CN102964699B - 一种煅烧陶土改性的三元乙丙橡胶电缆料 - Google Patents

一种煅烧陶土改性的三元乙丙橡胶电缆料 Download PDF

Info

Publication number
CN102964699B
CN102964699B CN201210454815.8A CN201210454815A CN102964699B CN 102964699 B CN102964699 B CN 102964699B CN 201210454815 A CN201210454815 A CN 201210454815A CN 102964699 B CN102964699 B CN 102964699B
Authority
CN
China
Prior art keywords
modification
calcinated argil
rubber
mixing
age resistor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210454815.8A
Other languages
English (en)
Other versions
CN102964699A (zh
Inventor
沈必亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Chunhui Instrument Cable Group Co Ltd
Original Assignee
Anhui Chunhui Instrument Cable Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Chunhui Instrument Cable Group Co Ltd filed Critical Anhui Chunhui Instrument Cable Group Co Ltd
Priority to CN201210454815.8A priority Critical patent/CN102964699B/zh
Publication of CN102964699A publication Critical patent/CN102964699A/zh
Application granted granted Critical
Publication of CN102964699B publication Critical patent/CN102964699B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种煅烧陶土改性的三元乙丙橡胶电缆料，由下列重量份的原料制成：德国朗盛三元乙丙橡胶3950？100-120、丁腈橡胶N41？20-30、氯磺化聚乙烯橡胶CSM2305？10-15、邻苯二甲酸二异癸酯10-15、环氧化甘油三酸酯2-5、柠檬酸三乙酯2-5、氯化石蜡5-8、硬脂酸0.5-1.0份、硬脂酸钙2-3、硫磺1-2、氧化锌3-5、煅烧陶土30-40等。本发明电缆料不仅具有优异的阻燃性和不延燃性，而且同时还具有良好的耐高低温性、耐腐蚀性、耐水性、耐磨性、耐臭氧、耐老化等优点，经久耐用。

Description

一种煅烧陶土改性的三元乙丙橡胶电缆料
技术领域
本发明涉及电缆料领域，具体涉及一种煅烧陶土改性的三元乙丙橡胶电缆料。
背景技术
自从1962年三元乙丙橡胶(EPDM)问世以来，就因其优良的耐臭氧、耐天候老化和耐热老化性能以及良好的电绝缘性、耐热变形和耐化学品腐蚀等性能，相对密度小，填充量大，受到电缆工业的重视。目前，它已替代传统的丁苯、天然、丁基橡胶，在船用及移动用低、中压电缆上得到广泛的应用。但同大多数碳氢高分子化合物一样，三元乙丙橡胶也很易燃烧，纯胶的氧指数只有19左右。因此，开发研制阻燃的三元乙丙橡胶电缆料，受到电缆行业的重视。
发明内容
本发明的目的是针对现有技术的不足，提供了一种煅烧陶土改性的三元乙丙橡胶电缆料。由本发明的电缆料加工成的电缆线具有耐高低温性能好，耐腐蚀性能好，耐水性、耐臭氧、耐老化，阻燃性能好。
本发明采用的技术方案为：
一种煅烧陶土改性的三元乙丙橡胶电缆料，由下列重量份的原料制成：德国朗盛三元乙丙橡胶3950100-120、丁腈橡胶N4120-30、氯磺化聚乙烯橡胶CSM230510-15、邻苯二甲酸二异癸酯10-15份、环氧化甘油三酸酯2-5、柠檬酸三乙酯2-5、氯化石蜡5-8、硬脂酸0.5-1.0、硬脂酸钙2-3、硫磺1-2、氧化锌3-5、煅烧陶土30-40、沉淀白炭黑20-30、炭黑N6605-15、硼酸锌3-5、铝酸酯偶联剂DL-4111-2、抗紫外剂UV-5310.1-1、交联剂TAIC1-2、3-氨丙基三甲氧基硅烷1-2、防老剂OD1-2、防老剂ODA1-2、防老剂TPPD1-2、促进剂Na-221-2、促进剂DM3-4、改性树木灰烬2-3。
所述的改性树木灰烬由以下方法制得：先用10-15%盐酸浸泡树木灰烬2-3h后，再用去离子水洗涤至中性，烘干；加入相当于树木灰烬重量2-3%的玻化微珠、1-2%的聚乙二醇200、2-3%的月桂醇硫酸钠、3-5%的氢氧化镁，高速4500-4800r/min搅拌20-30min，烘干粉碎成超细粉末。
煅烧陶土改性的三元乙丙橡胶电缆料的制备方法，包括以下步骤：
（1）按配方比例将德国朗盛三元乙丙橡胶3950、丁腈橡胶N41、氯磺化聚乙烯橡胶CSM2305和防老剂类投入开炼机，在75-85℃下混炼4-5min；
（2）将煅烧陶土、沉淀白炭黑、炭黑N660等填料加入到步骤（1）的混炼胶中，继续混炼2-3min后，将除硫化剂、促进剂外的剩下的物料加入到混炼料中，混炼4-6min后，再加入硫化剂、促进剂，薄通6-7次后，挤塑机塑化造粒，即可，挤塑机的挤出温度为155-175℃。
本发明的有益效果：
本发明通过对树木灰烬进行改性，可以改善电缆料的阻燃性和耐热性，并具有成本低，效果优良的特点。本发明通过对配方调整，添加了煅烧陶土，对电缆料有一定的补强作用，可提高电缆料的定伸应力、硬度、强度和耐磨性。本发明电缆料不仅具有优异的阻燃性和不延燃性，而且同时还具有良好的耐高低温性、耐腐蚀性、耐水性、耐磨性、耐臭氧、耐老化等优点，经久耐用。
具体实施方式
实施例
一种煅烧陶土改性的三元乙丙橡胶电缆料，由下列重量份的原料制成：德国朗盛三元乙丙橡胶3950108份、丁腈橡胶N4124份、氯磺化聚乙烯橡胶CSM230512份、邻苯二甲酸二异癸酯15份、环氧化甘油三酸酯4份、柠檬酸三乙酯3份、氯化石蜡6份、硬脂酸0.8份、硬脂酸钙3份、硫磺1.5份、氧化锌4份、煅烧陶土35份、沉淀白炭黑22份、炭黑N6608份、硼酸锌4份、铝酸酯偶联剂DL-4111.6份、抗紫外剂UV-5310.6份、交联剂TAIC1.8份、3-氨丙基三甲氧基硅烷1.5份、防老剂OD1.2份、防老剂ODA1.8份、防老剂TPPD1.5份、促进剂Na-222份、促进剂DM3份、改性树木灰烬3份。
其中，所述的改性树木灰烬由以下方法制得：先用12%盐酸浸泡树木灰烬3h后，再用去离子水洗涤至中性，烘干；加入相当于树木灰烬重量3%的玻化微珠、2%的聚乙二醇200、3%的月桂醇硫酸钠、5%的氢氧化镁，高速4500r/min搅拌30min，烘干粉碎成超细粉末。
煅烧陶土改性的三元乙丙橡胶电缆料的制备方法，包括以下步骤：
（1）按配方比例将德国朗盛三元乙丙橡胶3950、丁腈橡胶N41、氯磺化聚乙烯橡胶CSM2305和防老剂类投入开炼机，在78℃下混炼5min；
（2）将煅烧陶土、沉淀白炭黑、炭黑N660等填料加入到步骤（1）的混炼胶中，继续混炼3min后，将除硫化剂、促进剂外的剩下的物料加入到混炼料中，混炼5min后，再加入硫化剂、促进剂，薄通7次后，挤塑机塑化造粒，即可，挤塑机的挤出温度为164℃。
本发明的电缆料的性能测试结果如下：

Claims (1)

1.一种煅烧陶土改性的三元乙丙橡胶电缆料，其特征在于，由下列重量份的原料制成：德国朗盛三元乙丙橡胶3950100-120、丁腈橡胶N4120-30、氯磺化聚乙烯橡胶CSM230510-15、邻苯二甲酸二异癸酯10-15、环氧化甘油三酸酯2-5、柠檬酸三乙酯2-5、氯化石蜡5-8、硬脂酸0.5-1.0份、硬脂酸钙2-3、硫磺1-2、氧化锌3-5、煅烧陶土30-40、沉淀白炭黑20-30、炭黑N6605-15、硼酸锌3-5、铝酸酯偶联剂DL-4111-2、抗紫外剂UV-5310.1-1、交联剂TAIC1-2、3-氨丙基三甲氧基硅烷1-2、防老剂OD1-2、防老剂ODA1-2、防老剂TPPD1-2、促进剂Na-221-2、促进剂DM3-4、改性树木灰烬2-3；
所述的改性树木灰烬由以下方法制得：先用10-15%盐酸浸泡树木灰烬2-3h后，再用去离子水洗涤至中性，烘干；加入相当于树木灰烬重量2-3%的玻化微珠、1-2%的聚乙二醇200、2-3%的月桂醇硫酸钠、3-5%的氢氧化镁，高速4500-4800r/min搅拌20-30min，烘干粉碎成超细粉末；
所述的煅烧陶土改性的三元乙丙橡胶电缆料的制备方法，包括以下步骤：
（1）按配方比例将德国朗盛三元乙丙橡胶3950、丁腈橡胶N41、氯磺化聚乙烯橡胶CSM2305和防老剂类投入开炼机，在75-85℃下混炼4-5min；
（2）将煅烧陶土、沉淀白炭黑、炭黑N660加入到步骤（1）的混炼胶中，继续混炼2-3min后，将除硫化剂、促进剂外的剩下的物料加入到混炼料中，混炼4-6min后，再加入硫化剂、促进剂，薄通6-7次后，挤塑机塑化造粒，即可，挤塑机的挤出温度为155-175℃。
CN201210454815.8A 2012-11-13 2012-11-13 一种煅烧陶土改性的三元乙丙橡胶电缆料 Active CN102964699B (zh)