CN102851996A - 表面抗磨耗人造革制造方法 - Google Patents

表面抗磨耗人造革制造方法 Download PDF

Info

Publication number
CN102851996A
CN102851996A CN2011101752647A CN201110175264A CN102851996A CN 102851996 A CN102851996 A CN 102851996A CN 2011101752647 A CN2011101752647 A CN 2011101752647A CN 201110175264 A CN201110175264 A CN 201110175264A CN 102851996 A CN102851996 A CN 102851996A
Authority
CN
China
Prior art keywords
wear
artificial leather
manufacture method
resistant surface
embossing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101752647A
Other languages
English (en)
Inventor
赵建明
成峰
陆勤中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KUNSHAN ACHILLES ARTIFICIAL LEATHER CO Ltd
Original Assignee
KUNSHAN ACHILLES ARTIFICIAL LEATHER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KUNSHAN ACHILLES ARTIFICIAL LEATHER CO Ltd filed Critical KUNSHAN ACHILLES ARTIFICIAL LEATHER CO Ltd
Priority to CN2011101752647A priority Critical patent/CN102851996A/zh
Publication of CN102851996A publication Critical patent/CN102851996A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种表面抗磨耗人造革制造方法，将聚氯乙烯树脂100份、增塑剂30～100份、填料10～80份、润滑剂0.5～1份、耐热稳定剂2～5份、颜料3～5份、调整剂1～10份、加工助剂3～15份和耐磨改性材料30～50份经高速分散混合机在120～130℃搅拌100～200s；然后经密炼机在130～150℃混炼时间200～300s；至炼胶机在120～130℃塑炼10～20min；再将其在160～180℃压延成0.2～0.4mm的片材，将片材和压延基材贴合，贴合压力≥1T；然后将其送入发泡机在190～200℃发泡、压花，最后冷却定型；本发明使得人造革表面产生耐磨耗特性，不易磨花、使用寿命长。

Description

表面抗磨耗人造革制造方法
技术领域
本发明涉及一种人造革制造方法，特别涉及一种表面抗磨耗人造革制造方法。
背景技术
传统的人造革表面容易磨花、磨破，在地板革和脚踏等产品的使用上，需要经常更换，给使用成本高，反复更换给使用者带来很多麻烦。
发明内容
为了克服上述缺陷，本发明提供了一种表面抗磨耗人造革制造方法，该表面抗磨耗人造革制造方法工艺简单、表面耐磨、使用寿命长，使用成本低。
本发明为了解决其技术问题所采用的技术方案是：一种表面抗磨耗人造革制造方法，具体步骤如下：
步骤一：混合配料：将聚氯乙烯树脂100重量份、增塑剂30～100重量份、填料10～80重量份、润滑剂0.5～1重量份、耐热稳定剂2～5重量份、颜料3～5重量份、调整剂1～10重量份、加工助剂3～15重量份和耐磨改性材料30～50重量份在高速分散混合机里混合均匀，搅拌温度120℃～130℃，搅拌时间100s～200s；
步骤二：混炼：将步骤一中混合均匀的物料排入密炼机里进行混炼，混炼温度130℃～150℃，混炼时间200s～300s；
步骤三：塑炼：将混炼完成的物料排出至炼胶机上，通过炼胶机在120℃～130℃的温度条件下进行塑炼10min～20min；
步骤四：压延成型：将塑炼完成的物料输送至压延机里压延成厚度在0.2mm～0.4mm的片材，压延机作业条件温度为160℃～180℃，生产速度20m/min～40m/min；
步骤五：基材贴合：将压延成型的片材和压延基材进行贴合(具体贴合的位置根据设计要求进行)，贴合压力≥1T；
步骤六：发泡压花：将压延贴合后的半成品送入发泡机加热到190℃～200℃发泡，然后在热的状态下对产品进行压花，然后对压花后的产品冷却定型；压花生产速度10m/min～20m/min。
该种方法生产出的人造革表面耐磨，不易磨花，使用寿命长。
作为本发明的进一步改进，步骤一中混合配料的搅拌时间为150s。
作为本发明的进一步改进，步骤二中混炼时间为250s。
作为本发明的进一步改进，步骤三中塑炼时间为15min。
作为本发明的进一步改进，步骤三中所用炼胶机为开放式炼胶机。
作为本发明的进一步改进，步骤四中所用压延机为四辊压延机。
作为本发明的进一步改进，步骤五中基材贴合的生产速度为30m/min。
作为本发明的进一步改进，步骤五中所用基材为聚氯乙烯材料(PVC)的压延基材。
作为本发明的进一步改进，步骤六中压花的生产速度为15m/min。
作为本发明的进一步改进，步骤六中通过在压花辊中通冷却水的方法对压花后的产品冷却定型，该方法冷却速度快，冷却均匀。
本发明的有益效果是：本发明使得人造革表面产生耐磨耗特性，在使用过程中不易磨花、使用寿命长，适用于地板革、脚踏垫等产品，使用时不需经常更换，降低了使用成本。
具体实施方式
实施例：一种表面抗磨耗人造革制造方法，具体步骤如下：
步骤一：混合配料：将聚氯乙烯树脂100重量份、增塑剂30～100重量份、填料10～80重量份、润滑剂0.5～1重量份、耐热稳定剂2～5重量份、颜料3～5重量份、调整剂1～10重量份、加工助剂3～15重量份和耐磨改性材料30～50重量份在高速分散混合机里混合均匀，搅拌温度120℃～130℃，搅拌时间100s～200s；
步骤二：混炼：将步骤一中混合均匀的物料排入密炼机里进行混炼，混炼温度130℃～150℃，混炼时间200s～300s；
步骤三：塑炼：将混炼完成的物料排出至炼胶机上，通过炼胶机在120℃～130℃的温度条件下进行塑炼10min～20min；
步骤四：压延成型：将塑炼完成的物料输送至压延机里压延成厚度在0.2mm～0.4mm的片材，压延机作业条件温度为160℃～180℃，生产速度20m/min～40m/min；
步骤五：基材贴合：将压延成型的片材和压延基材进行贴合(具体贴合的位置根据设计要求进行)，贴合压力≥1T；
步骤六：发泡压花：将压延贴合后的半成品送入发泡机加热到190℃～200℃发泡，然后在热的状态下对产品进行压花，然后对压花后的产品冷却定型；压花生产速度10m/min～20m/min。
该种方法生产出的人造革表面耐磨，不易磨花，使用寿命长。
所述步骤一中混合配料的搅拌时间为150s。
所述步骤二中混炼时间为250s。
所述步骤三中塑炼时间为15min。
所述步骤三中所用炼胶机为开放式炼胶机。
所述步骤四中所用压延机为四辊压延机。
所述步骤五中基材贴合的生产速度为30m/min。
所述步骤五中所用基材为聚氯乙烯材料(PVC)的压延基材。
所述步骤六中压花的生产速度为15m/min。
所述步骤六中通过在压花辊中通冷却水的方法对压花后的产品冷却定型，该方法冷却速度快，冷却均匀。

Claims (10)

1.一种表面抗磨耗人造革制造方法，其特征在于：具体步骤如下：
步骤一：混合配料：将聚氯乙烯树脂100重量份、增塑剂30～100重量份、填料10～80重量份、润滑剂0.5～1重量份、耐热稳定剂2～5重量份、颜料3～5重量份、调整剂1～10重量份、加工助剂3～15重量份和耐磨改性材料30～50重量份在高速分散混合机里混合均匀，搅拌温度120℃～130℃，搅拌时间100s～200s；
步骤二：混炼：将步骤一中混合均匀的物料排入密炼机里进行混炼，混炼温度130℃～150℃，混炼时间200s～300s；
步骤三：塑炼：将混炼完成的物料排出至炼胶机上，通过炼胶机在120℃～130℃的温度条件下进行塑炼10min～20min；
步骤四：压延成型：将塑炼完成的物料输送至压延机里压延成厚度在0.2mm～0.4mm的片材，压延机作业条件温度为160℃～180℃，生产速度20m/min～40m/min；
步骤五：基材贴合：将压延成型的片材和压延基材进行贴合，贴合压力≥1T；
步骤六：发泡压花：将压延贴合后的半成品送入发泡机加热到190℃～200℃发泡，然后在热的状态下对产品进行压花，然后对压花后的产品冷却定型；压花生产速度10m/min～20m/min。
2.根据权利要求1所述的表面抗磨耗人造革制造方法，其特征在于：步骤一中混合配料的搅拌时间为150s。
3.根据权利要求1所述的表面抗磨耗人造革制造方法，其特征在于：步骤二中混炼时间为250s。
4.根据权利要求1所述的表面抗磨耗人造革制造方法，其特征在于：步骤三中塑炼时间为15min。
5.根据权利要求1所述的表面抗磨耗人造革制造方法，其特征在于：步骤三中所用炼胶机为开放式炼胶机。
6.根据权利要求1所述的表面抗磨耗人造革制造方法，其特征在于：步骤四中所用压延机为四辊压延机。
7.根据权利要求1所述的表面抗磨耗人造革制造方法，其特征在于：步骤五中基材贴合的生产速度为30m/min。
8.根据权利要求1所述的表面抗磨耗人造革制造方法，其特征在于：步骤五中所用基材为聚氯乙烯材料的压延基材。
9.根据权利要求1所述的表面抗磨耗人造革制造方法，其特征在于：步骤六中压花的生产速度为15m/min。
10.根据权利要求1所述的表面抗磨耗人造革制造方法，其特征在于：步骤六中通过在压花辊中通冷却水的方法对压花后的产品冷却定型。
CN2011101752647A 2011-06-27 2011-06-27 表面抗磨耗人造革制造方法 Pending CN102851996A (zh)