酸或硫酸铵调节,染色浴比 1:10-12,染色温度为140-155℃,染色时间为45-55min,染色液的具体配方为:Lonsperse EE系列分散染料0.7-0.8g/L、花青素1.1-1.3 g/L、高温分散剂1-2g/L与高温匀染剂0.5-1g/L。
作为优选,步骤4)中还原清洗液包括1.5-2.5g/L的净洗剂、1.5-2.5g/L的表面活性剂、10-15g/L海藻粉与1.2-2.1g/L的海藻酸钠,浴比1:20,温度50-55℃,清洗时间30min。在本技术方案中,在还原清洗柔软处理时,加入合成净洗剂及表面活性剂,使纤丝绒拉舍尔毛毯具有柔软滑爽、光泽亮丽,染深色时加入Na3CO3和保险粉,更有效的去除纤维表面的浮色。在还原清洗液中加入海藻粉是是为了使其在毛毯表面形成一层膜来保护毛毯,具有防氧化功能。在助剂中加入茶多酚与纳米二氧化钛,则是为了提高毛毯的抗氧化功能与抗菌性能。
作为优选,步骤5)后整理中,烘干定型采用FIR4烘干定型机,逆毛进机,定型门幅158-162cm,温度110-120℃,定型速度17-20m/min;刷毛采用MB211E型双辊刷毛机,速度3-4m/min,顺毛进机,刷毛隔距2.5mm;烫光采用SME473H型单辊二次烫剪机,烫光温度120-130℃,速度7-10m/min;烫剪采用MB322E型高速高效烫剪机,对纤丝绒拉舍尔毛毯正面进行烫剪,温度120-130℃,速度8-10m/min;起毛采用ME331E起毛机,对纤丝绒拉舍尔毛毯反面进行起毛,速度8-10m/min。
作为优选,所述生产工艺还包括印花、烘燥、蒸化固色、水洗;印花步骤是将坯布放入印花机进行印花,印花机的磁力采用12-15kg,磁车速度为20-24m/min,网版目数60-75目,刮印次数为5-7次;烘燥步骤是将印花后的花坯布放入渗透机,渗透压力位12-15kg,然后在160-170℃温度下将花坯布烘干;蒸化固色步骤是将烘燥后的花坯布放入蒸化锅进行蒸化固色处理,蒸化温度为145-155℃,蒸化时间为25-35min;其中,印花步骤是在步骤4)染色完成之后之后开始。
作为优选,蒸化固色完成后的坯布进行水洗,水洗工艺流程:清水槽→清水槽→清水槽→高温皂洗槽→清水槽→清水槽→清水槽→清水槽→柔软剂槽,高温皂洗槽的温度为92-95℃,柔软剂槽中柔软剂的质量分数为4.2-4.5%,平滑剂的质量分数为0.08-0.1%,柔软剂槽中还加有质量分数0.1-0.3%的香兰素,余量为水。
本发明的有益效果:
1)本发明制备的纤丝绒拉舍尔毛毯环保,具有手感滑爽、吸湿透气性好、色泽亮丽、毯面丰满圆滑、保暖性好,同时具有远红外发射、负离子等保健功能;
2)咖啡碳纤维是利用喝完咖啡后剩下的咖啡渣,经煅烧后制成晶体,再研磨成纳米粉体,加入到涤纶纤维中,生产出一种功能性涤纶基纤维-咖啡碳纤维,其具有抑菌除臭、发散负离子和抗紫外线、蓄热保温、低碳环保的功能和特色;
3)在染色过程中选用了环保的染料助剂,绝对绿色环保,该产品顺应国际纺织产业绿色、环保、生态的发展趋势,达到了天然、环保、舒适的效果,项目的实施有着良好的经济效益和社会效益。
具体实施方式
以下结合具体实施例,对本发明做进一步的解释:
在本发明中,若非特指,所有设备和原料均可从市场购得或是本行业常用的,其中,合成净洗剂购自上虞市海峰化工有限公司;表面活性剂购自广州弈城化工有限公司;下述实施例中的方法,如无特别说明,均为本领域常规方法。
多孔超细旦涤纶丝的规格为150D/72F,咖啡碳纤维变形丝的规格为140D/70F-160D/150F,涤纶牵伸丝的规格为150D/36F。
实施例1
一种纤丝绒拉舍尔毛毯的生产工艺,包括以下步骤:
1)纱线选择:以多孔超细旦涤纶丝与咖啡碳纤维变形丝作为毛绒纱,涤纶牵伸丝作为地纱,多孔超细旦涤纶丝与咖啡碳纤维变形丝的质量比为2:1;
2)编织:在双针床经编机上对毛绒纱和地纱进行编织、剖绒,得纤丝绒拉舍尔毛毯半成品;编织的具体工艺为:在机号为16-20,型号为E2291A的双针床经编机上,前后针床隔距为12mm,编织速度为430转/分;用1、6号梳栉在前后针床分别编织3针衬纬组织,2、5号梳栉在前后针床分别编织开口编链组织,3、4号梳栉在前后针床编织闭口编链组织毛绒;
3)前整理:将步骤2)得到的纤丝绒拉舍尔毛毯半成品进行定型、刷毛、烫光、打卷;定型时,将纤丝绒拉舍尔毛毯半成品在室温下浸入处理液中,处理液以2℃/min的速率升温至50℃,然后保温45min,以3℃/min的速率降温至室温后将纤丝绒拉舍尔毛毯半成品取出水洗,处理液中含有以下物质:硅酸钠0.3g/L、元明粉2g/L、硅酸铝0.22g/L、甲壳素1.2g/L与渗透剂0.5g/L,浴比1:20;
4)染色:将染色液pH调节至5.8后,将纤丝绒拉舍尔毛毯半成品置于染色液中进行染色,之后用还原清洗液对染色后的纤丝绒拉舍尔毛毯半成品进行还原清洗,再用质量百分浓度为0.5%的醋酸溶液中和,水洗出缸,之后烘干,对烘干后的纤丝绒拉舍尔毛毯半成品进行蒸化,蒸化后用柔软液进行柔软平滑处理,最后再烘干;染色液pH用硫酸铵调节,染色浴比 1:10,染色温度为140℃,染色时间为45min,染色液的具体配方为: Lonsperse黄棕EE 0.7g/L、花青素1.1 g/L、高温分散剂1g/L与高温匀染剂0.5g/L;还原清洗液包括1.5g/L的净洗剂、1.5g/L的表面活性剂、10g/L海藻粉与1.2g/L的海藻酸钠,浴比1:20,温度50℃,清洗时间30min;染色完成之后,开始印花步骤,印花步骤是将坯布放入印花机进行印花,印花机的磁力采用12kg,磁车速度为20m/min,网版目数60目,刮印次数为5次;烘燥步骤是将印花后的花坯布放入渗透机,渗透压力位12kg,然后在160℃温度下将花坯布烘干;蒸化固色步骤是将烘燥后的花坯布放入蒸化锅进行蒸化固色处理,蒸化温度为145℃,蒸化时间为25min;蒸化固色完成后的坯布进行水洗,水洗工艺流程:清水槽→清水槽→清水槽→高温皂洗槽→清水槽→清水槽→清水槽→清水槽→柔软剂槽,高温皂洗槽的温度为92℃,柔软剂槽中柔软剂的质量分数为4.2%,平滑剂的质量分数为0.08%,柔软剂槽中还加有质量分数0.1%的香兰素,余量为水;
5)后整理:对染色后的纤丝绒拉舍尔毛毯半成品依次进行烘干定型、正面烫光、正面刷毛、正面烫剪、背面起毛、背面刷毛、背面烫光、背面抓剪、复定型、正面烫剪、背面烫剪、切条缝合,即得纤丝绒拉舍尔毛毯成品,最后将成品检验后包装后入库;后整理中,烘干定型采用FIR4烘干定型机,逆毛进机,定型门幅158cm,温度110℃,定型速度17m/min;刷毛采用MB211E型双辊刷毛机,速度3m/min,顺毛进机,刷毛隔距2.5mm;烫光采用SME473H型单辊二次烫剪机,烫光温度120℃,速度7m/min;烫剪采用MB322E型高速高效烫剪机,对纤丝绒拉舍尔毛毯正面进行烫剪,温度120℃,速度8m/min;起毛采用ME331E起毛机,对纤丝绒拉舍尔毛毯反面进行起毛,速度8m/min。
实施例2
一种纤丝绒拉舍尔毛毯的生产工艺,包括以下步骤:
1)纱线选择:以多孔超细旦涤纶丝与咖啡碳纤维变形丝作为毛绒纱,涤纶牵伸丝作为地纱,多孔超细旦涤纶丝与咖啡碳纤维变形丝的质量比为2:1;
2)编织:在双针床经编机上对毛绒纱和地纱进行编织、剖绒,得纤丝绒拉舍尔毛毯半成品;编织的具体工艺为:在机号为16-20,型号为E2291A的双针床经编机上,前后针床隔距为12mm,编织速度为440转/分;用1、6号梳栉在前后针床分别编织3针衬纬组织,2、5号梳栉在前后针床分别编织开口编链组织,3、4号梳栉在前后针床编织闭口编链组织毛绒;
3)前整理:将步骤2)得到的纤丝绒拉舍尔毛毯半成品进行定型、刷毛、烫光、打卷;定型时,将纤丝绒拉舍尔毛毯半成品在室温下浸入处理液中,处理液以2℃/min的速率升温至50℃,然后保温45min,以3℃/min的速率降温至室温后将纤丝绒拉舍尔毛毯半成品取出水洗,处理液中含有以下物质:硅酸钠0.3g/L、元明粉2g/L、硅酸铝0.22g/L、甲壳素1.2g/L与渗透剂0.5g/L,浴比1:20;
4)染色:将染色液pH调节至6后,将纤丝绒拉舍尔毛毯半成品置于染色液中进行染色,之后用还原清洗液对染色后的纤丝绒拉舍尔毛毯半成品进行还原清洗,再用质量百分浓度为0.55%的醋酸溶液中和,水洗出缸,之后烘干,对烘干后的纤丝绒拉舍尔毛毯半成品进行蒸化,蒸化后用柔软液进行柔软平滑处理,最后再烘干;染色液pH用醋酸调节,染色浴比 1:11,染色温度为150℃,染色时间为50min,染色液的具体配方为:Lonsperse红玉EE 0.75g/L、花青素1.2 g/L、高温分散剂1.5g/L与高温匀染剂0.8g/L;还原清洗液包括1.8g/L的净洗剂、2g/L的表面活性剂、13g/L海藻粉与1.5g/L的海藻酸钠,浴比1:20,温度53℃,清洗时间30min;染色完成之后,开始印花步骤,印花步骤是将坯布放入印花机进行印花,印花机的磁力采用13kg,磁车速度为22m/min,网版目数68目,刮印次数为6次;烘燥步骤是将印花后的花坯布放入渗透机,渗透压力位14kg,然后在165℃温度下将花坯布烘干;蒸化固色步骤是将烘燥后的花坯布放入蒸化锅进行蒸化固色处理,蒸化温度为150℃,蒸化时间为30min;蒸化固色完成后的坯布进行水洗,水洗工艺流程:清水槽→清水槽→清水槽→高温皂洗槽→清水槽→清水槽→清水槽→清水槽→柔软剂槽,高温皂洗槽的温度为93℃,柔软剂槽中柔软剂的质量分数为4.3%,平滑剂的质量分数为0.09%,柔软剂槽中还加有质量分数0.2%的香兰素,余量为水;
5)后整理:对染色后的纤丝绒拉舍尔毛毯半成品依次进行烘干定型、正面烫光、正面刷毛、正面烫剪、背面起毛、背面刷毛、背面烫光、背面抓剪、复定型、正面烫剪、背面烫剪、切条缝合,即得纤丝绒拉舍尔毛毯成品,最后将成品检验后包装后入库;后整理中,烘干定型采用FIR4烘干定型机,逆毛进机,定型门幅160cm,温度115℃,定型速度18m/min;刷毛采用MB211E型双辊刷毛机,速度3.5m/min,顺毛进机,刷毛隔距2.5mm;烫光采用SME473H型单辊二次烫剪机,烫光温度125℃,速度8m/min;烫剪采用MB322E型高速高效烫剪机,对纤丝绒拉舍尔毛毯正面进行烫剪,温度125℃,速度9m/min;起毛采用ME331E起毛机,对纤丝绒拉舍尔毛毯反面进行起毛,速度9m/min。
实施例3
一种纤丝绒拉舍尔毛毯的生产工艺,包括以下步骤:
1)纱线选择:以多孔超细旦涤纶丝与咖啡碳纤维变形丝作为毛绒纱,涤纶牵伸丝作为地纱,多孔超细旦涤纶丝与咖啡碳纤维变形丝的质量比为2:1;
2)编织:在双针床经编机上对毛绒纱和地纱进行编织、剖绒,得纤丝绒拉舍尔毛毯半成品;编织的具体工艺为:在机号为16-20,型号为E2291A的双针床经编机上,前后针床隔距为12mm,编织速度为450转/分;用1、6号梳栉在前后针床分别编织3针衬纬组织,2、5号梳栉在前后针床分别编织开口编链组织,3、4号梳栉在前后针床编织闭口编链组织毛绒;
3)前整理:将步骤2)得到的纤丝绒拉舍尔毛毯半成品进行定型、刷毛、烫光、打卷;定型时,将纤丝绒拉舍尔毛毯半成品在室温下浸入处理液中,处理液以2℃/min的速率升温至50℃,然后保温45min,以3℃/min的速率降温至室温后将纤丝绒拉舍尔毛毯半成品取出水洗,处理液中含有以下物质:硅酸钠0.3g/L、元明粉2g/L、硅酸铝0.22g/L、甲壳素1.2g/L与渗透剂0.5g/L,浴比1:20;
4)染色:将染色液pH调节至6.8后,将纤丝绒拉舍尔毛毯半成品置于染色液中进行染色,之后用还原清洗液对染色后的纤丝绒拉舍尔毛毯半成品进行还原清洗,再用质量百分浓度为0.6%的醋酸溶液中和,水洗出缸,之后烘干,对烘干后的纤丝绒拉舍尔毛毯半成品进行蒸化,蒸化后用柔软液进行柔软平滑处理,最后再烘干;染色液pH用硫酸铵调节,染色浴比 1:12,染色温度为155℃,染色时间为55min,染色液的具体配方为:Lonsperse藏青EE 0.8g/L、花青素1.3 g/L、高温分散剂2g/L与高温匀染剂1g/L;还原清洗液包括2.5g/L的净洗剂、2.5g/L的表面活性剂、15g/L海藻粉与2.1g/L的海藻酸钠,浴比1:20,温度55℃,清洗时间30min;染色完成之后,开始印花步骤,印花步骤是将坯布放入印花机进行印花,印花机的磁力采用15kg,磁车速度为24m/min,网版目数75目,刮印次数为7次;烘燥步骤是将印花后的花坯布放入渗透机,渗透压力位15kg,然后在170℃温度下将花坯布烘干;蒸化固色步骤是将烘燥后的花坯布放入蒸化锅进行蒸化固色处理,蒸化温度为155℃,蒸化时间为35min;蒸化固色完成后的坯布进行水洗,水洗工艺流程:清水槽→清水槽→清水槽→高温皂洗槽→清水槽→清水槽→清水槽→清水槽→柔软剂槽,高温皂洗槽的温度为95℃,柔软剂槽中柔软剂的质量分数为4.5%,平滑剂的质量分数为0.1%,柔软剂槽中还加有质量分数0.3%的香兰素,余量为水;
5)后整理:对染色后的纤丝绒拉舍尔毛毯半成品依次进行烘干定型、正面烫光、正面刷毛、正面烫剪、背面起毛、背面刷毛、背面烫光、背面抓剪、复定型、正面烫剪、背面烫剪、切条缝合,即得纤丝绒拉舍尔毛毯成品,最后将成品检验后包装后入库;后整理中,烘干定型采用FIR4烘干定型机,逆毛进机,定型门幅162cm,温度120℃,定型速度20m/min;刷毛采用MB211E型双辊刷毛机,速度4m/min,顺毛进机,刷毛隔距2.5mm;烫光采用SME473H型单辊二次烫剪机,烫光温度130℃,速度10m/min;烫剪采用MB322E型高速高效烫剪机,对纤丝绒拉舍尔毛毯正面进行烫剪,温度130℃,速度10m/min;起毛采用ME331E起毛机,对纤丝绒拉舍尔毛毯反面进行起毛,速度10m/min。
经测试,纤丝绒拉舍尔毛毯向发射率为0.86,由于人体也是红外线放射提,所发射5.6-15μm远红外线占整个人体总能量的50%,因此本发明的纤丝绒拉舍尔毛毯对人体是及其有益的,人体70-80%是由水分子组成,在共振作用下,首先激活了水分子的振动能级。本发明的纤丝绒拉舍尔毛毯能够激活生物大分子的活性,促进和改善血液循环,增强新陈代谢,提高人体免疫功能,具有消炎、消肿、镇痛的作用。
以上所述的实施例只是本发明的一种较佳的方案,并非对本发明作任何形式上的限制,在不超出权利要求所记载的技术方案的前提下还有其它的变体及改型。

Claims (7)

1.一种纤丝绒拉舍尔毛毯的生产工艺,其特征在于,包括以下步骤:
1)纱线选择:以多孔超细旦涤纶丝与咖啡碳纤维变形丝作为毛绒纱,涤纶牵伸丝作为地纱,多孔超细旦涤纶丝与咖啡碳纤维变形丝的质量比为2:1;
2)编织:在双针床经编机上对毛绒纱和地纱进行编织、剖绒,得纤丝绒拉舍尔毛毯半成品;
3)前整理:将步骤2)得到的纤丝绒拉舍尔毛毯半成品进行定型、刷毛、烫光、打卷;
4)染色:将染色液pH调节至5.8-6.8后,将纤丝绒拉舍尔毛毯半成品置于染色液中进行染色,之后用还原清洗液对素染后的纤丝绒拉舍尔毛毯半成品进行还原清洗,再用质量百分浓度为0.5-0.6%的醋酸溶液中和,水洗出缸,之后烘干,对烘干后的纤丝绒拉舍尔毛毯半成品进行蒸化,蒸化后用柔软液进行柔软平滑处理,最后再烘干;
5)后整理:对染色后的纤丝绒拉舍尔毛毯半成品依次进行烘干定型、正面烫光、正面刷毛、正面烫剪、背面起毛、背面刷毛、背面烫光、背面抓剪、复定型、正面烫剪、背面烫剪、切条缝合,即得纤丝绒拉舍尔毛毯成品,最后将成品检验后包装后入库;
所述生产工艺还包括印花、烘燥、蒸化固色、水洗;印花步骤是将坯布放入印花机进行印花,印花机的磁力采用12-15kg,磁车速度为20-24m/min,网版目数60-75目,刮印次数为5-7次;烘燥步骤是将印花后的花坯布放入渗透机,渗透压力为12-15kg,然后在160-170℃温度下将花坯布烘干;蒸化固色步骤是将烘燥后的花坯布放入蒸化锅进行蒸化固色处理,蒸化温度为145-155℃,蒸化时间为25-35min;其中,印花步骤是在步骤4)染色完成之后开始;
蒸化固色完成后的坯布进行水洗,水洗工艺流程:清水槽→清水槽→清水槽→高温皂洗槽→清水槽→清水槽→清水槽→清水槽→柔软剂槽,高温皂洗槽的温度为92-95℃,柔软剂槽中柔软剂的质量分数为4.2-4.5%,平滑剂的质量分数为0.08-0.1%,柔软剂槽中还加有质量分数0.1-0.3%的香兰素,余量为水。
2.根据权利要求1所述的一种纤丝绒拉舍尔毛毯的生产工艺,其特征在于,多孔超细旦涤纶丝的规格为150D/72F,咖啡碳纤维变形丝的规格为140D/70F-160D/150F,涤纶牵伸丝的规格为150D/36F。
3.根据权利要求1所述的一种纤丝绒拉舍尔毛毯的生产工艺,其特征在于,步骤(2)中编织的具体工艺为:在机号为16-20,型号为E2291A的双针床经编机上,前后针床隔距为12mm,编织速度为430-450转/分;用1、6号梳栉在前后针床分别编织3针衬纬组织,2、5号梳栉在前后针床分别编织开口编链组织,3、4号梳栉在前后针床编织闭口编链组织毛绒。
4.根据权利要求1所述的一种纤丝绒拉舍尔毛毯的生产工艺,其特征在于,步骤3)定型时,将纤丝绒拉舍尔毛毯半成品在室温下浸入处理液中,处理液以2℃/min的速率升温至50℃,然后保温45min,以3℃/min的速率降温至室温后将纤丝绒拉舍尔毛毯半成品取出水洗,处理液中含有以下物质:硅酸钠0.3g/L、元明粉2g/L、硅酸铝0.22g/L、甲壳素1.2g/L与渗透剂0.5g/L,浴比1:20。
5.根据权利要求1所述的一种纤丝绒拉舍尔毛毯的生产工艺,其特征在于,步骤4)中,染色液pH用醋酸或硫酸铵调节,染色浴比 1:10-12,染色温度为140-155℃,染色时间为45-55min,染色液的具体配方为:Lonsperse EE系列分散染料0.7-0.8g/L、花青素1.1-1.3 g/L、高温分散剂1-2g/L与高温匀染剂0.5-1g/L。
6.根据权利要求1或5所述的一种纤丝绒拉舍尔毛毯的生产工艺,其特征在于,步骤4)中还原清洗液包括1.5-2.5g/L的净洗剂、1.5-2.5g/L的表面活性剂、10-15g/L海藻粉与1.2-2.1g/L的海藻酸钠,浴比1:20,温度50-55℃,清洗时间30min。
7.根据权利要求1所述的一种纤丝绒拉舍尔毛毯的生产工艺,其特征在于,步骤5)后整理中,烘干定型采用FIR4烘干定型机,逆毛进机,定型门幅158-162cm,温度110-120℃,定型速度17-20m/min;刷毛采用MB211E型双辊刷毛机,速度3-4m/min,顺毛进机,刷毛隔距2.5mm;烫光采用SME473H型单辊二次烫剪机,烫光温度120-130℃,速度7-10m/min;烫剪采用MB322E型高速高效烫剪机,对纤丝绒拉舍尔毛毯正面进行烫剪,温度120-130℃,速度8-10m/min;起毛采用ME331E起毛机,对纤丝绒拉舍尔毛毯反面进行起毛,速度8-10m/min。
CN201510724070.6A 2015-10-30 2015-10-30 一种纤丝绒拉舍尔毛毯的生产工艺 Active CN105310378B (zh)