CN102888117A - 高硬度混炼硅橡胶组合物及制备工艺 - Google Patents
高硬度混炼硅橡胶组合物及制备工艺 Download PDFInfo
- Publication number
- CN102888117A CN102888117A CN2012103426632A CN201210342663A CN102888117A CN 102888117 A CN102888117 A CN 102888117A CN 2012103426632 A CN2012103426632 A CN 2012103426632A CN 201210342663 A CN201210342663 A CN 201210342663A CN 102888117 A CN102888117 A CN 102888117A
- Authority
- CN
- China
- Prior art keywords
- preparation technology
- mixing
- rubber
- rubber composition
- hardness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种高硬度混炼硅橡胶组合物及制备工艺，其特征在于：a. 将甲基乙烯基硅橡胶生胶加入硅油、乙烯基三乙氧基硅烷、白炭黑、硅藻土，在捏合机中混炼均匀，在160℃下继续混炼2小时，配成胶料；b. 将胶料与二叔丁基过氧化物在双辊炼胶机上混合均匀，在160℃、30MPa条件下硫化10分钟，再在200℃烘箱中二次硫化4h即可。本发明的组合物制备的低硬度混炼硅橡胶性能好，制备工艺简单，成品的绍尔A硬度在60度以上。
Description
技术领域
本发明涉及橡胶技术领域，具体涉及一种高硬度混炼硅橡胶组合物及制备工艺。
背景技术
硅橡胶（英文名称Silicone rubber），分热硫化型（高温硫化硅胶HTV）、室温硫化型（RTV），其中室温硫化型又分缩聚反应型和加成反应型。高温硅橡胶主要用于制造各种硅橡胶制品，而室温硅橡胶则主要是作为粘接剂、灌封材料或模具使用。热硫化型用量最大，热硫化型又分甲基硅橡胶、甲基乙烯基硅橡胶、甲基乙烯基苯基硅橡胶，其他还有睛硅橡胶、氟硅橡胶等。在众多的合成橡胶中，硅橡胶是在其中的佼佼者。它具有无味无毒，不怕高温和抵御严寒的特点，在三百摄氏度和零下九十摄氏度时“泰然自若”、“面不改色”，仍不失原有的强度和弹性。硅橡胶还有良好的电绝缘性、耐氧抗老化性、耐光抗老化性以及防霉性、化学稳定性等。由于具有了这些优异的性能，使得硅橡胶在现代医学中广泛发挥了重要作用。近年来，由医院、科研单位和工厂共同协作，试制成功了多种硅橡胶医疗用品。而传统的高硬度混炼硅橡胶性能不好，制备工艺较为复杂。
发明内容
本发明所要解决的技术问题在于提供一种制备简单，性能好的高硬度混炼硅橡胶组合物及制备工艺。
本发明所要解决的技术问题采用以下技术方案来实现：
一种高硬度混炼硅橡胶组合物，其特征在于：所述的组合物由以下质量份的组分组成，
一种高硬度混炼硅橡胶组合物制备工艺，其特征在于：
1）将甲基乙烯基硅橡胶生胶加入硅油、乙烯基三乙氧基硅烷、白炭黑、硅藻土，在捏合机中混炼均匀，在160℃下继续混炼2小时，配成胶料；
2）将胶料与二叔丁基过氧化物在双辊炼胶机上混合均匀，在160℃、30MPa条件下硫化10分钟，再在200℃烘箱中二次硫化4h即可。
本发明的有益效果是：本发明的组合物制备的低硬度混炼硅橡胶性能好，制备工艺简单，成品的绍尔A硬度在60度以上。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
一种高硬度混炼硅橡胶组合物及制备工艺，制备绍尔A硬度在60度以上的混炼硅橡胶通常是采取调节生胶的交联密度、增加补强填料或 增量填料用量的方法配制。在100份甲基乙烯基硅橡胶生胶中加入20份运动粘度50mm/2s的硅油、0.3份乙烯基三乙氧基硅烷、40份沉淀法白炭黑、30份硅藻土，在捏合机中混炼均匀；160℃下继续混炼2h配成胶料。
将胶料在双辊炼胶机上与0.6份二叔丁基过氧化物混炼均匀；160℃、30MPa条件下硫化10mim，再在200℃烘箱中二次硫化4h即可。测其性能为；绍尔A硬度70度，拉伸强度8.0MPa,伸长率达到230%。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.高硬度混炼硅橡胶组合物，其特征在于：所述的组合物由以下质量份的组分组成，
2.高硬度混炼硅橡胶组合物的制备工艺，其特征在于：
a. 将甲基乙烯基硅橡胶生胶加入硅油、乙烯基三乙氧基硅烷、白炭黑、硅藻土，在捏合机中混炼均匀，在160℃下继续混炼2小时，配成胶料；
b. 将胶料与二叔丁基过氧化物在双辊炼胶机上混合均匀，在160℃、30MPa条件下硫化10分钟，再在200℃烘箱中二次硫化4h即可。