CN102964770A - 一种磁性耐热塑料合金材料及其制备方法 - Google Patents

一种磁性耐热塑料合金材料及其制备方法 Download PDF

Info

Publication number
CN102964770A
CN102964770A CN2012104714374A CN201210471437A CN102964770A CN 102964770 A CN102964770 A CN 102964770A CN 2012104714374 A CN2012104714374 A CN 2012104714374A CN 201210471437 A CN201210471437 A CN 201210471437A CN 102964770 A CN102964770 A CN 102964770A
Authority
CN
China
Prior art keywords
parts
magnetic heat
alloy material
mno
iron powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104714374A
Other languages
English (en)
Other versions
CN102964770B (zh
Inventor
高熠辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Aolin Magnetic Electric Industrial Co., Ltd.
Original Assignee
WUXI CHANG'AN GENERAL METAL PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI CHANG'AN GENERAL METAL PRODUCT CO Ltd filed Critical WUXI CHANG'AN GENERAL METAL PRODUCT CO Ltd
Priority to CN201210471437.4A priority Critical patent/CN102964770B/zh
Publication of CN102964770A publication Critical patent/CN102964770A/zh
Application granted granted Critical
Publication of CN102964770B publication Critical patent/CN102964770B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种磁性耐热塑料合金材料，由以下重量份的组分制备而成：Fe2O3：50-80份；MnO：10-30份；ABS树脂：10-20份；PET：10-20份；邻甲基苯二醇：1-5份；硫酸铵：1-5份；氧化苯甲酸叔丁基：1-5份；固化剂：0.5-2份；月桂酸：0.5-2份；碳粉：0.5-2份；铁粉：5-15份。本发明公开的磁性耐热塑料合金材料具有耐高温性好、力学性能高、发泡倍率高的优点。

Description

一种磁性耐热塑料合金材料及其制备方法
技术领域
本发明涉及一种金属材料，具体地，涉及一种磁性耐热塑料合金材料。
背景技术
目前市场上对于磁性耐热塑料合金材料的需求与日俱增，但却没有相应的产品与之对应，所以对此类产品的研发迫在眉睫。国内市场上少见高耐热磁性塑料合金，少量销售且口碑较好的基本都是进口产品，国内产品的市场占有率更少。
为了提高磁性耐热塑料合金材料的耐热温度，有研究者提出通过加入助交联剂和采用二次辐射交联的方法，提高材料的硫化程度，进而提高材料的耐热温度。加入助交联剂在室温下发挥其交联作用，提高材料的硫化程度，但采用的助交联剂效果有限，无法真正保证材料硫化的充分进行，在高温下该材料极易因硫化不完全发生链段的降解，导致性能迅速劣化，不宜在高温下使用。其次，室温硫化的硅橡胶泡沫材料，属单一基体组分的材料，只能体现出硅橡胶的性能，不如合金基体组分的材料的综合性能优异，如其耐热性和力学性能均不如合金基体组分的材料，不适于在高温及要求高力学性能的环境下使用。此类材料耐高温性差、力学性能低、发泡倍率低的问题。
发明内容
本发明要解决的技术问题是克服现有的缺陷，提供了一种磁性耐热塑料合金材料以及该材料的制备方法。
为了解决上述技术问题，本发明提供了如下的技术方案：
一种磁性耐热塑料合金材料，由以下重量份的组分制备而成：
Fe2O3：50-80份；MnO：10-30份；ABS树脂：10-20份 ；PET：10-20份；邻甲基苯二醇：1-5份 ；硫酸铵：1-5份；氧化苯甲酸叔丁基：1-5份 ；固化剂：0.5-2份 ；月桂酸：0.5-2份；碳粉：0.5-2份；铁粉：5-15份。
具体地，由以下重量份的组分制备而成：
Fe2O3：60-70份；MnO：20-25份；ABS树脂：15-18份 ；PET：15-18份；邻甲基苯二醇：3份 ；硫酸铵：3份；氧化苯甲酸叔丁基：3份 ；固化剂：1份 ；月桂酸：1份；碳粉：1份；铁粉：10份。
磁性耐热塑料合金材料的制备方法，包括如下步骤：
（1）预混合：按照比例称取各有机组分，充分混合搅匀，加热保温50摄氏度静置密封放置24小时；
（2）混合：在上述材料中加入Fe2O3、MnO、碳粉、铁粉搅拌均匀，温度为500摄氏度下保持36小时；
（3）成型：将上述原料放入已预热至200℃的模具中，冷却后制得产品。
本发明具有以下有益效果：
本发明提高了磁性塑料合金的的耐热温度，真正保证了材料硫化的充分进行，在高温下该材料克服了因硫化不完全发生链段的降解，进而导致性能迅速劣化，不宜在高温下使用的缺点，使得材料适于在高温及要求高力学性能的环境下使用。
具体实施方式
实施例1
一种磁性耐热塑料合金材料，由以下重量份的组分制备而成：
Fe2O3：50份；MnO：10份；ABS树脂：10份 ；PET：10份；邻甲基苯二醇：1份 ；硫酸铵：1份；氧化苯甲酸叔丁基：1份 ；固化剂：0.5份 ；月桂酸：0.5份；碳粉：0.5份；铁粉：5份。
磁性耐热塑料合金材料的制备方法，包括如下步骤：
（1）预混合：按照比例称取各有机组分，充分混合搅匀，加热保温50摄氏度静置密封放置24小时；
（2）混合：在上述材料中加入Fe2O3、MnO、碳粉、铁粉搅拌均匀，温度为500摄氏度下保持36小时；
（3）成型：将上述原料放入已预热至200℃的模具中，冷却后制得产品。
实施例2
一种磁性耐热塑料合金材料，由以下重量份的组分制备而成：
Fe2O3： 80份；MnO： 30份；ABS树脂： 20份 ；PET： 20份；邻甲基苯二醇： 5份 ；硫酸铵： 5份；氧化苯甲酸叔丁基： 5份 ；固化剂：2份 ；月桂酸： 2份；碳粉： 2份；铁粉： 15份。
磁性耐热塑料合金材料的制备方法，包括如下步骤：
（1）预混合：按照比例称取各有机组分，充分混合搅匀，加热保温50摄氏度静置密封放置24小时；
（2）混合：在上述材料中加入Fe2O3、MnO、碳粉、铁粉搅拌均匀，温度为500摄氏度下保持36小时；
（3）成型：将上述原料放入已预热至200℃的模具中，冷却后制得产品。
实施例3
一种磁性耐热塑料合金材料，由以下重量份的组分制备而成：
Fe2O3：65份；MnO：22份；ABS树脂：16份 ；PET：16份；邻甲基苯二醇：3份；硫酸铵：3份；氧化苯甲酸叔丁基：3份 ；固化剂：1份 ；月桂酸：1份；碳粉：1份；铁粉：10份。
磁性耐热塑料合金材料的制备方法，包括如下步骤：
（1）预混合：按照比例称取各有机组分，充分混合搅匀，加热保温50摄氏度静置密封放置24小时；
（2）混合：在上述材料中加入Fe2O3、MnO、碳粉、铁粉搅拌均匀，温度为500摄氏度下保持36小时；
（3）成型：将上述原料放入已预热至200℃的模具中，冷却后制得产品。
本发明提高了磁性塑料合金的的耐热温度，真正保证了材料硫化的充分进行，在高温下该材料克服了因硫化不完全发生链段的降解，进而导致性能迅速劣化，不宜在高温下使用的缺点，使得材料适于在高温及要求高力学性能的环境下使用。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (3)

1.一种磁性耐热塑料合金材料，其特征在于，由以下重量份的组分制备而成：
Fe2O3：50-80份；MnO：10-30份；ABS树脂：10-20份 ；PET：10-20份；邻甲基苯二醇：1-5份 ；硫酸铵：1-5份；氧化苯甲酸叔丁基：1-5份 ；固化剂：0.5-2份 ；月桂酸：0.5-2份；碳粉：0.5-2份；铁粉：5-15份。
2.根据权利要求1所述的磁性耐热塑料合金材料，其特征在于，由以下重量份的组分制备而成：
Fe2O3：60-70份；MnO：20-25份；ABS树脂：15-18份 ；PET：15-18份；邻甲基苯二醇：3份 ；硫酸铵：3份；氧化苯甲酸叔丁基：3份 ；固化剂：1份 ；月桂酸：1份；碳粉：1份；铁粉：10份。
3.权利要求1或2所述的磁性耐热塑料合金材料的制备方法，包括如下步骤：
（1）预混合：按照比例称取各有机组分，充分混合搅匀，加热保温50摄氏度静置密封放置24小时；
（2）混合：在上述材料中加入Fe2O3、MnO、碳粉、铁粉搅拌均匀，温度为500摄氏度下保持36小时；
（3）成型：将上述原料放入已预热至200℃的模具中，冷却后制得产品。
CN201210471437.4A 2012-11-20 2012-11-20 一种磁性耐热塑料合金材料及其制备方法 Expired - Fee Related CN102964770B (zh)