CN102926014A - 一种纤维素粘胶纤维的生产工艺 - Google Patents

一种纤维素粘胶纤维的生产工艺 Download PDF

Info

Publication number
CN102926014A
CN102926014A CN2012104287158A CN201210428715A CN102926014A CN 102926014 A CN102926014 A CN 102926014A CN 2012104287158 A CN2012104287158 A CN 2012104287158A CN 201210428715 A CN201210428715 A CN 201210428715A CN 102926014 A CN102926014 A CN 102926014A
Authority
CN
China
Prior art keywords
dipping
production process
cobalt chloride
cellulose
viscose fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104287158A
Other languages
English (en)
Other versions
CN102926014B (zh
Inventor
司玉莲
朱胜涛
尹利宾
张丽萍
邵长金
刘东奇
姚永新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xinxiang Chemical Fiber Co Ltd
Original Assignee
Xinxiang Chemical Fiber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xinxiang Chemical Fiber Co Ltd filed Critical Xinxiang Chemical Fiber Co Ltd
Priority to CN201210428715.8A priority Critical patent/CN102926014B/zh
Publication of CN102926014A publication Critical patent/CN102926014A/zh
Application granted granted Critical
Publication of CN102926014B publication Critical patent/CN102926014B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种纤维素粘胶纤维的生产工艺，包括混粨、浸渍、压榨、粉碎、黄化、溶解、过滤、熟成和纺丝工序，所述浸渍工序中的浸渍液中加入有氯化钴，所述氯化钴加入质量为甲种纤维素质量的（2.0-4.0）×10－4%，浸渍温度为48±1℃或55±1℃，在粉碎工序与黄化工序设备之间采用风送管路或皮运机连接。本发明与现有技术比较具有设备投资少、占地面积小和运行成本低的显著优点。

Description

一种纤维素粘胶纤维的生产工艺
 
技术领域：
本发明涉及一种纤维素生产工艺，特别是一种纤维素粘胶纤维的生产工艺。
背景技术：
传统的纤维素粘胶纤维的生产工艺中有一道老成降解工序，此降解工序用的设备为老成鼓或老成箱，这种设备体积庞大，占生产面积达，价格贵且运行费用高。
发明内容：
本发明的目的是提供一种设备投资小、占地面积小和运行成本低的一种纤维素粘胶纤维的生产工艺。
实现本发明目的的技术方案是，一种纤维素粘胶纤维的生产工艺，包括混粨、浸渍、压榨、粉碎、黄化、溶解、过滤、熟成和纺丝工序，其特征在于：所述浸渍工序中的浸渍液中加入有氯化钴，所述氯化钴加入质量为甲种纤维素质量的（2.0-4.0）×10－4%，浸渍温度为48±1℃或55±1℃，在粉碎工序与黄化工序设备之间采用风送管路或皮运机连接。
本发明与现有技术比较具有设备投资少、占地面积小和运行成本低的显著优点。
具体实施方式：
通过实验发现在粘胶纤维生产过程中通过加入适量催化剂，便可取消原生产工艺中的老成工序和老成用设备，所用催化剂可选用氯化钴，其加入量为甲种纤维素质量的（2.0-4.0）×10－4%。氯化钴加入到浸渍工序的浸渍液中，并适当提浸渍工序的浸渍温度，加速甲种纤维素的降解。本发明实施例：
实施例1、
单线生产能力为4000吨∕年，在浸渍工序中加入氯化钴的量为甲种纤维素质量的（1.0-2.0）×10－4%，浸渍温度为55±1℃，而原生产工艺的工序混粨（混合不同批次的甲种纤维素浆粨），压榨粉碎、黄化、溶解、过滤、熟成和纺丝不改变。这种新工艺省去了老成工序和老成设备，节省了设备投资、生产面积和老成设备运转的能耗，所增加的氯化钴由于加入量很少，浸渍温度的增高幅度较小（近5℃左右），因而总合费用节约明显，切缩短了生产周期。而所生产的产品的颜色、成品的百度均与老工艺相同，可纺性能正常。取消的老成设备采用常规的风送管路或皮运机代替。
实施例2、
单线生产能力为3000吨∕年，氯化钴的加入质量为甲种纤维素质量的（2.0-4.0）×10－4%，此氯化钴加入到浸渍工序的浸渍液中，浸渍液温度为48±1℃，采用风送管路或皮运机代替原老成设备，而混粨、浸渍、压榨、粉碎、黄化、溶解、过滤、熟成和纺丝不改变，所产生出的粘胶的过滤度为160左右，产品颜色正常、可纺性正常。

Claims (1)

1. 一种纤维素粘胶纤维的生产工艺，包括混粨、浸渍、压榨、粉碎、黄化、溶解、过滤、熟成和纺丝工序，其特征在于：所述浸渍工序中的浸渍液中加入有氯化钴，所述氯化钴加入质量为甲种纤维素质量的（2.0-4.0）×10－4%，浸渍温度为48±1℃或55±1℃，在粉碎工序与黄化工序设备之间采用风送管路或皮运机连接。
CN201210428715.8A 2012-11-01 2012-11-01 一种纤维素粘胶纤维的生产工艺 Active CN102926014B (zh)